• Journal of the Korean Institute of Gas
• /
• v.24 no.6
• /
• pp.47-54
• /
• 2020

A brittle fracture is one of the source of structural damage and can bring a fatal accident. The inner shell of LNG storage tank should be designed and applied to construction by ensure that no brittle crack will occur under -162℃ condition. In point of view of fracture mechanics brittle fracture in the structure could be referred as crack initiation and crack arrest. It should be designed no crack initiation. However, in the unlikely event of a brittle fracture occurring, a back-up function of arresting the brittle crack should be included for the design. In this paper investigated the characteristics of 9% Ni steel thick plates of having a capability of arresting brittle cracks under the thickness of 33 mm, 37mm, 40 mm. First, charpy test has performed to evaluate the fundamental brittle impact fracture property of 9% Ni steel under the temperature of 24℃, -162℃ and -196℃. In addition, Duplex ESSO tests were also performed under -196℃ to evaluate the capability of crack arrest for 9% Ni steel. From the experiments results, it was confirmed that all the thickness of 9% Ni steel plates exhibits sufficient brittle crack arrest fracture toughness for the application of LNG storage tank as a inner shell.

• Journal of Welding and Joining
• /
• v.33 no.1
• /
• pp.35-40
• /
• 2015

Recently, there have been the increase of ship size and the development of oil and gas in arctic region. These trends have led to the requirements such as high strength, good toughness at low temperature and good weldability for prevent of brittle fracture at service temperature. There has been the key issue of crack arrestability in large size structure such as container ship. In this report for the first time, crack arrest toughness of thick steel plate welds was evaluated by large scale ESSO test for estimate of brittle crack arrestability in thick steel plate. For large structures using thick steel plates, fracture toughness of welded joint is an important factor to obtain structural integrity. In general, there are two kinds of design concepts based on fracture toughness: crack initiation and crack arrest. So far, when steel structures such as buildings, bridges and ships were manufactured using thick steel plates (max. 80~100mm in thickness), they had to be designed in order to avoid crack initiation, especially in welded joint. However, crack arrest design has been considered as a second line of defense and applied to limited industries like pipelines and nuclear power plants. Although welded joint is the weakest part to brittle fracture, there are few results to investigate crack arrest toughness of welded joint. In this study, brittle crack arrest designs were developed for hatch side coaming of large container ships using arrest weld, hole, and insert technology.

• Journal of Ship and Ocean Technology
• /
• v.3 no.3
• /
• pp.25-44
• /
• 1999

Estimation efficiencies according to different sea trial are investigated in connection with sensitivity analysis, and new trial method is proposed which can improve the estimation efficiency of hydrodynamic derivatives. MMG Equation with Kijima's formula is used for simulation. Extended Kalman Filter is chosen for estimation technique and hydrodynamic derivatives of interest is limited to 12 of those in sway and yaw equations. Esso Osaka is selected for the test ship. Sensitivity analysis and estimation results based on conventional trials show that a more sensitive derivative gives more efficient estimation result. Sensitivities of nonlinear derivatives become pronounced in the trial where steady condition lasts longer such as turning test, while sensitivities of linear derivatives gas a larger values in the trial where unsteady condition lasts longer such as 10deg-10deg zigzag test. Consequently, in new method , named S-type trial, steady and unsteady condition are combined appropriately to increase sensitivities. Linear derivatives are estimated better in S-type trial and the estimation of nonlinear derivatives is improved to extent.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.103-103
• /
• 2009

As the size of containership increased over 14,000TEU, thick steel plate with high strength has been used. The plate thickness increased over 70mm and yield strength of the steel plate was around $47kg_f/mm^2$. Many researchers reported that the thick welded plate has low crack arrest toughness. They noticed the crack arrest ability is dependent on the plate thickness. In other words, brittle crack propagates straightly along the welded line and make abrupt fracture in the thick plate which causes low $K_{ca}$. In this study, the other factors, especially welding heat input, to cause low crack arrest toughness was investigated for thick steel plate welds. EH grade steel plates were used in this study and 50 to 80 thick plates were tested to confirm thickness sensitivity. Electro gas welding (EGW) and flux cored arc welding (FCAW) were adopted to prepare the welded joints. Temperature gradient ESSO test was performed to measure $K_{ca}$ values with the variation of welding variables. As a result of this study, regardless of plate thickness, welding heat input to cause welding residual stress around crack path is a key factor to control the brittle crack propagation in welded joints.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.92-92
• /
• 2009

조선업을 포함한 다양한 산업 분야에서 후판 강재의 수요량 증가와 함께 사용 범위 또한 폭넓게 되고 있다. 특히, 선박의 수송효율의 극대화를 위하여 컨테이너선의 대형화가 급속하게 진행되고 있으며, 2009년 현재1,300TEU 이상의 초대형 컨테이너선이 건조되고 이다. 이처럼 용접구조물의 초대형화에 따른 사용강재 또한 고강도 극후물화 되고 있다. 현재 선박에 적용중인 고강도 강재는 EH47 강재로 YP 460MPa 급의 강재가 Hatch Coamming부에 적용중에 있으며, 강재의 두께 또한 70mm 이상이다. 이러한 고강도 극후물재의 강구조물에 적용에 따른 선급협회에서는 용접부에서의 취성균열 전파에 의한 취성파괴의 위험성이 있으므로 강재의 두께를 제한하고 더욱 엄격한 파괴인성값을 요구하고 있다. 일본선급협회(NK)를 중심으로 취성균열의 정지를 위한 모재의 요구 성능등에 관한 연구들이 진행되고 있다. 이 연구의 대부분의 전제 조건은 선박의 블럭과 블럭의 조립시에 용접부가 직선형이 아닌 계단형(Butt shift)를 하는 것으로 하고 있으므로, 국내의 조선건조 공법의 현실과는 거리감이 있다. 본 연구에서는 국내 조선사에서 수행중인 직선 이음부에 대한 시공 공법에서 취성균열이 발생하여 진전 되더라도 균열을 정지 시킬 수 있는 기술에 관한 연구를 수행하였다. 균열의 진전은 대부부의 연속면에서는 정지를 시키지 못하고 직진 전파 하여서 파괴에 도달하게 된다. 따라서 뭔가의 불연속적인 면을 임의로 생성하여야 균열을 정지 시킬 수 있다. 본 연구에서는 이러한 균열의 정지 방법으로 형상적인 측면과 재료적인 측면에서 검토를 수행하였다. 형상적인 측면에서는 균열을 정지 시키고자 하는 위치에 불연속적인 면을 만들기 위하여 일정 크기의 hole을 만들어서 균열을 정지시켰으며, 재료적인 측면에서는 고인성의 용접재료를 사용하여서 취성균열이 진행하는 경로에 인성을 높은 재료를 적용하여 불연속적인 면의 생성과 함께 인성을 높여서 균열을 정지 시키는 기술을 개발하였다. 이러한 기술의 개발을 통하여 취성균열의 전파에 의한 파괴를 방지 할 수 있으며, 용접구조물의 안전성 확보를 가능하게 하였다.