• Journal of Welding and Joining
• /
• v.19 no.4
• /
• pp.406-412
• /
• 2001

This study is focussed on the numerical prediction of the thermal fatigue life of a ${\mu}BGA$(Micro Ball Grid Array) solder joint. Numerical method is used to perform three-dimensional finite element analysis for Sn-37mass%Pb. Sn-3.5mass%Ag solder alloys during the given thermal cycling. Strain values, along with the result of mechanical fatigue tests for solder alloys were then used to predict the solder joint fatigue life using the Coffin-Manson equation. In this study, a practical correlation for the prediction of the thermal fatigue life is suggested by using the dimensionless variable $\gamma$. As a result. it could be found that Sn-3.5mass%Ag has longer fatigue life than Sn-37mass%Pb in low cycle fatigue. In addition. the result with ${\gamm}ashow$a good agreement with the FEA results.

• International journal of steel structures
• /
• v.18 no.4
• /
• pp.1242-1251
• /
• 2018

Not all loads contribute to fatigue crack propagation in the welded detail of steel bridges when they are subjected to variable amplitude loading. For fatigue assessment, therefore, non-contributing stress cycles should be truncated. However, stress range truncation is not considered during typical fatigue reliability assessment. When applying the first order reliability method, stress range truncation occurs mismatch between the expected number of cycles to failure and the number of cycles obtained at the time of evaluation, because the expected number of cycles only counts the stress cycles that contribute to fatigue crack growth. Herein, we introduce a calibration factor to coordinate the expected number of cycles to failure to the equivalent value which includes both contributing and non-contributing stress cycles. The effectiveness of stress range truncation and the proposed calibration factor was validated via case studies.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.2
• /
• pp.264-274
• /
• 2001

An integrated fatigue strength assessment system was computerized. The system developed consists of 9 modules: user interface, cycle counting, load history construction, data searching, fatigue properties estimation, fatigue data analysis, true stress and strain analysis, expert system for crack initiation life prediction, fatigue crack initiation and propagation life prediction. Fatigue strength database also was included in this system. The fatigue expert system helps a beginner to predict a fatigue crack initiation life in fatigue strength assessment. The expert system module in this system is developed on the personal computer by using C language and UNiK, an expert system developing tool. To evaluate the system, the results of test under variable loading of SAE and failure data from a field were analyzed. The evaluation show that the system provided fatigue life prediction within 3-scatter band and gave reasonable predictions. To get more accurate predictions of fatigue life without fatigue properties, we recommend utilizing the system along with the fatigue strength database.

• Smart Structures and Systems
• /
• v.14 no.3
• /
• pp.469-477
• /
• 2014

As a kind of intelligent materials, conductive asphalt concrete has a broad application prospect including melting ice and snow on the pavement, closing cracks in asphalt concrete, sensing pavement damage, and so on. Conductive pavement will be suffered from fatigue failure as conventional pavement in the process of service, and this fatigue damage of internal structure can be induced by electrical signal output. The characteristics of electrical signal variation of conductive asphalt concrete in the process of fatigue cracking were researched in this paper. The whole process was clearly divided into three stages according to resistance changes, and the development of fatigue damage wasn't obvious in stage I and stage II, while in stage III, the synchronicity between the resistance and damage began to appear. Thus, fatigue damage variable D and initial damage value $D_0$ represented by the functions of resistance were introduced in stage III. After calculating the initial damage value $D_0$ under different stress levels, it was concluded that the initial damage value $D_0$ had no noticeable change, just ranged between 0.24 and 0.25. This value represented a critical point which could be used to inform the repair time of early fatigue damage in the conductive asphalt pavement.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.8 no.2
• /
• pp.167-175
• /
• 1988

The principle objective of this study is to evaluate the fatigue behavior of structural steel components of highway bridges subjected to service stresses. The main aspects of this investigation are; 1) a measurement and statistical analysis of service stress cycles observed in highway bridge. 2) fatigue tests under equivalent constant-amplitude(CA) loading and simulated variable-amplitude(VA) loading 3) a evaluation of the fatigue behavior under VA-loading by eqivalent root mean cube (RMC) stress range. Theoretically, the RMC model is adequate in evaluation of fatigue behavior under VA-loading, because the regression coefficient (m) of crack growth rate is 3 approximately. The result of fatigue test shows that the RMC model is fitter than the current RMS model in fatigue evaluation under VA-loading. The interaction effects and sequence effects under VA-loading affect little fatigue life of structural components. As the transition rate of stress ranges is higher, the crack growth rate is higher.

• Steel and Composite Structures
• /
• v.1 no.3
• /
• pp.283-294
• /
• 2001

In the present work a constitutive model is developed which permits the assessment of the structural performance through a criterion based on cumulative damage. For it, a damage index is defined and is evaluated through the application of the Miner's rule in low-cycle fatigue. However, the damage index is not considered as a posteriori variable since is incorporated explicitly as an internal variable in the constitutive equations which produces a direct coupling between the damage and the structural mechanical behaviour allowing the possibility of considering as a whole different coupled phenomena. For the elaboration of this damage model, the concepts of the mechanics of continuum medium are applied on lumped dissipative models in order to obtain a coupled simplified model. As a result an elastoplastic model coupled with damage and fatigue damage is obtained.

• Journal of Korean Society of Steel Construction
• /
• v.8 no.4 s.29
• /
• pp.19-29
• /
• 1996

In this paper, it is presumed that the stress time history was generated by simulation method and investigated compatibility in regard to the reappearance of stress time history. In this procedure, the identified frequency distribution of stress range of the steel railroad bridge varies with the rational values of cut off point and bar width. Thus, we show variable aspect of the equivalent stress range results from change of cut off point and bar width. In addition, we analyze the variable of RMC and RMS model due to the cut off point and bar width of the measured stress history which influencs the prediction of fatigue life in the steel railroad bridge. The simulated stress time history is carried out by the superposition method incorporating the vertical load with rotation moment obtained from the Hermition interpolation function, and compared with developing stress results from measured maxi mum stress. Through this study, we can estimate the remaining fatigue life from a safety point of view and comparative accuracy.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2006.05a
• /
• pp.397-398
• /
• 2006

The advanced piezoelectric ceramic composite actuator, which is called LIPCA with the FRP and the optimization of the laminate configuration, was performed to maximize the stress transfer and the fiber bridging effect. This study evaluated the effect of variable electric fields on the PZT characteristic, laminate configuration and fatigue characteristics under the resonance frequency, which meant the largest performance range and the changes of its interlaminar phase were also evaluated by stages. In conclusions, Comparing with the fatigue lift of intact LIPCA, the fatigue life of LIPCA embedded by the artificial delamination was decreased up to 50%. The micro void growth and the coalescence of epoxy were actively made at the interlaminar phase subject to the large tensile stress.

• Structural Engineering and Mechanics
• /
• v.59 no.5
• /
• pp.885-899
• /
• 2016

The energy-based approach to predict the fatigue crack growth behavior under constant and variable amplitude loading (VAL) of the aluminum alloy 2024 T351 has been investigated and detailed analyses discussed. Firstly, the plastic strain energy was determined per cycle for different block load tests. The relationship between the crack advance and hysteretic energy dissipated per block can be represented by a power law. Then, an analytical model to estimate the lifetime for each spectrum is proposed. The results obtained are compared with the experimentally measured results and the models proposed by Klingbeil's model and Tracey's model. The evolution of the hysteretic energy dissipated per block is shown similar with that observed under constant amplitude loading.

• Proceedings of the KSR Conference
• /
• 1998.11a
• /
• pp.553-559
• /
• 1998

This thesis studied to evaluate the fatigue behavior and propagation of rail steel under welding line. Test of crack growth was performed by all member of rail under constant amplitude loading at the structures laboratory in Hongik University. The effect of the following parameters with initiated crack length on the bottom edge of rail were studied. Here, fracture mechanics mode is opening mode. and Testing Material is KS50N Rail. From analysis and experimented result on the three Point bending in the lab, This paper presented a effect of crack growth , shape and remaining service life. Further more, according to the variable crack length, variable section and the ratio of section the fatigue behavior and propagation were studied.