• The Journal of Korean Academy of Prosthodontics
• /
• v.36 no.6
• /
• pp.846-857
• /
• 1998

The purpose of this study was to compare the fitness of the IPS Empress ceramic crowns according to margin type such as bevel, shoulder, rounded shoulder, shoulder with bevel, rounded shoulder with bevel and grooved bevel. After 10 experimental dies were constructed for each group, the IPS Empress ceramic crowns were fabricated on the dies, cemented with resin cement(Bistite resin cement, Tokuyama Soda Co. Ltd., Japan) and embeded in clear epoxy resin. Each specimen was sectioned with a low speed diamond saw in both the faciopalatal and the mesiodistal direction. The cement film thickness was measured with a measuring microscope. The obtained results were as follows : 1. The fitness at the external margin was good in the following order: rounded shoulder(28.99), shoulder with bevel(31.33), grooved bevel(31.79), rounded shoulder with bevel(34.65), bevel(35.02) and shoulder(35.08). However there is no significant statistical difference. 2. The fitness at the internal margin of bevel(25.75), rounded shoulder(31.24), shoulder with bevel(32.07) and rounded shoulder with bevel(34.45) was better than that of shoulder(47.98). 3. The fitness at the axial surface of bevel(26.58) was better than that of shoulder(49.59). 4. The fitness at the central fossa was good in the following order: shoulder with bevel(38.88), grooved bevel(40.46) rounded shoulder with shoulder(46.29), shoulder(48.91), bevel(49.47) and rounded bevel(52.07). However there is no significant statistical difference. 5. Overall fitness of bevel(29.71), rounded shoulder(32.49) and shoulder with bevel(34.47) was better than that of shoulder(44.73).

• The Journal of Korean Academy of Prosthodontics
• /
• v.37 no.4
• /
• pp.416-424
• /
• 1999

Simulation of naturally appearing enamel in fixed prosthodontics could be achieved with all ceramics. The purpose of this study was to investigate the stain resistance of 4 different all ceramics materials (In-ceram, IPS Empress, Celay, Vintage). Forty specimens were prepared using manifacture's instruction and the samples were divided into two groups. The specimens for one group were glazing and those for other group were ground to remove the glazing layer. All specimens were immersed in methylene-blue for 24hours. The color values for each specimen was measured with colorimeter (Mode Tc-6Fx, Tokyo Denshoku Co.) prior to and after immersion in methylene-blue. The following conclusions were drawn from this study. 1 The stain resistance of glazing ceramics was higher than that of unglazing ceramics. 2. The changes of ${\Delta}E^*$\;and\;L^*$ values were revealed in Vintage and unglazing Celay. 3. The changes of $a^*$ values were revealed in unglazing vintage, Celay, In-ceram. 4. The changes of $b^*$ value were revealed in Vintage, IPS Empress and unglazing Celay.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.4
• /
• pp.405-420
• /
• 2003

Purpose : The purpose of this study was to compare the fracture resistance of the IPS Empress ceramic crown with 1.0mm width rounded shoulder, which is usually recommended in all ceramic crown. and 0.5mm width chamfer finish lines on the maxillary central incisor. Material and method : After 15 metal dies were made for each group, the IPS Empress all ceramic crowns were fabricated and cemented with resin cement(Bistite resin cement, Tokuyama Soda Co. LTD., Japan) on the metal die. The cemented crowns were mounted on the positioning jig and the universal testing machine(Zwick Z020, Zwick Co. Germany)was used to measure the fracture strength with loading on the incisal edge. And also, three-dimensional finite element stress analysis was used to measure the stress distribution with the various types of the finish lines(1.0mm width rounded shoulder, 0.5mm width chamfer), the loading site(incisal edge, incisal $\frac{1}{3}$) and the type of loading(concentration loading, distribution loading). Results and conclusion : 1. In the fracture resistance experiment according to the finish line, the mean fracture strength of rounded shoulder(876N) and the mean fracture strength of chamfer(882N) did not skew any significant difference between each other(p>0.05). 2. The stress distribution of all ceramic crown in three dimensional finite element analysis showed concentration aspect at loading point and cervical area or labial surface. 3. In metal die, there were no differences in stress distribution between finish lines, but in natural teeth model, chamfer finish line showed higher stress than rounded shoulder finish line. 4. When force was loaded on the incisal edge the stress was concentrated on the incisal edge and the cervical area of labial surface. When force was loaded on the incisal $\frac{1}{3}$, the stress concentrated on the cervical area of labial surface and the cingulum area. 5. Generally, natural teeth model showed higher and various stress than the metal die.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.1
• /
• pp.130-143
• /
• 1997

A heat-pressed technique(IPS-Empress, Ivoclar) has been described to construct single unit crown, inlay/onlay and veneers using a partially pre-cerammed and pre-colored glass-leucite ingot that has the greateast strength by the combination of heat-pressed procedure through the smalldiameter sprue and heat treatment procedure. The purpose of this study was to evaluate the flexure strength of a heat-pressed ceramic material(IPS-Empress) without simulated firing treatments according to pontic designs. Two groups of 9 disks(1.4mm thick, 14mm in diameter) each using two types of sprues with different diameters($({\Phi}2.8\;,{\Phi}1.8)$) and numbers were prepared. The specimens were mounted in the testing jig. The flexural strengths were determined, by means of the bi-axial bending test, by loading the center of disk to failure using a universal testing machine(Zwick 145141, Zwick, Germany) at a cross-head speed of 1.0 mm/min. The means flexural strength value of one group using a sprue with ${\Phi}2.8$ was $140.4{\pm}8.0Mpa$. That of the other group using two sprues with ${\Phi}1.8$ was $151.8{\pm}10.3Mpa$. After analysis, results showed that there was a statistical difference between groups(t=2.33m p<0.05). No clnical implications were drawn from these data because of absence of simulated firing treatment.

• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.5
• /
• pp.514-523
• /
• 2004

Statement of problem: All-ceramic restorations have been advocated for superior esthetics. Various post and core systems have been used to improve the strength of damaged teeth, but it is unclear whether they affect the final shade of finished all-ceramic restorations. Purpose: The influence of different types of post and core systems on light transmission through all-ceramic crowns was assessed by spectrophotometric analysis. Also the masking effect of different thickness of ceramic ingot was evaluated. Material and Methods : Forty-five sample disks (15mm in diameter) at several thickness(1.0, 1.5, 2.0mm) and value(shade 100, 200, 300) were made in heat pressed ceramic(IPS-Empress). Background specimens simulating gold-alloy cast posts(Type III casting gold alloy), metal posts(Ni-Cr casting alloy) and ceramic posts(CosmoPost) were fabrica-ted. Resin composite(Z250, A3 shade) was used as a tooth substrate reference. For each combination, the change in color was measured with a spectrophotometer. Readings were performed for 2 conditions (1) ability of ceramic to mask the core in relation to its thickness(1.0, 1.5, or 2.0mm) ; (2) influence of post and core types on the final color of the ceramic. Data were recorded according to the CIE $L^*a^*b^*$ systems and color difference($\Delta$E) was calculated. Results: 100 shade ingot: when ceramic thickness was 1.0mm, $\Delta$E value for ceramic post larger than 1 but $\Delta$E value for metal and gold post was larger than 2. For ceramic thickness of 1.5mm, only $\Delta$E value for metal was larger than 2, and the other samples' $\Delta$E value was smaller than 2. For ceramic thickness of 2.0mm, $\Delta$E values for all specimens was smaller than 2. 200 shade ingot: when ceramic thickness was 1.0mm, $\Delta$E value for ceramic post was smaller than 1 but $\Delta$E value for metal and gold post was larger than 2. For ceramic thickness of 1.5 mm, only the $\Delta$E value for metal was larger than 2, and the other samples' $\Delta$E value was smaller than 2. For ceramic thickness of 2.0mm, $\Delta$E values for all specimens was smaller than 1. 300 shade ingot: when ceramic thickness was 1.0mm, only $\Delta$E value for metal was larger than 2 and the other samples' $\Delta$E value was smaller than 2. For ceramic thickness of 1.5mm, $\Delta$E values for all specimens was smaller than 1. For ceramic thickness of 2.0mm, $\Delta$E values for all specimens was smaller than 1. Conclusion: The final esthetic result of the IPS-Empress glass-ceramic restoration was not affected by the presence of different core materials when the thickness was more than 2.0 mm. When ceramic thickness decreases to 1.5mm, it is advised to take the substrate aspects into consideration. If the ceramic thickness is less than 1.0mm, using the tooth color matched substrate is strongly recommended.

• The Journal of Korean Academy of Prosthodontics
• /
• v.40 no.4
• /
• pp.365-373
• /
• 2002

The purpose of this study was to investigate the effects of desensitizer on shear bond strength of adhesive resin cements for all ceramic crown. For this study, Gluma $desensitizer^{(R)}$(Heraeus Kulzer, Germany) and MS $Coat^{(R)}$(Sun medical, Japan) were used as desensitizer, and Bistite $II^{(R)}$ resin cement(Tokuyama, Japan) and Variolink $II^{(R)}$ resin cement (Ivoclar, Liechtenstein) were used. IPS Empress ceramics were bonded to dentin surfaces after application of desensitizer and shear bond strength of specimens were measured using UTM(Zwick 1456 41. Zwick, Germany) at a crosshead speed of 1mm/min. The obtained results were as follows : 1. The shear bond strength of both resin cements were not affected by Gluma $desensitizer^{(R)}$ containing HEMA 2. The shear bond strength of Bistite $II^{(R)}$ resin cement was significantly decreased by MS $Coat^{(R)}$. 3. The failure mode in MS $Coat^{(R)}-Bistite \;II^{(R)}$ group was mainly adhesive type between dentin and resin cement. but that of Gluma $desensitizer^{(R)}$-Variolink $II^{(R)}$ group was mainly mixed type, combined adhesive failures between dentin and resin cement or porcelain and resin cement.

• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.5
• /
• pp.501-513
• /
• 2004

Purpose : The purpose of this study was to evaluate the effects of etching time on shear bond strength of four resin cements to IPS Empress 2 ceramic. Material and Methods: Forty rectangular shape ceramic specimens ($10{\times}15{\times}3.5mm$ size) were used for this study. The ceramic specimens divided into four groups and were etched with 10% hydrofluoric acid for 0, 10, 30, 60, 180, 300, 420, 600, and 900 seconds respectively. Etched surfaces of ceramic specimens were coated with ceramic adhesive system and bonded with four resin cement (Variolink II, Panavia F, Panavia 21, Super-Bond C&B) using acrylic glass tube. All cemented specimens were tested under shear loading untill fracture on universal testing machine at a crosshead speed 1mm/min: the maximum load at fracture (kg) was recored. Shear bond strengh data were analyzed with oneway analysis of variance and Tukey HSD tests (p<.05). Etched ceramic surfaces (0-, 60-, 300-, and 600-seconds etching period) and fracture surfaces after shear testing were examined mophologically using scanning electron microscopy. Results : Ceramic surface treatment with 10% hydrofluoric acid improved the bond strength of three resin cement except for Super-Bond C&B cement. Variolink II (41.0$\pm$2.4 MPa) resin cement at 300-seconds etching time showed statistically higher shear bond strength than the other resin cements (Panavia F: 28.3$\pm$2.3 MPa, Panavia 21: 21.5$\pm$2.2 MPa, Super-Bond C&B: 16.7$\pm$1.6 MPa). Ceramic surface etched with 10% hydrofluoric acid for 300 seconds showed more retentive surface texture. Conclusion: Within the limitation of this study, Variolink II resin cement are suitable for cementation of Empress 2 all-ceramic restorations and etching with 10% hydrofluoric acid for 180 to 300 seconds is required to enhance the bond strength.