• 한국분말재료학회지
• /
• 제20권1호
• /
• pp.53-59
• /
• 2013

Fe-TiC composite powder was fabricated via two steps. The first step was a high-energy milling of FeO and carbon powders followed by heat treatment for reduction to obtain a (Fe+C) powder mixture. The optimal condition for high-energy milling was 500 rpm for 1h, which had been determined by a series of preliminary experiment. Reduction heat-treatment was carried out at $900^{\circ}C$ for 1h in flowing argon gas atmosphere. Reduced powder mixture was investigated by X-ray Diffraction (XRD), Field Emission-Scanning Electron Microscopy (FE-SEM) and Laser Particle Size Analyser (LPSA). The second step was a high-energy milling of (Fe+C) powder mixture and additional $TiH_2$ powder, and subsequent in-situ synthesis of TiC particulate in Fe matrix through a reaction of carbon and Ti. High-energy milling was carried out at 500 rpm for 1 h. Heat treatment for reaction synthesis was carried out at $1000{\sim}1200^{\circ}C$ for 1 h in flowing argon gas atmosphere. X-ray diffraction (XRD) results of the fabricated Fe-TiC composite powder showed that only TiC and Fe phases exist. Results from FE-SEM observation and Energy-Dispersive X-ray Spectros-copy (EDS) revealed that TiC phase exists uniformly dispersed in the Fe matrix in a form of particulate with a size of submicron.

• 한국수소및신에너지학회논문집
• /
• 제19권4호
• /
• pp.359-366
• /
• 2008

Hydrogen as a high-quality and clean energy carrier has attracted renewed and ever-increasing attention around the world in recent years, mainly due to developments in fuel cells and environmental pressures including climate change issues. In this processes for hydrogen production from fossil fuels, separation and purification is a critical technology. $(Ni_{60}-Nb_{40})_{95}-Pd_5$ alloy ingots were prepared by arc-melting the mixture of pure metals in an Ar atmosphere. Melt-spun ribbons were produced by the single-roller melt-spinning technique in an Ar atmosphere. Amorphous structure and thermal behavior were characterized by XRD and DSC. The permeability of the $(Ni_{60}-Nb_{40})_{95}-Pd_5$ amorphous alloy membrane was characterized by hydrogen permeation experiments in the temperature range 623 to 773 K and pressure of 2 bars. The maximum hydrogen permeability was $3.54{\times}10^{-9}[mol{\cdot}m^{-1}s^{-1}{\cdot}pa^{-1/2}]$ at 773 K for the $(Ni_{60}-Nb_{40})_{95}-Pd_5$ amorphous alloy.

• Bulletin of the Korean Chemical Society
• /
• 제27권2호
• /
• pp.219-223
• /
• 2006

The thermal decomposition of tetrakis(ethylmethylamido) titanium (TEMAT) has been investigated in Ar and $H_2$ gas atmospheres at gas temperatures of 100-400 ${^{\circ}C}$ by using Fourier Transform infrared spectroscopy (FTIR) as a fundamental study for the chemical vapor deposition (CVD) of titanium nitride (TiN) thin film. The activation energy for the decomposition of TEMAT was estimated to be 10.92 kcal/mol and the reaction order was determined to be the first order. The decomposition behavior of TEMAT was affected by ambient gases. TEMAT was decomposed into the intermediate forms of imine (C=N) compounds in Ar and $H_2$ atmosphere, but additional nitrile (RC$\equiv$N) compound was observed only in $H_2$ atmosphere. The decomposition rate of TEMAT under $H_2$ atmosphere was slower than that in Ar atmosphere, which resulted in the extension of the regime of the surface reaction control in the CVD TiN process.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2004년도 학술대회지
• /
• pp.253-259
• /
• 2004

The Jeju Island in Korea is the clean area which the tradition culture is preserved locally well with the nature environment of Heaven's blessing. An air pollution is becoming recently serious problem as the industrial development is proceeded with the urbanization. This study investigates that the atmosphere environment at Jeju area influences on the metal corrosion. A study of the atmosphere corrosion for carbon steel, copper, zinc ana aluminium exposed on five test sites indoors and outdoors. Corrosion results are treated statistically and adjusted to a model previously proposed for carbon steel, copper, zinc and aluminium based on the influence of environmental parameters and main pollutants($SO_2$ and chlorides) on tire atmosphere corrosion of metals. Through this study, we try to set the standards atmosphere corrosion at Jeju Island.

• 한국전기전자재료학회논문지
• /
• 제16권11호
• /
• pp.1055-1061
• /
• 2003

A study has been made of surface modification of various organic materials by ion implantation to increase the surface electrical properties. The substrate used were PP(polypropylene), PET(polyethylene teraphthalate), ECOP(ethylene copolyester), PS(polystyrene). N$_2$, Ar ion implantation was performed at energies of 40 and 50keV with fluences from 5${\times}$ 10$\^$15/ to 7${\times}$10$\^$16/ ions/$\textrm{cm}^2$ with and without H$_2$O gas environment. Surface resistance decrease of implanted polymers was affected by ion implantation energy, ion species, atmosphere of chamber and kind of polymer. In result, surface conductivity of polymers irradiated with atmosphere gas H$_2$O was 10 times more higher than normal vacuum atmosphere, but after 90 hours, surface conductivity returned to the without H$_2$O gas atmosphere condition caused by aging effect. After vacuum forming, surface resistance value was changed to over 10$\^$16/$\Omega$/$\square$, because creation of surface cracks.

• Nuclear Engineering and Technology
• /
• 제28권5호
• /
• pp.458-466
• /
• 1996

The effects of dopants on the modification of microstructure of UO$_2$ and UO$_2$-4wt%CeO$_2$ sintered pellets have been studied in hydrogen and $CO_2$/CO mixture atmospheres by using $Ta_2O_5$, TiO$_2$ and $Nb_2O_5$ as sintering additives. The dopant were added as oxide powders and homogenized by attrition milling. The mixed powders were pressed, and then sintered in hydrogen at 1$700^{\circ}C$ , or in oxidizing atmosphere using Controlled $CO_2$/CO mixtures at 125$0^{\circ}C$. Both density and microstructure of UO$_2$ are modified by the addition of dopants in reducing atmosphere. The sintered density is increased with $Ta_2O_5$ addition up to 0.33wt% and subsequently decreased with higher content of the additive. The effect on the densification and the gain growth are apparent with the addition of 0.24wt% $Nb_2O_5$. With 0.lwt% titania and 0.6wt% $Ta_2O_5$, the sintered density is decreased, but the grain size is increased. In oxidizing atmosphere, the grain sizes for UO$_2$ doped with the above additives are smaller than that for pure UO$_2$. The grain size of Ta or Nb-doped UO$_2$ is decreased with increasing $CO_2$/CO ratio, but that of pure UO$_2$or T-doped UO$_2$ is increased. A large portion of second phases is observed in UO$_2$ doped with 0.lwt% TiO$_2$ sintered in hydrogen atmosphere, while, in $CO_2$/CO atmospheres, the second phases or dopant agglomerates are not observed. For UO$_2$-4wt%CeO$_2$ mixed oxide, the effect of additives on the gain growth is not so much as that for the pure UO$_2$. This is attributed to the formation of clusters by dopant cations and Ce ions, so that the additives contribute to a lesser exent to the grain growth for the mixed oxide.

• Nuclear Engineering and Technology
• /
• 제54권1호
• /
• pp.177-185
• /
• 2022

Hydrogen risk in the containment filtered venting system (CFVS) vessel was analyzed, considering operation pressure and modes with the effect of PAR and accident scenarios. The CFVS is to depressurize the containment by venting the containment atmosphere through the filtering system. The CFVS could be subject to hydrogen risk due to the change of atmospheric conditions while the containment atmosphere passes through the CFVS. It was found that hydrogen risk increased as the CFVS opening pressure was set higher because more combustible gases generated by Molten Core Concrete Interaction flowed into the CFVS. Hydrogen risk was independent of operation modes and found only at the early phase of venting both for continuous and cyclic operation modes. With PAR, hydrogen risk appeared only at the 0.9 MPa opening pressure for Station Black-Out accidents. Without PAR, however, hydrogen risk appeared even with the CFVS opening set-point of 0.5 MPa. In a slow accident like SBO, hydrogen risk was more threatening than a fast accident like Large Break Loss-of-Coolant Accident. Through this study, it is recommended to set the CFVS opening pressure lower than 0.9 MPa and to operate it in the cyclic mode to keep the CFVS available as long as possible.

• 한국분말재료학회지
• /
• 제17권4호
• /
• pp.295-301
• /
• 2010

Multi shell graphite coated Ag nano particles with core/shell structure were successfully synthesized by pulsed wire evaporation (PWE) method. Ar and $CH_4$ (10 vol.%) gases were mixed in chamber, which played a role of carrier gas and reaction gas, respectively. Graphite layers on the surface of silver nano particles were coated indiscretely. However, the graphite layers are detached, when the particles are heated up to $250^{\circ}C$ in the air atmosphere. In contrast, the graphite coated layer was stable under Ar and $N_2$ atmosphere, though the core/shell structured particles were heated up to $800^{\circ}C$. The presence of graphite coated layer prevent agglomeration of nanoparticles during heat treatment. The dispersion stability of the carbon coated Ag nanoparticles was higher than those of pure Ag nanoparticles.

• Environmental Engineering Research
• /
• 제11권5호
• /
• pp.250-256
• /
• 2006

The combustion kinetics of poly(ethylene terephthalate) (PET) was studied by the dynamic model which accounts for the thermal decomposition of polymer at any time. The kinetic analysis was performed by a conventional nonisothermal thermogravimetric (TG) technique at several heating rates between 10 and 40 K/min in air atmosphere. The thermal decomposition of PET in air atmosphere was found to be a complex process composed of at least two stages for which kinetic values can be calculated. The combustion kinetic analysis of PET gave apparent activation energy for the first stage of $257.3{\sim}269.9\;kJ/mol$, with a value of $140.5{\sim}213.8\;kJ/mol$ for the second stage. To verify the effectiveness of the kinetic analysis method used in this work, the kinetic analysis results were compared with those of various analytical methods. The kinetic parameters were also compared with values of the pyrolysis of PET in nitrogen atmosphere.

• 대한화학회지
• /
• 제15권6호
• /
• pp.370-377
• /
• 1971

The Carbon-14 content in surface air at Seoul, Korea, was measured from February 1970 to August 1971 and a Larix Leptolepis, Gordon tree (Ip-Gal Namu) grown at Kwang-Nung, Kyunggi-Do, Korea, having 37 growth rings, was assayde for $^{14}C$. From the results of the surface air study, it was calculated that during the above period the inventory of excess $^{14}C$ in the atmosphere decreased with a half-time of 4.6 years. The overall yearly decrease was also checked. The tree-ring study showed that the tree's atmosphere was affected by $^{14}C$ from nuclear tests after 1956. In one study, atmospheric $CO^2$ samples were collected bi-monthly by the absorption of $CO^2$ in alkaline hydroxide solution. In the other, 5 year annual growth rings were assayed for radiocarbon. For the radioactivity measurement, carbon atoms in samples were converted to carbon atoms of benzene. The resulting benzene was taken as primary solvent for liquid scintillation counting.