• Journal of Welding and Joining
• /
• v.19 no.5
• /
• pp.512-519
• /
• 2001

Sink roll has been used in molten Zn-0.2%Al alloy bath of continuous galvanizing line in sinking and stabilizing process of the steel strip in molten metal bath. In this process, although the scraper scraps off the sink roll surface, the dross compounds is builded up on the sink roll surface and the life time of the sink roll is shorten by the dross compounds. The present study was investigated the application of the spray coating layer on sink roll body for improving durability In molten Zn-0.2%Al alloy. Through the durability tests in molten Zn-0.2%Al alloy with various ceramic and cermet coating layer, the optimum bond and top coating material was obtained. As the results, the system of STS430F base metal, WC-l7Co bond and $ZrO_2-SiO_2$ top coating was clarified to be the best quality of durability in molten Zn-0.2%Al alloy.

• Journal of Welding and Joining
• /
• v.18 no.3
• /
• pp.51-59
• /
• 2000

Sink roll has been used in molten 55%Al-Zn alloy bath of continuous galvanizing line for sinking and stabilizing working steel strip in molten metal bath. In the process, the sink roll body inevitably build up dross compounds and pitting on the sink roll surface during 55%Al-Zn alloy coated strip production, and the life time of the sink roll is shorten by build up dross compounds and pitting. The present study examined the application of thermally sprayed ceramic coatings method on sink roll body for improving erosion resistance at molten 55% Al-Zn pool. In this experiment, the stainless steels such as STS 316L and STS 430F were used as the substrate materials. The CoNiCr and WE-Co powder were selected as bond coating materials. Moreover $Al_2O_3-ZrO_2-SiO_2 and ZrO_2-SiO_2$ powders selected as the top coating materials. Appearances of the specimens before and after dipping to molten 55%Al-Zn pool were compared and analyzed. As a result of this study, STS430F of substrate, WC-Co of bond spray coatings, $ZrO_2-SiO_2$ power of top spray coatings is the best quality in erosion resistance test at molten 55%Al-Zn pool

• Corrosion Science and Technology
• /
• v.9 no.5
• /
• pp.175-186
• /
• 2010

The auto industry is demanding more ductile high-strength steel grades to build lighter and stronger car bodies. The hot-dip galvanizing problems of these new steel grades are creating a demand for an improved method to control zinc wettability. The simplest way to improve zinc wettability on industrial hot-dip galvanizing lines is to increase the strip immersion temperature at zinc bath entry for enhancing the aluminothermic reaction. However, this practice increases the reactivity due to overheating the zinc in the snout which induces the formation of brittle Fe-Zn compounds at the strip/coating interface with the formation of higher amounts of dross in the zinc bath and snout contamination. Thus, this simple practice can only be utilized for short production periods of one to two hours without deteriorating coating quality. This problem has been solved by employing a technique that allows the use of a higher and attuned strip immersion temperature at zinc bath entry while still maintaining a constantly low zinc bath temperature. This has been proven to provide the solution for both the improved wettability and a significant reduction in the amounts of dross in the zinc bath.

• Korean Journal of Materials Research
• /
• v.22 no.9
• /
• pp.445-449
• /
• 2012

We investigate the effects of redox reaction on preparation of high purity ${\alpha}$-alumina from selectively ground aluminum dross. Preparation procedure of the ${\alpha}$-alumina from the aluminum dross has four steps: i) selective crushing and grinding, ii) leaching process, iii) redox reaction, and iv) precipitation reaction under controlled pH. Aluminum dross supplied from a smelter was ground to separate metallic aluminum. After the separation, the recovered particles were treated with hydrochloric acid(HCl) to leach aluminum as aluminum chloride solution. Then, the aluminum chloride solution was applied to a redox reaction with hydrogen peroxide($H_2O_2$). The pH value of the solution was controlled by addition of ammonia to obtain aluminum hydroxide and to remove other impurities. Then, the obtained aluminum hydroxide was dried at $60^{\circ}C$ and heat-treated at $1300^{\circ}C$ to form ${\alpha}$-alumina. Aluminum dross was found to contain a complex mixture of aluminum metal, aluminum oxide, aluminum nitride, and spinel compounds. Regardless of introduction of the redox reaction, both of the sintered products are composed mainly of ${\alpha}$-alumina. There were fewer impurities in the solution subject to the redox reaction than there were in the solution that was not subject to the redox reaction. The impurities were precipitated by pH control with ammonia solution, and then removed. We can obtain aluminum hydroxide with high purity through control of pH after the redox reaction. Thus, pH control brings a synthesis of ${\alpha}$-alumina with fewer impurities after the redox reaction. Consequently, high purity ${\alpha}$-alumina from aluminum dross can be fabricated through the process by redox reaction.

• Journal of Welding and Joining
• /
• v.16 no.3
• /
• pp.157-166
• /
• 1998

Recently as environmental pollution caused by Pb has posed a serious threat to the global environment, the trend to regulate the usage of Pb in electronic industry is one the rise. Currently, the solder alloy with high Pb content, Sn-37%Pb, is utilized in the electronic assembly therefore, the objective of this study is to develop an alternative solder alloy for the existing Sn-37%Pb solder alloy. First thing, this work choosed Sn-5%Pb-1.5%Ag, Sn-5%Pb-1.5%Ag-x%Bi(x=1~5%) for candidate solder alloys, and examined their properties such as melting range, wettability, microhardness, tensile property, oxidation behavior and microstructure. Wettability was on the same level of Sn-37%Pb. Dissolution of Pb ion in Sn-5%Pb solder was 0.46ppm. This solder alloy revealed cellular dendrite microstructure $\beta$-Sn matrix, Pb-rich phase, Ag/Sn, and Cu/Sn Intermetallic compounds. The range of solidification temperature was within 3$0^{\circ}C$. Also these alloy displayed higher tensile strength and lower elongation than Sn-37%Pb. The resistance of oxidation in Sn-5%Pb-1.5%Ag solder alloy was superior to that of Sn-37%Pb solder alloy. But that of Sn-5%Pb-1.5%Ag-5%Bi solder alloy was equal to that of Sn-37%Pb solder alloy.