• 한국세라믹학회지
• /
• 제32권5호
• /
• pp.549-558
• /
• 1995

Mn-Zn ferrite granules were prepared by spray drying of the slurry containing different kinds and concentration of binders at various spray drying temperatures and atomizing pressures. The characteristics of the spraydried granules were analyzed according to the processing variables of spray drying and the slurries containing different solid loading and kinds and concentration of binders. Typical shape of the spray dried granules was spherical. The granules spray dried at 15$0^{\circ}C$ were more spherical and containing lower hollow percentage than any other granules prepared at higher temperature. The granules prepared at higher atomizing pressures were more spherical and become smaller in size. The granules prepared using slurry containing higher solid loading were larger in size and less defective in shape. As increasing the concentration of binder the number of donut-shaped granules was increased and the size distribution become broader. The granules prepared using the slurry containing PVA 205 were more spherical than those containing PVA 217 and PVA 117. As the amount of granules which were donut-shaped or dimpled increased the compaction response were less effective. The hollows were not fractured completely even at hight pressures and remained after sintering.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 춘계학술대회 논문집 방전 플라즈마 유기절연재료 초전도 자성체연구회
• /
• pp.69-72
• /
• 2004

In recent, there have been several developments in lamp technology that promise savings in electrical power consumption and improved quality of the lighting space. Above all, the advantage of ring-shaped electrodeless fluorescent lamp is the removal of internal electrodes and heating filaments that are a light-limiting factor of conventional fluorescent lamps. The ring-shaped electrodeless lamp is intended as a high efficacy replacement for the incandescent reflector lamp in many applications. Therefore, the life time of ring-shaped electrodeless fluorescent lamps is substantially higher than that of conventional fluorescent lamps and last up to 60,000 hours. In this paper, we present measurement results of electrical characteristics of a ring-shaped electrodeless fluorescent lamp as a function of frequency and number of coil turns using a highly permeable Mn-Zn ferrite. It is found that the impedance are increased while the quality factor decreases as frequency increases.

• 대한금속재료학회지
• /
• 제50권11호
• /
• pp.793-800
• /
• 2012

The effect of cold rolling on the microstructural evolution in 22Cr-0.2N micro-duplex stainless steel was investigated. The 22Cr-xNi-yMn-0.2N duplex stainless steel plates with various Ni and Mn contents were fabricated. The steels were vacuum induction melted and hot rolled, followed by annealing treatment at the temperature range of $1000-1100^{\circ}C$, in which both the austenite and ferrite phases were stable. The volume fraction of the ferrite phase depending on the alloy compositions of Ni and Mn increased with an increase in the annealing temperature. Grain growth in the ferrite phase occurred markedly after cold rolling followed by annealing, while fine recrystallised grains were still found in the austenite phase. A large number of martensite laths was found in the microstructure of cold rolled steels, which should be formed by strain-induced martensite from the austenite phase. The intersections of stacking faults were revealed by TEM observation. The volume fraction of the martensite phase increased with an increase of the reduction ratio by cold rolling.

• 한국산업융합학회 논문집
• /
• 제24권5호
• /
• pp.525-530
• /
• 2021

The purpose of this study was to investigate the effect of spherodizing heat treatment holding time on the microstructure and mechanical properties of the accelerated cooling-treated API X70 steel, which is mainly used as a structural material for line pipe steel for natural gas pipes. The accelerated cooling-treated API X70 steel was spherodizing treated at 700℃ for 12~48 h. The microstructure was observed using an OM and a FEG-SEM, and mechanical properties were obtained by tensile test. The microstructure of the API X70 steel was banded in the hot rolling direction, and the polygonal ferrite(PF) adjacent to pearlite(P) has mainly a fine size, and coarse PF and fine acicular ferrite were formed in the middle of P and P. As the spherodizing treatment time increased, the number of carbide particles decreased and its distribution interval increased, and the ferrite grain size was coarsened. The tensile strength decreased and the ductility increased with spherodizing treatment time, and the yield point elongation was disappeared in a stress-strain curve after the spherodizing treatment.

• 동력기계공학회지
• /
• 제14권2호
• /
• pp.71-77
• /
• 2010

This paper was studied on microstructure, mechanical properties and corrosion characteristics of 316L stainless steel pipe welds was fabricated by orbital welding process. S-Ar specimen was fabricated by using Ar purge gas and S-$N_2$ specimen was fabricated by using $N_2$ purge gas. Ferrite was not detected in weld metal of S-$N_2$ specimen but the order of 0.13 Ferrite number(FN) was detected in weld metal of S-Ar specimen. Oxygen and Nitrogen concentration of S-$N_2$ specimen was higher than S-Ar specimen on HAZ and inner bead. The welds microstructural characteristics of S-Ar and S-$N_2$ specimens are similar. The microvickers hardness values of S-Ar and S-$N_2$ specimens welds were similar and average values of each regions were in the range of 174~194. The microstructures of S-Ar and S-$N_2$ weld metal were full austenite by primary austenite solidification. The Solidification structures of S-Ar and S-$N_2$ weld metal were formed directional dendrite toward bead center. The potentiodynamic polarization curve of STS 316L pipe welds exhibited typical active, passive, transpassive behaviour. Corrosion current density$(I_{corr.})$ and corrosion rate values of S-Ar specimen in 0.1M HCl solution were $0.95{\mu}A/cm^2$ and $0.31{\mu}A$/year respectively. The values of S-$N_2$ specimen were $1.4{\mu}A/cm^2$ and $0.45{\mu}m$/year.

• 열처리공학회지
• /
• 제25권2호
• /
• pp.74-79
• /
• 2012

This study has been carried out to investigate the precipitation behavior of ${\chi}$ phase and effect of ${\chi}$ phase precipitation on the impact toughness of 25%Cr-7%Ni-4%Mo super duplex stainless steel. It was proved that the ${\chi}$ phase was a intermetallic compound, which represented the higher chromium and molybdenum concentration than the matrix phases, and also showed the higher molybdenum concentration than the ${\sigma}$ phase. The ${\chi}$ phase was precipitated at the interface between ferrite and austenite or inside the ferrite matrix in the early stage of aging. The number of ${\chi}$ phase precipitates increased with increasing aging time, however, after showing the maximum value, the number was decreased due to the gradual transformation of ${\chi}$ phase into ${\sigma}$-phase. Aging ferrite phase was decomposed by the $r^2$ phase and ${\sigma}$-phase. Impact toughness rapidly decreased with time in the initial stage of aging at ${\chi}$ phase start to precipitate. Thus, the impact toughness was greatly influence for the precipitation of ${\chi}$ phase.

• 열처리공학회지
• /
• 제35권4호
• /
• pp.211-219
• /
• 2022

It is known that superplastic materials with ultrafine grains have high elongation mainly due to grain boundary sliding. Therefore, in the present study we examined the influence of grain refinement, caused by a repetitive cold rolling and annealing process, on both superplastic elongation and superplastic deformation mechanism. The cold rolling and annealing process was repetitively applied up to 4 times using Fe-10Mn-3.5Si alloy. High-temperature tensile tests were conducted at 763 K with an initial strain rate of 1 × 10^-3 s^-1 using the specimens. The superplastic elongation increased with the number of the repetitive cold rolling and annealing process; in particular, the 4 cycled specimen exhibited the highest elongation of 372%. The primary deformation mechanism of all specimens was grain boundary sliding between recrystallized α-ferrite and reverted γ-austenite grains. The main reason for the increase in elongation with the number of the repetitive cold rolling and annealing process was the increase in fractions of fine recrystallized α-ferrite and reverted γ-austenite grains, which undergo grain boundary sliding.

• Corrosion Science and Technology
• /
• 제13권2호
• /
• pp.48-55
• /
• 2014

Influence of annealing temperature on the microstructure and resistance to pitting corrosion of the hyper duplex stainless steel was investigated in acid and neutral chloride environments. The pitting corrosion resistance is strongly dependent on the microstructure, especially the presence of chromium nitrides ($Cr_2N$), elemental partitioning behavior and volume fraction of ferrite phase and austenite phase. Precipitation of deleterious chromium nitrides reduces the resistance to pitting corrosion due to the formation of Cr-depleted zone. The difference of PREN (Pitting Resistance Equivalent Number) values between the ferrite and austenite phases was the smallest when solution heat-treated at $1060^{\circ}C$. Based on the results of electrochemical tests and critical crevice temperature tests, the optimal annealing temperature is determined as $1060^{\circ}C$.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2004년도 추계학술대회 논문집 전기기기 및 에너지변환시스템부문
• /
• pp.110-112
• /
• 2004

The magnetization directions of a polar anisotropic ferrite-bonded magnet are analyzed by finite element method (FEM). The influence of the width of Sm-Co magnets for magnetic field generation is investigated. The surface flux densities of the polar anisotropic magnets are analyzed and compared according to the pole number and thickness of the magnets. And the electromotive force (EMF) values of brushless DC motors with the magnets are investigated.

• 한국의학물리학회지:의학물리
• /
• 제9권2호
• /
• pp.73-75
• /
• 1998

Mossbauer spectroscopy methods are discussed when applied to test the properties of magnetic suppositories used in medicine. The experiments were carried out on magnetic rectal suppositories containing parmadine and fine-dispersed ferrite powder (BaOㆍnFe$_2$O$_3$) as a magnetic filler. According to the data on the value of effective magnetic field on $^{57}$ Fe nuclei in ferrite magnetic sublattices, the stoichiometric n-number equals approximately 5.5; this value corresponds to the composition range of optimal magnetic properties.