• Polymer(Korea)
• /
• v.38 no.1
• /
• pp.62-68
• /
• 2014

To improve the compatibility of bentonite with rubber matrix, organo-modified bentonite was synthesized with a silane coupling agent, [3-(2-aminoethylamino)propyl]trimethoxysilane (AEAPTMS) in the suspension of bentonite. The structure and characteristics of organo-modified bentonite were investigated using FTIR-spectroscopy, thermogravimetric analysis (TGA) and X-ray diffraction (XRD). Ethylene-propylene-diene monomer (EPDM) rubber/organo-bentonite composites were compounded by a two-roll mill. The vulcanization and mechanical properties were studied. Results showed that the concentration of hydrochloric acid and $H_2O$ in the synthesis had significant influence on the modification of bentonite, which further contributed to the properties of the composites. Filled with 20 phr modified bentonite, the tensile strength and elongation at break of the rubber increased from 1.95 to 4.8 MPa and 300% to 500%, respectively.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.3C no.2
• /
• pp.48-54
• /
• 2003

To evaluate the radiation degradation of ethylene propylene rubber (EPR), radiation effects on EPR were investigated by using dielectric analysis and thermal-gravimetric analysis. Permittivity, loss factor, tan$\delta$, and thermal decomposition temperature were observed for ${\gamma}$-ray irradiated EPR. As the radiation dose was increased, the peak temperature of the loss factor and tans of EPR were increased and loss factor and tan$\delta$ at peak temperature were decreased. Activation energies were calculated using loss factor and thermal decomposition for ${\gamma}$-ray irradiated EPR as well. The trends of both calculated activation energies showed the same tendencies as radiation dose was increased.

• Journal of Radiation Industry
• /
• v.5 no.3
• /
• pp.237-242
• /
• 2011

In this research, the radiation resistance of ethylene propylene rubber (EPR) and chlorosulfonated polyethylene (CSPE) which can be used as a insulating materials of for electrical cable in the nuclear power plant were investigated. EPR and CSPE were irradiated by ${\gamma}$-ray at various doses ranging from 50 to 500 kGy at room temperature in air. The irradiated EPR and CSPE was investigated in terms of activation energy, mechanical properties, and oxidation stability. The experimental results revealed that CSPE exhibited the higher radiation resistance in comparison to that of EPR.

• Journal of the Korea Safety Management & Science
• /
• v.2 no.2
• /
• pp.187-200
• /
• 2000

The charge and discharge current in EPR(Ethylene Propylene Rubber), which were irradiated with the radiant capacity of 0~600 ［kgy/h］, have been measured in order to investigate the influence of the atmosphere (oxygen, air and vacuum) on electrical properties. It has been shown that the charge and discharge current increase as the amount of radiant capacity increases in air and vacuum atmosphere. This electrical property degradation can be speculated due to that the C＝O radicals or impurities, which comes from during shaping process, may act as dipoles. On the other hand, the charge and discharge current are shown to be higher in the amount of 1［kgy/h］ than these in 10［kgy/h］ in air atmosphere, because the charge and discharge current can be increased as the exposure time is extended with slower rate. Under the same amount of irradiation, the charge and discharge current in oxygen atmosphere are shown to be higher than those in vacuum. This is possibly due to that the main chain can be broken by oxidation when it is exposed to the $\gamma$ -rays.

• Elastomers and Composites
• /
• v.43 no.2
• /
• pp.104-112
• /
• 2008

The ethylene propylene diene terpolymer (EPDM) blends with styrene butadiene rubber (SBR) were prepared from an open 2-roll mill following the conventional rubber blend method, and then cure characteristics, mechanical properties and ozone resistance were subsequently examined. With incorporation of SBR the torque value of the EPDM and SBR blends showed a gradual increase in the cure curve. The maximum torque value was obtained with lowest level at 25wt% of SBR and it was increased linearly with more than 25wt%. As the SBR loading increased scorch time and optimum cure time decreased. Hardness represented a maximum at 50wt% of SBR. However upper and lower than that value it decreased. It was found that the unfavorable characteristics of ozone resistance of pure SBR was significantly improved through the blending of SBR with EPDM.

• Applied Chemistry for Engineering
• /
• v.32 no.4
• /
• pp.472-477
• /
• 2021

The crosslinking behavior of polyhedral oligomeric silsesquioxane (POSS) containing eight acrylate groups in a cage form in ethylene-propylene-diene rubber (EPDM) peroxide crosslinking, the effect on mechanical properties, and the thermal stability were investigated. An EPDM/POSS composite material was prepared by mixing 0 to 12 parts per hundreds of rubber (phr) of POSS per 100 phr of rubber by content and adding a peroxide crosslinking agent. As a result of crosslinking properties, it was found that the acrylate group of POSS was activated by peroxide and improved the peroxide crosslinking efficiency. Although the dispersion stability of POSS in EPDM/POSS composites was poor, the fracture strength, elongation and thermal stability were improved.

• Polymer(Korea)
• /
• v.37 no.5
• /
• pp.571-578
• /
• 2013

Polyamide12 (PA12) is blended with ethylene propylene diene rubber (EPDM) at various compositions in the presence of maleated EPDM (mEPDM) to afford blend materials having the characteristics of thermoplastic elastomer (TPE). The EPDM/PA12 melt-blends are further irradiated with electron-beam (e-beam) at 0~100 kGy dosage, yielding selective crosslinking between EPDM chains while retaining melt-processibility originated from PA12 phase. mEPDM acts as a compatibilizer and affords additional improvements in mechanical properties of the EPDM/PA12 blend. With 25 kGy of e-beam irradiation and mEPDM, the EPDM/PA12 blends successfully exhibit TPE behaviors with reasonable elastomeric and mechanical properties.

• Elastomers and Composites
• /
• v.29 no.2
• /
• pp.121-130
• /
• 1994

The physical properties of rubber blend between natural rubber(NR) and ethylene propylene diene terpolymer(EPDM) were investigated as a study of EPDM composite materials. For EPDM/NR blends, the effects of ethylene and diene contents in EPDM, blend ratio, dicumyl peroxide(DCP) curing system on the physical properties, interfacial adhesion force and dynamic crack growth etc. were studied. EPDM/NR blends loaded with carbon black were prepared by mechanical mixing and cured by plate heating cure press. Crosslinking density was measured by swelling method with toluene. The physical properties of all blends were measured with Instron, fatigue to failure(FTF), Demattia flex cracking tester(DMFC), scanning electron microscopy (SEM), etc. As the ethylene and diene contents in EPDM increased, the physical properties, such as dynamic crack growth, adhesion to other component were increased too. Interfacial adhesion force of EPDM/NR blends to dissimilar layer was improved by the use of optimum peroxide curing system.

• Elastomers and Composites
• /
• v.53 no.3
• /
• pp.124-130
• /
• 2018

Recently, microwaves have been used for desulfurization because they can selectively dissociate C-S and S-S bonds present in vulcanized rubber. In this study, we investigated the changes in structural and physical properties of EPDM (Ethylene propylene diene monomer) rubber by irradiating it with microwaves for different durations. The surface chemical composition of the irradiated EPDM rubber was analyzed by FT-IR, XPS, and EDS analyses. It was confirmed by XPS that C-S and S-S S2p peak heights greatly decreased when microwave irradiation was performed for more than 5 min. In the EPDM sample irradiated with microwaves for 10 min, the number of S-O bonds significantly increased owing to oxidation. As the microwave irradiation time was increased, SEM images showed cracks and voids on the EPDM surface. The 20% decomposition temperature of the EPDM rubber sample was investigated by TGA, and it was found to be about $435.23^{\circ}C$ for the EPDM rubber irradiated for 10 min. The crosslinking density of the EPDM rubber was determined by measuring the degree of swelling, and the highest value was observed for the E5 sample irradiated for 5 min. The degree of swelling of the E10 sample irradiated for 10 min was lower than that of the E5 sample. These results indicate that when irradiated with microwaves for more than a certain time, desulfurization occurs and the side chain of the EPDM rubber dissociates and forms additional crosslinking bonds.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.25 no.5
• /
• pp.368-376
• /
• 2005

Coolant rubber hoses for automobile radiators can be degraded and thus failed due to the influence of contacting stresses of air and coolant liquid under thermal and mechanical loadings. In this study, for EPDM(ethylene-propylene diene monomer) rubber conventionally used as a radiator hose material the aging behaviors of the skin part due to thermo-oxidative and electro-chemical stresses were nondestructively evaluated. Through the thermo-oxidative aging test, it was shown that the surface hardness IRHD(International Rubber Hardness Degrees) of the rubber increased with a considerable reduction of failure strain. On account of the penetration of coolant liquid into the skin part the weight of rubber specimens degraded by electro-chemical degradation(ECD) test increased, whereas their. failure strain and IRHD hardness decreased largely. The penetration of coolant liquid seemed to induce some changes in inner structure and micro hardness distribution of the rubbers. Consequently, EPDM rubbers degraded by thermo-oxidative aging and ECD could be characterized nondestructively by micro-hardness and chemical structure analysis methods.