• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.20 no.3
• /
• pp.284-291
• /
• 2011

Numerical experiments on biological interfacial layer, DEJ by finite element software ABAQUS have been conducted to study its fracture behavior including crack bridging / arresting characteristics in the model. Crack growth simulation has been carried out by numerical tool, XFEM, devoted to study cracks and discontinuities. The fracture toughness of DEJ has been estimated before and after crack bridging. The implications of bridging in numerical study of fracture behavior of DEJ-like biological interface have been discussed. It has been observed that the results provided by the numerical studies without proper accommodation of bridging phenomenon can mislead. This study can be helpful for understanding the DEJ-like biological interface in terms of its fracture toughness, an important material characteristics. This property of the material is an important measure that has to be taken care during design and manufacturing processes.

• Journal of the Korean Ceramic Society
• /
• v.26 no.5
• /
• pp.645-654
• /
• 1989

Specimens of WC-Co were indented to measure the resulting crack size and unindented samples were fractured in 3-point flexure to obtain the strength and to measure characteristic features on the fracture surface. Fracture toughness was determined using fractography and compared to those determined using identation techniques. We show that principles of fracture mechanics can be applied WC-Co composites and can be used to analyze the fracture process. The fracture surfaces were examined by scanning electron microscopy and optical microscopy. Characteristic feature observed in glasses, single crystals and polycrystalline materials known as mirror, mist, hackle, and crack branching were identified for these composites. We discuss the importance of fracture surface analysis in determining the failure-initiating sources and the failure behaviorof WC-Co composites.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.9 no.5
• /
• pp.173-178
• /
• 2001

This study investigates the effect of fiber content on the fracture behavior of thermoplastic composites (glass fiber/polypropylene). The fiber contents used were 20%, 30%, and 40% by weight. Fracture tests were performed using compact tension (CT) specimens made of composite sheets of three fiber contents (20%, 30%, 40%). The results showed that compliance, fracture load, and fracture toughness were affected by the fiber content. The compliance decreased with fiber content while the fracture load increased as the fiber content increased. The fracture toughness also increased as fiber content increased. Specifically, the fracture toughness increased 14% as the fiber content increased from 20% to 40%.

• Journal of Ocean Engineering and Technology
• /
• v.19 no.5 s.66
• /
• pp.65-70
• /
• 2005

Fracture behavior and pipe strength are very important to the integrity of energy plants, ocean structures, and so forth. The pipes of energy plants and ocean structures are subject to local wall thinning, resulting from severe erosion-corrosion damage. Recently, the effects of local wall thinning on fracture strength and fracture behavior of piping systems have been the focus of many studies. In this paper, the elasto-plastic analysis is performed by FE code ANSYS on straight pipes with wall thinning. We evaluated the failure mode, fracture strength and fracture behavior, using FE analysis. Also, the effect of the axial strain on deformations and failure modes was estimated by FE analysis.

• Structural Engineering and Mechanics
• /
• v.71 no.2
• /
• pp.153-163
• /
• 2019

Longitudinal fracture behavior of non-linear elastic beam configurations is studied in terms of the strain energy release rate. It is assumed that the beams exhibit continuous material inhomogeneity along the width as well as along the height of the crosssection. The Ramberg-Osgood stress-strain relation is used for describing the non-linear mechanical behavior of the inhomogeneous material. A solution to strain energy release rate is derived that holds for inhomogeneous beams of arbitrary cross-section under combination of axial force and bending moments. Besides, the solution may be applied at any law of continuous distribution of the modulus of elasticity in the beam cross-section. The longitudinal crack may be located arbitrary along the beam height. The solution is used to investigate a longitudinal crack in a beam configuration of rectangular cross-section under four-point bending. The crack is located symmetrically with respect to the beam mid-span. It is assumed that the modulus of elasticity varies continuously according a cosine law in the beam cross-section. The longitudinal fracture behavior of the inhomogeneous beam is studied also by applying the J-integral approach for verification of the non-linear solution to the strain energy release rate derived in the present paper. Effects of material inhomogeneity, crack location along the beam height and non-linear mechanical behavior of the material on the longitudinal fracture behavior are evaluated. Thus, the solution derived in the present paper can be used in engineering design of inhomogeneous non-linear elastic structural members to assess the influence of various material and geometrical parameters on longitudinal fracture.

• International Journal of Concrete Structures and Materials
• /
• v.18 no.3E
• /
• pp.213-219
• /
• 2006

Modified singular fracture process zone(S-FPZ) model is proposed in this paper to determine a fracture criterion for continuous crack propagation in concrete. The investigated fracture properties of the proposed fracture model are strain energy release rate at a micro-crack tip and the relationship between crack closure stress(CCS) and crack opening displacement(COD) in the FPZ. The proposed model can simulate the actual fracture energy of experimental results fairly well. The results of the experimental data analysis show that specimen geometry and loading condition did not affect the CCS-COD relation. However, the strain energy release rate is a function of not only specimen geometry but also crack extension. The strain energy release rate remained constantly at the minimum value up to the crack extension of 25 mm, and then it increased linearly to the maximum value. The maximum fracture criterion occurred at the peak load for specimens of large size. The fracture criterion remained at the maximum value after the peak load. The variation of the fracture criterion is caused by micro-cracking and micro-crack localization. The fracture criterion of strain energy release rate can simply be the size effect of concrete fracture, and it can be used to quantify the micro-cracking and micro-crack localizing behavior of concrete.

• Steel and Composite Structures
• /
• v.23 no.3
• /
• pp.263-271
• /
• 2017

A theoretical study was carried-out of mode II delamination fracture behavior of the End Loaded Split (ELS) functionally graded beam configuration with considering the material non-linearity. The mechanical response of ELS was modeled analytically by using a power-law stress-strain relation. It was assumed that the material is functionally graded transversally to the beam. The non-linear fracture was investigated by using the J-integral approach. Equations were derived for the crack arm curvature and zero axes coordinate that are needed for the J-integral solution. The analysis developed is valid for a delamination crack located arbitrary along the beam height. The J-integral solution was verified by analyzing the strain energy release rate with considering material non-linearity. The effects of material gradient, non-linear material behavior and crack location on the fracture were evaluated. The solution derived is suitable for parametric analyses of non-linear fracture. The results obtained can be used for optimization of functionally graded beams with respect to their mode II fracture performance. Also, such simplified analytical models contribute for the understanding of delamination fracture in functionally graded beams exhibiting material non-linearity.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.05a
• /
• pp.265-270
• /
• 2002

In this paper, structural behaviors of anchor systems subjected to shear loads are analyzed by using fracture analysis and experiments. Two dimensional finite element analyses of concrete anchor systems to predict breakout failure of concrete through progressive fracture are carried out by utilizing the so-called embedded crack model. Three dimensional finite element analyses are also carried out to investigate the fracture behavior of anchor systems having different effective lengths, edge distances, spacings between anchors, and direction of loads. Results of analyses are compared with both experimental results and design values of ACI code on anchor, and then applicability of finite element method for predicting fracture behavior of concrete anchor systems is verified.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.3
• /
• pp.806-815
• /
• 1996

The interlaminar fracture behavior of woven laminates under static and cyclic loadings has been studied using DCB(double cantilever beam) specimens. The effects of surface treatment and stiching on the fracture behavior of composite laminates are investigated experimentally. Fracture toughness has been improved by surface treatment because the surface treatment can change the fracture mechanism of laminates. SCB(stitched cantilever beam) model has been proposed to quantify the effect of through-thickness resinforcement(stiching) in improving the delamination crack growth resistance. Distributed loads which are transfered to through-thickness fibers can be calculated by the SCB model. And fracture energy increase due to the distributed load can be predicted by a power function of the distributed load. A new parameter agreed well proposed predict fatigue crack growth rate. The predictions using this parameter agreed well with the experimental data.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.39 no.3
• /
• pp.167-173
• /
• 2003

Many of researches regarding mechanical properties of composite materials are associated with humid environment and temperature. Especially the temperature is a very important factor influencing the design of thermoplastic composites. However, the effect of temperature on impact behavior of reinforced composites have not yet been fully explored. An approach which predicts critical fracture toughness G$_{IC}$ was performed by the impact test in this work. The main goal of this work is to study the effect of temperature and span of specimen supports on the results of Charpy impact test for GF/PE composite. The critical fracture energy and failure mechanism of GF/PE composites were investigated in the temperature range of $60^{\circ}C;to;-50^{\circ}C$ by the Charpy impact test. The critical fracture energy showed the maximum at the ambient temperature, and it tended to decrease as the temperature increased or decreased from the ambient temperature. The major failure mechanisms are the fiber matrix debonding, the fiber pull-out and/or delamination and the matrix deformation.n.