• Journal of Ocean Engineering and Technology
• /
• v.26 no.2
• /
• pp.26-32
• /
• 2012

In this paper, the effects of irregular bead shapes on fatigue life were investigated. A modified S-N curve method was used to estimate the fatigue life, which considered the inherent multiaxiality caused by the geometrical feature produced by the welding process. The point method of the critical distance method was used to determine the fatigue effective stress. Three types of fillet joint models were tested in the fatigue experiments. For each model, real bead shapes were collected using a 3D laser scanner, and finite element analyses were performed. The results of the analyses with actual bead shapes were compared with those using an idealized bead shape model. The results of the present analytical methods showed good agreement with the experimental results.

• Proceedings of the KSR Conference
• /
• 2007.11a
• /
• pp.30-34
• /
• 2007

Structural integrity of railway vehicles should last for a long period against various and continuous fatigue loadings, and the carbody structures of railway vehicle are manufactured by applying multiform welding types for each material. Since the most of cracks are occurred and proceeded at the vicinity of welding area during the lifetime of carbody structure, the fatigue strength evaluation for welding area of carbody structure should have been carried out. Rotem Company has evaluated lifetime and fatigue strength of carbody structure according to the fatigue analysis based on the international standard and/or inner-official regulation. This study introduces the fatigue analysis method that we have evaluated and calculated the damages for the welding areas of carbody structure under various fatigue loading conditions using cumulative fatigue damage rule(Miner's rule) to verify whether the cumulative damage does exceed unity. This study contains the fatigue test of specimens to derive stress-life relations(S-N curve), sub-modeling analysis and the calculation of cumulative damages under fatigue loading. The fatigue analysis verifies the welding area shall be capable of withstanding under fatigue loading, identifies how critical area shall be selected and presents the principles to be used for design verification.

• Steel and Composite Structures
• /
• v.33 no.3
• /
• pp.433-444
• /
• 2019

Fatigue failure of a grid structure using bolt-sphere joints is liable to occur in a high-strength bolt due to the alternating and reciprocal actions of a suspension crane. In this study, variable amplitude fatigue tests were carried out on 20 40 Cr steel alloy M30 high-strength bolts using an MTS fatigue testing machine, and four cyclic stress amplitude loading patterns, Low-High, High-Low, Low-High-Low, and High-Low-High, were tested. The scanning electron microscope images of bolt fatigue failure due to variable amplitude stress were obtained, and the fractographic analysis of fatigue fractures was performed to investigate the fatigue failure mechanisms. Based on the available data from the constant amplitude fatigue tests, the variable amplitude fatigue life of an M30 high-strength bolt in a bolt-sphere joint was estimated using both Miner's rule and the Corten-Dolan model. Since both cumulative damage models gave similar predictions, Miner's rule is suggested for estimating the variable-amplitude fatigue life of M30 high-strength bolts in a grid structure with bolt-sphere joints; the S-N fatigue curve of the M30 high-strength bolts under variable amplitude loading was derived using equivalent stress amplitude as a design parameter.

• Journal of Biosystems Engineering
• /
• v.40 no.4
• /
• pp.305-313
• /
• 2015

Purpose: This study was performed to predict the fatigue life of a crank-type rotavator operated in domestic soil conditions using Recurdyn$^{(R)}$, a dynamic analysis program. Methods: Torque on the PTO shaft was measured using experiments conducted on the uplands and paddy fields in Korea. On the basis of the experimental and analytical results, the fatigue life of the crank-type rotavator was predicted by constructing an S-N curve according to the GL (Germanischer Lloyd Wind Energie GmbH) guideline. Results: The torques experienced by the PTO shaft in the paddy soil and the uplands were in the range of 472~797 N m and 313~430 N m, respectively, for every condition. In case of load condition, the peak torques (846 N m, 770 N m) were applied for severe conditions, resulting in a maximum (von Mises) stress of 75 MPa at the crank arm. The fatigue life of the crank-type rotavator was predicted to be 1,167 h that satisfies the target value of 1,110 h, by substituting the analysis results into an S-N curve of crank arm. Conclusions: The fatigue life of the crank-type rotavator was within the target life for the studied soil conditions; however, further field experiments for various soil conditions would be required to verify the prediction results.

• Journal of Ocean Engineering and Technology
• /
• v.3 no.2
• /
• pp.617-617
• /
• 1989

This paper deals with a fatigue life prediction of a surface crack based on the experimentally obtained relationship between surface crack length ratio $a/a_{f}$ and cycle ratio $N/N_{f}$ using micro computer. Firstly $a/a_{f}$-$N/N_{f}$ curves obtained from experimental tests, were assumed as three curves UC(the upper limit curve), LC(the lower limit curve) and MC(the middle curve), and these were utilized to predict the fatigue life. Comparing the calculated values which represent the characteristics of crack growth behaviors from the three assumed curves with the experimental ones, it has been found that in the stable crack growth region, they coincide reasonably well each other. And the differences between the fatigue lives obtained from the assumed curves and the experimental fatigue life did not exceed 20%. Using the characteristics of $a/a_{f}$-$N/N_{f}$ curves, it is possible to predict the da/dN-Kmax curves and the S-$N_{f}$ curves.

• Journal of Ocean Engineering and Technology
• /
• v.3 no.2
• /
• pp.108-117
• /
• 1989

This paper deals with a fatigue life prediction of a surface crack based on the experimentally obtained relationship between surface crack length ratio $a/a_{f}$ and cycle ratio $N/N_{f}$ using micro computer. Firstly $a/a_{f}$-$N/N_{f}$ curves obtained from experimental tests, were assumed as three curves UC(the upper limit curve), LC(the lower limit curve) and MC(the middle curve), and these were utilized to predict the fatigue life. Comparing the calculated values which represent the characteristics of crack growth behaviors from the three assumed curves with the experimental ones, it has been found that in the stable crack growth region, they coincide reasonably well each other. And the differences between the fatigue lives obtained from the assumed curves and the experimental fatigue life did not exceed 20%. Using the characteristics of $a/a_{f}$-$N/N_{f}$ curves, it is possible to predict the da/dN-Kmax curves and the S-$N_{f}$ curves.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.3 s.174
• /
• pp.761-768
• /
• 2000

In order to investigate how the fatigue damage effects on the critical properties of superconductor, a fatigue test at room temperature and an Ic measurement test at 4.2K were carried out in this study, respectively, using a 9 strand Cu-Ni/NbTi/Cu composite cable. Through the fatigue test of a 9 strand Cu-NUNbTi/Cu composite cable, a conventional S-N curve was plotted even though there was a possibility of fretting among strands. It was found that the maximum stress corresponding to the inflection point on the S-N curve obtained was nearly the same value as the yielding strength of cable obtained from the static tensile test. However, the effect of cabling in multi-strands superconducting cable on the fatigue strength was not noticeable. The critical current(Ic) measurement was carried out at 4.2K in a NbTi strand out of the fatigued cable. It showed a degradation of lc at high stress amplitude regions over 380NTa, and the degradation became significant as the applied stress amplitude increased.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.12 no.4
• /
• pp.207-212
• /
• 2004

Full-beads of multi-layer steel engine head gaskets that are used to seal the combustion gas between the head and the block are subject to cyclic bending stresses due to the variation of the head/block gap during engine operation. The S-N curve for the fatigue durability assessment of the full-bead formed on NBR-coated SUS301 thin plate is deduced from the axial fatigue test results because of the difficulty in conducting the bending fatigue test of thin plate. The experimental verification of the deduced S-N curve is presented. It is shown that the NBR coating increases the endurance limit of the plate significantly. Mechanism of crack nucleation and propagation in the full-bead is discussed with photographs of the fatigue cracks.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.384-389
• /
• 2008

An accelerated fatigue test is essentially required to maintain the reliability of the actual structure of KTX under operation conditions. However, actual fatigue life cannot be obtained if specimens are not adequate to the conventional fatigue test. Moreover component maker did not provide data of loading stress (S) - cycles at the failure (N). In this study, we suggest a prediction method of the S-N curve for establishing an accelerating test under various load levels. Load history was acquired from the field tests. A Rainflow method was used on the cycle counting of the field load data, and then, an S-N curve was obtained through the iteration process under the condition that the damage index satisfies to 1 in the Miner's rule.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.690-693
• /
• 2005

In this paper, probabilistic distribution of fatigue life of chassis component is determined statistically by applying the design of experiments and the Pearson system. To construct $p-\varepsilon-N$ curve, the case that fatigue data are random variables is attempted. Probabilistic density function(p.d.f) for fatigue life is obtained by design of experiment and using this p.d.f fatigue reliability about any aimed fatigue life can be calculated. Lower control arm and rear torsion bar of chassis component are selected as examples for analysis. Component load histories, which are obtained by multi-body dynamic simulation for Belsian load history, are used. Finite element analysis are performed using commercial software MSC Nastran and fatigue analysis are performed using FE Fatigue. When strain-life curve itself is random variable, probability density function of fatigue life has very little difference from log-normal distribution. And the case of fatigue data are random variables, probability density functions are approximated to Beta distribution. Each p.d.f is verified by Monte-Carlo simulation.