• 대한조선학회지
• /
• 제9권2호
• /
• pp.43-48
• /
• 1972

Inertia friction welding, a relatively recent innovation in the art of joining materials, is a forge-welding process that releases kinetic energy stored in the flywheel as frictional heat when two parts are rubbed together under the right conditions. In a comparatively short time, the process has become a reliable method for joining ferrous, and dissimilar metals. The process is based on thrusting one part, attached to a flywheel and rotating at a relatively high speed, against a stationary part. The contacting surfaces, heated to plastic temperatures, are forged together to produce a reliable, high-strength weld. Welds are made with little or no workpiece preparation and without filler metal or fluxes. However, In order to obtain a good weld, the determination of the optimum weld parameters is an important problem. Especially, because the amount of the flywheel mass will be determined according to the initial rotating velocity values at the constant thrust load, the initial rotating velocity is an important factor to affect a weld character of the inertia-welded IN713C-SAE8630, which is used for the wheel-shafts of turbine rotors or turbochargers, exhausting valves, etc. In this paper, the effects of initial rotational velocity on a weld character of inertia-welded IN713C-SAE8630 was studied through considerations of weld parameters determination, micro-structural observations and tensile tests. The results are as the following: 1) As initial rotating velocity was reduced to 267 FPM, cracks and carbide stringers were completely eliminated in the micro-structure of welded zone. 2) As initial rotating velocity was reduced and flywheel mass was increased correspondingly, the maximum welding temperatures were decreased and the plastic working in the weld zone was increased. 3) As initial rotating velocity was progressively decreased and carbides were decreased, the tensile strengths were increased. 4) And also the fracture location moved out of the weld zone and the tensile tests produced, the failures only in the cast superalloy IN713C which do not extend into the weld area. 5) The proper initial rotating velocity could be determined as about 250 thru 350 FPM for the better weld character.

• 수산해양기술연구
• /
• 제17권2호
• /
• pp.93-103
• /
• 1981

Si-Cr계 내열강 SUH3와 Cr-Ni계 stainless강 SUS 303 및 이들이 마찰용접재 SUH3-SUS303을 $1,060^{\circ}C$에서 용체화처리하고 다시 $700^{\circ}C$에서 10, 100시간 시효열처리한 각 시험편의 고온 피로강도에 대한 시효열처리의 효과를 알기 위하여 $700^{\circ}C$에서 고온 회전굽힘 피로시험을 하고 파약거동을 미시적으로 관찰하여 다음과 같은 결과를 얻었다. 1) SUH3재와 SUS303재의 최적마찰용접조건은 회전수 2420rpm, 마찰가압력 $8kg/mm^2$, 전 upset량 7mm(마찰가압시간 3sec, upset시간 2sec)이었다. 2) $700^{\circ}C$ 고온에서 장시간 이루어지는 고온피로시험에 있어, 용체화처리재의 S-N 곡선 경사부의 기울기가 가장 급하게 나타났다. 3) SUH3-SUS303 마찰용접재는 $1,060^{\circ}C$에서 1시간용체화 처리하고, $700^{\circ}C$에서 시효처리하는 경우 최적시효시간은 10시간이었다. 4) 10시간 시료재의 고온피로한도는 모재보다 SUH3은 75.4%, SUS303은 28.5% 높았으며, 용접재 SUH3-SUS303은 44.2% 정도 높았다. 100시간 시효재는 모재보다 SUH3은 64.91% SUS303은 30.4% 높았으며, SUH3-SUS303은 30.4% 높았으며, SUH3-SUS303은 36.6% 높았다. 5) 마찰용접재의 상온 및 고온의 피로파단은 모두 SUS303의 모재측에 발생하였으며, 용접면에서의 파단은 전혀 없었다. 6) SUS303재와 마찰용접재 SUH3-SUS303재의 크랙은 입내파양형이었으나 SUH3은 입계크랙의 전파로 파양한다.