• Journal of the Korea Concrete Institute
• /
• v.26 no.1
• /
• pp.63-70
• /
• 2014

This experimental study was intended to improve the compressive strength of multi-walled CNT reinforced cementitious composites with efficiency. The variables considered are the degree of sonication, the amount of surfactant, the replacement ratio of silica fume, etc. Optical microscope informed that fiber dispersion of CNT was improved with the increase of sonication time, and the compressive strength was proved to be enhanced as the degree of sonication increased. When superplasticizer as a surfactant had SP/CNT ratio of 4~6, the best improvement in strength was obtained. Silica fume was shown to produce the highest compressive strength at 10% replacement. Microstructure of CNT composites was also analyzed; XRD and SEM results indicated that CNT addition hardly changed hydration products and microstructure, and MIP analysis found the reduction of total porosity as well as the increase of nano-pores with the size of tens of nm instead of the decrease of pore distribution in the region of around 10 ${\mu}m$ and 100 nm. The results of microstructure analysis explains that the strength improvement is closely related to physical contribution rather than chemical influence by adding CNT.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.7
• /
• pp.4960-4968
• /
• 2015

In this study to improve the chloride durability of the shotcrete structure depending on types and contents of mineral admixture chloride resistance was evaluated by NT BUILD 492 of european test standards. It was also evaluated with the mechanical properties such as static strength and chloride penetration resistance. For shotcrete mixed crushed stone aggregate of the maximum size 10mm of coarse aggregates was produced. Based on 28days compression strength the variable mixed with 15% silica fume showed the highest strength in 67.55MPa. As the content of fly ash and blast furnace slag increased, the strength lowered. In the chloride penetration resistance test, OPC showed "high grade" and In the case of admixture, the penetration resistance tended to increase in all variables except the fly ash. In order to evaluate the service life, the accelerated chloride penetration test was conducted by the standards of KCL, ACI, FIB. Test results were obtained with the lowest spreading factor in a variable mixed with silica fume of 15%. At the KCI standards, It was found to have a service life of about 65 years and at the FIB standards, It was found to have a service life of 131 years. Among standards, the service life of KCI standard in all of the variables was evaluated as the lowest.

• Journal of the Korea Concrete Institute
• /
• v.13 no.6
• /
• pp.527-535
• /
• 2001

The watertight property of concrete was examined, that is affected by the sort of self waterproofing admixture and the change of the addition ratio of admixture. Various self waterproofing admixtures were made by changing the mixing ratio of silica fume, zinc stearate and silica sand. The result showed as follows. As the adding ratio of self waterproofing admixture increases, the fluidity is increased and the setting time is delayed. While compressive strength of concrete with self waterproofing admixture A which is currently using is increased until the adding ratio of self waterproofing admixture reached 18kg/㎥ and decreased over 24 kg/㎥, that with self waterproofing admixture B, C and D which are developed are higher than that of A. Absorption is decreased as the adding ratio of self waterproofing admixture and the increasing of age in concrete. Especially, when self waterproofing admixture has a lot of zinc stearate, absorption is decreased manifestly. The property of permeability is similar to that of absorption; permeability is decreased as the adding ratio of self waterproofing admixture and the increasing of age in concrete. Consequently, when the ratio of silica fume, zinc stearate and silica sand in self waterproofing admixture is 1 : 2 : 1 and addition ratio of self waterproofing admixture is 6kg/㎥, the high quality concrete is obtained comparing to the concrete with existent self waterproofing admixture.

• Tunnel and Underground Space
• /
• v.17 no.4
• /
• pp.266-284
• /
• 2007

Recently, many efforts have been made to construct the first unlined tunnel, without in-situ concrete lining, in Korea. However, the lack of reliability in the performance of shotcrete as permanent tunnel support prevented from its realization. Shotcrete has been regarded to have significant problems in field application and long term performance because of unsatisfactory strength level and durability compared to those of European countries. In this study, the high strength shotcrete satisfying compressive strength over 40 MPa and flexural strength over 4.5 MPa was developed from optimized mix design. The type of accelerators and the amount of silica fume were selected as the main factors in mixing process and the analyses were carried out up to the elapsed time of 2 years. In order to evaluate the short term durability of shotcrete, an array of laboratory test consisting of freeze-thaw, carbonation chloride penetration and permeability test was performed. For long-term durability tests, specimens have been put in an operated highway tunnel to expose them to the similar environment when they are actually used as an unlined tunnel support. From the strength and durability tests, it was found that only alkali-free based accelerator satisfied the target strength of this study and also, the developed shotcrete showed very high performance in its durability.

• Journal of the Korea Concrete Institute
• /
• v.17 no.1 s.85
• /
• pp.35-41
• /
• 2005

Recently, various fiber reinforced cementitious composites are used in order to solve problems of concrete as the brittleness breaking. Especially, in U.S.A., Europe, and Japan, ultra-high strength steel fiber reinforced cementitious composites(ultra-high strength SFRCC) with compressive strength in excess of 100 MPa were developed. However few studies have been investigated on the high-strength SFRCC in Korea. Therefore, in this paper, to make ultra-high strength SFRCC with the range of compressive strength 180MPa, it was investigated the constitute factors of ultra-high strength SFRCC influenced on the compressive strength. The experimental variables were water-binder ratio, replacement of silica fume, size and proportion of sand, type and replacement of filling powder, and using of steel fiber in ultra-high strength SFRCC. As a result, in water-binder ratio 0.20, we could make ultra-high strength SFRCC with compressive strength of 180MPa through using of silica fume, quartz sand with below 0.5mm filling powder and steel fiber.

• Journal of the Korea Concrete Institute
• /
• v.15 no.6
• /
• pp.785-793
• /
• 2003

This study is intended to analyze the effectiveness of expansive additive, shrinkage reducing agent and combination of the two to reduce the autogenous and drying shrinkage of high performance concrete using mineral admixture such as fly ash, blast furnace slag powder and silica fume. According to results, when expansive additive and shrinkage reducing agent are mixed within an appropriate mixing ratio, fluidity and air content are not influenced, and the enhancement of compressive strength is favorable at the age of 91 and 180days. At the mixing ratio of expansive additive of 5% and 10%, the autogenous and drying shrinkage is reduced by 32∼68% and 25∼49% respectively in comparison with plain concrete. And they are reduced by 18∼34% and 16∼26% respectively at the mixing ratio of shrinkage reducing agent of 0.5% and 1.0%, compared with plain concrete. The mixture of EA-SR combined with expansive additive and shrinkage reducing agent is most effective for reduction of shrinkage. Therefore, it is considered that the using method in combination with expansive additive and shrinkage reducing agent is effective to reduce the shrinkage of high performance concrete using mineral admixture such as fly ash, blast slag powder and silica fume.

• Journal of the Korea Concrete Institute
• /
• v.19 no.4
• /
• pp.499-506
• /
• 2007

According to the high demand of concrete structures with high performance, various studies have examined on the high performance concrete, especially high strength concrete. Various admixtures are required to produce high strength concrete and silica fume has been the most popular admixture. Recently, however, metakaolin, which is similar to silica fume in properties but cheaper, has been introduced to high strength concrete. In this study, high-strength concrete using metakaolin were studied of capillary pore structure by mercury intrusion porosimetry technique and the accelerated chloride diffusivity by electrical difference. In result, it was found that the pore structure improved and compressive strength increased and chloride diffusivity reduced as more metakaolin content was added. In addition, a regression analysis of $5{\sim}2,000nm$ pore volume and both compression strength and chloride diffusivity revealed that each these had a high correlation of about 0.76 and 0.68.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.3
• /
• pp.66-74
• /
• 2016

The aim of this research work is to investigate the mix proportion of multi-component cement incorporating ground granulated blast furnace(GGBFS), fly ash(FA) and silica fume(SF) as an addition to cement in ternary and quaternary combinations. The water-binder ratio was 0.45. In this study, 50% and 60% replacement ratios of mineral admixture to OPC was used, while series of combination of 20~40% GGBFS, 5~35% FA and 0~15% SF binder were used for fundamental characteristics tests. This study concern the GGBFS/FA ratio and SF contents of multi-component cement including the compressive strength, water absorptions, ultrasonic pulse velocity(UPV), drying shrinkage and X-ray diffraction(XRD) analysises. The results show that the addition of SF can reduce the water absorption and increase the compressive strength, UPV and drying shrinkage. These developments in the compressive strength, UPV and water absorption can be attributed to the fact that increase in the SF content tends basically to consume the calcium hydroxide crystals released from the hydration process leading to the formation of further CSH(calcium silicate hydrate). The strength, water absorption and UPV increases with an increase in GGBFS/FA ratios for a each SF contents. The relationship between GGBFS/FA ratios and compressive strength, water absorption, UPV is close to linear. It was found that the GGBFS/FA ratio and SF contents is the key factor governing the fundamental properties of multi-component cement.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.5
• /
• pp.133-142
• /
• 2008

This paper studies the early-aged chloride binding capacity of various blended concretes including OPC(ordinary Portland cement), PFA(pulversied fly ash), GGBFS(ground granulated blast furnace slag) and SF(silica fume) cement paste. Cement pastes with 0.4 of a free water/binder ratio were cast with chloride admixed in mixing water, which ranged from 0.1 to 3.0% by weight of cement and different replacement ratios for the PFA, GGBFS and SF were used. The content of chloride in each paste was measured using water extraction method after 7 days curing. It was found that the chloride binding capacity strongly depends on binder type, replacement ratio and total chloride content. An increase in total chloride results in a decrease in the chloride binding, because of the restriction of the binding capacity of cement matrix. For the pastes containing maximum level of PFA(30%) and GGBFS(60%) replacement in this study, the chloride binding capacity was lower than those of OPC paste, and an increase in SF resulted in decreased chloride binding, which are ascribed to a latent hydration of pozzolanic materials and a fall in the pH of the pore solution, respectively. The chloride binding capacity at 7 days shows that the order of the resistance to chloride-induced corrosion is 30%PFA > 10%SF > 60%GGBFS > OPC, when chlorides are internally intruded in concrete. In addition, it is found that the binding behaviour of all binders are well described by both the Langmuir and Freundlich isotherms.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.1
• /
• pp.72-79
• /
• 2011

This study is performed to analyze the effects of CASB by applying the superplasticizer combined CASB on the ultra high strength mortar and concrete that uses different mineral admixture depending on whether the silica fume was used and the results are summarized below. From the characteristics of Fresh mortar and concrete, the fluidity was lower in B2-CASB than B2-PC from the mixing of CASB and based on the viscosity of the mortar and concrete in the binary proportion but in the ternary proportion, B3-CASB showed a larger fluidity than B3-PC because of a reduction in the restriction level due to the effects of an improvement of particle size distribution. The compression strength was higher in ternary proportion than in binary proportion and higher in CASB than in PC from the characteristics of hardening mortar and concrete and this is analyzed as a result of increased minuteness from the calcium silicate hydrates produced from the pozzolan reaction of a mineral admixture, SF, and also the charging effects of capillary pore of CASB. Overall, when using the nanomaterial, CASB in combination with a superplasticizer, the fluidity and the strength aspects of the ternary proportion of ultra high strength mortar and concrete with silica fume may be improved to a higher quality.