• 대한기계학회논문집A
• /
• 제29권3호
• /
• pp.462-469
• /
• 2005

Single phase bainite structure which is obtained by the conventional austempering treatment reduces the ductility of ductile cast iron. Because of the reduction of ductility it is possible to worsen the fatigue properties. Therefore, semi austempered ductile iron which is treated from ${\alpha}+{\gamma}$ is prepared to investigate the static strength and fatigue properties in comparison with fully austempered ductile iron (is treated from ${\gamma}$). In spite of semi austempered ductile iron shows the $86{\%}$ increase of ductility. Also, semi austempered ductile iron shows the higher fatigue limit and lower fatigue crack growth rate as compared with fully austempered ductile iron. By the fractographical analysis, it is revealed that the ferrite obtained by semi austempering process brings about the plastic deformation(ductile striation) of crack tip and gives the prior path of crack propagation. The relatively low crack growth rate in semi austempered specimen is caused by above fractographical reasons.

• 대한기계학회논문집A
• /
• 제23권11호
• /
• pp.1922-1928
• /
• 1999

Rotary bending fatigue tests were carried out to investigate the influence of artificial defects on fatigue limit in annealed and austempered ductile iron. Obtained main results are as follows : (1) Artificial defect(micro hole type, dia.<0.4 mm) on specimen surface did not bring about a obvious reduction of fatigue limit in austempered ductile iron(ADI) as compared with annealed ductile iron. (2) According to the investigation of $\sqrt{area}_c$ which is the critical defect size to crack initiation at artificial defect, $\sqrt{area}_c$ of ADI is larger than that of annealed ductile iron. This shows that the situation of crack initiation at artificial defect in ADI is more difficult in comparison with annealed ductile iron. (3) One of the reasons for the low rate of crack initiation from artificial defect in ADI is that the resistance of matrix to crack initiation is higher than that of annealed ductile iron. (4) In case that the $\sqrt{area}$ of artificial defect and graphite nodule is the same, the rate of crack initiation from graphite nodule is higher than that from artificial defect. This reason is that the serious ruggedness around graphite nodule is formed by austempering treatment.

• 한국자동차공학회논문집
• /
• 제7권5호
• /
• pp.221-229
• /
• 1999

We examined the governing factors of fatigue limit in annealed and austempered ductile iron specimens machined micro hole(dia.<0.4mm) in rotary bending fatigue test. Also, the quantitative relationship between fatigue limit and maximum defect size in specimens was investigated. Artificial defect(micro-pit type, dia.<0.4mm) on specimen surface did not bring about an obvious reduction of fatigue limit in austempered ductile iton(ADI) as compared with annealed ductile iron. According to the investigation of ${\sqrt{area}}_c$ which is the critical defect size to crack initiation at artificial defect, ${\sqrt{area}}_c$ of ADI was larger than that of annealed ductile iron. This shows that the situation of crack initiation at artificial defect in ADI is more difficult in comparison with annealed ductile iron. Maximum defect size is one of the important parameters to predict fatigue limit. And, the quantitative relationship, between the fatigue limit ${\sigma}_{\omega}$ and the maximum defect size ${\sqrt{area}}_{max}$ can be expressed to ${\sigma}_{\omega}^n{\cdot}{\sqrt{area}}_{max}=C_2$ where, $C_2$ are constant. Moreover, it is possible to explain the difference in fatigue limit between, austempered and annealed ductile iron by introducing the parameter ${\delta}(=N_{sg}/N_{total})$in a plain spectimen.

• 한국주조공학회지
• /
• 제6권2호
• /
• pp.93-103
• /
• 1986

It is very important to obtain wear resistant ductile iron by adding more economical alloying elements. In this study, 10 heat of Mg-treated ductile iron were made according to Sb content (0-0.1% Sb). Each melt was tasted to 30 ${\o}test$ bars in $CO_2$ mold under the same condition and inspected wear characteristics, mechanical properties and microstructures. The results obtained from this study are as follows; 1. It is confirmed that Sb should be a simple and useful additive for improving wear resistance in ductile iron. 2. Hardness of ferrite and pearlite is improved with increasing Sb amount in ductile iron. 3. For ductile iron, the recommended ladle addition of Sb amount is to 0.02-0.03%. 4. Sb has adverse influence on spheroidizing of graphite if the amount is over 0.04%.

• 열처리공학회지
• /
• 제12권3호
• /
• pp.215-220
• /
• 1999

Rotary bending fatigue tests were carried out to investigate the artificial defect sensitivity of fatigue limit in annealed and austempered ductile irons. Artificial defect(hole, diameter${\leq}0.4mm$) machined on specimen surface did not bring about an obvious reduction of fatigue limit in austempered ductile iron as compared with annealed. As a result of investigation on $\sqrt{area}$ c which is the critical artificial defect size. $\sqrt{area}$ c of austempered ductile iron is larger than that of annealed. This means that the crack initiation at artificial defect in austempered ductile iron is more difficult in comparison with annealed. In case that the $\sqrt{area}$ c of artificial defect and graphite nodule are same, the rate of crack initiation for graphite nodule is higher than that of artificial defect.

• Journal of Advanced Marine Engineering and Technology
• /
• 제23권3호
• /
• pp.284-291
• /
• 1999

Recently the ductile cast iron is being used successfully to the parts for processing machinery vessels and gear etc. This study is mainly concerned with the heat treatment for the specimens of crank shaft which are made of ductile cast iron. The results obtained are summarized as follows. Comparing the mechanical properties of the specimens for the normalized ductile cast irons the specimen heat treated at $550^{\circ}C$ was the best for crank shaft of air-compressor. After austenizing at $910^{\circ}C$ it was observed that the higher the reheating temperature is the less tensile strength and the hardness became which was supposedly attributed to the fact that the amount of pearlite. Austenite matrix was reduced by reheating after normalizing and that as the reheating tem-perature went up the pearlite generated was less and the distance between the pearlites were widened at last made pearlite globular. In the comparsison of crank shaft for air compressor made of ductile cast iron with that made by forged steel the crank shaft made of ductile cast iron was superior in economical terms. And ductile cast iron could be practically enough if only the elonga-tion which was inferior mechanical property to forged steel could be reinforced by increasing the diameter of crank pin when designing the crank shaft.

• 산업기술연구
• /
• 제24권A호
• /
• pp.3-8
• /
• 2004

This study was performed to investigate the effect of two step austenitized treatment on the mechanical properties and fracture characteristic of the ductile cast iron and austempered ductile cast iron(ADI). The obtained results of this study were as follows. The matrix structures of specimens were changed differently by austenitizing heat treatment. Microstructure of austempered ductile cast iron obtained by two step austenitized treatment was bainitic ferrite and retained austenite. With two step austenitized treatment, vield strength, tensile strength and hardness decreased, while the elongation increased.

• Journal of Mechanical Science and Technology
• /
• 제14권10호
• /
• pp.1021-1027
• /
• 2000

In this study, fatigue tests were performed to examine the effects of micro drill hole on fatigue limit of as cast and austempered ductile cast iron (ADI) using the rotary bending fatigue tester. As results, micro drill holes ($diameter{\leq}0.4mm$) did not influence the fatigue limit of ADI, compared to annealed ductile cast iron; the critical defect size of crack initiation, in ADI was larger than as cast. If the ${\sqrt{area}}$ of micro drill hole and graphite nodule in ADI are comparable, crack initiates at the graphite nodule. When the ruggedness developes through austempering treatment process, microstructure on crack initiation at micro drill hole is tougher than that of as cast ductile cast iron.

• 한국주조공학회지
• /
• 제14권1호
• /
• pp.75-81
• /
• 1994

It is very important to obtain high performance ductile iron by addition a small amount of alloying elements. In this study, to improve the characteristics of small piston ring casted from ductile iron melt a small amount of boron($0{\sim}0.008wt.%$) that is powerful carbide stabilizer was added in ductile iron, and inspected it`s effects on the microstructure, wear resistance, machinability and mechanical properties. The results obtained from this study are as follows. 1. As the amount of boron increased to 0.04wt.%, the machinability of ductile iron is increased, and if the amount is in excess of 0.04wt.% the machinability is decreased conversely. 2. The wear resistance of ductile iron is improved by boron addition. 3. The recommended ladle addition of boron amount ranges from 0.04wt.% to 0.06wt.% for the use of small piston ring.

• 한국주조공학회지
• /
• 제28권6호
• /
• pp.273-281
• /
• 2008

Effects of alloying elements on the mechanical properties of hardened and austempered 3.60wt%C - 2.50wt%C ductile cast iron were investigated. Strength and hardness were increased and ductility was decreased as the amount of alloying element increased. The increasing effect of copper addition on the strength was the most pronounced. The strength and hardness were greatly increased and ductility was decreased by hardening. The effect of alloying element on the mechanical properties of the hardened ductile cast iron was not so pronounced due to the high contents of C and Si. The strength and hardness of austempered ductile cast iron were greatly increased, meanwhile the difference of strength from that of hardened one was not so big. The ductility of the former was higher than that of the latter. The strength and ductility of austempered ductile cast iron with 0.25%Mn were the maximum of all Mn added ones. The maximum strength of that was obtained with the addition of 0.80wt%Cu or 2.00wt%Ni along with this amount of Mn added.