• Journal of dental hygiene science
• /
• v.14 no.2
• /
• pp.140-149
• /
• 2014

The purpose of this study was to investigate the influence of etching surface treatment and aging treatment of zirconia on the shear bond strength between zirconia core and veneered ceramic. Four groups of zirconia-ceramic specimens were prepared; 1) NEZ group (no etching zirconia), 2) EZ group (etching zirconia), 3) ANEZ group (aging and no etching zirconia), 4) AEZ group (aging and etching zirconia). The shear bond strength between zirconia and porcelain was measured using Instron Universal Testing Machine. Surface texture with crystalline structure of zirconia surface was examined by the field emission scanning electron microscopy (FE-SEM) with ingredient analysis. The fractured surfaces of specimens were examined to determine the failure pattern by a digital microscope. The mean${\pm}$standard deviation of shear bond strengths were $23.47{\pm}3.47$ Mpa in NEZ, $28.30{\pm}4.34$ Mpa in EZ, $21.85{\pm}4.65$ Mpa in ANEZ, $24.65{\pm}3.65$ Mpa in AEZ group, respectively, and were significantly different (p<0.05). The average shear bond strength was largest in EZ group, followed by AEZ, NEZ, and ANEZ groups. Most specimens in NEZ group showed adhesive failure and most specimens in EZ, AEZ, and ANEZ group showed mixed failure. Surface of etching treatment group (EZ and AEZ) showed complex micro-structure and irregular surface texture which may facilitate mechanical interlocking, while untreated zirconia surface presented simpler micro-structure. In conclusion, an etching treatment improved bonding strength between zirconia and porcelain by forming mechanical interlocking.

• Journal of Information Display
• /
• v.11 no.1
• /
• pp.8-11
• /
• 2010

In this study, a new thin films passivation technique using Zn with high electronegativity and $MgF_2$, a fluorine material with better optical transmittance than the sealing film materials that have thus far been reported was proposed. Targets with various ratios of $MgF_2$ to Zn (5:5, 4:6 and 3:7) were fabricated to control the amount of Zn in the passivation films. The Mg-Zn-F films were deposited onto the substrates and Zn was located in the gap between the lattices of $MgF_2$ without chemical metathesis in the Mg-Zn-F films. The thickness and optical transmittance of the deposited passivation films were approximately 200 nm and 80%, respectively. It was confirmed via electron dispersive spectroscopy (EDS) analysis that the Zn content of the film that was sputtered using a 4:6 ratio target was 9.84 wt%. The Zn contents of the films made from the 5:5 and 3:7 ratio targets were 2.07 and 5.01 wt%, respectively. The water vapor transmission rate (WVTR) was determined to be $38^{\circ}C$, RH 90-100%. The WVTR of the Mg-Zn-F film that was deposited with a 4:6 ratio target nearly reached the limit of the equipment, $1\times10^{-3}\;gm^2{\cdot}day$. As the Zn portion increased, the packing density also increased, and it was found that the passivation films effectively prevented the permeation by either oxygen or water vapor. To measure the characteristics of gas barrier, the film was applied to the emitting device to evaluate their lifetime. The lifetime of the applied device with passivation was increased to 25 times that of the PLED device, which was non-passivated.

• Journal of Electrochemical Science and Technology
• /
• v.11 no.2
• /
• pp.172-179
• /
• 2020

The impact of effective parameters on the electrodeposition rate optimization of Au-Cu alloy at high thicknesses on the silver substrate was investigated in the present study. After ensuring the formation of gold alloy deposits with the desired and standard percentage of gold with the cartage of 18K and other standard karats that should be observed in the manufacturing of the gold and jewelry artifacts, comparing the rate of gold-copper deposition by direct and pulsed current was done. The rate of deposition with pulse current was significantly higher than direct current. In this process, the duty cycle parameter was effectively optimized by the "one factor at a time" method to achieve maximum deposition rate. Particular parameters in this work were direct and pulse current densities, bath temperature, concentration of gold and cyanide ions in electrolyte, pH, agitation and wetting agent additive. Scanning electron microscopy (SEM) and surface chemical analysis system (EDS) were used to study the effect of deposition on the cross-sections of the formed layers. The results revealed that the Au-Cu alloy layer formed with concentrations of 6gr·L^-1 Au, 55gr·L^-1 Cu, 24 gr·L^-1 KCN and 1 ml·L^-1 Lauryl dimethyl amine oxide (LDAO) in the 0.6 mA·cm^-2 average current density and 30% duty cycle, had 0.841 ㎛·min^-1 Which was the highest deposition rate. The use of electrodeposition of pure and alloy gold thick layers as a production method can reduce the use of gold metal in the production of hallow gold artifacts, create sophisticated and unique models, and diversify production by maintaining standard karats, hardness, thickness and mechanical strength. This will not only make the process economical, it will also provide significant added value to the gold artifacts. By pulsating of currents and increasing the duty cycle means reducing the pulse off-time, and if the pulse off-time becomes too short, the electric double layer would not have sufficient growth time, and its thickness decreases. These results show the effect of pulsed current on increasing the electrodeposition rate of Au-Cu alloy confirming the previous studies on the effect of pulsed current on increasing the deposition rate of Au-Cu alloy.

• Applied Chemistry for Engineering
• /
• v.28 no.2
• /
• pp.214-220
• /
• 2017

The spherical Al/RDX/AP composites with an average size of $550{\mu}m$ were successfully prepared by drowning-out/agglomeration (D/A) process. The surface morphology and dispersion of Al particles of those composites were investigated using SEM and EDS (energy dispersive spectrometry). As a result of thermal analysis, the onset temperature of thermal decomposition of the Al/RDX/AP composites by the D/A process was found to decrease about $50^{\circ}C$ and their thermal stability was shown to be relatively enhanced due to the increase of activation energy compared to those of using the physical mixing method. In the first decomposition region of AP, Prout-Tompkins model was shown to describe well the thermal decomposition of both composites by the physical mixing and D/A process. On the other hand, in the second decomposition region of AP, the decomposition mechanisms of composites by the physical mixing and D/A process were explained by the zero-order and contracting volume model, respectively.

• Korean Journal of Environmental Agriculture
• /
• v.28 no.1
• /
• pp.69-74
• /
• 2009

In Korea, large amounts of chestnut shell as by-products are produced from food industries. However, most of the by-products exist with no disposal options. Biosorption uses biomass that are either abundant or wastes from industrial operations to remove toxic metals from water. Objective of this research was to evaluate the feasibility of using chestnut shell as by-products for removal of metal ions(Pb, Cu and Cd) from aqueous solution. The chestnut shell was tested for its efficiency for metal removal by adopting batch-type adsorption experiments. The adsorption selectivity of chestnut shell for metals was Pb > Cu > Cd at solution pH 5.5. The Langmuir isotherm adequately described the adsorption of chestnut shell for each metal. Using The maximum adsorption capacity predicted using Langmuir equation was 31.25 mg $g^{-1}$ 7.87 mg $g^{-1}$ and 6.85 mg $g^{-1}$ for Pb, Cu and Cd, respectively. Surface morphology, functional group and existence of metals on chestnut shell surface was confirmed by FT-IR, SEM and EDX analysis. The chestnut shell showed an outstanding removal capability for Pb compared to various adsorbents reported in the literatures. The overall results suggested that chestnut shell might can be used for biosorption of Pb from industrial wastewater.

• Asian Journal of Atmospheric Environment
• /
• v.6 no.4
• /
• pp.288-303
• /
• 2012

In this study, real time measurements of particle number size distribution in urban Gwangju, coastal Taean, and industrial Yeosu in Korea were conducted in 2008 to understand the occurrence of ultrafine particle (UFP) (<100 nm) events, the variation of its concentration among different sampling sites, and UFP formation pathways. Also, to investigate seasonal and long-term variation of the UFP number concentration, data were collected for the period of 5 years (2007, 2008, 2010, 2011, and 2012) in urban Gwangju. Photochemical and combustion events were found to be responsible for the formation of UFP in the urban Gwangju site, whereas only photochemical event led to the formation of UFP in the coastal Taean site. The highest UFP concentration was found in industrial Yeosu (the average UFP number fractions were 79, 59 and 58% in Yeosu, Gwangju, and Taean, respectively), suggesting that high amount of gas pollutants (e.g., $NO_2$, $SO_2$, and volatile organic carbon (VOC)) emitted from industries and their photochemical reaction contributed for the elevated UFP concentration in the industrial Yeosu site. The UFP fraction also showed a seasonal variation with the peak value in spring (61.5, 54.5, 50.5, and 40.7% in spring, fall, summer, and winter, respectively) at urban Gwangju. Annual average UFP number concentrations in urban Gwangju were $5.53{\times}10^3\;cm^{-3}$, $4.68{\times}10^3\;cm^{-3}$, $5.32{\times}10^3\;cm^{-3}$, $3.99{\times}10^3\;cm^{-3}$, and $2.16{\times}10^3\;cm^{-3}$ in the year 2007, 2008, 2010, 2011, and 2012, respectively. Comparison of the annual average UFP number concentration with urban sites in other countries showed that the UFP concentrations of the Korean sites were lower than those in other urban cities, probably due to lower source strength in the current site. TEM/EDS analysis for the size-selected UFPs showed that the UFPs were classified into various types having different chemical species. Carbonaceous particles were observed in both combustion (soot and organics) and photochemical events (sulfate and organics). In the photochemical event, an internal mixture of organic species and ammonium sulfate/bisulfate was identified. Also, internal mixtures of aged Na-rich and organic species, aged Ca-rich particles, and doughnut shaped K-containing particles with elemental composition of a strong C with minor O, S, and K-likely to be originated from biomass burning nearby agricultural area, were observed. In addition, fly ash particles were also observed in the combustion event, not in the photochemical event.

• Korean Journal of Materials Research
• /
• v.9 no.7
• /
• pp.747-752
• /
• 1999

The interfacial reaction and joint properties of Sn-3.5Ag/Cu and Sn-3.5Ag-1Zn/Cu joint were studied. Modified double lap shear solder joints of Sn-3.5Ag and Sn-3.5Ag- lZn solder were aged for 60days at $100^{\circ}C$ and $150^{\circ}C$ and then loaded to failure in shear. The Sn-3.5Ag/Cu had a fast growth rate of the reaction layer in comparison with the Sn-3.5Ag-lZn at the aging temperature of $150^{\circ}C$ Through the SEM/EDS analysis of solder joint, it was proved that intermatallic layer was $Cu_{6}Sn_5$ phase and aged specimens showed that intermatallic layer grew in proportion to $t_{1/2}$, and the precipitate of $Ag_3Sn$ occur to both inner layer and interface of layer and solder. In case of Zn-containing composite solder, $Cu_{6}Sn_{5}$ phase formed at the side of substrate and $Cu_{5}Zn_{8}$ phase formed at the other side in double layer. The shear strength of the Sn-3.5Ag/Cu joint improved by addition of IZn. The strength of the joint increases with strain rate and decreases with aging temperature

• Journal of Powder Materials
• /
• v.24 no.6
• /
• pp.437-443
• /
• 2017

SiC-based composite materials with light weight, high durability, and high-temperature stability have been actively studied for use in aerospace and defense applications. Moreover, environmental barrier coating (EBC) technologies using oxide-based ceramic materials have been studied to prevent chemical deterioration at a high temperature of $1300^{\circ}C$ or higher. In this study, an ytterbium silicate material, which has recently been actively studied as an environmental barrier coating because of its high-temperature chemical stability, is fabricated on a sintered SiC substrate. $Yb_2O_3$ and $SiO_2$ are used as the raw starting materials to form ytterbium disilicate ($Yb_2Si_2O_7$). Suspension plasma spraying is applied as the coating method. The effect of the mixing method on the particle size and distribution, which affect the coating formation behavior, is investigated using a scanning electron microscope (SEM), an energy dispersive spectrometer (EDS), and X-ray diffraction (XRD) analysis. It is found that the originally designed compounds are not effectively formed because of the refinement and vaporization of the raw material particles, i.e., $SiO_2$, and the formation of a porous coating structure. By changing the coating parameters such as the deposition distance, it is found that a denser coating structure can be formed at a closer deposition distance.

• Economic and Environmental Geology
• /
• v.33 no.5
• /
• pp.391-404
• /
• 2000

This study investigated the geochemical characteristics of mine drainage discharged from an abandoned coal mine in the Hwasoon area. Surface water samples were collected from 23 locations along the Hancheon creek. The concentration of Zn and Cu in stream waters was highest at low pH (3.53), whereas the content of TDS and TDI was highest at high pH (7.78) due to the concentration of Ca, $HCO_3$ and $SO_4$. At the upstream site, the Ba, Fe, Mn, Zn, and $SO_4$ contents were relatively high but decreased significantly with the distance from the coal mine. On the contrary, the Na and $NO_3$ contents were low at the upstream site but increased downstream. Yellow precipitate material collected in the Hancheon consisted mainly of iron and LOI. This yellow precipitate was heated from 100 to $900^{\circ}C$ for 1 hour. With increasing temperature, the intensity of hematite peaks were sharply produced in X-ray pattern and the absorption band Fe-O of hematite increased in IR due to dehydration and melting. The yellow to brown precipitate and evaporite materials were collected by a air-dry from the acid mine water at the laboratory. After drying, the concentration of ions in the acid water samples increased progressively in oversaturation with respect to either gypsum, ferrohexahydrite or quenstedetite. The X-ray powder diffraction studies identified that the precipitated and evaporated materials after drying were well crystallized gypsum, ferrohexahydrite and quenstedetite. Diagnostic peaks used for identification of gypsum were the 7.65, 4.28, 3.03, 2.87 and 2.48$\AA$ peaks and those for ferrohexahydrite were the 5.46, 5.12, 4.89, 4.44, 4.05, 3.62, 3.46, 3.40, 3.20, 3.03, 2.94, 2.53, 2.28, 2.07, 1.88 and 1.86${\AA} peaks. The IR spectra with OH-stretching, deformation of $H_2O$and ${SO_4}^{2-}$stretching vibration include the existence of gypsum, ferrohexahydrite and quenstedetite in the precipitated and evaporite materials. In the SEM and EDS analysis for the evaporite material, gypsum with well-crystallized, acicular, and columnar form was distinctly observed.

• Journal of Veterinary Clinics
• /
• v.27 no.1
• /
• pp.93-96
• /
• 2010

We describe a case of enterolithiasis in an eight-year-old male Grant's zebra (Equus burchelli boehmi) that died after a 10-day history of depression, anorexia, dehydration and colic. On necropsy, an enterolith was discovered at the conjunction of the descending colon and the rectum. The spherical enterolith weighed 1,660 g and was $13.5cm{\times}8cm$ in size. According to scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS), the nidus consisted primarily of $SiO_2$ with outer layers of magnesium and phosphate. The formation of enteroliths is closely related to diet. We suggest that this captive zebra's diet, which consisted primarily of alfalfa hay with mineral supplements, was the cause of enterolithiasis in this case. This is the first report of enterolithiasis in a captive equid in Korea. Our findings provide information valuable for the development of dietary guidelines to prevent enterolithiasis in captive wild equids.