• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.1
• /
• pp.40-46
• /
• 1999

Rotary bending fatigue tests were carried out to investigate the improvement of fatigue limit in annealed and austempered spheroidal graphite cast iron. Main results obtained are as follows. (1) The tensile strength(hardness) of Series C is higher than that of Series B, and fatigue limits are 245MPa in Series C, 230MPa in Series B and 195MPa in Series A, respectively. (2) The fatigue limits of Series B and Series A are mainly governed by the resistance to fatigue crack initiation. Whereas, the fatigue limit of Series C is governed by the resistance to fatigue crack initiation and growth. The defect size and the resistance to crack initiation and growth should be considered to clarify the fatigue properties in spheroidal graphite cast iron. (3) Improvement of fatigue limit by half-austempering is more reasonable than that of full-austempering treatment in multi defective materials as spheroidal graphite cast iron.

• International journal of steel structures
• /
• v.18 no.5
• /
• pp.1631-1638
• /
• 2018

In the periodic repainting of steel bridges, often the steel surface has to be prepared by using power tools to remove surface contaminants, such as deteriorated paint film and rust, and to increase the adhesive strengths of the paint films to be applied newly. Surface preparation by bristle roll-brush grinding, which is a type of power tool, may additionally introduce compressive residual stress and increase the fatigue resistance of welded joints owing to the impact of rotating bristle tips. In this study, fatigue tests were conducted for longitudinally out-of-plane gusset fillet welded joints and transversely butt-welded joints to evaluate the effect of bristle roll-brush grinding prior to repainting on the fatigue resistance of the welded joints. The test results showed that bristle roll-brush grinding introduced compressive residual stress and significantly increased fatigue limits by over 50%.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2005.11a
• /
• pp.228-229
• /
• 2005

The compressive residual stress, which is induced by shot peening process, has the effect of increasing the intrinsic fatigue strength of surface and therefore would be beneficial in reducing the probability of fatigue damage. However, it was not known that the effect of shot peening in corrosion environment. In this study, the effect of shot peening on corrosion fatigue crack growth of sping steel immersed in 6% $FeCl_3$ solution and corrosion characteristics with considering fracture mechanics. The results of the experimental study corrosion fatigue characteristics of spring steel are as follows; the fatigue crack growth rate of the shot peening material was lower than of the un peening material. And fatigue life shows more improvement in the shot peening material than un peening material. This is because the compressive residual stress of surface operate resistance of corrosion fatigue crack propagation. It is assumed that the shot peening process improve corrosive resistance and mechanical property.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.12 no.1
• /
• pp.196-202
• /
• 2004

The development of new materials with light weight and high strength has become vital to the machinery, aircraft and auto industries. However, there are a lot of problems with developing such materials that require expensive tools, and a great deal of time and effort. Therefore, the improvement of fatigue strength and fatigue life are mainly focused on adopting residual stress(in this thesis). The compressive residual stress was imposed on the surface according to each shot velocity(57, 70, 83, 96 m/sec) based on Shot-peening, which is the method of improving fatigue life and strength. By using the methods mentioned above, the following conclusions have been drawn. 1. The fatigue crack growth rate(da/dN) of the Shot-peened material was lower than that of the Un-peened material. And in stage I, ΔKth, the threshold stress intensity factor, of the shot-peen processed material is high in critical parts unlike the Un-peened material. Also m, fatigue crack growth exponent and number of cycle of the Shot-peened material was higher than that of the Un-peened material. That is concluded from effect of da/dN. 2. Fatigue life shows more improvement in the Shot-peened material than in the Un-peened material. And compressive residual stress of surface on the Shot-peen processed operate resistance force of fatigue crack propagation.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.14 no.3
• /
• pp.88-94
• /
• 2006

The compressive residual stress, which is induced by shot peening process, has the effect of increasing the intrinsic fatigue strength of surface and therefore would be beneficial in reducing the probability of fatigue damage. However, the effect of shot peening in corrosion environment was not known. In this study, investigated is the effect of shot peening on corrosion fatigue crack growth of SAE 5155 steel immersed in 6% $FeCl_3$ solution and corrosion characteristics with considering fracture mechanics. The results of the experimental study corrosion fatigue characteristics of SAE 5155 are as follows; the fatigue crack growth rate of the shot peening material was lower than that of the non-peening material. And fatigue life shows more improvement in the shot peening material than in non-peening material. This is due to the compressive residual stress of surface increases resistance of corrosion fatigue crack propagation. It is assumed that the shot peening process improve corrosive resistance and mechanical property.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.6 no.1
• /
• pp.62-70
• /
• 2007

The development of new materials that are light-weight, yet high in strength has become vital to the machinery, aircraft and auto industries. However, there are a lot of problems with developing such materials that require expensive tools, and a great deal of time and effort. Therefore, the improvement of fatigue strength and fatigue life are mainly focused on by adopting residual stress. The fatigue crack growth rate of the Shot-peened material was lower than that of the Un-peened material. And in stage I, threshold stress intensity factor of the shot-peen processed material is high in critical parts unlike the Un-peened material. Also, fatigue crack growth exponent and number of cycle of the Shot-peened material was higher than that of the Un-peened material. That is concluded from effect of da/dN. And Fatigue life shows more improvement in the Shot-peened material than in the Un-peened material. And compressive residual stress of surface on the Shot-peen processed operate resistance force of fatigue crack propagation.

• Tribology and Lubricants
• /
• v.22 no.2
• /
• pp.73-78
• /
• 2006

The surface modification of automobile parts is of great technological importance for the improvement of corrosion resistance, wear resistance, fatigue strength and so on. Recently, research on the development of the technology of surface modification substituting 6-balance chrome process has progressively been achieved in automobile parts. Although the innovation technology for the improvement of the corrosion-resisting and wear resistant properties through post oxidation after nitrocarburising process had attracted a great attention. For this, anodically potentiodynamic polarisation testing was carried out to corrosion resistance and friction and wear experiment according to applied load and sliding distance was carried out to evaluate the wear resistance of machine structural steel with nitrocarburising and non-nitrocarburising SM45C. The presumed wear volume was calculated with the image processing far evaluation of wear resistance of two materials. The results show that the nitrocarburising had a distinguished corrosion resistance and wear resistance than non-nitrocarburising.

• Journal of Advanced Marine Engineering and Technology
• /
• v.29 no.4
• /
• pp.426-435
• /
• 2005

The lightness of components required in automobile and machinery industries is requiring high strength of components. Therefore this requirement is accomplished as the process of shot-peening method that the compressive residual stress is made on the metal surface as one of various improvement methods. Special research is, therefore, needed about compressive residual stress on the metal surface in the process of shot-peening method. Therefore, in this paper the effect of compressive residual stress of spring steel(JISG SUP-9) by shot-peening on fatigue crack growth characteristics in environmental condition(temperature) and mechanical condition(shot velocity, stress ratio) was investigated with considering fracture mechanics. By using the methods mentioned above, the following conclusions have been drawn. (1) The fatigue crack growth rate(da/dN) of the shot-peened material was lower than that of the un-peened one. In high temperature range. fatigue crack growth rate decreased with increasing temperature range, while fatigue crack growth rate increased by decreasing temperature in low temperature. (2) Fatigue life shows more improvement in the shot-peened material than in the un-peened material. And compressive residual stress of surface on the shot-peen processed operate resistance force of fatigue crack propagation.

• Journal of the Korean Society of Safety
• /
• v.19 no.4 s.68
• /
• pp.20-24
• /
• 2004

Antifatigue failure technology take an important the part of current industries. Currently, the shot peening is used for removing the defect from the surface of steel and improving the fatigue strength on surface. Therefore in this paper the effect of compressive residual stress by shot peening on fatigue crack growth characteristics in stress ratio(R=0.1, 0.3, 0.6)was investigated with considering fracture mechanics. There is difference between shot peening specimen and unpeening specimen. Fatigue crack growth rate of shot peening specimen was lower than that of unpeening specimen. Fatigue lift shows more improvement in the shot peening material than in the unpeening material. And compressive residual stress of surface on the shot peening processed operate resistance force of fatigue crack propagation. That is the constrained force about plasticity deformation was strengthened by resultant stress, which resulted from plasticity deformation and compressive residual stress in the process of fatigue crack propagation.

• Applied Microscopy
• /
• v.48 no.3
• /
• pp.73-80
• /
• 2018

Ductile cast iron is widely used for many automotive components due to its high wear resistance and fatigue resistance in addition to the low cost of fabrication. The improvement of wear resistance and fatigue properties is key to the life time extension and performance increase of the automobile parts. Surface nanocrystallization is a very efficient way of improving the performance of materials including the wear- and fatigue-resistance. Shot peening treatment, as one of the popular and economic surface modification methods, has been widely applied to various materials. In this study, ductile cast iron specimens were ultrasonic shot peening (USP) treated for 5 to 30 min using different ball size. The microstructures were then microscopically analyzed for determination of the microstructural evolution. After the USP treatment, the hardness of pearlite and ferrite increased, in which ball size is more effective than treatment time. With USP treatment, the graphite nodule count near the surface was decreased with grain refinement. The lager balls resulted in an increased deformation, whereas the smaller balls induced more homogenously refined grains in the deformation layer. In addition, formation of nanoparticles was formed in the surface layer upon USP.