• Tribology and Lubricants
• /
• 제12권3호
• /
• pp.55-62
• /
• 1996

Present study was undertaken to investigate the effects of composition ratio and temperature on the friction and wear of PTFE-polyimide composites under the atmosphere of nitrogen gas. The load range was 0.62-3.46 MPa, and the temperature range was room temperature and 200$^{\circ}$C. To mention some of the notable results, friction coefficient of PTFE 100% varied relatively little within the given load and temperature ranges. Polyimide 100% showed the lowest friction coefficient of 0.06 at 200$^{\circ}$C among all the experiments. PTFE 80%-polyimide 20% showed the lowest wear factors on the whole. Friction coefficient of PTFE 20%-polyimide 80% varied from the highest 0.35 to the lowest 0.09 among all the materials at room temperature, and showed almost the same lowest values with polyimide 100% at 200$^{\circ}$C. Suggestion of friction and wear mechanisms of the materials was tried to explain the observed phenomena including above mentioned results.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1997년도 제26회 추계학술대회
• /
• pp.93-99
• /
• 1997

High Temperature wear behavior of plasma sprayed ZrO$_2$ and MoS$_2$, $Fe_2O_3$ coatings were investigated for high temperature wear resistance applications. The MoS$_2$, $Fe_2O_3$ added powders containing 2.5, 5.0, 7.5, 10.0 mol% of $MoS_2$, $Fe_2O_3$ for plasma spray were made by spray drying method. Wear test were performed at temperature ranges from room temperature to 600$\circ$C. The microstructural change of coatings and the worn. surface were examined by SEM and XRD. In ZrO$_2$ coating, the coefficient of friction and wear amount of room temperature to 400$\circ$C was increased with temperature and decreased with temperature over 400$\circ$C. The coefficient of friction and wear amount of MoS$_2$ added coatings were increased with temperature, but those of $Fe_2O_3$ added coatings had lower coefficient of friction and higher wear resistance than ZrO$_2$ coating.