• Transactions of Materials Processing
• /
• v.12 no.5
• /
• pp.457-464
• /
• 2003

In the powder compact melting technique, proper precursor fabrication is very important because density distribution after foaming and foamability are determined during precursor fabrication process. The fabrication of the precursor has to be performed very carefully because any residual porosity or other defects will lead to poor results in further processing. In order to evaluate the effect of the compaction parameters on the kinetics of the foaming process, a series of experiments were performed. In this study, aluminium foams with a closed cell structure were fabricated by using both the powder compact method and the induction heating process. A proper induction coil was designed to obtain a uniform temperature distribution over the entire cross sectional area of precursor. To establish the foamable precursor fabrication conditions, effects of process parameters such as the titanium hydride content (0.3∼1.5 wt.%), pressing pressure of the foamable precursor (50∼150kN) on the pore morphology were investigated.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2001.10a
• /
• pp.289-292
• /
• 2001

Aluminium foams, having a closed cell structure, fabricated by applying the powder compact method and an induction heating were studied. The powdered A6061 mixed with the powdered titanium hydride as a foaming agent was hot pressed into a foamable precursor. The resulting precursor was foamed by induction heating up to desired temperature. The effects of the titanium hydride content ($0.3{\~}1.5 wt.\%$), pressing pressure of the foamable precursor material (50-150kN), the forming temperature ($610{\~}690^{\circ}C$) and heating rate during foaming on the expansion behavior of the foam were investigated.