• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.5
• /
• pp.3602-3609
• /
• 2015

HPFRCC is characterized by a very low water-to-binder ratio which induce extremely large autogenous shrinkage at early age. The restriction of such autogenous shrinkage through the use of forms and reinforcing bars will increase substantially the risk of excessive residual stresses and shrinkage cracking. The exact understanding of the shrinkage behavior and studies on solutions to reduce shrinkage should be imperatively undertaken for further application of HPFRCC to real structures. Therefore, this paper investigated the mechanical properties of HPFRCC with respect to the eventual introduction of expansive admixture(EA) and shrinkage reducing agent (SRA) in the mixture. Autogenous shrinkage test was conducted considering the coefficient of thermal expansion (CTE) measured at early age so as to examine the effects of EA and SRA on the autogenous shrinkage behavior of HPFRCC.

• Journal of the Korea Concrete Institute
• /
• v.16 no.6 s.84
• /
• pp.805-811
• /
• 2004

In this paper, effects of mixture proportion and material condition on both fundamental properties, drying and autogenous shrinkage of high performance concrete are discussed. According to the results, for the effect of mixture proportion on the fundamental properties, decrease in W/B and unit water content results in reduction of fluidity, while air content has no variation. Compressive strength exhibits an decreasing tendency with an increase in W/B and unit water content do not remarkable affect the compressive strength. For the effect of materials on the fluidity, the fluidity of low heat portland cement(LPC) is smaller than that of ordinary portland cement(OPC). The use of Polycarbonic acid based superplasticizer(PS) has more favorable effect on enhancing fluidity than Naphtalene based superplasticlzer(NS) and Melamine based superplasticizer(MS). Air content of concrete using LPC is larger than that using OPC. The effects of superplasticizer type on the air content is larger in order of MS, PS and NS. The use of LPC exhibited lower strength development at early age than OPC, whereas after 91days, similar level of compressive strength is achieved regardless of cement type. Compressive strength of concrete is not affected by SP type. For the effect of mixture proportion and materials on drying and autogenous shrinkage, an increase in W/B results in reduction of drying shrinkage and an decrease in water content leads to reduce drying shrinkage. Autogenous shrinkage is not observed until 49 days with the concrete mixture with $35\%$ of W/B and $145 kg/m^3$ of water content. This is due to the combination effects of expansion admixture and shrinkage reducing admixture, which causes an offset of autogenous shrinkage. The use of LPC results in a reduction in autogenous shrinkage compared with OPC. SP type has little influence on the autogenous shrinkage. It is found from the results that mixture proportioning of high performance concrete incorporating fly ash, silica fume, expansion admixture and shrinkage reducing admixture is need to focus on the increase in W/B and the reduction in water content and the use of LPC and MS is also required to use to secure the stability against shrinkage properties.

• Journal of the Korea Institute of Building Construction
• /
• v.8 no.5
• /
• pp.85-91
• /
• 2008

Prepacked concrete has recently been used in the special constructions fields such as underwater concrete work, heavy-weight concrete work, underground structure work, partial repair works for damaged reinforced concrete structures. and polymer-modified mortars have been employed as grouting mortars for the prepacked concrete. The purpose of this study is to recommend the optimum mix design of polymer-modified grouting mortars for prepacked concrete. Polymer-modified mortars using SBR and EVA emulsions as admixture of grouting mortars for prepacked concrete are prepared with various mix proportions such as sand-binder ratio, fly ash replacement ratio, polymer-binder ratio. and tested for flowability, viscosity of grouting mortars, bleeding ratio, expansion ratio, flexural and compressive strengths of grouting mortars and compressive and tensile strengths of prepacked concretes. From the test results, it is apparent that polymer-modified mortars can be produced as grouting mortars when proper mix design is chosen. We can design the mix proportions of high strength mortars for prepacked concrete according to the control of mix design factors such as type of polymer, polymer-binder ratio, sand-binder ratio and fly ash replacement ratio. Water-binder ratio of plain mortars for a constant flowability value are in the ranges of 43% to 50%. SBR-modified mortar has a little water-binder ratios compared to those of plain mortar, however, EVA-modified mortar needs a high water-binder ratio due to a high viscosity of polymer dispersion. The expansion and bleeding ratios of grouting mortars are also controlled in the proper value ranges. Polymer-modified grouting mortars have good flexural. compressive and tensile strengths, are not affected with various properties with increasing fly ash replacement to cement and binder-sand ratio. In this study, SBR-modified grouting mortar with a polymer-binder ratio of 10% or less, a fly ash replacement of 10% to cement and a sand-binder ratio of 1.5 is recommended as a grouting mortar for prepacked concrete.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.1
• /
• pp.9-14
• /
• 2022

Most of the existing research on ferronickel slag has focused on its potential as aggregate and fine aggregate, this study was conducted focusing on the potential of ferronickel slag powder as a concrete admixture. For concrete, which fly ash, blast furnace slag, and FSP were mixed with each 10 % type the reactivity was evaluated by applying ASTM C 1260 of the United States. As a result, compared with the control group, the expansion rate of fly ash decreased by 8.43 % and that of fine blast furnace slag powder decreased by 14.46 %, while the expansion rate of ferronickel slag decreased by 49.40 %. it was confirmed that ferronickel slag can sufficiently be replaced existing supplementary cementitious admixtures such as fly ash and blast furnace slag in terms of suppressing the reactivity of aggregates. However as a result of SEM analysis, ettringites were generated, and additional research about how it affects concrete is needed.

• Journal of the Mineralogical Society of Korea
• /
• v.17 no.3
• /
• pp.277-288
• /
• 2004

Alkali-silica reaction (ASR) is a chemical reaction between alkalies in cement and chemically unstable aggregates and causes expansion and cracking of concrete. In the Present study, we studied the effects of metakaolin, which is a newly introduced mineral admixture showing excellent pozzolainc reaction property, on the inhibition of ASR. We prepared mortar-bars of various replacement ratios of metakaolin and conducted alkali-silica reactivity test (ASTM C 1260), compressive strength test and flow test. We also carefully analyzed the mineralogical changes in hydrate cement paste by XRD qualitative analysis. The admixing of metakaolin caused quick pozzolanic reaction and hydration reaction that resulted in a rapid decrease in portlandite content of hydrated cement paste. The expansion by ASR was reduced effectively as metakaolin replaced cement greater than 15%. This resulted in that the amounts of available portlandite decreased to less than 10% in cement paste. It is considered that the inhibition of ASR expansion by admixing of metakaolin was resulted by the combined processes that the formation of deleterious alkali-calcium-silicate gel was inhibited and the penetration of alkali solution into concrete was retarded due to the formation of denser, more homogeneous cement paste caused by pozzolanic effect. Higher early strength (7 days) than normal concrete was developed when the replacement ratios of metakaolin were greater than 15%. And also, late strength (28 days) was far higher than normal concrete for the all the replacement ratios of metakaolin. The development patterns of mechanical strength for metakaolin admixed concretes reflect the rapid pozzolanic reaction and hydration properties of metakaolin.

• Journal of the Korea Institute of Building Construction
• /
• v.11 no.4
• /
• pp.345-352
• /
• 2011

The purpose of this study was to investigate the expansion of alkali-activated mortar based on ground granulated blast furnace slag containing reactive aggregate due to alkali-silica reaction. In addition, this study was particularly concerned with the behavior of these alkaline materials in the presence of reactive aggregates. The experimental program included expansion measurement of the mortar bar specimens, as well as the determination of the morphology and composition of the alkali-silica reaction products by using scanning electron microscopy(SEM), and energy dispersive x-ray(EDX). The experiment showed that while alkali-activated ground granulated blast furnace slag mortars showed expansion due to the alkali-silica reaction, the expansion was 0.1% at Curing Day 14, showing that it is safe. After the accelerated test, SEM and BEM analysis showed the presence of alkali-silica gel and rim around the aggregate and cement paste. According to the EDX, the reaction products decreased markedly as alkali-activated ground granulated blast furnace slag was used. In addition, for the substitutive materials of mineral admixture, a further study on improving the quality of alkali-activated ground granulated blast furnace slag is needed to assure of the durability properties of concrete.

• Journal of Ocean Engineering and Technology
• /
• v.25 no.3
• /
• pp.40-46
• /
• 2011

This paper describes the effects of fly ash replacement on the sulfate resistance of antiwashout underwater concrete which was replaced cement by fly ash from 0% to 50%. and the experimental works were performed on sulfate acceleration test of 5%$Na_2SO_4$ solution to find out the variance of length and weight of specimens. The experimental result shows that the length of specimens of antiwashout underwater concrete age at 180day was highly increased compare with normal concrete by acceleration test. but the mixture which was replaced 50% of fly ash shows reduction of the expansion, weight various, compare with normal concrete specimen. accordingly by using fly ash as admixture in antiwashout underwater concrete in sea environment, it will makes more durable for the attacks of sulfate by sea water.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.565-568
• /
• 2008

Because of low early compressive strength, the usage of fly ash is subject to restriction in comparison with blast-furnace slag powder. Therefore, high amount of fly ash is reclaimed in landfill in face of better economical efficiency and more production. In this paper, the primary aim is to determine to what the basic material characteristics of fly ash concrete is affected by activator, the second aim is to check a possibility of increase in fly ash application. This study show that compared with fly ash concrete using general admixture, fly ash concrete using activator have higher early compressive strength under similar slump, air content, loss. If additional study will inspect performance of activator in various factor, expansion of application of fly ash concrete using activator can be possible.

• Journal of Ocean Engineering and Technology
• /
• v.19 no.6 s.67
• /
• pp.29-34
• /
• 2005

This paper describes the effect of fly ash replacement on seawater resistance of anti-washout underwater concrete, which was replaced cement by fly ash from $0\%$ to $50\%$. The experimental work was performed to find out the variations of length and weight of specimens, using a chloride acceleration test in $40\^{\circ}$C The results shaw that the admixture using fly ash on an anti-washcout underwater concrete in the sea environment makes it more durable for the attacks of chloride by seawater. Also, the length of specimens of anti-washout underwater concrete, at age 180 days, increased substantially, compared with normal concrete; however, the mixture in which cement was replaced $50\%$ of fly ash shows $93\%$ reduction of the expansion, compared with the normal anti "washout underwater concrete specimen.

• Journal of the Korean Society for Railway
• /
• v.7 no.4
• /
• pp.312-318
• /
• 2004

The wall in a subway structure is easily subject to crack occurrence since its expansion and shrinkage associated with hydration heat reaction is constrained by the slab. The greater problem is that the crack in the wall may be developed to pass through thickness and eventually deteriorate the structure due to rusting of reinforced steel. Thus, this study aims at controlling thermal cracks as much as possible and determining an optimized size of concrete placement through hydration heat analysis. For this study, effects of placement height, length, temperature and types of cement on the thermal cracks were evaluated by temperature rise, thermal stress and crack index. As results of parametric study, it was found that placement height and length do not have an effect on the temperature rise but have significant one on thermal stress which relates to direct possibility of thermal crack occurrence. This means that proper selection of size balancing internal constraint with external one is much more important than reducing the placement height and length simply. In order to prevent from thermal cracks most effectively, in addition, it was noted to reduce placement temperature and to use the cement blended with mineral admixture.