• 한국재료학회지
• /
• 제24권8호
• /
• pp.393-400
• /
• 2014

NiO catalysts were successfully coated onto FeCrAl metal alloy foam as a catalyst support via a dip-coating method. To demonstrate the optimum amount of NiO catalyst on the FeCrAl metal alloy foam, the molar concentration of the Ni precursor in a coating solution was controlled, with five different amounts of 0.4 M, 0.6 M, 0.8 M, 1.0 M, and 1.2 M for a dip-coating process. The structural, morphological, and chemical bonding properties of the NiO-catalyst-coated FeCrAl metal alloy foam samples were assessed by means of field-emission scanning electron microscopy(FESEM), scanning electron microscopy-energy dispersive spectroscopy(SEM-EDS), X-ray diffraction(XRD), and X-ray photoelectron spectroscopy(XPS). In particular, when the FeCrAl metal alloy foam samples were coated using a coating solution with a 0.8 M Ni precursor, well-dispersed NiO catalysts on the FeCrAl metal alloy foam compared to the other samples were confirmed. Also, the XPS results exhibited the chemical bonding states of the NiO phases and the FeCrAl metal alloy foam. The results showed that a dip-coating method is one of best ways to coat well-dispersed NiO catalysts onto FeCrAl metal alloy foam.

• Corrosion Science and Technology
• /
• 제23권2호
• /
• pp.113-120
• /
• 2024

An attempt was made to apply digital image correlation (DIC) strain analysis to in-situ scanning electron microscopy (SEM) observations of bending deformation to quantify local strain distribution inside a ZnMgAl-alloy coating in deformation. Interstitial-free steel sheets were hot-dipped in a Zn-3Mg-6Al (mass%) alloy melt at 400 ℃ for 2 s. The specimens were deformed using a miniature-sized 4-point bending test machine inside the SEM chamber. The observed in situ SEM images were used for DIC strain analysis. The hot-dip ZnMgAl-alloy coating exhibited a solidification microstructure composed of a three-phase eutectic of fine Al (fcc), Zn (hcp), and Zn2Mg phases surrounding the primary solidified Al phases. The relatively coarsened Zn₂Mg phases were locally observed inside the ZnMgAl-alloy coating. The DIC strain analysis revealed that the strain was localized in the primary solidified Al phases and fine eutectic microstructure around the Zn₂Mg phase. The results indicated high deformability of the multi-phase microstructure of the ZnMgAl-alloy coating.

• Corrosion Science and Technology
• /
• 제9권2호
• /
• pp.74-80
• /
• 2010

For the purpose of applying a hot-dip Zn-6mass%Al-3mass%Mg alloy coated steel sheet (ZAM) to automotive body materials, a laboratory study of the general properties required for inner and outer panels of automotive bodies was performed. Even with only light coating weight, ZAM showed an excellent corrosion resistance in terms of both cosmetic and perforation corrosion compared to the currently used materials for automotive bodies, GI70 and GA45. In our study, it was confirmed that ZAM exhibits as good as or better properties than GI70 in terms of spot weldability and press formability. Furthermore, since the same corrosion resistance can be achieved with less coating weight by applying ZAM, laser weldability is better than GI and GA.

• 한국수소및신에너지학회논문집
• /
• 제25권2호
• /
• pp.145-150
• /
• 2014

This study investigates the preparation of anti-reflective (AR) coating film to improve the efficiency of solar cell. The AR coating film was successfully obtained by dip-coating with AR coatings prepared by sol-gel method. Fluoroalkylsilane was additionally introduced into the coatings to give the self-cleaning effect of AR coating film. We performed the abrasion test, pencil scratch hardness test and cross-cut test to identify the mechanical strength of AR coating film. As the results, the transmittance of AR coating films with 9.07, 18.13 and 27.20 of IPA/MTMS molar ratios were 93.1, 93.6 and 95.3%, respectively. The water contact angle and transmittance of AR coating film increased by the introduction of hydrophobicity. The prepared AR coating film shows the high level of abrasion, hardness and adhesion. The IPA/MTMS molar ratio of 27.20 and the withdrawing speed range of 0.20 ~ 0.28cm/sec are the optimal coating condition in terms of the transmittance and mechanical strength of AR coating film.

• Corrosion Science and Technology
• /
• 제23권3호
• /
• pp.221-227
• /
• 2024

During hot stamping of hot-dip zinc-coated steel sheets such as hot-dip galvanized steel sheets and hot-dip galvannealed steel sheets, an oxide mainly composed of ZnO is formed on the sheet surface. However, excessive formation of ZnO can lead to a decrease in the amount of metal Zn in the coating layer, decreasing the corrosion resistance of hot-stamped members. Therefore, it is important to suppress excessive formation of ZnO. While the formation of Al oxides and Mn oxides along with ZnO layer during the hot stamping of hot-dip zinc-coated steel sheets can affect ZnO formation, crystal structures of such oxides have not been elucidated clearly. Thus, this study aimed to analyze structures of oxides formed during hot stamping of hot-dip galvannealed steel sheets using transmission electron microscopy. Results indicated the formation of an oxide layer comprising ZnAl₂O₄ at the interface between ZnO and the coating layer with Mn₃O₄ at the outermost of an oxide layer.

• 한국세라믹학회지
• /
• 제50권6호
• /
• pp.485-488
• /
• 2013

A SiC-$CeO_2$ composite membrane was successfully fabricated using an ally-hydridopolycarbosilane (AHPCS) binder and treated by dip-coating at 60 times with a $CeO_2$ sol solution. The dip-coated SiC membrane was calcined at 773 K and then sintered at 1173 K under an air atmosphere. The coated membrane was characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM) and a BET surface analysis. The difference in permeation performance between $H_2$ and CO gases was measured by varying the temperature. The permeation flux of $H_2$ on the SiC membrane with layered $CeO_2$ was obtained as $8.45{\times}10^{-6}\;mol/m^2sPa$ at room temperature. The CO permeation flux was $2.64{\times}10^{-6}\;mol/m^2sPa$ at room temperature. The reaction enthalpy (${\Delta}H^{\circ}$) for the hydrogen permeation process was calculated as -7.82 J/mol by Arrhenius plots.

• Composites Research
• /
• 제21권1호
• /
• pp.8-15
• /
• 2008

담지 방법을 통해 유리 기판 위에 단일벽탄소나노튜브 네트워크를 형성하였고, 코팅 공정변수(담지 횟수, 콜로이드 용액의 농도, 기판의 인출 속도)에 따른 탄소나노튜브 네트워크의 전기적 및 광학적 특성 변화를 관찰하였다. 그 결과 네트워크의 면저항 및 투과도는 코팅 공정변수들에 의해 민감하게 조절됨을 확인할 수 있었다. 탄소나노튜브 네트워크는 매우 균일한 면저항을 보이는 동시에, 가시광선 영역에서 우수한 투과도 특성을 보였다.

• 한국표면공학회지
• /
• 제28권5호
• /
• pp.300-308
• /
• 1995

The effect of nitrogen finishing for the control of coating weight in a nitrogen sealing box on the coating surface property in hot dip galvanizing process has been studied. The coated surface is free of oxide marks and edge overcoated. The coating uniformity is excellent ; the standard deviation of the coating thickness along width of the specimen was $1~1.2\mu\textrm{m}$ in the box whereas $2.5~3\mu\textrm{m}$ in the air. Considering surface quality of the coating such as oxide mark, edge overcoated and zinc dust, the oxygen content between 40 and 200 ppm was suggested in the box in addition the oxygen content of at least 40 ppm or the minimum dew point of $-27^{\circ}C$ is required to prevent a zinc vaporization.

• 한국표면공학회지
• /
• 제36권6호
• /
• pp.466-474
• /
• 2003

To develop a method of detecting dross in coating layer on hot-dip galvanizing steel, chemical etching behavior of the artificial coating layers with top and bottom dross were investigated. After chemical etching with the mixture of picric acid and sodium thiosulfate, each of the top and bottom dross take its distinct color, and alloy layer in coating is also observed. Defects in the coating layers of HGI(hot rolled galvanized iron), CGI(continuous galvanized steel sheet) and GA(galvannealed steel) were analysed, and methods of dross detection which can be applied to inspection process in manufacture were suggested.

• 한국수소및신에너지학회논문집
• /
• 제17권2호
• /
• pp.204-211
• /
• 2006

The electrolyte in the solid oxide fuel cell must be dense enough to avoid gas leakage and thin enough to reduce the ohmic resistance. In order to manufacture the thin and dense electrolyte layer, 8 mol% $Y_2O_3$ stabilized-$ZrO_2$ (8YSZ) electrolyte layers were coated on the porous tubular substrate by the novel vacuum slurry dip-coating process. The effects of the slurry concentration, presintering temperature, and vacuum pressure on the thickness and the gas permeability of the coated electrolyte layers have been examined in the vacuum slurry coating process. The vacuum-coated electrolyte layers showed very low gas permeabilities and had thin thicknesses. The single cell with the vacuum-coated electrolyte layer indicated a good performance of $495\;mW/cm^2$, 0.7 V at $700^{\circ}C$. The experimental results show that the vacuum dip-coating process is an effective method to fabricate dense thin film on the porous tubular substrate.