• Journal of Welding and Joining
• /
• v.28 no.2
• /
• pp.47-53
• /
• 2010

According to the research report for the recent a few years, the dissimilar welding of Cu and STS 304 alloy have been presented that a weldability is very poor. This article present a study on Lap joint by Electron beam welding dissimilar materials. The weld metals was constituted between pure copper and STS 304 steel. The experiment was performed with 125mA welding current, 520mA focusing current. The Vacuum condition of chamber is 5${\times}$10-5torr and welding speed is 300mm/min. Showing the bead shape of weld metal, the thickness of the stainless 304 using as the protect materials is 3mm and the thickness of a copper is 15mm. The analysis about the microstructure were carried out in which it was observed with SEM. The results showed that complex heterogeneous fusion zone microstructure characterized both by rapid cooling and mixing of the molten metal, however the liquation crack was formated in the fusion line.

• Journal of Advanced Marine Engineering and Technology
• /
• v.35 no.1
• /
• pp.68-74
• /
• 2011

This papers investigated the mechanical characteristics and the weldability of identical as well as dissimilar welding by GTAW for STS 304 and STS 316L. It is applied to double wall gas pipe of duel fuel engine for LNG carrier. Consequently, the weldability of dissimilar and identical welded zone of STS 304 decreased compared to base metal significantly. The result of microstructure observation for welded zone, a degree of acicular ferrite in welding zone for STS 304 presented more than STS 316L. The hardness of welding zone for STS 304 presented higher value than that for STS 316L by this effect.

• Journal of Powder Materials
• /
• v.20 no.4
• /
• pp.302-307
• /
• 2013

A5J32-T4 and A5052-H32 dissimilar aluminum alloy plates with thickness of 1.6 and 1.5 mm were welded by friction stir lap welding (FSLW). The FSLW were studied using different probe length tool and various welding conditions which is rotation speed of 1000, 1500 rpm and welding speed of 100 to 600 mm/min and material arrangement, respectively. The effects of plunge depth of tool and welding conditions on tensile properties and weld nugget formation. The results showed that three type nugget shapes such as hooking, void, sound have been observed with revolutionary pitch. This plunge depth and material arrangement were found to effect on the void and hooking formation, which in turn significantly influenced the mechanical properties. The maximum joint efficiency of the FSLWed plates was about 90% compared to base metal, A5052-H32 when the A5052-H32 was positioned upper plate and plunge depth was positioned at near interface between upper and lower plates.

• Journal of the Korean Society of Industry Convergence
• /
• v.22 no.5
• /
• pp.491-497
• /
• 2019

Dissimilar friction welding were produced using 15 mm diameter solid bar in superalloy(Alloy718) to chrome molybdenum steel(SCM440) to investigate their mechanical properties. Consequently, optimal welding conditions were n=2000 rpm, HP=60 MPa, UP=120 MPa, HT=10 sec and UT=10 sec when the metal loss(Mo) is 3.5 mm. Acoustic Emission(AE) technique was applied to analyze the dissimilar friction welding of Alloy718 and SCM440. The relationship between the AE parameters and dissimilar friction welding of both material was discussed. In the case of heating time of 6 sec, 10 sec, 14 sec and 20 sec, 5 AE events per 0.5 seconds and energy about $2.7{\times}10^{10}$ were exhibited in heating time. In upsetting time, resulting in various numbers of events per second and very low energy. The frequency range of the signal generated during the heating time was about 200 kHz. However, the upsetting time resulted in a wide range of signals from very low frequency to high frequency of 500 kHz due to rapid plasticity of the material.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.85-87
• /
• 2008

DMWs are common feature of the PWR in the welded connections between carbon steel and stainless steel piping. The nickel-based weld metal, Alloy 82/182, is used for welding the dissimilar metals and is known to be susceptible to PWSCC. A round-robin program has been implemented to benchmark the numerical simulation of the transient temperature and weld residual stresses in the DMWs. To solve the round-robin problem related to Pressurizer Safety & Relief nozzle, the thermal elasto-plastic analysis is performed in the DMW by using the FEM. The welding includes both the DMW of the nozzle to safe-end and the SMW of the safe-end and piping. Major results of the analyses are discussed: The axial and circumferential residual stresses are found to be -88MPa(225MPa) and -38MPa(293MPa) on the inner surface of the DMW; where the values in parenthesis are the residual stresses after the DMW. Thermo-mechanical interaction by the SMW has a significant effect on the residual stress fields in the DMW.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.4
• /
• pp.239-245
• /
• 2000

A copper-tungsten sintered alloy(WCu) has been friction-welded to a tough pitch copper (Cu) in order to investigate friction weldability. The maximum tensile strength of the SWu-Cu friction welded joints had cp to 96% of those of the Cu base metal under the condition of friction time 0.6sec, friction pressure 45MPa, upset pressure 125MPa and upset time 5.0sec. And it is confirmed that the tensile strength of friction welded joints are influenced highly by upset pressure rather than friction time. And it is considered that mixed layer was formed in the Cu adjacent side to the weld interface, W particles included in mixed layer induced fracture in the Cu adjacent side to the weld interface and also, thickness of mixed layer was reduced as upset pressure increase.

• Coupled systems mechanics
• /
• v.7 no.5
• /
• pp.627-634
• /
• 2018

Laser beam welding is more advantageous compared to conventional methods. Titanium/Aluminium dissimilar alloy thin sheet metals are difficult to weld due to large difference in melting point. The performance of the weldment depends upon interlayer formation and distribution of intermetallics. During welding, aluminium gets lost at the temperature below the melting point of titanium. Therefore, it is needed to improve a new metal joining techniques between these two alloys. The present work is carried for welding TI6AL4V and AA2024 alloy by using Nd:YAG Pulsed laser welding unit. The performance of the butt welded interlayer structures are discussed in detail using hardness test and SEM. Test results reveal that interlayer fracture is caused near aluminium side due to low strength at the weld joint.

• Journal of Welding and Joining
• /
• v.17 no.4
• /
• pp.46-52
• /
• 1999

Some of the pressurized reactor pressure vessels used in many chemical plants are made of low alloy carbon steel plates internally clad with an austenitic stainless steel for improved anti-corrosion properties. In this study, metallurgic structure of the weld interface of A 387 Grade12Class1 low alloy carbon steel claded with A182-F321 austenitic stainless steel after thermal exposure simulation heat treatment was investigated to display a characteristic behavior of dissimilar metal weld interface with thermal exposure during service at high temperature and pressure. EPMA, STEM, vickers-hardness test were performed and the results were correlated with the microstructure. To estimate the depth of the carburized/decarburized bands quantitatively, a model for carbon diffusion was proposed. The validity of the proposed theoretical relationships was confirmed by the directly measured data from the welded parts failed during service.

• Journal of Ocean Engineering and Technology
• /
• v.13 no.2 s.32
• /
• pp.83-89
• /
• 1999

In this paper an experimental study on the development of the shielded metal are welding(SMAW) optimization technique for the dissimilar materials SS41 and STS304 of Auto-Lifting Magnet core plate was carried out. It was confirmed that the optimum welding heat input range was 37.5 to 45 kj/cm by considering on the strength and fatigue life of the welded joints more than 100% joint efficiency. And the quantitative relationship empirical wquation between the strength toughness adn fatigue life and the weld heat input was obtained.

• Journal of Ocean Engineering and Technology
• /
• v.26 no.1
• /
• pp.64-69
• /
• 2012

Dissimilar friction welds were produced using 15-mm diameter solid bars of chrome molybdenum steel (KS SCM440) and carbon steel (KS SM20C) to investigate their mechanical properties. The main friction welding parameters were selected to ensure good quality welds on the basis of visual examination, tensile tests, Vickers hardness surveys of the bond area and HAZ, and macro-structure investigations. The specimens were tested as-welded and post-weld heat treated (PWHT). The tensile strength of the friction welded steel bars was increased to 100% of the SM20C base metal under the condition of a heating time of more than four seconds. Optimal welding conditions were n = 2,000 (rpm), HP = 60 (MPa), UP = 100 (MPa), HT = 5 (s),and UT = 5 (s), when the total upset length was 7.8 (mm). The hardness distribution peak of the friction welded joints could be eliminated using PWHT. The two different kinds of materials were strongly mixed to show a well-combined structure of macro-particles, with no molten material, particle growth, or defects.