• Journal of the Korean Magnetics Society
• /
• v.13 no.1
• /
• pp.6-14
• /
• 2003

The purpose of this study is to investigate the effect of chemical reaction with a bonding glass on physical and magnetic properties of Fe-Hf-N/SiO$_2$ and Fe-Hf-N/Cr/SiO$_2$ thin films. When the Fe-Hf-N/SiO$_2$ films were reacted with the bonding glass, the soft magnetic properties of them were extremely degraded. At $600^{\circ}C$, the saturation magnetization of the reacted film decreased to 1 kG, and its coercivity increased to 27 Oe, and its effective permeability decreased to 70. It was found that the degradation of soft magnetic properties of the Fe-Hf-N/SiO$_2$ films reacted with the bonding glass were attributed to the oxidation of the Fe-Hf-N layers to HfO$_2$ and Fe$_3$O$_4$. The soft magnetic properties of the Fe-Hf-N/Cr/SiO$_2$ films reacted with the bonding glass were degraded less than those of Fe-Hf-N/SiO$_2$ films. At $600^{\circ}C$, the saturation magnetization of the reacted film decreased to 13.5 kG, and its coercivity increased to 4 Oe, and its effective permeability decreased to 700. It was found that the Cr layer suppressed the oxidation of the Fe-Hf-N layers during the chemical reaction between the Fe-Hf-N layer and bonding glass.

• Korean Journal of Materials Research
• /
• v.14 no.11
• /
• pp.780-785
• /
• 2004

The degradation mechanism of soft magnetic properties of $Fe-Hf-N/Cr/SiO_2$ thin films reacted with a bonding glass was investigated. When $Fe-Hf-N/Cr/SiO_2$ films were annealed under $600^{\circ}C$ without the bonding glass, the compositions and the soft magnetic properties of Fe-Hf-N layers were not changed. However, after reaction with the bonding glass at $550^{\circ}C$, the soft magnetic properties of the film were degraded. At $600^{\circ}C$, the saturation magnetization of the reacted film decreased to 13.5 kG, and its coercivity increased to 4 Oe, and its effective permeability decreased to 700. It was founded that O diffused from the glass into the Fe-Hf-N layers during the reaction and generated $HfO_2$ phases. It was considered that the soft magnetic properties of the $Fe-Hf-N/Cr/SiO_2$ films reacted with the bonding glass were primarily degraded by the formation of the Fe-Hf-O-N layer of which the Fe content was below 60 $at\%$, and secondarily degraded by the Fe-Hf-O-N layer above 70 $at\%$.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.6
• /
• pp.255-259
• /
• 2011

The thickness dependence of magnetic properties was experimentally investigated in nanocrystalline Fe-Hf-N thin films fabricated by a RF magnetron sputtering method. In order to investigate the thickness effect on their magnetic properties, the films are prepared with different thickness ranges from 90 nm to 330 nm. It was revealed that the coercivity of the thin film increased with film thickness. On the contrary, the saturation magnetization decreased with film thickness. On the basis of the SEM and TEM, an amorphous phase forms during initial growth stage and it changes to crystalline structure after heat treatment at $550^{\circ}C$. Nanocrystalline Fe-Hf-N particles are also generated.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1997.05a
• /
• pp.52-53
• /
• 1997

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2005.05a
• /
• pp.285-285
• /
• 2005

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.11a
• /
• pp.132-132
• /
• 2002

• Korean Journal of Crystallography
• /
• v.12 no.3
• /
• pp.182-187
• /
• 2001

The purpose of this study is to investigate the degradation of soft magnetic properties of Fe-Hf-N thin films after annealing in vacuum. They were annealed at 450℃∼650℃. The microstructure and crystal phase of the selected area of the thin films were analyzed by TEM and SAD. After annealing at 450℃-600℃, the coercivity of the films increased by 0.2 Oe and the effective permeability decreased by 1500 as compared with them before annealing due to the growth of α-Fe crystallites. The saturation magnetic flux density of the films increased by 0.5 KG after annealing under 600℃. However, the soft magnetic properties of the film annealed at 650℃ degraded abruptly, which was attributed to the destruction of nano-crystalline microstructure of the film due to the rapid growth of α-Fe crystallites with the segregation of N sited in the α-Fe lattice into HfN.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.519-523
• /
• 1995

The Fe-TM-C-N nanocrystalline films (TM : Hf, Zr and Nb) are investigated to examine the relation between microstructure and soft magnetic properties. In these films, as the atomic radius of TM element increases, $P_{N2}$ which was added to get good soft magnetic properties was decreased and the maximum value of the permeability shifted to the high Fe range in the composition diagram. The best soft magnetic properties achieved in these films are : Hc of 0.15 Oe, $\mu_{eff}$ of 7800 (1MHz) and $4{\pi}M_{s}$ of 17.5 kG in Fe-Hf-C-N film ; Hc of 0.06 Oe, $\mu_{eff}$ of 2750 (1MHz) and $4{\pi}M_{s}$ of 16.8 kG in Fe-Zr-C-N film and Hc of 0.31 Oe; $\mu_{eff}$ of 2100 (1MHz) and $4{\pi}M_{s}$ of 15.5 kG in Fe-Nb-C-N film. It was considered that the stronger the bonding force between TM and C(N), the finer TM(C,N) phase is precipitated and therefore, the finer $\alpha$-Fe grains are formed. The effective permeability of the Fe-Zr-C-N films and Fe-Nb-C-N films remains nearly constant up to 10 MHz.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.6
• /
• pp.480-490
• /
• 2003

Effects of plasma-nitriding on the pitting corrosion of Fe-30at%Al-5at%Cr alloy containing Ti, Hf, and Zr were investigated using potentiostat in 0.1M HCl. The specimen was casted by the vacuum arc melting. The subsequent homogenization was carried out in Ar gas atmosphere at $1000^{\circ}C$ for 7days and phase stabilizing heat treatment was carried out in Ar gas atmosphere at $500^{\circ}C$ for 5 days. The specimen was nitrided in the $N_2$, and $H_2$, (1:1) mixed gas of $10^{-4}$ torr at $480^{\circ}C$ for 10 hrs. After the corrosion tests, the surface of the tested specimens were observed by the optical microscopy and scanning electron microscopy(SEM). For Fe-30at%Al-5Cr alloy, the addition of Hf has equi-axied structure and addition of Zr showed dendritic structure. For Fe-30at%Al-5Cr alloy containing Ti, plasma nitriding proved beneficial to decrease the pitting corrosion attack by increasing pitting potential due to formation of TiN film. Addition of Hf and Zr resulted in a higher activation current density and also a lower pitting potential. These results indicated the role of dendritic structure in decreasing the pitting corrosion resistance of Fe-30Al-5Cr alloy. Ti addition to Fe-30Al-5Cr decreased the number and size of pits. In the case of Zr and Hf addition, the pits nucleated remarkably at dendritic branches.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2002.12a
• /
• pp.214-215
• /
• 2002

High saturation magnetization (B$\_$s/) and excellent high frequency characteristics of magnetic thin films has been recognized as the most important requirement for further miniaturization and higher frequency operation in magnetic devices, such as magnetic heads and magnetic sensors. Up to now, Fe-X-N (X =Ti, Hf, and Al etc.) films with B$\_$s/ of 15 ∼ 19 kG and coercivity (H$\_$c/) of 0.5 ∼ 5.0 Oe have been successfully fabricated and proven to satisfy various requirements as a potential candidate for thin film head materials. (omitted)