• 수산해양교육연구
• /
• 제9권2호
• /
• pp.198-208
• /
• 1997

Recently, with rapid increase of gas demand, there occurs much interest their security of safety in the gas storage tanks and pressure vessels etc. In order to solve the problems, the occurrence of corrosion fatigue crack and the propagation behavior must be investigated. Especially the occurrence of corrosion fatigue crack and the propagation behavior in the part which has concentrated stress or defects, must be studied more carefully. In this paper, the high-tensile steel of SPV 50 which is much used for building the LPG storage tanks was tested by the use of a plane bending corrosion fatigue tester under the various marine environment and in the air. These experiments were carried out to investigate the surface crack propagation behavior, the value of experimental constant for Paris' rule(da/dN=$C(K)^m$), the crack depth propagation rate and the accelerative factor of the surface crack propagation rate. The main results obtained are as follows ; 1) As the specific resistances of marine environment decreases, the exponential value of slope m of Paris' rule(da/dN=$C(K)^m$) decreases and the value of intercept C increases. 2) The surface crack propagation rate and the crack depth propagation rate are delayed, as the specific resistances of marine environment is increased. 3) The accelerative factor of the surface crack propagation rate by corrosion fatigue is higher, according as the stress intensity factor range ${\Delta}K_A$ is small.

• 수산해양기술연구
• /
• 제34권1호
• /
• pp.30-36
• /
• 1998

Recently, with rapid increase of gas demand, there occurs much interest their security of safety in the gas storage tanks and pressure vessels etc. In order to solve the problems, the occurrence of corrosion fatigue crack and the propagation behavior must be investigated. Especially the occurrence of corrosion fatigue crack and the propagation behavior in the part which has concentrated stress or defects, must be studied more carefully. In this paper, the high-tensile steel of SPV 50 which is much used for building the LPG storage tanks was tested by the use of a plane bending corrosion fatigue tester under the various marine environments and in the air. These experiments were done to investigate the corrosion fatigue crack propagation behavior, the variation of aspect ratio for part through crack and electro-chemical characteristics of the metal. The main results obtained are as follows ; 1. Comparing the same surface crack length with the crack depth, the crack depth toward the thickness of specimen in air propagated faster than that in corrosion environment. 2. The aspect variation of the half elliptical crack can be estimated as following equation; b/a=i-jb/t where a : surface crack length, b : crack depth, t : specimen thickness, i,j : experimental constants but the slope j is decreased as specific resistance decreases. 3. As the specific resistance of corrosion environment decrease or the corrosion fatigue crack propagates, the corrosion potential become less noble.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2003년도 춘계학술대회 논문집
• /
• pp.409-412
• /
• 2003

Fatigue strength. especially crack initiation behavior of high strength steel under marine water environment was investigated. Marine structures were usually constructed by lot of weld joints and were designed by basis of the fatigue strength of weld joints. This study was carried out to mini. The fatigue initiation behavior is more important rather than crack propagation behavior under the design of marine structures, because it is very difficult to find out the crack propagation phenomena and repair the damaged part of welded joints in sea water Then, the new configuration specimen for fatigue crack initiation tests was proposed. Using this new specimen, it is easy to carry out the crack initiation tests with relatively low cycling loading and clearly find out a crack initiation fatigue life.

• 한국안전학회지
• /
• 제12권2호
• /
• pp.57-64
• /
• 1997

Fatigue crack propagation behaviors and life prediction for SUS 321 plate and its electron beam weld metal were investigated using compact tension specimens. The larger the stress ratio is, the faster the crack propagates, but the variation of crack propagation rate decreases. The effect of stress ratio is greater in the slow crack propagation area than in the faster one. The crack propagation rate of electron beam weld metal is faster than that of base metal because of hardening, weld defect and residual stress in welding area. The crack propagation rate of transverse weld metal has a lower than that of base metal due to the effect of residual stress, but in the time of passing through welding area, has a higher rate. The crack propagation rate using $\Delta$K$_{eff}$ can be well plotted regardless of stress ratio. The fatigue life prediction method of considering crack closure more exactly predicts fatigue life than conventional one. conventional one.e.

• Journal of Advanced Marine Engineering and Technology
• /
• 제19권2호
• /
• pp.36-46
• /
• 1995

In this paper, fatigue crack propagation behaviors were investigated experimentally for the materials, carbon steel forgings (SF45A, SF50A, SF60A) which are used in the marine propeller shaft. The results obtained are as follows: The number of cycles required to grow crack length 1.30mm from microcrack initiation was about 60% of the total fatigue life. Fatigue crack propagation rate was expressed by the equation d(2a)/dN_B 2a/$N_f$ and the result was agreed well with the experimented data. And the equation d(2a)/dN=$C{\sigma}_a^m(2a)^n$ was evaluated also. Obtained material property m and n are 3~5 and 1-1.5 respectably, and the result was reasonably agreed to the data obtained from experiments.

• Journal of Mechanical Science and Technology
• /
• 제20권12호
• /
• pp.2136-2146
• /
• 2006

A study on a creep-fatigue crack growth behavior has been carried out for a cylindrical structure with weldments by using a structural test and an evaluation according to the assessment procedures. The creep-fatigue crack growth behavior following the creep-fatigue crack initiation has been assessed by using the French A16 procedure and the conservatism for the present structural test has been examined. The structural specimen is a welded cylindrical shell made of 316 L stainless steel (SS) for one half of the cylinder and 304 SS for the other half. In the creep-fatigue test, the hold time under a tensile load which produces the primary nominal stress of 45 MPa was one hour at $600^{\circ}C$ and creep-fatigue loads of 600 cycles were applied. The evaluation results for the creep-fatigue crack propagation were compared with those of the observed images from the structural test. The assessment results for the creep-fatigue crack behavior according to the French Al6 procedure showed that the Al6 is overly conservative for the creep-fatigue crack propagation in the present case with a short hold time of one hour.

• 대한기계학회논문집
• /
• 제13권5호
• /
• pp.938-946
• /
• 1989

본 연구에서는 CT시험편을 이용하여 소규모 항복조건하에서 하한계(near threshold)영역과 안전균열성장(제II)영역의 균열진전거동을 파악하고 피로균열 진전속도와 음향방출거동, 파단면 특성을 각각 비교, 고찰하여 각 파라미터간의 상관 관계 및 유용성을 검토하고자 한다.

• 한국정밀공학회지
• /
• 제18권1호
• /
• pp.201-212
• /
• 2001

If defects are located far apart, fatigue cracks are independently initiated from them and gradually approach other cracks so that the fatigue life becomes influenced by the crack growth behavior of those interacting cracks. In this study, the effect of the stress interaction between defects on the fatigue crack propagation behavior is investigated experimentally and these results are verified by finite element method. In addition, fatigue crack propagation behaviors under micro hole interaction field are studied.

• 대한기계학회논문집
• /
• 제10권6호
• /
• pp.898-905
• /
• 1986

본 논문에서는 강의 피로균열진전거동과 미시조직과의 관계를 밝히기 위한 연 구의 일환으로 제이상 마르텐사이트 중에 모상 페라이트가 존재하는 복합조직강을 준 비하여 이들 강의 제이상 경도변화에 따른 피로균열진전저항을 균열휨과 균열닫힘을 통하여 검토하였다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1995년도 춘계학술대회 논문집
• /
• pp.28-32
• /
• 1995

This effective way for repairing a fatigue crack is making indetations around fatigue crack tip. In this paper, we performed fatigue test to investigate the optimal position of the indentations, and observed crack opening behavior at the same time. The indentation positions of specimens were on the crack tip, front and back of the crack tip. The results of the experiment showed taht it was veryeffective way to increase fatigue life that making indentations on the crack tip, and it was the optimal position that making indentations on the crack tip.