• 대한금속재료학회지
• /
• 제48권5호
• /
• pp.401-409
• /
• 2010

This study was performed to develop an antibacterial film that can be dried at room temperature. A nanosized TiO$_2$ particle-dispersed solution was prepared by the hydrothermal treatment of peroxo-titanic acid at 160${^{\circ}C}$ for 4h. The binder was synthesized through the hydrolysis and condensation reactions of TEOS (10cc) and GPTS (3.5cc) in the mixture of H$_2$O (30cc) and EtOH (30cc). The synthesized binder was mixed with 0.1 M of TiO$_2$ solution in a volume ratio of binder/TiO$_2$ solution=0.25~0.5. The glass substrate was coated after using the dip coating method, which was then followed by drying for over 2h at room temperature. Although the TiO$_2$ particles did not chemically-bond to the binder, the coating layer strongly adhered to the substrate and displayed good antibacterial properties.

• 멤브레인
• /
• 제28권1호
• /
• pp.21-30
• /
• 2018

본 연구에서는 sol-gel법을 이용하여 균일하고 결함을 최소화한 세라믹 한외여과막을 제조하였다. 알루미나 중공사 정밀여과막 지지체의 기공 크기를 줄이기 위해, 합성된 boehmite sol과 sol-ethanol 혼합 용액을 사용하여 dip coating법으로 지지체 표면 위에 ${\gamma}$-알루미나 활성층을 형성시켰다. pristine sol을 이용하여 4회 이상 코팅했을 경우 박막층의 두께가 상당히 증가하여 균열 및 박리현상을 야기시키고, 3회 코팅을 진행하였을 경우 표면 결함이 최소화된 최적의 시료를 얻을 수 있었다. 또한, 소결 온도가 ${\gamma}$-알루미나 활성층의 기공 크기에 미치는 영향을 분석하였다. 소결 온도가 $1000^{\circ}C$일 때 가장 높은 순수 투과도 값을 보였으며, 10 nm 크기의 dextran 분획분자량(molecular weight cut-off (MWCO) : 51 kDa)이 관찰되었다. 600, $800^{\circ}C$에서 소결한 막의 경우, 12 kDa MWCO (dextran 5 nm)를 갖는 것으로 확인되었다. 결과적으로, 코팅 용액의 조성은 박막층의 두께에 큰 영향을 주었고, 소결 온도에 따라 분획분자량이 크게 영향을 받는 것을 알 수 있었다.

• 멤브레인
• /
• 제28권3호
• /
• pp.180-186
• /
• 2018

Polyvinylidene fluoride (PVDF)의 중공사막 표면에 2번 딥코팅하여 layer-by-layer 방식으로 나노복합막을 제조하였다. 1차 코팅에서 poly(vinylsulfonic acid)(PVSA)와 Poly(styrene sulfonic acid)(PSSA)의 농도, 이온세기(Ionic strength, IS) 등을 변화시키며 막을 제조하였으며, 2차 코팅 용액으로는 Poly(ethyleneimine) 10,000 ppm I.S = 0.3으로 고정하였다. 막의 특성평가를 위해 각각의 100 ppm NaCl, $CaSO_4$, $MgCl_2$, 그리고 25 ppm Methyl Orange (MO) 공급액에 대한 막의 투과도와 염배제율을 측정하였다. 코팅용액의 코팅 물질의 농도가 올라갈수록 염배제율이 상승하였으며, 본 실험 조건에서 PVSA보다는 PSSA를 이용하여 제조한 중공사막이 염배제율이 높은 것을 확인하였다. 대표적으로 PSSA 30,000 ppm I.S = 1.0에서 중 공사막을 제조하였을 때 25 ppm MO용액의 투과도 1.848 LMH, 염배제율 76.3%로 가장 높은 값을 나타내었다.

• 한국초전도ㆍ저온공학회논문지
• /
• 제7권3호
• /
• pp.9-12
• /
• 2005

[ $Y_1Ba_2Cu_3O_{7-8}$ ] (YBCO) coated conductor has been fabricated by batch-type process using oxide-precursor-based metal-organic deposition (MOD) method. The batch-type process can be scaled up more simply to Produce long-length YBCO conductor than the reel-to-reel process. Also, it has less handling problems and is adequate to the ambient gas environment. In this work, YBCO oride powder was used as a starting precursor for MOD method. After reel-to-reel dip coating process, me ter-long-buffered metal tape was wound around a cylinder and underwent calcination and annealing processes. Annealed YBCO films showed good c-axis alignment and dense surface morphology with no cracks, but exhibited very low critical current density of $10^5\;A/cm^2$.

• 전자공학회논문지T
• /
• 제36T권3호
• /
• pp.19-25
• /
• 1999

플라즈마 중합법과 dip-coating법에 의해 이층형 유기 감광체를 제조하였다. 알루미늄 기판위에 장벽 층으로 Al₂O₃막을 만들었고, 전하 생성층으로 H₂ phthalocyanine(H₂Pc)를, 전하 수송층으로는 Poly 9-Vinylcarbazole을 채택하여 CGL/CTL의 이층 구조가 되도록 하였다. 플라즈마 중합법과 진공 증착법에 의해 각각 H₂ phthalocyanine 박막을 제조하여 흡광 특성을 검토한 결과 진공 증착막의 경우 613.6[nm]와 694.8[㎚]에서 흡수 피크가 관찰되었으나 플라즈마 중합막에서는 600-700[㎚]사이에서 완만한 피크가 관찰되었다. PVCz막의 표면전위는 인가한 코로나 방전 전압과 PVCz의 두께가 증가함에 따라 증가하였고, 암 감 쇠 특성과 광 감쇠 시간 그리고 잔류 시간도 PVCz의 두께의 증가와 함께 증가하였다. 15[㎛] 두께의 PVCz의 표면 전하량을 계산한 결과, 인가 전위 -600[V]에서 134[nc/㎠]이었으며 H₂Pc의 전하 생성 효율은 0.034이었다.

• 한국산학기술학회논문지
• /
• 제19권6호
• /
• pp.98-103
• /
• 2018

산업의 발전에 따라 설비 및 재료 등 따라서 재료 표면의 특성을 내식성 및 고강도, 내마모성 등을 향상 시키기 위하여 지금까지 많은 코팅 기술들이 발전해 왔다. 그 중 CCO(CaCoO, 이후 CCO) 박막 형성은 전자재료 영역에서 연구, 사용이 되어오고 있는데, 이 CCO 박막의 특징 중 하나가 고온의 열에 강하다는 것이 있다. 특히 CCO 박막을 형성 시키는 방법 또한 비교적 간단하여 고온의 산화 분위기에 도입이 가능 할 것으로 판단되었다. 따라서 본 연구에서는 이 CCO 박막의 코팅이 용융 아연 도금 설비에 적용을 하기 전에, 고온 및 Zn fume에 대한 부식성을 파악하여 용융 아연 도금 설비에 적용이 가능한지를 파악하기 위한 실험 및 분석을 실시 하였다. 우선 기본 소재 STS304 표면에 CCO 박막을 형성 시키고, 650도의 대기로에서 Zn fume의 분위기 내에서 산화 시킨 후 CCO 박막의 부식 정도를 확인 및 측정 하였다. 산화는 30일간 진행되었고, 30일 후 SEM을 이용하여 CCO박막의 형상을 확인 하였으며 동전위분극 실험을 통하여 부식성을 분석하였다.

• 한국초전도ㆍ저온공학회논문지
• /
• 제16권1호
• /
• pp.14-18
• /
• 2014

The mechanical, electrical and thermal characteristics of insulating materials may significantly affect the performance and reliability of electrical devices using superconductors. General method to provide insulating layer between coated conductors is wrapping coated conductor with Kapton tape. But uniform and compact wrapping without failure or delamination in whole coverage for long length conductor is not a simple task and need careful control. Coating of insulating layer directly on coated conductor is desirable for providing compact insulating layer rather than wrapping insulating layers around conductor. Ceramic added polymer has been widely used as an insulating material for electric machine because of its good electrical insulating properties as well as excellent heat resistance and fairy good mechanical properties. The insulating layer of coated conductor should have high breakdown voltage and possesses suitable mechanical strength and maintain adhesiveness at the cryogenic temperature where it is used and withstand stress from thermal cycling. The insulating and mechanical properties of polymer can be improved by adding functional filler. In this study, insulating layer has been made by adding ceramic particles such as $SiO_2$ to a polymer resin. The size, amount and morphology of added ceramic powder was controlled and their effect on dielectric property of the final composite was measured and discussed for optimum composite fabrication.

• 한국세라믹학회지
• /
• 제45권10호
• /
• pp.579-583
• /
• 2008

A porous $Al_2O_3$, scaffold coated with tricalcium phosphate(TCP) was fabricated by replica method using polyurethane(PU) foam as a fugitive material. Successive coatings of $Al_2O_3$ and hydroxyapatite(HAp) were applied via dip coating onto polyurethane foam, which has a slender and well interconnected network. A porous structure was obtained after sequentially burning out the foam and then sintering at $1500^{\circ}C$. The HAp phase was changed to TCP phase at high temperature. The scaffold showed excellent interconnected porosity with pore sizes ranging from $300{\sim}700{\mu}m$ in diameter. The inherent well interconnected structural feature of PU foam remained intact in the fabricated porous scaffold, where the PU foam material was entirely replaced by $Al_2O_3$ and TCP through a consecutive layering process. Thickness of the $Al_2O_3$ base and the TCP coating was about $7{\sim}10{\mu}m$ each. The TCP coating was homogeneously dispersed on the surface of the $Al_2O_3$ scaffold.

• 폴리머
• /
• 제35권6호
• /
• pp.520-525
• /
• 2011

초다공성 하이드로젤은 다공성 공극구조를 이용하여 기존 수화젤의 팽윤성을 획기적으로 향상시킨 것으로, 빠른 팽윤거동과 높은 흡수율로 다양한 의약용 응용분야에 유용한 재료이다. 본 연구에서는 장용 코팅제인 Eudragit 계열 고분자들을 사용하여 poly(acrylic acid-co-acrylamide)계 초다공성 하이드로젤을 코팅함으로써 pH 의존성 팽윤거동을 보이는 초다공성 하이드로젤을 제조하고자 하였다. 서로 다른 pH 영역에서 작용하는 Eudragit L100과 S100을 이용하여 딥 코팅에 의해 표면을 코팅한 후 SEM을 이용해 공극구조를 관찰하고 pH에 따른 초다공성 하이드로젤의 팽윤거동을 관찰하였다. Eudragit 계열 고분자들로 코팅된 하이드로젤은 낮은 pH 환경하에서는 팽윤이 억제되다가, 특정 pH 이상에서 팽윤성이 향상되는 pH 의존성 팽윤거동을 보였고, 이러한 pH 의존성은 사용한 장용 코팅제용 고분자들의 pH 특성에 의존하였다.

• 한국초전도저온공학회:학술대회논문집
• /
• 한국초전도저온공학회 2002년도 학술대회 논문집
• /
• pp.149-152
• /
• 2002

SrZrO3 resistive oxide barriers on Ag sheathed Bi2223 tapes prepared by the sol-gel and dip coating method were evaluated with an aid of Taguchi method and orthogonal arrays to elucidate the effects of experimental parameters, such as ratio of starting solution, amount of additives, and heat treatment temperature and time on the properties of the thin films. Six experimental parameters were selected and then Ll8(21x37) orthogonal arrays were constructed. Finally, SEM and XRD results were related to signal to noise (S/N) ratio to evaluate the optimized experimental condition.