• Transactions of the Korean Society of Automotive Engineers
• /
• v.18 no.1
• /
• pp.120-126
• /
• 2010

It was known that the excellent wear resistance of hyper eutectic aluminum alloy is based on the primary Si particles which are distributed in the base metal. When the primary Si volume fraction increases, the smaller size have excellent wear resistance characteristics. However, this trend always does not match. There is no investigation result based on the materials and methods for real using parts. In this study, using the automotive parts manufacturer currently in use hyper eutectic Al alloy tensile test specimen type sample was fabricated by 350Ton high pressure die-casting machine. Then, fluidity, tensile, impact and wear resistance properties were evaluated. If the casting quality, primary Si size, fraction and distribution are similar, mechanical properties and wear resistance are equivalent.

• Journal of Korea Foundry Society
• /
• v.15 no.3
• /
• pp.262-271
• /
• 1995

It is well known what is impossible to refine primary and eutectic Si simultaneously by addition of both Cu-P and Sr(or Na). Because of the formation of compound $Sr_3P_2(or Na_3P)$ in the melt, in the result, both effects disappear. In this study Al-Cu-P alloy that comprises AlP compounds inside is added in the melt with Sr simultaneously. As AlP compounds that act on nucleation sites of primary Si are not formed but added directly an the melt, it is difficult to form $Sr_3P_2$ by reaction with Sr. Therefore it is possible to refine primary and eutectic Si simultaneously in the general casting process by use of Al-Cu-P alloy and Sr.

• Journal of Korea Foundry Society
• /
• v.17 no.6
• /
• pp.608-614
• /
• 1997

The effect of mold preheating temperature on the microstructure such as grain size, eutectic silicon morphology was investigated for the Al-7wt%Si-0.3wt%Mg alloy. Microstructural variations have been characterized as a function of Sr addition and cooling rate during solidification. Microstructures were correlated with cooling rate, local solidification time and eutectic nucleation temperature, etc. In this study, Sr addition caused increase of local solidification time, undercooling and reduction of eutectic plateau temperature. In logarithmic scale, local solidification time was in inverse proportion to cooling rate. Eutectic nucleation temperature was in inverse proportion to cooling rate of logarithmic scale. Increasing the cooling rate refined dendrite arm spacing and eutectic silicon. Dendrite arm spacing was logarithmically in inverse proportion to cooling rate. Without modifier addition, eutectic silicon was modified at cooling rate of $7^{\circ}C/s$ or higher.

• Journal of Korea Foundry Society
• /
• v.30 no.5
• /
• pp.161-166
• /
• 2010

In this examination, the effect of Sr addition and holding time on microstructure of Al-10.5wt%Si-2wt%Cu secondary die-casting alloy was investigated. Degree of undercooling was improved with increasing the Sr content in this alloy. Up to 0.02wt%Sr addition, acicular and lamellar eutectic structure was observed in the microstructure. Meanwhile, the eutectic Si was modified toward the fine fibrous form by increasing Sr content with more than 0.03wt% and holding time of the melt. The well- modified alloys showed decreased eutectic silicon size from 3.25 ${\mu}m$ to less than 0.8 ${\mu}m$. From these results, the optimal strontium content and holding time were identified on the Al-10.5wt%Si-2wt%Cu secondary die-casting alloy.

• Journal of Korea Foundry Society
• /
• v.36 no.2
• /
• pp.53-59
• /
• 2016

The effects of ultrasonic melt treatment on the microstructures of aluminum piston were examined at five observation parts having different cooling rates. The microstructure of aluminum piston consisted of primary Si, eutectic Si, and various types of intermetallic compounds. Regardless of cooling rate, the ultrasonic melt treatment transformed dendritic eutectic cells to equiaxed eutectic cells and it decreased the sizes of eutectic Si and intermetallic compounds that exist at eutectic cell boundaries. In the absence of ultrasonic treatment, coarse primary Si particles were severely segregated and its size was increased with decreasing the cooling rate. The ultrasonic treatment decreased the size of primary Si particles from $25.5{\sim}31.0{\mu}m$ to $17.6{\sim}23.1{\mu}m$, depending on the cooling rate. In the presence of ultrasonic treatment, relatively fine primary Si particles were homogeneously distributed throughout the piston. In addition, the ultrasonic treatment increased the population density and area fraction of fine primary Si particles.

• Journal of Korea Foundry Society
• /
• v.6 no.1
• /
• pp.5-11
• /
• 1986

The Wear Characteristics of Al-Si alloys were investigated with various Si contents by using the not-dispersed alloys and uncoated-graphite dispersed alloys. Uncoated-graphite dispersions were accomplished by Vortex method carrying 1 hr. heating at $400^{\circ}C$ on uncoated-graphite. Wear loss were increased by increasing Si contents at the elevated final load. Hyper-eutectic alloys showed higher wear resistance values at the small final load of 2.1Kg and 3.2Kg, but at the more increased final load, hypo-eutectic alloys showed higher wear resistance values than hyper-eutectic alloys. The property of wear resistance of uncoated-graphite dispersed Al-Si alloys showed more good values than not-dispersed alloys. This peroperty of increased war resistance were resulted from lubricating action of dispersed graphite.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.1398-1401
• /
• 2005

The nano/microstructure, the aging response (in T5 heat treatment), and the mechanical/tribological properties of the eutectic regions in squeeze-cast A356 alloy were investigated using nano/micro-indentation and mechanical scratching, combined wit optical microscopy and atomic force microscope(AFM). Most eutectic Si crystals in the A356 alloy showed a modified morphology as fine-fibers. The loading curve for the eutectic region was more irregular than that of the primary Al region due to the presence of various particles of varying strength. In addition, the eutectic region showed lower pile-up and higher elastic recovery than the primary Al region. The aging responses of the eutectic regions in the squeeze-cast A356 alloys aged at $150^{\circ}C$ for different times(0, 2, 4, 8, 10, 16, 24, 36 and 72 h) were investigated. As the aging time increased, acicular Si particles in the eutectic regions gradually came to a fine structure. Both Vickers hardness ($H_V$) and indentation ($H_{IT}$) test results showed almost the same trend of aging curves, and the peak was obtained at the same aging time of 10 h. A remarkable size-dependence of the tests was found. The friction coefficient for the eutectic region was lower than that for the primary Al region.

• Journal of Korea Foundry Society
• /
• v.29 no.5
• /
• pp.225-232
• /
• 2009

For comprehensive understanding of the formation behavior of $\beta-Al_5FeSi$ phase in Al-Si-Cu alloys with the existence of Fe element, microstructure characterizations were performed using combined analysis of OM, SEM-EDS, XRD. Especially, experimental and predictive works on solidification events of $\beta-Al_5FeSi$ phase as well as other phases formed together with $\beta-Al_5FeSi$ have been carried out by using DSC analysis and Java-based Materials Properties software (J. Mat. Pro.). Primary and eutectic $\beta-Al_5FeSi$ phases were able to distinguish from each other on microstructures by their morphological features. Primary $\beta-Al_5FeSi$ phase was seen to have rough surface perpendicular to growth direction, indicating free attachment of solute atoms in liquid state. On the other hand, the eutectic $\beta-Al_5FeSi$ phase was formed with plain and straight surface during eutectic reaction together with $\alpha$-Al phase. The eutectic reaction of $\beta-Al_5FeSi$ and $\alpha$-Al phases was seen to be able to separate into each formation depending on cooling rate.

• Current Photovoltaic Research
• /
• v.1 no.1
• /
• pp.63-68
• /
• 2013

We investigated the effects of Au eutectic reaction on Si thin film growth by hot wire chemical vapor deposition. Small SiC and Si nano-particles fabricated through a wet etching process were coated and biased at 50 V on micro-textured Si p-n junction solar cells. Au thin film of 10 nm and a Si thin film of 100 nm were then deposited by an electron beam evaporator and hot wire chemical vapor deposition, respectively. The Si and SiC nano-particles and the Au thin film were structurally embedded in Si thin films. However, the Au thin film grew and eventually protruded from the Si thin film in the form of Au silicide nano-balls. This is attributed to the low eutectic bonding temperature ($363^{\circ}C$) of Au with Si, and the process was performed with a substrate that was pre-heated at a temperature of $450^{\circ}C$ during HWCVD. The nano-balls and structures showed various formations depending on the deposited metals and Si surface. Furthermore, the samples of Au nano-balls showed low reflectance due to surface plasmon and quantum confinement effects in a spectra range of short wavelength spectra range.

• Journal of Korea Foundry Society
• /
• v.34 no.5
• /
• pp.156-161
• /
• 2014

This study is focused on the effect of $Al_2Ca$ as a modifier on eutectic Si modification of A356 alloy. Microstructural observation was carried out for as-cast, as-solution treated and as-aged samples. Solution treatment and aging were performed for 2, 4, 6 and 10 hrs at $540^{\circ}C$ and $170^{\circ}C$, respectively. Although A356 alloy, which $Al_2Ca$ was added, has no significant difference in as-cast phases with normal A356 alloys, it shows much more modified eutectic Si, grain refinement and improved tensile property both in as-cast and as-heat treated conditions. TGA result shows that $Al_2Ca$ added A356 alloy has a certain improvement in oxidation resistance.