• Restorative Dentistry and Endodontics
• /
• 제28권5호
• /
• pp.402-408
• /
• 2003

This study was done to present a criterion in selection of the most proper light sources and materials by measuring metamerism index(MI) of the light curing composite resins with spectrocolorimeter. Metamerism is defined when two objects appear to be the same color in one illuminant but different in another. This is due to the fact that they have different spectral curves that fail to match under the second illuminant. In this study, A1 & A3 shade of five light curing composite resins (Esthet-X, Filteck Z250, Filteck A110. Charisma. Vitalescence) were chosen based on Vita shade. Five samples were made for shade of each product with Teflon mold (diameter: 15mm, thickness: 2mm). Metamerism index of each samples on a Barium sulfate plate($L^{*}=96.54,{\;}a^{*}=0.19,{\;}b^{*}=0.01$) prepared for sample fixation were measured with spectrocolorimeter(Miniscan XE plus. Model 4000s. Hunter Lab. USA) by applying standard light source D^{65}, C. Fcw, TL84 and A. Standardization was done with reference standard(X=80.8, Y=85.7, Z=90.8) and light trap. The results were as follows. 1. Different resins with same Vita shade showed recognizable color difference (${\delta}E^{*}>2$). 2. All composites had MI below accepted value 0.5 between standard illuminant(D$_{65}$, C, & A) and below 1.5 under fluorescent condition (Fcw & TL84). 3. MI value between $D^{65}$ and A showed higher value than MI value between other source of light(p<0.01). 4. All resins except Z250 showed MI value that A3 is higher than A1 between $D^{65}$ and A(p<0.05).except Z250 showed MI value that A3 is higher than A1 between $D^{65}$ and A(p<0.05).

• 대한소아치과학회지
• /
• 제48권3호
• /
• pp.280-290
• /
• 2021

치수복조제는 치관부에 위치하기 때문에 색 안정성이 최종적인 심미성에 영향을 미치는 중요한 요소로 간주된다. 이 연구는 시간에 따른 치관의 색조 변화를 분석하여 치수복조제의 색조 안정성을 비교해보고자 하였다. 발거된 소구치의 치관에 와동을 형성하고 4가지 종류의 치수복조제를 충전하였다. 색상 변화는 분광광도계를 사용하여 재료를 넣기 전, 재료를 넣은 즉시, 재료를 넣고 1일 후, 1주 후, 2주 후, 4주 후, 8주 후, 12주 후, 16주 후에 측정을 시행하였다. Proroot white MTA^®와 TheraCal LC^®는 시간이 지남에 따라 지속적인 L^* 값의 감소와 ∆E^* 값의 증가를 보였다. 반면 Biodentine^®과 Well-root^TM PT는 유의한 L^* 값의 변화가 없었고 일정한 ∆E^* 값을 유지하였다. 방사선 불투과성 물질로 산화 비스무트가 포함된 치수복조제의 적용 시 치아의 색조 변화가 나타날 수 있으며, 법랑질의 두께가 얇은 유치의 수복이나 전치부의 심미 수복 시 치수복조제의 장기적인 색 안정성을 고려해야 한다.

• 구강회복응용과학지
• /
• 제23권3호
• /
• pp.249-257
• /
• 2007

State of problem : The use of zirconium oxide all-ceramic material provides several advantages, including a high flexural strength(>1000MPa) and desirable optical properties, such as shading adaptation to the basic shades and a reduction in the layer thickness. Along with the strength of the materials, the cementation technique is also important to the clinical success of a restoration. Nevertheless, little information is available on the effect of different surface treatments on the bonding of zirconium high-crystalline ceramics and resin luting agents. Purpose : The aim of this study was to test the effects of surface treatments of zirconium on shear bond strengths between bovine teeth and a zirconia ceramic and evaluate differences among cements Material and methods : 54 sound bovine teeth extracted within a 1 months, were used. They were frozen in distilled water. These were rinsed by tap water to confirm that no granulation tissues have left. These were kept refrigerated at $4^{\circ}C$ until tested. Each tooth was placed horizontally at a plastic cylinder (diameter 20mm), and embedded in epoxy resin. Teeth were sectioned with diamond burs to expose dentin and grinded with #600 silicon carbide paper. To make sure there was no enamel left, each was observed under an optical microscope. 54 prefabricated zirconium oxide ceramic copings(Lava, 3M ESPE, USA) were assigned into 3 groups ; control, airborne-abraded with $110{\mu}m$ $Al_2O_3$ and scratched with diamond burs at 4 directions. They were cemented with a seating force of 10 ㎏ per tooth, using resin luting cement(Panavia $F^{(R)}$), resin cement(Superbond $C&B^{(R)}$), and resin modified GI cement(Rely X $Luting^{(R)}$). Those were thermocycled at $5^{\circ}C$ and $55^{\circ}C$ for 5000 cycles with a 30 second dwell time, and then shear bond strength was determined in a universal test machine(Model 4200, Instron Co., Canton, USA). The crosshead speed was 1 mm/min. The result was analyzed with one-way analysis of variance(ANOVA) and the Tukey test at a significance level of P<0.05. Results : Superbond $C&B^{(R)}$ at scratching with diamond burs showed the highest shear bond strength than others (p<.05). For Panavia $F^{(R)}$, groups of scratching and sandblasting showed significantly higher shear bond strength than control group(p<.05). For Rely X $Luting^{(R)}$, only between scratching & control group, significantly different shear bond strength was observed(p<.05). Conclusion : Within the limitation of this study, Superbond $C&B^{(R)}$ showed clinically acceptable shear bond between bovine teeth & zirconia ceramics regardless of surface treatments. For the surface treatment, scratching increased shear bond strength. Increase of shear bond strength by sandblasting with $110{\mu}m$ $Al_2O_3$ was not statistically different.

• Restorative Dentistry and Endodontics
• /
• 제24권2호
• /
• pp.310-321
• /
• 1999

In this in vitro study, confocal laser scanning microscopic morphology of dentin-resin interface and its relationship to shear bond strength were investigated after the exposed dentin surfaces were treated with 3 different kinds of dentin adhesive systems[three-step; Scotchbond Multi-Purpose Plus(SMPP), self-priming bonding resin; Single Bond(SB), self-etching primer; Clearfil Liner Bond 2(LB2)]. 52 extracted human molar teeth without caries and/or restorations. The experimental teeth were randomly divided into three groups of seventeen teeth each. In five teeth of each group, class V cavities(depth: 1.5mm) with 900 cavosurface angles were prepared at the cementoenamel junction on buccal and lingual surfaces. Bonding resins of each dentin adhesive system were mixed with rhodamine B. Primer of SMPP was mixed with fluorescein. In group 1. the exposed dentin was conditioned with etchant, applied with above primer and bonding resin of SMPP. In group 2, with etchant and self-priming bonding agent of SB. In group 3, with self-etching primer and bonding agent of LB2. After treatment with dentin adhesive systems, composite resin were applied and photocured. The experimental teeth were cut longitudinally through the center line of restoration and grounded so that about $90{\mu}m$-thick wafers of buccolingually orientated dentin were obtained. And, $70{\sim}80{\mu}m$-thick wafers sectioned horizontally, thus presenting a dentinal tubules at 900 to the cut surface of a remaining tooth, were obtained. Primer of SMPP mixed with rhodamine B was applied to these wafers. Confocal laser scanning microscopic investigations of these wafers were done within of 24 hours after treatment. To measure shear bond strength, the remaining twelve teeth of each group were grounded horizontally below the dentinoenamel junction, so that no enamel remained. After applying dentin adhesive systems on the dentin surface, composite was applied in the shape of cylinder. The cylinder was 5mm in diameter, and 2mm in thickness. Shear bond strength was measured using Instron with a cross-head speed of 0.5mm/min. It was concluded as follows ; 1. Hybrid layer of SMPP(mean: $4.56{\mu}m$) was thicker than that of any other groups. This value was not statistically significant thicker than that of SB(mean: $3.41{\mu}m$, p>0.05), and significant thicker than that of LB2(mean: $1.56{\mu}m$, p<0.05). There was a statistical difference between SB and LB2(p<0.05). 2. Although there were variations in the length of resin tag even in a sample, and in a group, most samples in SMPP and SB showed resin tags extending above $20{\mu}m$. But samples in LB2 showed resin tags of $10{\mu}m$ at best. 3. Besides primer's infiltration into demineralized peritubular dentin and dentinal tubules, fluorophore of primer was detected in the lateral branches of dentinal tubules. 4. All groups demonstrated statistically significant differences from one another(p<0.05), with shear bond strengths given in descending order as follows: SMPP(18.3MPa), SB(16.0MPa) and LB2(12.4MPa). 5. LB2 having thinnest hybrid layer($1.56{\mu}m$) showed the lowest shear bond strength(12.4MPa).

• Restorative Dentistry and Endodontics
• /
• 제32권1호
• /
• pp.69-79
• /
• 2007

이 연구의 목적은 쐐기형 비우식성 5등급와동을 복합레진으로 수복하기 전, 후에 과도한 교합력에 의한 응력분포 변화를 비교 연구하기 위함이었다. 발치된 상악 제 2소구치를 이용하여 쐐기형 비우식성 치경부병소를 가진 3차원 유한요소모형을 제작한 후 탄성계수가 서로 다른 혼합형 복합레진과 흐름성 복합레진으로 각각 충전하고 이때의 상아질 접착제의 두께는 $40{\mu}m$로 하였다. 협측교두와 설측교두에 500 N의 하중을 각각 가한 후 ANSYS 프로그램을 이용하여 주응력분석법으로 병소의 심부와 와동 수직병의 응력분포를 비교하여 다음과 같은 결과를 얻?B다. 1. 협측교두에 하중이 가해지면 병소에 압축응력이 나타나고, 설측교두에 가해지면 인장응력이 나타난다. 두 가지 하중에서 모두 병소의 근심 끝 부위와 인접한 백악법랑경계 그리고 병소의 심부에 응력이 집중되었다. 2. 응력의 집중을 보였던 병소의 금심부근과 심부는 수복 후 응력이 많이 감소하였으며 대신 다른 부위에서는 응력이 약간 증가하였다. 3. 병소의 근심부위와 심부는 흐름형 복합레진으로 수복하였을 때 보다 혼합형 복합레진으로 수복하였을 때 응력이 더 많이 감소하였다.