• Textile Coloration and Finishing
• /
• v.11 no.5
• /
• pp.22-29
• /
• 1999

The increase in color depth of polyester fiber dyed with black disperse dyes was investigated with respect to the kinds of resins and alkali treatment. The color depth of the dyed polyester fiber increased continuously according to the concentration of resins coated onto the fabrics. The alkali treatment to polyester fiber before dyeing also enhanced the color depth. It was thought that the polyester fiber was hydrolyzed by alkali resulting micropores on the sample. And the following treatment with a resin, Jet Black T-101, to the polyester fiber increased the color depth much higher. The successive process of alkali treatment, dyeing and Jet Black T-101 treatment could give the best color depth to polyester fiber. Although the alkali treatment reduced the tensile strength of polyester fiber, the color depth of polyester fiber enhanced sufficiently within the range of practically acceptable weight loss and strength. To analyze the micropore on the polyester fiber formed by alkali treatment, nitrogen porosimeter was used. As the weight loss of polyester fiber treated with alkali increased, the BET(Brunauer-Emmett-Teller) surface area, total pore volume, and average pore size of the sample increased.

• Computers and Concrete
• /
• v.14 no.5
• /
• pp.527-546
• /
• 2014

Portland cement concrete, which has higher strength and stiffness than asphalt concrete, has been widely applied on pavements. However, the brittle fracture characteristic of cement concrete restricts its application in highway pavement construction. Since the polypropylene fiber can improve the fracture toughness of cement concrete, Polypropylene Fiber-Reinforced Concrete (PFRC) is attracting more and more attention in civil engineering. In order to study the effect of polypropylene fiber on the generation and evolution process of the local deformation band in concrete, a series of three-point bending tests were performed using the new technology of the digital speckle correlation method for FRC notched beams with different volumetric contents of polypropylene fiber. The modified Double-K model was utilized for the first time to calculate the stress intensity factors of instability and crack initiation of fiber-reinforced concrete beams. The results indicate that the polypropylene fiber can enhance the fracture toughness. Based on the modified Double-K fracture theory, the maximum fracture energy of concrete with 3.2% fiber (in volume) is 47 times higher than the plain concrete. No effort of fiber content on the strength of the concrete was found. Meanwhile to balance the strength and resistant fracture toughness, concrete with 1.6% fiber is recommended to be applied in pavement construction.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.32 no.1A
• /
• pp.55-64
• /
• 2012

Experimental investigation on the structural behavior of steel fiber-reinforced ultra high performance concrete (UHPC) beams subjected to shear are presented. Six tests carried out on simply supported I-beams under concentrated loads are presented. The parameters varied were the volume fraction of the fibers (1.0, 1.5 and 2.0%) and shear span-effective depth ratio (2.5, 3.4). The test results indicated that ultimate shear strength increased with increasing fiber volume, and that ultimate shear strength decreased with increasing shear span-effective depth ratio. In addition, applicability of predictive equations for evaluating the ultimate shear strength of steel fiber-reinforced UHPC beams are estimated based on the test results. The comparison between computed values and the experimentally observed values are shown to validate the proposed theoretical equations. It is found that predictions by using AFGC and JSCE recommendations provide the most accurate estimates of shear strength of steel fiber-reinforced UHPC beams.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.3 no.2
• /
• pp.56-65
• /
• 1999

The relationship of the winding process variables and the mechanical properties of filament wound composites is investigated experimentally. The winding process variables considered are the fiber tensions and the fiber ends. The filament wound ring specimens are fabricated using 3-axis controlled filament winding machine. Two types of carbon fibers, TZ-507 and IZ-40, are used as reinforcements and epoxy for filament winding is used as resin. During the winding process, the fiber tensions are varied from 0.5kgf to 3.0kgf, and the number of the fiber ends are varied from 1 to 6. The fiber volume fractions and the void contents for the ring specimens are measured through the resin digestion. The mechanical properties of the ring specimens are also evaluated by the split disk test. The test results show that the winding process variables affect the fiber volume fractions and the void contents of the ring specimens, which result in the variation of the tensile properties of the ring specimens. Therefore, suitable winding process variables should be applied to maximize the structural performance and the productivity for filament wound structures.

• Magazine of the Korea Concrete Institute
• /
• v.6 no.2
• /
• pp.118-128
• /
• 1994

There have been conducted a lot of works on shear behavior of steel fiber reinforced concrete beams. Fiber reinforced concrete beams without shear reinforcement were tested to determine their cracking shear strengths and ultimate shear capacities. Results of tests on 14 reinforced concrete beams (including 11 containing steel fibers) are reported. Two parameters were varied in the study, namely, the volume fraction of fibers and shear span-to-depth ratio.The effects of fiber incorporation on failure modes, deflections, cracking shear strength, and ul~imate shear strength have been examined. Resistance to shear stresses have been found to be improved by the inclusion of fibers, The mode of failure changed from shear to flexure when the shear span-to-depth ratio exceeds 3.4. Based on these investigations, a method of computing the shear strength of steel fiber reinforced concrete beam is suggested. The comparisons between computed values and expenmentally observed values are shown to verify the proposed theoretical treatment and steel fibers efficiency.

• Computers and Concrete
• /
• v.14 no.3
• /
• pp.299-313
• /
• 2014

Effects of polypropylene (PP) fibers, steel fibers (SF) and hybrid on the properties of highstrength fiber reinforced self-consolidating concrete (HSFR-SCC) under different volume contents are investigated in this study. Comprehensive laboratory tests were conducted in order to evaluate both fresh and hardened properties of HSFR-SCC. Test results indicated that the fiber types and fiber contents greatly influenced concrete workability but it is possible to achieve self consolidating properties while adding the fiber types in concrete mixtures. Compressive strength, dynamic modulus of elasticity, and rigidity of concrete were affected by the addition as well as volume fraction of PP fibers. However, the properties of concrete were improved by the incorporation of SF. Splitting tensile and flexural strengths of concrete became increasingly less influenced by the inclusion of PP fibers and increasingly more influenced by the addition of SF. Besides, the inclusion of PP fibers resulted in the better efficiency in the improvement of toughness than SF. Furthermore, the inclusion of fibers did not have significant effect on the durability of the concrete. Results of electrical resistivity, chloride ion penetration and ultrasonic pulse velocity tests confirmed that HSFR-SCC had enough endurance against deterioration, lower chloride ion penetrability and minimum reinforcement corrosion rate.

• Journal of the Korean Society of Safety
• /
• v.12 no.4
• /
• pp.230-240
• /
• 1997

An experimental research investigation of the fracture properties of polypropylene fiber reinforced concrete is reported. Fibers used in this experiment were two types, monofilament and fibrillated polypropylene fibers. Fiber length was 19 mm, and volume fractions were 0, 1, 2, and 3%. Also, as initial notch depths influence the fracture properties of fiber reinforced concrete, the notch depth ratios by specimen height were 0.15, 0.30 and 0.45. The main objective of this experimental program is to obtain the load-deflection and the load-CMOD curves, to investigate the fracture properties of the polypropylene fiber reinforced concretes. Therefore, the flexural specimen testings on the four-point bending were conducted. Then, the load-load point displacement and the load-crack mouth opening displacement curves were measured. The effects of different volume fractions of the monofilament and the fibrillated polypropylene fiber reinforced concrete on the compressive strength, flexural strength and toughness, stress intensity factor, and fracture energy were investigated through the experimental results.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.4
• /
• pp.407-412
• /
• 2010

The objective of this study is the estimation of the mechanical properties of HIP-treated MMCs by an optimized manufacturing process. The Ti-MMCs were fabricated by HIP and rotary swaging (RS) for secondary processing. The Ti-MMCs with different tungsten fiber contents of 0, 6, 9, and 12 vol% were subjected to tensile tests, fatigue tests, and hardness tests. The results show that the hardness values of Ti-MMCs increased with the increasing volume percent of tungsten fibers, the tensile strength increased by approximately 50% (specific strength: 38%) at the 9 vol%. The value of tungsten-fiber orientation F affects the tensile strength. The fatigue strengths of the Ti-MMCs did not improve. HIP is a useful manufacturing method for Ti-MMCs and RS is an important process for improving fiber orientation during secondary processing.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.6
• /
• pp.21-29
• /
• 2014

This paper deals with the bonding characteristic of grouted joint connections of monopile support structures for offshore wind power facilities. For the integration of pile connection of wind power supporting structure, fiber reinforced high performance cementeous grout was developed and the ultimate compressive strength of it is 125MPa and the direct tensile strength is 7.5 MPa at 7 days. To assess the bond strength of grout filled in pile connection, small scaled direct bond tests under axially loaded was performed and analyzed according the existing guidelines. The fiber volume fraction (0%, 0.5% and 0.9%), aspect ratio of fiber (60 and 80) and the ratio of height to spacing of shear key (0.013 and 0.056) were adopted as the experimental variables. From the test results, the maximum bond strength among the all specimens was 30.8MPa and the bond strength of grouted connection was affected by the ratio of height to spacing of shear key than the fiber volume fraction.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.6
• /
• pp.189-196
• /
• 2018

Degraded shear performance of reinforced concrete members with recycled coarse aggregate (RCA) compared to flexural strength is a problem. To address this, steel fibers can be used as concrete reinforcement material. In this study, the strength and deformation characteristics of SFRC beams using RCA were to be determined by shear tests. Major experimental variables include the volume fraction of steel fiber (0, 0.5%, 1%), the replacement rate of RCA (0%, 100%), and the shear span ratio (a/d = 1, 2). As a result of the experiment, the shear strength of the specimen increased as the rate of mixing steel fiber increased. For specimens with RCA and 1% steel fiber, the maximum shear strengths increased by 1.77 - 6.25% compared to specimens with normal coarse aggregate (NCA). On the other hand, at 0-0.5% steel fiber, the shear strengths of RCA specimens were reduced by 24.2% to 49.2% compared to NCA specimens. This indicates that reinforcement with 1% volume fraction of steel fiber greatly contributes to preventing shear strength reduction due to the use of RCA.