• 한국표면공학회지
• /
• 제42권6호
• /
• pp.294-300
• /
• 2009

The Friction Stir Welding (FSW) has mainly been used for making butt joints in Al alloys. The development of Friction Stir Lap Welding (FSLW) would expand the number of applications. In this study, for effective application on thin aluminum alloy lap joint, non-heat treatment A5052 alloys were joined by FSLW with the length of probe 2.3 mm and 3.0 mm. Investigating the characteristics of joint area showed the results were as below ; When the length of probe was 2.3 mm, good joint area was formed at all welding condition except for 600 rpm-700 mm/min. In the case of 3.0 mm probe length, there was formed good joint area without defects at 1500 rpm-100 mm/min. The width of joint area, position and size of defects were very important factors for FSLW, due to heat input and stirring intensity.

• Journal of Welding and Joining
• /
• 제27권6호
• /
• pp.17-24
• /
• 2009

The Friction Stir Welding(FSW) has mainly been used for making butt joints in Al alloys. Development of Friction Stir Lap Welding(FSLW) would expand the number of applications. Microstructure of FSLW in A5052-H112 alloy was investigated under varying rotation and welding speed. As the rotation speed was increased and the welding speed was decreased, a amount of heat was increased. As a result, bead interval was narrower, bead width are larger, and experimental bead interval was almost similar to theoretical bead interval. Typical microstructures of FSLW A5052-H112 alloy consist of three zones, including Stir Zone(SZ), Thermo-Mechanically Affected Zone(TMAZ) and Heat Affected Zone(HAZ). As a amount of heat was increased, average grain size was larger in three zones. Nevertheless, the aspect ratio was almost fixed for FSLW conditions. The misorientation of SZ, HAZ and TMAZ was examined. A large number of low angle grain boundaries, which were formed by severe plastic deformation, were showed in TMAZ as comparison with SZ and HAZ. Microhardness distribution was high in order of BM, SZ, TMAZ, and HAZ. The Micro-hardness distribution in HAZ, TMAZ of upper plate were lager than lower plate. Relationship between average grain size and microhardness was almost corresponded to Hall-Petch equation.

• 한국표면공학회지
• /
• 제45권5호
• /
• pp.181-187
• /
• 2012

The Friction Stir Welding (FSW) has mainly been used for making butt joints in Al alloys. The development of Friction Stir Lap Welding (FSLW) would expand the number of applications. In this study, microstructures and mechanical properties of FSLW in A5052 alloy were investigated under varying rotating speed and probe length. Investigating the characteristics as FSLWed conditions were as below ; Failure Maximum load by shear fracture was increased proportional to the width of joint area, which was increased by input heat, stirring intensity in the case of 2.3 mm probe length. Tensile fracture occurred, and maximum load was determined due to side worm hole of joint area and softening of microstructure in the case of 3.0 mm probe length. In the case of 3.7 mm probe length, material hook and bottom worm hole were appeared at the end interface of joint area. The most sound FSLW condition with no defects was 3.0 mm probe length and 1500 rpm-100 mm/min. No defects were showed in 1500 rpm-100 mm/min and 1800 rpm-100 mm/min, but Vickers microhardness distribution in TMAZ/HAZ which was fracture zone was lower in 1800 rpm-100 mm/min than in 1500 rpm-100 mm/min. In this condition highest tensile strength, 215 MPa (allowable rate 78% of joint efficient) was obtained.

• 한국분말재료학회지
• /
• 제20권4호
• /
• pp.302-307
• /
• 2013

A5J32-T4 and A5052-H32 dissimilar aluminum alloy plates with thickness of 1.6 and 1.5 mm were welded by friction stir lap welding (FSLW). The FSLW were studied using different probe length tool and various welding conditions which is rotation speed of 1000, 1500 rpm and welding speed of 100 to 600 mm/min and material arrangement, respectively. The effects of plunge depth of tool and welding conditions on tensile properties and weld nugget formation. The results showed that three type nugget shapes such as hooking, void, sound have been observed with revolutionary pitch. This plunge depth and material arrangement were found to effect on the void and hooking formation, which in turn significantly influenced the mechanical properties. The maximum joint efficiency of the FSLWed plates was about 90% compared to base metal, A5052-H32 when the A5052-H32 was positioned upper plate and plunge depth was positioned at near interface between upper and lower plates.

• Journal of Welding and Joining
• /
• 제28권1호
• /
• pp.34-40
• /
• 2010

In Friction Stir Lap Welding(FSLW), the movement of material within the weld was more important than the microstructure, due to the interface present between the sheets. Thus, The soundness of free defect, Effective Sheet Thickness(EST) and width of joint were most important factor of mechanical properties. Specimens by lap joint types that were 'A-type' and 'R-type' were made in this study. A-type tensile specimen was loaded at advancing side and R-type tensile specimen was loaded at retreating side. Macro-, micro-structural observation and mechanical properties of FSLW A5052-H112 alloy ware investigated under varying rotating and welding speed. The results were as follows: Material hook formed decreasing after sharply increasing was appeared at the end interface of joint area in advanced side, and material hook formed decreasing after smoothly increasing was observed at that in retreated side. Tensile load had no relation with defects. As rotating speed was higher, tensile strength was increasing and EST was decreasing regardless of joint types. joint efficiency was over 70%. In a result of fractography, fracture in A-type was partially occurred by dimple in SZ, and fracture in R-type was generally occurred by dimple in HAZ.