• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05a
• /
• pp.84-87
• /
• 2003

The interfacial diffusion in Fe/Cr/MgO(001) multilayers has been studied using synchrotron x-ray techniques, such as x-ray reflectivity, extended x-ray absorption fine structures (EXAFS), and anomalous x-ray scattering (AXS). The results of x-ray reflectivity indicated that the interfacial roughness of Fe/Cr multilayers with Cr-$4{\AA}$-thick was larger than that with Cr-$4{\AA}$-thick. The results of EXAFS indicated that the Fe element dominantly diffuse into the stable Cr layers at the Fe/Cr interface. The AXS was certified the existence of the interdiffused Fe element in the Cr layers. Our study revealed that the rough interface of the Fe/Cr multilayers was caused by the interfacia diffusion of Fe element into the Cr layers.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.2
• /
• pp.223-227
• /
• 2004

We have studied the interfacial diffusion of Fe/Cr multilayers using synchrotron x-ray techniques, such as x-ray reflectivity, extended x-ray absorption fine structures (EXAFS), and high-resolution x-ray scattering. The results of x-ray reflectivity indicated that the interfacial roughness of Fe/Cr multilayers increased with the Cr-layer thickness. The Fourier transform (FT) of EXAFS data clearly showed that the Fe atoms dominantly diffused into the stable Cr layers at the Fe/Cr interface. The results of high-resolution x-ray scattering supported the interfacial diffusion of Fe atoms. Out study revealed that the dominantly interfacial diffusion of Fe atoms into the Cr layers effects the interfacial roughness of the Fe/Cr multilayers.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.5
• /
• pp.386-392
• /
• 1996

The epitaxial TM/bcc-Cr(001) (TM=Fe, Co, Ni) multilayers have been prepared using MBE. The crystal structure, interlayer exchange coupling and magnetoresistance of those multilayers have been discussed. The structure of Fe, Co and Ni grown on bcc-Cr(001) exhibited bcc(001), distorted hcp(1120) and fcc(110), respectively. In Fe/Cr multilayes, an oscillatory exchange coupling has been observed, but not observed in Ni/Cr system, which may come from the large mixing at interfaces. Large MR ratio (116%, 4.2K) has been obtained in Fe/Cr system, but only 2% in Co/Cr system. This difference can be understood from the view point of the relative potential geight for down spin electrons between TM and Cr.

• Journal of the Korean Magnetics Society
• /
• v.5 no.3
• /
• pp.210-215
• /
• 1995

$Glass\Cr_{40\AA}\{[Cr_{10\AA}\NiFe_{50\AA}]}_N$ multilayers (number of layer N = 1, 2, 3, 4, 5, 6, 10) were made by dc magnetron sputtering under magnetic anisotropy of 200 G. Magnetoresistance curve MR(xx), MR(xy) were measured for the parallel and perpendicular current direction to external magnetic field. MR(xx) curves for the number of layer N=1, 5, 10 were almost became about zero percent, however the curves of other numbers appeared the phenomena of "positive magnetoresistance" that the resistance increased to external magnetic field, and the irregular and reversed curves in the vicinity of H=0 Oe.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.702-709
• /
• 1995

In this paper we review recent work in our laboratory on nanocomposite CoSm-based films including CoSm with Cr underlayer (CoSm//Cr), exchange-coupled magnetic films consisting of CoSm and FeCo layers (CoSm/FeCo), and CoSm multilayers with nonmagnetic spacing layers of SmO (CoSm/SmO). The emphasis is on detailed investigations of microstructure and magnetic properties for CoSm//Cr films, exchange-spring effects for CoSm/FeCo films, and interlayer effects for (CoSm/ SmO) multilayers.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2002.04a
• /
• pp.54-55
• /
• 2002

• Journal of the Korean Magnetics Society
• /
• v.9 no.1
• /
• pp.41-47
• /
• 1999

$Buffer/[NiFe/Cu/CoFe(Co)/Cu]_N$ spin valve multilayers prepared by dc magnetron sputtering on a corning glass substrate using NiFe and CoFe(Co) posses different coercivities. Dependence of magnetoresistance on the type and thickness of buffer layer, thickness of Cu, NiFe, stacking number of multilayer, substrate temperature and annealing temperature in the form $[NiFe/Cu/CoFe(Co)/Cu]_N$ spin-valve multilayers were investigated. To evaluate effect of magnetoresistance for this samples, X-ray diffraction analysis, vibrating sample magnetometer analysis, and magnetoresistance measurement (4-probe method) were performed the maximum magnetoresistance ratio and coercivity were 7.5 % and 140 Oe, respectively for $Cr-50{\AA}/[NiFe-20{\AA}/Cu-{\AA}/Co-20{\AA}/Cu-50{\AA}]_10$ at substrate temperature of 9$0^{\circ}C$. Magnetoresistance slope maintained 0.25%/Oe until 15$0^{\circ}C$ of annealing temperature, and then decreased to 0.03%/Oe at 20$0^{\circ}C$. It was confirmed that the main factor of thermal stability was deteriorating of soft magnetic properties in the NiFe layer.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2003.12a
• /
• pp.195-195
• /
• 2003

• Journal of the Korean Magnetics Society
• /
• v.8 no.6
• /
• pp.362-368
• /
• 1998

The magnetic properties, thermal stability and anti-corrosion properties of $Cr_86Al_14$ spin valves multilayers were studied. It was found that the magnetic properties of $Cr_86Al_14$ spin valves depend on the thickness of antiferromagnetic, ferromagnetic and non-ferromagnetic layers. Exchange coupled field ($H_{ex}$) and magnetoresistance ratio (%) showed the largest value of 20 Oe, 2 % in $glass/Cr_{86}Al_{14}(600 $\AA$)/Ni_{81}Fe_{19}(50$\AA$)/Cu(40 $\AA$)/Ni_{81}Fe_{19}(40 $\AA$)$ spin valves. The $H_{ex}$ MR ratios (%) of CrAl and FeMn spin valves were decreased with increasing annealing temperatures and were lost at 150 $^{\circ}C$, 250 $^{\circ}C$ respectively. Based on these result, it was elucidated that CrAl is more thermally stable than FeMn. It was also shown that there was no change of $H_{ex}$ MR ratios in CrAl, while FeMn was changed and lost 15 days later in corrosion resistance test under 35 $^{\circ}C$, 90 % humidity condition. FeMn was found to be pitted and peeled off 15 days later by SEM micrographic analysis.

• Journal of the Korean Magnetics Society
• /
• v.8 no.6
• /
• pp.374-379
• /
• 1998

$Mn_1-xCr_xPt_3$ alloy films have been prepared by depositing (Mn, Cr)/Pt multilayers using a rf magnetron sputterer followed by heat treatment. Small and wide angle x-ray diffractometry, magnetic hysteresis loops and Kerr rotation angle spectra of the films have been measured and used to investigate structural, magnetic and magneto-optic properties of the films. The films had a crystal structure of ordered AuCu$_3$ type and the strong preferred orientation of a (111)plane parallel to the film surface. The saturation magnetization of the films was decreased with Cr content reaching almost zero near x=0.58 and then increased for further increasement of Cr content up to x=0.77 over that stayed almost constant. This indicated that Cr atoms were antiferromagnetically coupled with Mn atoms. The magnetic easy axis of MnPt$_3$(x=0) film was parallel to the film surface but those of the films with x$\geq$0.58 increased as Cr content increased reaching about 4 kOe at x=1(CrPt$_3$). The dependence of the Kerr rotation angle on the Cr content was similar to that of the saturation magnetization on the Cr content. The films with x=0.77 and x=1 showed the larger Kerr rotation angle at the wavelengths of near infrared compared to the magneto-optic recording medium, TbFeCo, currently being used.