The earlier studies on the fire resistance performance of woods used as building materials have focused on confirming combustion characteristics of fire retardant or flame resistant treated wood. In this paper, to confirm internal temperature changes closely related to pyrolysis of woods exposed to the flame, heating experiments were conducted in a heating furnace according to the standard heating temperature curves after Douglas-fir, which is widely used as structural materials, was treated with a flame resistant solution and flame retardant paint. As a result of the experiment, it was confirmed that the thermal diffusion inside the wood has decreased when the wood was treated with the flame resistant solution. However, in high temperature, the flame resistant effect could not be expected due to the peeling of the coating in the case of the flame resistant paint treated wood. Therefore, it can be considered that it is more effective to use the flame resistant solution which penetrates in to the inside of the wood than flame resistant paint which forms the coating on the surface of the wood in order to enhance the flame resistance effect on the thick wood.

• Fire Science and Engineering
• /
• v.30 no.6
• /
• pp.9-13
• /
• 2016

Anti-oxidation and flame resistant polyurethane nanofibers were prepared by electrospinning and aluminum hydroxide addition. Electrospinning was carried out under the following procedure conditions; applied voltage, 20 kV; polymer solution feeding rate, 1.2 ml/h; collector rolling speed, 120 rpm; and tip to collector distance, 15 cm. Aluminum hydroxide was added to the prepared polymer solution for electrospinning to enhance the oxidation and flame resistant properties. The thermal properties were investigated by thermogravimetric analysis to determine the polymer decomposition temperature, integral procedure decomposition temperature, final decomposition temperature, and remaining amount after thermal decomposition. The activated energy for polymer degradation was also investigated using the Horowitz-Metzger equation. The activation energy increased to more than 50%. The thermal properties of the polyurethane nanofibers were improved by a hydration reaction during the thermal decomposition of aluminum hydroxide around $300{\sim}500^{\circ}C$.