• Journal of Ceramic Processing Research
• /
• v.13 no.spc2
• /
• pp.363-367
• /
• 2012

DLC (diamond liked carbon) coating of the tungsten carbide (WC) alloy core surface for molding a glass aspheric lens improves the quality of glass lens and the molding core and is characterized by high hardness, high elasticity, abrasion resistance and chemical stability. In this study, the effect of DLC coating of a thin film by means of the filtered AIP (arc ion plating) technique was examined on Ra and shape of the coated surface. Roughness before and after DLC coating was measured and the result showed that the roughness was improved after coating as compared to before coating. It was observed that DLC coating of the WC alloy core surface for molding had an effect on improving the roughness and shape of the core surface. It is considered that this will have an effect on improving abrasion resistance and the service life of the core surface.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2005.08a
• /
• pp.191-191
• /
• 2005

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.67 no.10
• /
• pp.1375-1381
• /
• 2018

In this paper, we studied coatings of the DLC thin film for improving loosening torque of dental implant screw. We used a filtered arc ion plating process which can realize the most dense DLC layer by coating the DLC thin film on the surface of the dental abutment screw. It showed both hardness comparable to diamond and low friction coefficient similar to graphite, and to improve the loosening phenomenon by increasing the screw tightening force Cr/CrN, Ti/TiN or Ti/TiN/Cr/CrN buffer layers were deposited for 5 to 10 minutes to improve the adhesion of the DLC thin film to the surface of the Ti (Gr.5), and then the DLC thin film was coated for about 15 minutes. As a result, the Cr/CrN buffer layer exhibited the highest hardness of 29.7 GPa, the adhesion of 18.62N on average, and a very low coefficient of friction of less than 0.2 as a whole. And we measured loosening torque after one million times with masticatory movement simulator. As a result, the values of the coated screw loosening torque were clearly higher than those of the uncoated screw. From this, it was found that the DLC coating was effective methods improving the loosening torque. In addition, it was confirmed that the cytotoxicity test and cell adhesion test showed high biocompatibility.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.66 no.6
• /
• pp.962-967
• /
• 2017

The Diamond-Like-Carbon (DLC) coating is a new carbon-based amorphous material. Carbon ions in the plasma are electrically accelerated and collide with the substrate to form a thin film. This film has similar properties to diamonds such as high surface hardness, low coefficient of friction, corrosion resistance and durability that do not react with acids and bases. Also, since there is no thermal deformation, it can be printed at room temperature. and coated on almost all materials such as paper, polymer, ceramics and various metals even aspheric lens it is possible to mirror surface coating with excellent surface roughness. In this paper, we have analyzed the DLC film formed by Filtered Arc Ion Plating (Filtered AIP) process.

• Korean Journal of Materials Research
• /
• v.20 no.11
• /
• pp.570-574
• /
• 2010

A diamond-like carbon (DLC) film deposited on a WC disk was investigated to improve disk wear resistance for injection molding of zirconia optical ferrule. The deposition of DLC films was performed using the filtered vacuum arc ion plating (FV-AIP) system with a graphite target. The coating processing was controlled with different deposition times and the other conditions for coating, such as input power, working pressure, substrate temperature, gas flow, and bias voltage, were fixed. The coating layers of DLC were characterized using FE-SEM, AFM, and Raman spectrometry; the mechanical properties were investigated with a scratch tester and a nano-indenter. The friction coefficient of the DLC coated on the WC was obtained using a pin-on-disk, according to the ASTM G163-99. The thickness of DLC films coated for 20 min. and 60 min. was about 750 nm and 300 nm, respectively. The surface roughness of DLC films coated for 60 min. was 5.9 nm. The Raman spectrum revealed that the G peak of DLC film was composed of $sp^3$ amorphous carbon bonds. The critical load (Lc) of DLC film obtained with the scratch tester was 14.6 N. The hardness and elastic modulus of DLC measured with the nano-indenter were 36.9 GPa and 585.5 GPa, respectively. The friction coefficient of DLC coated on WC decreased from 0.2 to 0.01. The wear property of DLC coated on WC was enhanced by a factor of 20.