Dissimilar friction welds were produced using 15-mm diameter solid bars of chrome molybdenum steel (KS SCM440) and carbon steel (KS SM20C) to investigate their mechanical properties. The main friction welding parameters were selected to ensure good quality welds on the basis of visual examination, tensile tests, Vickers hardness surveys of the bond area and HAZ, and macro-structure investigations. The specimens were tested as-welded and post-weld heat treated (PWHT). The tensile strength of the friction welded steel bars was increased to 100% of the SM20C base metal under the condition of a heating time of more than four seconds. Optimal welding conditions were n = 2,000 (rpm), HP = 60 (MPa), UP = 100 (MPa), HT = 5 (s),and UT = 5 (s), when the total upset length was 7.8 (mm). The hardness distribution peak of the friction welded joints could be eliminated using PWHT. The two different kinds of materials were strongly mixed to show a well-combined structure of macro-particles, with no molten material, particle growth, or defects.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2006.11a
• /
• pp.205-208
• /
• 2006

Similar friction welding were produced using 15 mm diameter solid bar in Ni-base superalloy(alloy718) to investigate their mechanical properties. The main friction welding parameters were selected to endure good quality welds on the basis of visual examination, tensile tests, AE total counts and ultrasonic attenuation coefficient. The specimens were tested as welded, not heat-treated. The tensile strength of the friction welded joints was increased up to 90% of the alloy718 base metal under the condition of all heating time. Optimal welding conditions were n=2,000 (rpm), $P_1=200$ (MFa), $P_2=200$ (MFa), $t_1=8$ (s), $t_2=5$ (s) when the total upset length is 4.4(mm). The weld interface of similar friction welded steel bars was mixed strongly.

• Tribology and Lubricants
• /
• v.25 no.4
• /
• pp.207-216
• /
• 2009

Friction tests were carried out in order to investigate the effects of temperature on the friction and wear behaviors between a PMMA film and a fused silica lens using a microtribometer. The friction forces on the PMMA film were measured under atmospheric condition as the temperature of the film was increased from 300 K to 443 K. The contact area between the film and the lens was observed. The tribological characteristics of the film were significantly changed as the temperature increased. The changes were discussed with the change of the film state from glassy to viscous flow. In addition, the results showed that the friction behavior can be varied with the thermal history of the PMMA film. Residual solvent in the PMMA film could emerge to the PMMA surface due to an additional heating and the solvent on the film surface decreased the friction force.

• Tribology and Lubricants
• /
• v.22 no.6
• /
• pp.314-319
• /
• 2006

In this paper, the friction and wear characteristics of contact type sealing unit far a water turbine have been presented. The sealing unit for a small hydropower generation is to stop a leakage of circulating water from an outside of an impeller to an inside of a rolling bearing. The friction heating between a seal ring and a seal seat may radically increase a surface temperature in which increase a power loss and wear on the rubbing surface. The surface wear strongly affect to the seal life of a mechanical face seal. In this study, the hardness of a stainless steel in which is a heat-treated is 892.8 in Victors hardness and the hardness of silicone carbide of SiC is 714.1 in Victors hardness. The surface hardness of a heat-treated stainless steel is 25% high compared with that of a ceramic material of SiC. The contact modes of rubbing surfaces are a dry friction, a water film friction and a mixed friction that is contaminated by a dust, silt, and moistures, etc. These two factors of a contact rubbing modes and a material property are very important parameters on the tribological performance such as a friction and wear between a seal ring and a seal seat in primary sealing unit. The experimental result shows that the surface hardness of a seal material is very important on the friction coefficient and a wear volume. Thus, the results recommend higher hardness of a seal material, which may reduce a friction loss and increase a wear life of primary seal components.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2004.05a
• /
• pp.331-336
• /
• 2004

Dissimilar friction welding were produced using 10mm and 11mm diameter solid bar in Inconel ally(IN X-750) to Stainless steel(STS316L) to investigate their mechanical properties. The main friction welding parameters were selected to endure good quality welds on the basis of visual examination, tensile tests, Virkers hardness surveys of the bond of area and HAZ and macro-structure investigations. The specimens were tested as welded, not heat-treated. The tensile strength of the friction welded steel bars was increased up to $95\%$ of the STS316L base metal under the condition of all heating time. Optimal welding conditions were n=2,000(rpm), $P_1=220(MPa),\;P_2=260(MPa),\;t_1=4(s),\;t_2=4(s)$ when the total upset length is 7(mm).

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2003.10a
• /
• pp.158-162
• /
• 2003

A study on friction welding of chrome molybedenum steel(SCM440) to carbon steel(S45C) is examined experimentally through tensile test, hardness test. So, this paper deals with optimizing the welding conditions and analyzing various mechanical properties about friction welds of SCM440 to S45C steel. The tensile strength of the friction welded joint was increased up to 100% of the S45C base matal under the condition of all heating time. Optimal welding conditions were n=2,000(rpm), $P_{1}=60(MPa)$, $P_{2}=100(MPa)$, $t_{1}=4(s)$, $t_{2}=5(s)$ when the total upset length is 5.7(mm).

• Journal of Ocean Engineering and Technology
• /
• v.22 no.1
• /
• pp.53-57
• /
• 2008

Friction welding was performed to investigate mechanical properties for Ni-base superalloy with 15 mm diameter solid bar. The main friction welding parameters were selected to endure good quality welds on the basis of visual examination, tensile tests, impact energy test, Vickers hardness surveys of the bond of area and heat affected zone. And then, the nondestructive technique to evaluate the weld quality was carried out by acoustic emission(AE) and ultrasonic attenuation coefficient. The tensile strength of the friction welded joint was shown up to 90 % of the Alloy718 base metal under the condition of the heating time over 5 sec. The optimal welding conditions were n=2,000 rpm, $P_1=200$ MPa, $P_2=200$ MPa, $t_1=8$ sec and $t_2=5$ sec when the total upset length was 4.4 mm.

• Tribology and Lubricants
• /
• v.10 no.3
• /
• pp.29-38
• /
• 1994

The friction and wear of mild steel at dry sliding surfaces under different vacuum conditions have been investigated to understand the wear mechanisms. For the test, a ball-ondisk typed wear-rig has been built and implemented, allowing control of sliding speed, load and vacuum. Results show that, at a high sliding velocity, friction of low carbon steel (SS41) under a high vacuum is much higher than that of ambient condition and wear is much severer. It is due to lack of effective oxidation film formation on which steel surfaces could protect themselves against the severe wear. It has been shown, however, that there is a critical regime with contact conditions (at a low sliding velocity, a low load, and under a medium vacuum) at which effective, protective films of low carbon steel have been built on the surfaces in a friction process with a self-regulating way, resulting in both very low coefficients of friction (about 0.3) and mild wear. In order to investigate the protective films on steel surfaces, the worn surfaces and the wear debris have been experimentally analyzed with SEM, AES/SAM and XRD. A theoretical analysis of frictional heating at sliding surfaces, and an experimental analysis of the influence of oxidation wear under various vacuum conditions are described. The important variables on which self-formations of protective films at dry sliding surfaces depend, and the wear mechanisms are also investigated.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.5
• /
• pp.517-523
• /
• 2004

Recently, wheel slip controllers with controlling the wheel slip directly has been studied using the brake-by-wire actuator. The wheel slip controller is able to control the braking force more accurately and can be adapted to various different vehicles more easily than the conventional ABS systems. The wheel slip controller requires the information about the tire braking force and road condition in order to achieve the control performance. In this paper, the tire braking forces are estimated considering the variation of the friction between brake pad and disk due to aging of the brake, moisture on the contact area or heating. In addition, the road friction coefficient is estimated without using tire models. The estimated performance of tire braking forces and the road friction coefficient is evaluated in simulations.

• Nuclear Engineering and Technology
• /
• v.56 no.1
• /
• pp.233-240
• /
• 2024

The wall friction correlations of oscillatory natural circulation loops are highly loop-specific, making it difficult to perform 1-D system simulations before obtaining specific experimental data. To better predict the friction characteristics, the nonlinear dynamics of a toroidal single-phase natural circulation loop were numerically investigated, and the transition effect was considered. The k-k_L-ω transitional turbulence and k-ω SST turbulence models were used to compute the flow characteristics of the loop under different heating powers varying from 0.48 to 1.0 W/cm², and the results of both models were compared with previous experiments. The mass flow rates and friction factors predicted by the k-k_L-ω model showed a better agreement with the experimental data than the results of the k-ω SST model. The oscillation frequencies calculated using both models agreed well with the experimental data. The k-k_L-ω transitional turbulence model provided better friction-factor predictions in oscillatory natural circulation loops because it can reproduce the temporal and spatial variation of the wall shear stress more accurately by capturing the movement of laminar, transition turbulent zones inside unstable natural circulation loops. This study shows that transition effects are a possible explanation for the highly loop-specific friction correlations observed in various oscillatory natural circulation loops.