• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2008년도 추계학술대회A
• /
• pp.1355-1360
• /
• 2008

Stainless steel sheets are widely used as the structure material for the railroad cars and the commercial vehicles. These kinds structures used stainless steel sheets are commonly fabricated by using the gas welding. Gas welding is very important and useful technology in fabrication of an railroad car and vehicles structure. However fatigue strength of the gas welded joints is considerably lower than parent metal due to stress concentration at the weldment, fatigue strength evaluation of gas welded joints are very important to evaluate the reliability and durability of railroad cars and to establish a criterion of long life fatigue design. In this paper, ${\Delta}P-N_f$ curve were obtained by fatigue tests. Using these results, the accelerated life test (ALT) is conducted. From the experimental results, an acceleration model is derived and acceleration factors are estimated. So it is intended to obtain the useful information for the fatigue lifetime of plug and ring gas welded joints and data analysis by statistic reliability method, to save time and cost, and to develop optimum accelerated life prediction plans.

• 한국자동차공학회논문집
• /
• 제19권3호
• /
• pp.1-8
• /
• 2011

Stainless steel sheets are widely used as the structure material for the railroad cars and the commercial vehicles. These kinds structures used stainless steel sheets are commonly fabricated by using the gas welding. Gas welding is very important and useful technology in fabrication of an railroad car and vehicles structure. However fatigue strength of the gas welded joints is considerably lower than parent metal due to stress concentration at the weldment, fatigue strength evaluation of gas welded joints are very important to evaluate the reliability and durability of railroad cars and to establish a criterion of long life fatigue design. In this paper, ${\Delta}-N_f$ curve were obtained by fatigue tests. Using these results, the accelerated life test (ALT) is conducted. From the experimental results, an acceleration model is derived and acceleration factors are estimated. So it is intended to obtain the useful information for the fatigue lifetime of plug and ring gas welded joints and data analysis by statistical reliability method, to save time and cost, and to develop optimum accelerated life prediction plans.

• 한국정밀공학회지
• /
• 제17권5호
• /
• pp.160-167
• /
• 2000

In this research, the fatigue behaviors of carbonitrided Cr-Mo(SCM415) steel are examined. From fatigue test results, we propose a modified fatigue strength evaluation model and modified formulae. That is, we develop improved models fur evaluating and predicting the fatigue strength of carbonitrided SCM415 by modifying specific terms in the Murakami and Endo's model which is the representative fatigue strength evaluation formulae fur high strength steel.

• 한국정밀공학회지
• /
• 제15권10호
• /
• pp.113-119
• /
• 1998

Ship structures and aircraft structures are consisted of thin sheet alloy, so it is very important to understand the characteristics of fatigue crack propagation of that material and to establish the data base. The data for fatigue crack propagation behavior scatter very much even under identical experimental conditions with constant loading. The behavior of fatigue crack propagation under regular and irregular cyclic loadings is known to be highly affected by complicated factors such as plastic zone developed at the vicinity of crack tip and reduction of cross sectional area. In this paper, the controlled stress amplitude and overload fatigue crack propagation tests have been conducted to investigate the effect of varying factors such as plastic zone size near the crack tip and area reduction factor (AF) on the fatigue crack propagation behavior A better simulation of fatigue crack propagation behavior is found to be obtainable by using Wheeler and Willenborg models with AF effect.

• 한국산업융합학회 논문집
• /
• 제20권2호
• /
• pp.195-204
• /
• 2017

Predicting the failure life of automated manufacturing systems can reduce overall downtime, maintenance costs, and total plant operation costs. Therefore, there is a growing interest in fatigue failure mechanisms as the safety or service life assessment of manufacturing systems becomes an important issue. In particular, fretting fatigue is caused by repeated tangential stresses that are generated by friction during small amplitude oscillatory movements or sliding between two surfaces pressed together in intimate contact. Previous studies in fretting fatigue have observed size effects related to contact width such that a critical contact width exists where there is drastic change in the fretting fatigue life. However, most of them are the two-dimensional finite element analyses based on the plane strain assumption. The purpose of this study is to investigate the contact size effects on the three-dimensional finite element model of a finite width of a flat specimen and a cylindrical pad exposed to fretting fatigue. The contact size effects were analyzed by means of the stress and strain averages at the element integration points of three-dimensional finite element model. This study shows that the fretting fatigue life of manufacturing systems can be predicted by three-dimensional finite element analysis based on SWT critical plane model.

• Structural Engineering and Mechanics
• /
• 제49권2호
• /
• pp.237-259
• /
• 2014

Wind-induced failure around screwed connections has been documented in roof and wall cladding systems made with steel sheet cold-formed panels during high wind events. Previous research has found that low cycle fatigue caused by stress concentration and fluctuating wind loads is responsible for most such failures. A dynamic load protocol was employed in this work to represent fatigue under wind effects. A finite element model and fatigue criteria were implemented and compared with laboratory experiments in order to predict the fatigue failure associated with fluctuating wind loads. Results are used to develop an analytical model which can be employed for the fatigue analysis of steel cold-formed cladding systems. Existing three dimensional fatigue criteria are implemented and correlated with fatigue damage observed on steel claddings. Parametric studies are used to formulate suitable yet simple fatigue criteria. Fatigue failure is predicted in different configurations of loads, types of connections, and thicknesses of steel folded plate cladding. The analytical model, which correlated with experimental results reported in a companion paper, was validated for the fatigue life prediction and failure mechanism of different connection types and thicknesses of cold-formed steel cladding.

• 한국세라믹학회지
• /
• 제31권10호
• /
• pp.1141-1146
• /
• 1994

Cyclic fatigue experiment was carried out to predict the life time of alumina ceramics. Four kinds of model were suggested to obtain the adequate representative static stress corresponding to the cyclic stress applied to the alumina specimens. Arithmetic mean stress model gives 21.81 of the crack growth exponent, integrated stress model gives 22.15, maximum stress model gives 24.57, and equivalent static stress model gives 24.43. It is considered that the equivalent static stress model is the most reasonable and gives the best adequate crack growth exponents value.

• 한국신뢰성학회지:신뢰성응용연구
• /
• 제7권2호
• /
• pp.45-55
• /
• 2007

In this study, two types of fatigue tests were conducted. Firs, cyclic bending tests were performed using the micro-bending tester. Second, thermal fatigue tests were conducted using a pseudo power cycling machine which was newly developed for a realistic testing condition. A three-dimensional finite element analysis model was constructed. A finite element analysis using ABAQUS was performed to extract the applied stress and strain in the solder joints. Creep deformation was dominant in thermal fatigue and plastic deformation was main parameter for bending failure. From the inelastic energy dissipation per cycle versus fatigue life curve, it can be found that the bending fatigue life is longer than the thermal fatigue life.

• Computers and Concrete
• /
• 제27권1호
• /
• pp.55-62
• /
• 2021

The concrete fatigue analysis can be performed with the use of fracture mechanics. The fracture mechanics defines the fatigue crack propagation as the relationship of crack growth rate and stress intensity factor. In contrast to metal, the application of fracture mechanics to concrete is more complicated and therefore many authors have introduced empirical expressions using Paris law. The topic of this paper is development of a new prediction of fatigue crack propagation for concrete using rheological-dynamical analogy (RDA) and finite element method (FEM) in the frame of linear elastic fracture mechanics (LEFM). The static and cyclic fatigue three-point bending tests on notched beams are considered. Verification of the proposed approach was performed on the test results taken from the literature. The comparison between the theoretical model and experimental results indicates that the model proposed in this paper is valid to predict the crack propagation in flexural fatigue of concrete.

• Composites Research
• /
• 제24권1호
• /
• pp.10-16
• /
• 2011

복합재 적층판의 피로수명을 평가하는 것은 여러 가지 재료와 섬유적층각에 따라 수많은 인증실험이 요구된다. 본 논문에서는 미시역학적 파손이론을 이용하여 복합재의 구성재료인 섬유, 기지 및 섬유/기지 경계면의 피로수명 예측를 통해 복합재 적층판의 피로수명 평가를 할 수 있는 방법을 제시하였다. 기지는 다축응력상태을 고려할 수 있는 일반적인 등방성 재료의 등가응력파손식을 이용하였고, 섬유는 이방성 재료이지만 섬유방향의 응력이 주요하므로 섬유방향의 응력만 고려한 최대응력 파손식을 사용하였다. 섬유/기지 경계면에서는 임계단면파손식을 사용하였고, 경계면의 피로강도가 크다고 가정하여 경계면에서의 피로파손는 무시하였다. 인장과 압축강도가 다른 재료의 평균응력효과를 고려할 수 있도록 수정된 Goodman 식을 이용하였다. 순수 기지의 피로실험 데이터를 기반으로 미시역학적 파손이론을 이용하여 단일 플라이와 복합재 적층판인 UDT[$90^{\circ}2$], BX[${\pm}45^{\circ}$]S와 TX[$0^{\circ}/{\pm}45^{\circ}$]S의 피로수명을 예측해 보았고, 실험 데이터와 잘 일치함을 확인하였다.