• Journal of the Korean institute of surface engineering
• /
• v.49 no.3
• /
• pp.245-251
• /
• 2016

Galvanizing method has been extensively used to the numerous constructional steels such as a guard rail of high way, various types of structural steel for ship building and various types of steels for the industrial fields etc.. However, the galvanized structures would be inevitably corroded rapidly with increasing exposed time because an acid rain due to environmental contamination has been much dropped more and more. Therefore, it has been made an effort to improve the corrosion resistance of the galvanizing film through various methods. In this study, comparison evaluation on the corrosion resistance of three types of the samples, that is, the hot dip galvanizing with pure zinc(GI), the hot dip galvanizing of alloy bath with zinc and aluminum(GL) and the pure zinc galvanizing steel immersed again to chromate treatment bath(Chro.)were investigated using electrochemical methods in 1% $H_2SO_4$ solution. The Chro. and GI samples exhibited the highest and lowest corrosion resistance respectively in 1% $H_2SO_4$ solution, however, the GI sample revealed the highest impedance at 0.01 Hz due to its high resistance polarization caused by corrosion products deposited on the surface, while Chro. sample exhibited the lowest impedance at 0.01 Hz because of little corrosion products on the surface. Consequently, it is suggested that the chromate treated steel has a better corrosion resistance in acid environment compared to pure galvanizing(GI) or galvalume(GL) steels.

• Corrosion Science and Technology
• /
• v.8 no.1
• /
• pp.40-43
• /
• 2009

We investigated the corrosion resistance of Zn and Cu coated steel pipes as a substitute for Cu pipe in an air-conditioner system. In addition, the galvanic corrosion tendency between two dissimilar metal parts was studied. The corrosion resistance of the Cu electroplated steel was similar to that of Cu, while the corrosion rate of the Zn electro- galvanized and the galvalume (Zn-55 % Al) coated steels was much higher and not suitable for Cu substitute in artificial sea water and acidic rain environments. Furthermore, the galvanic difference between Cu electroplated steel and Cu was so small that the Cu coated steel pipe can be used as a substitute for Cu pipe in an air-conditioner system.

• Corrosion Science and Technology
• /
• v.9 no.3
• /
• pp.116-121
• /
• 2010

For over a decade, research and development on submerged hardware in continuous galvanizing pots has been carried out at Teck's Product Technology Centre. The outcome of numerous laboratory tests and field trials has demonstrated that dissimilar materials with comparable surface hardness are most suitable for the manufacture of roll bearings. Wear debris can be easily retained in bearings made of the same material, thereby negatively affecting bearing performance and service life. Bearings made of the same materials are also vulnerable to catastrophic failures. The dissolution of iron from the coated strip creates an iron-rich zone associated with a high concentration gradient in the vicinity of the sink roll. Consequently, the sink roll becomes a preferential site for dross pick-up. In operations involving extremely high temperatures, such as in Galvalume production, the material selection for pot hardware is immaterial to the final corrosion product of the hardware and the pick-up on the hardware.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.25 no.10
• /
• pp.109-115
• /
• 2011

Apartments covered with a metal roof made from galvalume steel are prevailing due to their economic and technical advantages. The metal roof, however, has disadvantages in terms of the installation of air-termination system on it because of the slip thickness of the metal roof. In this paper, the impacts of the lightning current to a metal roof were verified experimentally with a short lightning impulse current (10/350[${\mu}s$]). Also, we developed various supporters of air-termination conductor for the metal roof and verified their excellent workability and economical strength through field application test.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.298-298
• /
• 2012

갈바륨 강판은 주로 건자재나 가전용으로 많이 사용되는 알루미늄-아연 합금도금강판이다. 최근 환경 규제로 인하여 아연도금강판의 후처리에 크롬이 배제되고 있는 추세에 힘입어, 가전용 갈바륨 강판에도 크롬프리 후처리제가 많이 사용되고 있는 추세이다. 반면에, 건자재용으로 사용되는 갈바륨 강판은 고내식성 및 내후성을 필요로 하여 크롬이 함유된 후처리제를 사용하고 있으며, 아직까지는 환경규제 대상으로 지정되어 있지 않다. 본 연구에서는 가전용 및 건재용 물성을 동시에 만족시킬 수 있는 통합형 크롬프리 갈바륨 강판을 개발하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.163-163
• /
• 2016

아연계 도금 강판은 우수한 내식성을 가지며 특히 아연의 희생방식기구에 의해 철의 부식을 억제하므로 선박, 건축자재, 전자기기 및 자동차 등 다양한 분야에서 그 수요와 사용범위가 증가하고 있다. 또한 도금 조성비 변화 및 다양한 표면처리 방법을 통해 가혹한 환경에서의 우수한 내식성에 대한 연구가 활발히 진행되고 있다. 그 중 갈바륨(Galvalume)은 55%의 알루미늄(Al)과 45%의 아연(Zn)으로 되어 있으며, 아연의 장점인 희생방식성과 내알카리성, 알루미늄의 장점인 내구성과 내열성, 내산성을 이상적으로 결합시킨 알루미늄(Al)-아연(Zn) 고내식 합금용융도금강판이다. 본 연구에서는 갈바륨 소재를 여러 산업현장에서 강관 형태로 사용할 경우의 내식성을 파악하기 위해 갈바륨 강관과 기존에 사용되고 있는 용융도금재인 용융아연도금 강관을 비교하며 실험을 진행하였다. 냉간압연강관에 용융아연도금 약 $25{\mu}m$, 갈바륨 약 $20{\mu}m$ 두께로 제작된 강관을 사용하였으며 제작된 도금층 표면 모폴로지는 SEM을 통해 관찰하였고, XRD 분석을 통해 결정 구조를 확인하였다. 또한 5% 염수분무 환경 중 노출시험(Salt spray test), 3% NaCl 용액에서의 자연침지 시험 및 3% NaCl 용액 중 전기화학적 양극분극 시험을 진행하여 평가하였다. 5% NaCl 환경에서의 염수분무 시험 결과 용융아연도금의 경우 단면에서는 90시간, 표면에서는 260시간 경과 후 적청이 발생하였다. 반면, 갈바륨의 경우에는 단면에서 210시간 경과 후에 적청이 발생하였고, 표면의 경우에는 900시간 이상에서도 적청이 발생하지 않았다. 이 결과를 통해 용융아연도금에 비해 갈바륨 도금의 내식성이 단면에서는 3배, 표면에서는 4~5배 이상 향상된 것으로 확인되었다. 또한 3% NaCl 용액 중 자연침지 시험 결과 용융아연도금 강관 표면은 24시간 경과 후 열화부를 중심으로 흑변하는 것을 확인할 수 있었으나 갈바륨의 경우에는 900시간 이상 실험이 진행되는 동안 No Scribe 및 Scribe 시편 모두 외관상 변화가 거의 없었다. 단면의 경우, 용융아연도금 시편은 900시간 이상 실험이 진행되는 동안 외관상 변화가 없었으며, 갈바륨 시편의 경우 300시간 경과 하면서 흰색의 아연 부식생성물이 나타났으나 900시간 이후로도 적청은 발생하지 않았다. 자연전위 측정결과 용융아연도금 및 갈바륨 시편 모두 유사한 전위거동을 나타냈지만 단면의 경우 갈바륨 시편이 용융아연도금에 비해 안정적인 거동을 보였다. 3% NaCl 용액 중 전기화학적 양극 분극 시험 결과 용융아연도금이 갈바륨에 비해 귀한 방향의 부식 전위 값을 나타냈으며, 부식 전류밀도도 용융아연도금이 갈바륨에 비해 더 높은 값을 나타내는 것을 확인할 수 있었다. 이상의 염수분무시험, 자연침지시험 및 전기화학적 양극분극시험을 통해 종합적으로 분석-고찰하여 보면, 그 부식이 진행되는 과정은 융융아연도금과 달리 갈바륨 도금의 경우가 다단계적인 부식 과정을 거치면서 우수한 내식 특성을 나타낸다는 것을 알 수 있었다. 즉, 갈바륨 도금은 그 도금 막에 분포된 합금상 원소 성분들이 상호 갈바닉(Galvanic) 작용하며 형성된 부식생성물이 수평적으로 자체 차단(Barrier) 역할을 하는 과정과 부분적 부식-회복 과정을 거치면서 다단계적으로 부식속도를 감소시키게 된다는 것을 확인 할 수 있었다.

• Corrosion Science and Technology
• /
• v.9 no.6
• /
• pp.325-330
• /
• 2010

Many surface protection methods have been developed to apply for constructional steels used under severe corrosive environment. Thermal spray coating has been known to be an attractive technique due to its relatively high coating speed. Furthermore high corrosion resistance of coated film with thermal spray is required to expand its application. Four types of coated films(DFT:300 um) such as pure zinc, pure aluminum and two Al-Zn alloy (Al:Zn=85:15 and Al:Zn=95:5) onto the carbon steel (SS401) were prepared with arc spray, and the corrosion behavior of their samples were evaluated by electrochemical method in this study. Pure aluminum sample showed high corrosion resistance behavior exposed to sea water solution and pure zinc and alloy (Al:Zn=95:5) samples followed pure aluminum sample. The other alloy(Al:Zn=85:15) so called galvalume coated onto the carbon steel ranks the 4th corrosion resistance in this study. The results of porosity ratio of those samples by observation are well matched with the electrochemical data.

• Corrosion Science and Technology
• /
• v.22 no.5
• /
• pp.387-392
• /
• 2023

The objective of this study was to evaluate corrosion resistance of Zn-Al-Mg alloy coated steel in residential water with trace quantities of Cl^-. Comparative evaluations were performed using two commercial coated steel products, GI and Galvalume, as reference samples. Examination of corrosion morphology and measurement of weight loss revealed that the Zn-Al-Mg alloy coated steel exhibited higher corrosion resistance than reference samples. This finding suggests that the alloy coated steel possesses long-term corrosion resistance not only in highly Cl^- concentrated environments such as seawater, but also in environments with extremely low levels of Cl^- found in residential water. The primary factor contributing to the superior corrosion resistance of the Zn-Al-Mg alloy coated steel in residential water is the formation of an inhibiting corrosion product composed primarily of two phases: Zn₅(OH)₆(CO₃)₂ and Zn₅(OH)₈Cl₂·H₂O. The preferential dissolution of Mg from the corroded coating layer can increase alkalinity, which might enhance the thermodynamical stability of Zn₅(OH)₆(CO₃)₂.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.95-95
• /
• 2009

Zinc coatings provide the most effective and economical way of protecting steel against corrosion. There are three types of galvanizing lines typically used in production line in galvanizing industries,Galvanize (GI) coating (Zn-0.1-0.3%Al), Galfan coating (Zn-5%Al), Galvalume(GL) coating (45%Zn-Al). In continuous Galvanizing lines, the immersed bath hardware (e.g. bearings, sink, stabilizer, and corrector rolls, and also support roll arms and snout tip) are subjected to corrosion and wear failure. Understanding the reaction of these materials with the molten Zn alloy is becomes scientific and commercial interest. To investigate the reaction with molten Zn alloys, static immersion test performed for 4, 8, 16, and 24 Hr. Two different baths used for the static immersion, which are molten Zn and molten Zn-55%Al. Microstructures characterization of each of the materials and intermetallic layer formed in the reaction zone was performed using optical microscope, SEM and EDS. The thickness of the reaction layer is examined using image analysis to determine the kinetics of the reaction. The phase dominated by two distinct phase which are eutectic carbide and matrix. The morphology of the intermetallic phase formed by molten Zn is discrete phase showing high dissolution of the material, and the intermetallic phase formed by Zn-55wt%Al is continuous. Aluminum reacts readily with the materials compare to Zinc, forming iron aluminide intermetallic layer ($Fe_2Al_5$) at the interface and leaving zinc behind.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.65-65
• /
• 2018

갈바륨 도금강판은 알루미늄의 우수한 차폐 특성과 내열성, 열 반사성을 가지며 아연의 희생방식 특성을 겸비하여 동일 부착량의 용융 아연도금 및 알루미늄 도금강판에 비해 우수한 내식성을 나타낸다고 알려져 있다. 또한 이것은 표면이 미려하고 경제성이 높아 건자재 용도로 현재까지도 세계적으로 널리 이용되고 있다. 여기서 지칭하는 바륨 도금강판(galvalume steel)은 아연과 알루미늄 도금강판의 장점을 접목하기 위해 55 Al-43.4 Zn-1.6 Si (wt.%)로 구성되어 개발된 3원계 성분의 합금도금강판이다. 한편, 최근에는 강재의 내식성을 향상시키기 위한 다양한 연구 결과에 의해 Zn-Al-Mg의 3원계 합금도금강판도 개발되어 사용되고 있다. 이것은 기존의 아연도금 강판 보다 10배 정도의 우수한 내식성을 나타내는 것으로 보고되고 있다. 특히, 이것은 도금된 평판부의 내식성은 물론 절단된 도금 단면부의 내식성도 매우 우수하다고 알려져 있다. 그러나 상기한 갈바륨 도금강판의 경우에는 도금된 표면부에 비해 단면부의 내식성이 상대적으로 취약한 것으로 알려져 있다. 따라서 본 연구에서는 갈바륨 도금강판의 내식성을 종합적으로 향상시키기 위하여 이 갈바륨 도금강판 상에 PVD 스퍼터링법에 의해 Mg 코팅막의 제작을 시도하였다. 여기서 Mg 코팅막은 후처리 된 갈바륨 도금강판 상에 Ar 공정압력 2 및 20 mTorr 조건 중 1.5 및 $3{\mu}m$ 두께로 제작하였다. 또한 제작한 코팅막에 대해서는 모폴로지 관찰(SEM) 및 결정구조 분석(XRD)을 하였고, 분극측정, 염수분무 시험(SST) 및 복합부식 시험(CCT)에 의해 표면 및 단면부의 내식성평가를 수행하였다. 또한 여기서는 염수분무 및 복합부식 시험 후의 시험편도 채취 하여 표면 및 단면부위에 대한 원소조성 분석(EPMA)과 결정구조 분석(XRD)을 실시하였다. 이상의 실험 결과에 의하면, 본 실험에서 제작한 Mg 코팅막은 그 두께가 두꺼울수록 표면 Mg 결정립의 크기가 증가하였고, 그 부식속도가 증가하는 경향을 나타내었다. 또한 여기서는 공정압력이 높은 조건에서 제작한 막일수록 Mg(002)면 피크 강도가 감소하고 Mg(101)면 피크의 배향성이 증가하였다. 그때 그 막의 내식성은 향상되는 경향을 나타내었다. 그리고 종합적으로 염수분무 및 복합부식 시험 결과에 의하면 Mg이 코팅된 갈바륨 도금강판은 기존 갈바륨 도금강판 보다 내식성이 현저히 향상되었다. 특히, 단면부 내식성의 경우에는 기존 대비 5배 이상 향상되는 경향을 나타내었다. 여기서 단면부 내식특성 분석을 위한 EPMA 원소조성 분석 결과에 의거하면, 부식 초기에는 마그네슘의 부식생성물에 의해 단면부가 치밀하게 보호되고 있음을 확인할 수 있었다. 그 이후에는 부식이 지속적으로 진행됨에 따라 갈바륨 도금층에서 용출된 알루미늄 및 아연 성분이 마그네슘과 함께 치밀한 부식생성물을 형성하여 단면부를 차폐함에 따라 단면부의 내식성이 크게 향상된 것으로 생각된다. 이러한 부식생성물의 결정구조 분석 결과에 따르면, 염수분무와 복합부식 시험에서는 공통적으로 MgO, $Mg(OH)_2$ 이외에도 Simonkolleite상 등이 형성되었다. 또한 건-습 반복 부식시험인 복합부식시험 후에는 $Mg_5(CO_3)_4(OH)_24H_2O$(Hydromagnesite)상 등이 형성됨을 확인할 수 있었다. 즉, 본 실험에서 후처리된 갈바륨 도금강판 상에 제작한 마그네슘 코팅막의 경우에는 상기와 같은 다양한 부식반응에 의해 표면 및 단면부에 형성된 Mg계 부식생성물과 $Zn_5(OH)_8Cl_2H_2O$(Simonkolleite)상에 의해서 표면은 물론 단면부 내식성이 크게 향상된 것으로 사료된다.