• 한국정밀공학회지
• /
• 제25권4호
• /
• pp.86-92
• /
• 2008

This paper is to investigate the behavior of linear static structure stress, the fatigue and experimental shock fracture far engine base in the Auxiliary Power Unit to resolve its restricted electrical power problem. The shock fracture test was experimentally made under MIL standard criteria. The numerical results by finite element method had a good agreement with those from the shock test. The design data of predicting the fracture at the initial crack and the damage behavior of structure with shock and vibration load in the battle field can be obtained from shock test. In the functional shock test, the crack at the side parts of the engine base was found at peak acceleration of 40g.

• 대한기계학회논문집
• /
• 제9권2호
• /
• pp.140-149
• /
• 1985

본 연구는 오오스테나이트계 STS 316 스테인레스강에 대하여 온도 550.deg. C의 대 기중에서, 변형율제어에 의한 인장-압축에 크리이프 유지시간을 갖는 고온저사이클 피 로시험을 하여 변형율폭 및 크리이프 유지시간이 피로수명에 미치는 영향과 파단면을 주사형 전자현미경으로 관찰하여 크리이프-피로 상호작용이 피로파단면에 미치는 크리 이프 효과를 실험 고찰하였다.

• Design & Manufacturing
• /
• 제14권1호
• /
• pp.49-55
• /
• 2020

In this study, the fatigue behavior and fatigue life characteristics of PA2200 specimens fabricated by SLS 3D printer were studied. Fatigue tests were performed according to the standard specification (ASTM E468) and fatigue life curves were obtained. In order to perform the fatigue test, mechanical properties were measured according to the test speed of the simple tensile test, and the self-heating temperature of the specimen according to the test speed was measured using an infrared temperature measuring camera in consideration of heat generation due to plastic deformation. There was no significant difference within the set test speed range and the average self-heating temperature was measured at 38.5 ℃. The mechanical strength at the measured temperature showed a relatively small difference from the mechanical strength at room temperature. Fatigue test conditions were established through the preceding experiments, and the loading conditions below the tensile strength at room temperature 23 ℃ were set as the cyclic load. The maximum number of replicates was less than 100,000 cycles, and the fracture behavior of the specimens with the repeated loads showed the characteristics of Racheting. It was confirmed that SLS 3D printing PA2200 material could be applied to the Basquin's S-N diagram for the fatigue life curve of metal materials. SEM images of the fracture surface was obtained to analyze the relationship between the characteristics of the fracture surface and the number of repetitions until failure. Brittle fracture, crazing fracture, grain melting, and porous fracture surface were observed. It was shown that the larger the area of crazing damage, the longer the number of repetitions until fracture.

• Journal of Mechanical Science and Technology
• /
• 제17권6호
• /
• pp.836-843
• /
• 2003

The polymer composites contain numerous internal boundaries and its structural elements have different responses and different resistances under the same service environment. Fatigue phenomenon is much more complex in composites than homogeneous materials. An understanding of the fracture behavior of polymer composite materials subjected to constant and cyclic loading is necessary for predicting the life time of structures fabricated with polymers. There is a need to acquire a better understanding of the fatigue performance and failure mechanisms of composites under such conditions. Therefore, in this study the analyses of fiber orientation and fracture mechanism for low cycle fatigue crack have been studied by SEM and LM for observing the ultrathin sections.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 춘계학술대회
• /
• pp.247-254
• /
• 2003

The lightness of components required in automobile and machinery industry is requiring high strength of components. In particular manufacturing process and new materials development for solving the fatigue fracture problem attendant upon high strength of suspension of automobile are actively advanced. In this paper, the effect of compressive residual stress of spring steel(JISG SUP-9) by shot-peening on fatigue crack growth characteristics in high temperatures($100^{\circ}$, $150^{\circ}$, $180^{\circ}$) was investigated with considering fracture mechanics. So, we can obtain followings. (1)Compressive residual stress decreases in high temperature, that is, with increasing temperature. (2)The effect of compressive residual stress on fatigue crack growth behavior in high temperature increases below ${\Delta}K=17{\sim}19MPa$ (3)It was investigated by SEM that the constraint of compress residual stress for plastic zone of fatigue crack tip was decreased in high temperature as compared with room temperature.

• 한국자동차공학회논문집
• /
• 제11권4호
• /
• pp.117-124
• /
• 2003

The lightness of components required in automobile and machinery industry is requiring high strength of components. In particular, manufacturing process and new materials development for solving the fatigue fracture problem attendant upon high strength of suspension of automobile are actively advanced. In this paper, the effect of compressive residual stress of spring steel(JISG SUP-9) by shot-peening on fatigue crack growth characteristics in high temperatures($100^{\circ}C$, $150^{\circ}C$, $180^{\circ}C$) was investigated with considering fracture mechanics. So, we can obtain followings. (1)Compressive residual stress decreases in high temperature, that is, with increasing temperature. (2)The effect of compressive residual stress on fatigue crack growth behavior in high temperature increases below $\Delta$K=17~19MPa (3)It was investigated by SEM that the constraint of compressive residual stress for plastic zone of fatigue crack tip was decreased in high temperature as compared with room temperature.

• International Journal of Precision Engineering and Manufacturing
• /
• 제2권3호
• /
• pp.5-10
• /
• 2001

Due to the development of high-strength fibers and adhesives, it is now possible to repair cracked metallic plates by bonding reinforced patches to the plate over the crack. In this study, pre-cracked aluminum 6061-T6 alloy plates repaired with bonded carbon/epoxy composite patch are applied to investigate the effect of various patch shapes on the tensile strength and the fatigue behavior of the structure. A non-patch-boned cased and 2 type-50$\times$50, 40$\times$20 mm-composite patch-bonded cases were tested to obtain fracture loads and fatigue crack growth rate. The results showed that the patch-bonded repair improves the static strength by 17% and the fatigue life by 200% compared to non-repaired case. It means that patch-boned repair is more effective in the fatigue life. It was also revealed that the patching method along crack growth direction is more efficient in cost and weight reduction. By observing the fractography, patch-bonded repair specimens demonstrated zigzag fracture patterns compared with the non-patched specimens, which shows a typical ductile fracture.

• 열처리공학회지
• /
• 제23권3호
• /
• pp.131-136
• /
• 2010

The LCF (low cycle fatigue) behavior and the serration phenomena in the plastically deformed and non-deformed 5052 Al alloy were investigated. The plastic deformation was performed by 1 pass or 4 passes in ECAP (equal channel angular pressing) followed by annealing. Only cyclic hardening continued from the beginning until fracture at all strain amplitudes during LCF in the non-deformed alloy, which was caused by the increase in dislocation density during fatigue. Slight cyclic hardening followed by plateau until fracture was observed during LCF in the ECAPed alloy, which was caused by the slight increase in dislocation density in the beginning and then keeping constant in dislocation density afterward until fracture by forming subgrains in this stage of fatigue. The serrations on the stress-strain curves of this alloy were observed, which indicate that the dynamic strain aging (DSA) is occurring during plastic deformation. The variation in amplitudes of serration was studied by changing the strain rate in tensile or fatigue tests.

• 대한기계학회논문집A
• /
• 제31권4호
• /
• pp.432-440
• /
• 2007

In this study, we have investigated the closure behavior of fatigue cracks in SAPH440 steel plates under a mixed-mode I+II loading. A crack image capturing system as a direct measuring method was used to measure the closure levels at a crack tip. The crack closure levels in the fluctuation and stable sections were increased with the increase of the mode mixture ratio. The mode mixture ratio independent fatigue crack propagation rates equation was calculated by considering mixed-mode crack closure levels. The equation was examined according to the application method of crack opening ratio. The fracture surface analysis by C-scan method was also performed in order to investigate the closure mechanism and propagation mode of crack under the mixed-mode I+II loading. The crack closure under the mixed mode I+II is confirmed as a surface roughness closure by the quantitative analysis of fracture surface using the proposed surface roughness parameter.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1997년도 춘계학술강연 및 발표대회 강연 및 발표논문 초록집
• /
• pp.34-34
• /
• 1997

The effect of alloying mode and porosity on the axial tension-tension fatigue behavior of a P/M steel of nominal composition Fe-4w/o Ni-1.5w/o Cu-O.5w/o Mo-O.5w/o C has been evaluated. Alloying modes utilized were elemental powder mixing, partial alloying(distaloy) and prealloying by water atomization; in each case the carbon was introduced as graphite prior to sintering. Powder compacts were sintered($1120{\circ}C$/30 min.) in 7Sv/o $H_2$/25v/o $N_2$ to densities in the range 6.77-7.2 g/$cm^3$. The dependence of fatigue limit response on alloying mode and porosity was interpreted in terms of the constituent phases and the pore and fracture morphologies associated with the three alloying modes. For the same nominal composition, the three alloying modes resulted in different sintered microstructures. In the elemental mix alloy and the distaloy, the major constituent was coarse and fine pearlite, with regions of Ni-rich ferrite, Ni-rich martensite and Ni-rich areas. In contrast, the prealloy consisted primarily of martensite by with some Ni-rich areas. From an examination of the fracture surfaces following fatigue testing it was concluded that essentially all of the fracture surfaces exhibited dimpled rupture, characteristic of tensile overload. Thus, the extent of growth of any fatigue cracks prior to overload was small. The stress amplitude for the three alloying modes at 2x$l0^6$ was used for the comparison of fatigue strengths. For load cycles <3x$l0^5$, the prealloy exhibited optimum fatigue response followed by the distaloy and elemental mix alloy, respectively. At load cycles >2x$l0^6$, similar fatigue limits were exhibited by the three alloys. It was concluded that fatigue cracks propagate primarily through pores, rather than through the constituent phases of the microstructure. A decrease in pore SIze improved the S-N behavior of the sintered steel.