• Proceedings of the Materials Research Society of Korea Conference
• /
• 2000.11a
• /
• pp.155-155
• /
• 2000

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.1
• /
• pp.51-57
• /
• 2013

We have applied mechanical alloying (MA) to produce Heusler $Fe_2VAl$ thermoelectric alloy using a mixture of elemental $Fe_{50}V_{25}Al_{25}$ powders. An optimal milling and heat treatment conditions to obtain the single phase of Fe2VAl compound with fine microstructure were investigated by X-ray diffraction and differential scanning calorimetry (DSC) measurement. The $Fe_{50}V_{25}Al_{25}$ MA sample ball-milled for 60 hours exhibits a bcc ${\alpha}$-(Fe,V,Al) solid solution. Single phase of Heusler $Fe_2VAl$ compound can be obtained by MA of $Fe_{50}V_{25}Al_{25}$ mixture for 60 hours and subsequently heated up to $700^{\circ}C$. Sintering of the MA powders was performed in a spark plasma sintering (SPS) machine using graphite dies at $900{\sim}1000^{\circ}C$ under 60 MPa. The Vickers hardness of bulk sample sintered at $1000^{\circ}C$ was high value of Hv 870. All compact bodies have a high relative density above 90 % with metallic glare on the surface.

• Korean Journal of Materials Research
• /
• v.22 no.4
• /
• pp.169-173
• /
• 2012

Recently, various attempts to produce a heat sink made of Al 6xxx alloys have been carried out using die-casting. In order to apply die-casting, the Al alloys should be verified for die-soldering ability with die steel. It is generally well known that both Fe and Mn contents have effects on decreasing die soldering, especially with aluminum alloys containing substantial amounts of Si. However, die soldering has not been widely studied for the low Si aluminum (1.0~2.0wt%) alloys. Therefore, in this study, an investigation was performed to consider how the soldering phenomena were affected by Fe and Mn contents in low Si aluminum alloys. Each aluminum alloy was melted and held at $680^{\circ}C$. Then, STD61 substrate was dipped for 2 hr in the melt. The specimens, which were air cooled, were observed using a scanning electron microscope and were line analyzed by an electron probe micro analyzer. The SEM results of the dipping soldering test showed an Al-Fe inter-metallic layer in the microstructure. With increasing Fe content up to 0.35%, the Al-Fe inter-metallic layer became thicker. In Al-1.0%Si alloy, the additional content of Mn also increased the thickness of the inter-metallic layer compared to that in the alloy without Mn. In addition, EPMA analysis showed that Al-Fe inter-metallic compounds such as $Al_2Fe$, $Al_3Fe$, and $Al_5Fe_2$ formed in the die soldering layers.

• Journal of Korea Foundry Society
• /
• v.21 no.6
• /
• pp.328-335
• /
• 2001

The objective of this study is to investigate on manufacturing Al-scrap into hypereutectic Al-Si alloy by using electromagnetic force. The Fe element in the aluminium scrap was controlled by intermetallic compound method and using EMF(electromagnetic force). The most lumped compound was found after 10min holding at $690^{\circ}C$. A number of segregated compound was revealed when imposed to EMF at 30A. The refinement of primary Si particles was achieved by EMF stirring. Primary Si particles were refined and spheroidized most of all with the magnetic intensity of 180G for 10 min.

• Korean Journal of Materials Research
• /
• v.11 no.9
• /
• pp.733-739
• /
• 2001

In Al-25Nb binary system, it was observed only formation of $D0_{22}$ $Al_3Nb$ intermetallic compound after 5hr milling but it was not observed formation of meta stable phase like L1$_2$ phase. In this state, $D0_{22}$ $Al_3Nb$ fabricated had nano sized grain of approximately 20nm. Ternary systems, transition metals such as Cr, Cu, Fe, Mn were added 6~12at.% as substitution of Al, showed formation of $D0_{22}$ $Al_3Nb$ like Al-25Nb binary system. In Al- l2Cu-25Nb system, it was observed that broad XRD pattern like amorphization of Al and not observed formation of $D0_{22}$ $Al_3Nb$ after 5hr milling. But there was mixed phase of a lot of amorphous Al and little $D0_{22}$ $Al_3Nb$ through TEM. In the states of unalloyed, 5~7hr milling time, those showed exothermic reaction at 35$0^{\circ}C$, which was formation of $D0_{22}$ $Al_3Nb$ like Al-25Nb binary system. With increasing milling time to 10hr, $D0_{22}$ $Al_3Nb$ was transformed to mixed phase of amorphous and nanocryatlline, having approximately 10nm grain but the meta stable $Al_3Nb$ was not fabricated by adding transition metals.

• Korean Journal of Materials Research
• /
• v.10 no.8
• /
• pp.569-574
• /
• 2000

To improve the ductility of $Al_3Hf$ and $Al_3Ta$ intermetallic compounds, which are the potential temperature structural materials, the mechanical alloying behaviour and the effect of ternary additions on the $Ll_2$ phase formation were investigated. During the mechanical alloying by the SPEX mill, the $Ll_2$ $Al_3Hf$ intermetallic compound was formed after 6 hours of milling in AL-25%Hf system. In AL-25%Ta system, however, only the $D0_{22}$ $Al_3Ta$ intermetallic compound was formed until 30 hours of milling and the $Ll_2$ phase was not observed. In AL-12.5%M-25%Ta(M=Cu, Zn, Mn, Fe, Ni) systems, the additions of Cu and Zn had no effect on the $D0_{22}$ structure of the binary $Al_3Hf$ and the additions of Mn, Fe and Ni produced the amorphous phase. Therefore it was considered that these ternary additions could not overcome the energy difference between $Ll_2$ and $D0_{22}$ structures in the $Al_3Hf$ intermetallic compound. In AL-12.5%M-25%Hf(M=Cu, Zn, Mn, Fe, Ni)systems, the additions of Cu and Zn did not affect the $Ll_2$ structure of the binary $Al_3Hf$ but the additions of oMn, Fe and Ni produced the amorphous phase as they did in AL-12.5%M-25%Ta systems. Therefore, it was considered that the Ni, Mn and Fe additions promote the formation of amorphous phase in $Al_3X$ intermetallic compounds.

• Korean Journal of Materials Research
• /
• v.9 no.11
• /
• pp.1102-1107
• /
• 1999

FeAl matrix composite was fabricated successfully by hot-pressing. The mechanical properties of FeAl alloys have been widely studies, but their behaviors of surface hardening effect by plasma nitriding has not yet been studied. This study was to analysis the relationship between microstructure of the sintered composite by hot-pressing and surface hardening at plasma nitriding treatment. Surface hardening of FeAl base alloys was improved by plasma nitriding with increasing plasma treatment time. Excellent surface hardness in the FeAl alloys could be obtained by plasma nitriding($\textrm{H}_{\textrm{v}}$ 100gf, diffusion layer: 1100~1450kg/$\textrm{mm}^2$, matrix : 330~360kg/$\textrm{mm}^2$). Diffusion layer size increased with increasing plasma nitriding times and decreased with increasing Sic, content.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1316-1317
• /
• 2006

The paper investigates the possibility to avoid extrinsic embrittlement of $Ni_3Al$, also increasing the high temperature strength, by alloying with both Fe - of a high strengthening effect and Cr - able to remove a part of diffused oxygen along the grain boundaries. As Cr homogenization in $Ni_3Al$ is difficult because of its low diffusion coefficient, for its improving a mechanical alloying (MA) step before the compound synthesis by Self-propagating High-temperature Synthesis (SHS) was adopted. The obtained better homogenization resulted in higher mechanical resistance and deformability than of the unalloyed $Ni_3A/Ni_3Al$ alloys of the same composition obtained without MA step.

• Journal of Korea Foundry Society
• /
• v.21 no.3
• /
• pp.179-186
• /
• 2001

Melt super-heating which promotes shape modification of ${\beta}$ intermetallic compounds was conducted to improve mechanical properties of recycled AC2B aluminum alloy. Modification of needle-shape ${\beta}$ intermetallic compounds was effective for the specimens of AC2B aluminum alloys containing 0.85wt.% Fe by melt super-heating, in which the melts had been held at $850^{\circ}C$ or $950^{\circ}C$ for 30 minutes respectively. Owing to the modification of needle-shape of ${\beta}$ intermetallic compounds by melt superheating of the alloy with containing 0.85wt.% Fe to $950^{\circ}C$, increases in elongation and tensile strength were prominent to be more than double and 55% respectively in comparison with the melt heated to $740^{\circ}C$. Moreover, modification of needle-shape ${\beta}$ intermetallic compounds in the alloy containing O.85wt.% Fe by $950^{\circ}C$ melt super-heating led to 48% improvement of the value of impact absorbed energy as compared with the melt heated to $740^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.33 no.1
• /
• pp.8-14
• /
• 2023

In order to broaden the range of application of light weight aluminum alloys, it is necessary to enhance the mechanical properties of the alloys and combine them with other materials, such as cast iron. In this study, the effects of adding small amounts of Cu and Zr to the Al-Si-Mg based alloy on tensile properties and corrosion characteristics were investigated, and the effect of the addition on the interfacial compounds layer with the cast iron was also analyzed. Although the tensile strength of the Al-Si-Mg alloy was not significantly affected by the additions of Cu and Zr, the corrosion resistance in 3.5 %NaCl solution was found to be somewhat lowered in this research. The influence of Cu and Zr addition on the type and thickness of the interfacial compounds layer formed during compound casting with cast iron was not significant, and the main interfacial compounds were identified to be Al₅FeSi and Al₈Fe₂Si phases, as in the case of the Al-Si-Mg alloys.