• Journal of Welding and Joining
• /
• v.13 no.3
• /
• pp.65-76
• /
• 1995

Weldability of DS100 and HY type high strength-toughness steel plates, tentatively produced as domestic production, was investigated. DS100 and DS130A had nearly same hardenability in HAZ in spite of its difference in Ceq. Based upon the y-groove test results, cold cracking susceptibility of DS130 was superior to that of DS100 because of its lower hydrogen level in weld metal. Solidification cracking tested by the Trans-Varestraint test was occured in all of the weld metals, and its susceptibility was high in the row of DS100, DS130A and DS130B. However, no liquation cracking and ductility-dip cracking tested by the Longi-Varestraint test with 6.0% augmented strain were detected in base metal and reheated weld metal. Toughness in the GMA welding joint was satisfied with the relative Mill Spec, even though welded joint of DS100 had relatively low impact energy especially at the weld metal.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.56-56
• /
• 2009

AISI 316L 스테인리스강에 새롭게 디자인한 서로 다른 3가지 응고모드를 가진 와이어로 FCAW(Flux Cored Arc Welding)을 하였다. 각각의 3가지 와이어는 Pseudobinary phase diagram에 따라 AF, FA, F모드를 가졌다. 미세조직은 $Cr_{eq}/Ni_{eq}$이 증가할수록 델타 페라이트 함량이 증가하였으며, 초정 상의 경우 초정 오스테나이트에서 초정 페라이트로 변태하였고, 연성저하균열의 민감도가 감소하였다. 연성저하균열은 이동결정립계의 형상에 따라 좌우되며, 미량의 페라이트를 함유한 오스테나이트에서는 페라이트가 핀(Pin) 역할을 제대로 하지 못하여 직선형태의 이동 결정립계 따라 입계 미끄러짐의 메커니즘을 통해 전파되었으며, 곡선형태의 이동 결정립계에서는 델타 페라이트가 핀 역할을 하여 역할을 하여 구속 상태에서 응력집중을 막고 응력을 분산시켜 균열이 전파되는 것을 방해하여 균열이 발생되지 않았다.

• Korean Journal of Metals and Materials
• /
• v.48 no.12
• /
• pp.1090-1096
• /
• 2010

This pitting corrosion study of welded joints of austenitic stainless steels (AISI 304L and 316L) has addressed the differentiating solidification mode using three newly introduced filler wires with a flux-cored arc welding process (FCAW). The delta ferrite (${\delta}$-ferrite) content in the welded metals increased with an increasing equivalent weight ratio of chromium/nickel ($Cr_{eq}/Ni_{eq}$). Ductility dip cracking (DDC) was observed in the welded metal containing ferrite with none of AISI 304L and 0.1% of AISI 316L. The potentiodynamic anodic polarization results revealed that the $Cr_{eq}/Ni_{eq}$ ratio in a 3.5% NaCl solution didn't much affect the pitting potential ($E_{pit}$). The AISI 316L welded metals with ${\ddot{a}}$-ferrite content of over 10% had a superior $E_{pit}$ value. Though the AISI 316L welded metal with 0.1% ferrite had larger molybdenum contents than AISI 304L specimens, it showed a similar $E_{pit}$ value because the concentration of chloride ions and the corrosion product induced severe damage near the DDC.