A Study on the Properties of CSPE According to Accelerated Thermal Aging Years

  • Lee, Jung-Hoon;Kang, Myeong-Kyun;Jeon, Jun-Soo;Lee, Seung-Hoon;Kim, In-Yong;Park, Hyun-Shin;Shin, Yong-Deok
    • Journal of Electrical Engineering and Technology
    • /
    • v.9 no.2
    • /
    • pp.643-648
    • /
    • 2014
  • The accelerated thermal aging of CSPE (chlorosulfonated polyethylene) was carried out for 40.41, 121.22, and 202.04 days at $100^{\circ}C$, which are equivalent to 20, 60, and 100years of aging at $50^{\circ}C$, respectively. The volume electrical resistivities of the accelerated thermally aged CSPE samples for 0, 40.41, 121.22, and 202.04 days were $1.107{\times}10^{14}-2.097{\times}10^{14}$, $7.752{\times}10^{13}-1.556{\times}10^{14}$, $7.693{\times}10^{13}-1.521{\times}10^{14}$, and $7.380{\times}10^{13}-1.304{\times}10^{14}{\Omega}{\cdot}cm$, respectively, at room temperature. The permittivities of the accelerated thermally aged CSPE samples for 0, 40.41, 121.22, and 202.04 days were $2.89{\times}10^{-11}-3.65{\times}10^{-11}$, $3.40{\times}10^{-11}-3.70{\times}10^{-11}$, $3.50{\times}10^{-11}-3.82{\times}10^{-11}$, and $3.76{\times}10^{-11}-4.13{\times}10^{-11}$ F/m, respectively, at room temperature. The EAB (elongation at break) of the accelerated thermally aged CSPE samples for 0, 40.41, 121.22, and 202.04 days were 98.8-101.3, 59.5-60.3, 37.8-39.2, and 41.8-44.3%, respectively, at room temperature. The apparent densities of the accelerated thermally aged CSPE samples for 0, 40.41, 121.22, and 202.04 days were 1.603-1.614, 1.611-1.613, 1.622-1.628, and $1.618-1.620g/cm^3$, respectively, at room temperature. The measured currents of the accelerated thermally aged CSPE and the standard sample were almost constant after 5 min of applying a 300-V/mm electric field to the CSPE. The V-I slope of the accelerated thermally aged CSPE sample was increased if the applied electric field was increased at room temperature, and the V-I slope of the accelerated thermally aged CSPE was higher than that of standard CSPE.