• Journal of the Korean institute of surface engineering
• /
• v.44 no.5
• /
• pp.207-212
• /
• 2011

In this study, the change in diffusion coefficient and wear characteristic with depth in the carbonitriding layer of SCM415 steel was discussed. To determine the diffusion coefficient, depth profile of carbon was measured from the surface using the Glow Discharge Spectrometer. In otherwise, measurements of carbide fraction, micro vickers hardness of surface and observation of microstructure have been implemented through the SEM image. $Fe_3$(C,N) layer and effective depth were increased as the time for carbonitriding takes longer. According to wear experiment, the results showed that wear resistance was improved by $Fe_3$(C,N) layer and effective depth.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.185-188
• /
• 2005

This study selected three different specified concrete strength types of mixture which were applied to domestic seawater concrete structure and measured compressive strength and chloride diffusion coefficient and composed the formula of prediction model of chloride diffusion coefficient in order to provide the useful data for concrete mix decision of seawater structures. As a result, the formula of prediction model of chloride diffusion coefficient which set W/C and compressive strength as parameters and performed multiplex regression analysis which was based on the mathematical theory was confirmed more reliable than the formula of prediction which was composed existing water-cement ratio function.

• Communications of the Korean Mathematical Society
• /
• v.12 no.2
• /
• pp.419-425
• /
• 1997

Consider a d-dimensional domain D that has finite Lebesque measure and a Dirichlet form which has discontinuous coefficient. Then the stationary Markov process corresponding to the given Dirichlet form is a semimartingale under suitable condition for D and the coefficient.

• Journal of the Korea Concrete Institute
• /
• v.24 no.4
• /
• pp.481-490
• /
• 2012

Evaluation of chloride penetration is very important, because induced chloride ion causes corrosion in embedded steel. Diffusion coefficient obtained from rapid chloride penetration test is currently used, however this method cannot provide a correct prediction of chloride content since it shows only ion migration velocity in electrical field. Apparent diffusion coefficient of chloride ion based on simple Fick's Law can provide a total chloride penetration magnitude to engineers. This study proposes an analysis technique to predict chloride penetration using apparent diffusion coefficient of chloride ion from neural network (NN) algorithm and time-dependent diffusion phenomena. For this work, thirty mix proportions with the related diffusion coefficients are studied. The components of mix proportions such as w/b ratio, unit content of cement, slag, fly ash, silica fume, and fine/coarse aggregate are selected as neurons, then learning for apparent diffusion coefficient is trained. Considering time-dependent diffusion coefficient based on Fick's Law, the technique for chloride penetration analysis is proposed. The applicability of the technique is verified through test results from short, long term submerged test, and field investigations. The proposed technique can be improved through NN learning-training based on the acquisition of various mix proportions and the related diffusion coefficients of chloride ion.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.2
• /
• pp.39-47
• /
• 1997

Creep rate the elevated temperature is known to be controller by the softening process of microstructure especially in the solid solution alloys such as 125 Cr rotor steel. The change of structure is a decreasing process of the free energy of the state including stress, diffusivity of the material, and tmeperature. This study shows that diffusion coefficient, D of 12% Cr rotor steel at 953K with 74.8 MPa is 1.084~3.140*$10^{15}mm^2sec^1$ compared to $1.658*10^{24}mm^2sec^1$at 963K without stress. During creep, the growth of martensite laths accelerates the diffusion coefficient under stress due to incoherency of interface between carbides and matrix.

• Proceedings of the Korean Society of Soil and Groundwater Environment Conference
• /
• 1997.05a
• /
• pp.79-82
• /
• 1997

토양내에서 오염유기물질이 불포화토양내에 유입될 때의 dispersion coefficient를 adsorption과 desorption과정에 대해 알아보았다. apparent dispersion coefficient를 측정하기 위해 일상적인 상대습도(46%)조건에서 parametric analysis를 행하였다. 실험에 사용된 토양은 fine sand와 silt-clay혼합시료였고, 흐름방향은 상향과 하향으로 하였다. 그리고, Freon gas를adsorbing solute로 사용하였다. 오염물질로는 DCM, TCE, DCB를 사용하였다. 분석을 위해서 linear와 probability scale의 breakthrough curve를 사용하였다. 공기에서의 diffusion coefficient의 예측을 위하여 Graham's law를 계산에 사용하였고, DCM diffusion coefficient는 0.098$\textrm{cm}^2$/s로 계산되었다. 연구결과, adsorption과 desorption의 속도는 차이가 있는 것으로 나타났으며, diffusion이 flow regime을 좌우하는 것으로 나타났다. 그리고, desorption에서의 D$^{a}$ D$^{o}$ 는 1보다 클수도 있다. 또한, dispersion은 silt-clay혼합시료에서의 속도와 함께 증가한다. dispersion은 Freon의 sorption방향에 크게 의존한다.

• Journal of the Korean Applied Science and Technology
• /
• v.24 no.1
• /
• pp.79-85
• /
• 2007

The diffusion behavior of phenol, toluene and benzoic acid in aqueous SDS solution was examined. It showed a similar experimental results for phenol and toluene. The diffusion coefficients of the solutes were characterized by the presence of two distinct regions: below the cmc and above the cmc. For phenol and toluene, it remained approximately unchanged when the SDS concentration was below the cmc. Above the cmc there was an apparent decrease in the diffusion coefficients of the two solutes with increasing SDS concentration. However, for benzoic acid the diffusion behavior was different from that of phenol and toluene. The diffusion coefficient of benzoic acid decreased slightly with increasing SDS concentration, however the diffusion coefficient was almost constant above the cmc. For benzoic acid the diffusion behavior was dependent on the joint contribution of benzoic acid molecules as well as the benzoate ions.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.14 no.2
• /
• pp.58-62
• /
• 2004

The shape evolution of the interface void of copper metallization for intergrated circuits under electromigration stress is modeled. A 2-dimensional finite-difference numerical method is employed for computing time evolution of the void shape driven by surface diffusion, and the electrostatic problem is solved by boundary element method. When the diffusion coefficient is isotropic, the numerical results agree well with the known case of wedge-shape void evolution. The numerical results for the anisotropic diffusion coefficient show that the initially circular void evolves to become a fatal slitlike shape when the electron wind force is large, while the shape becomes non-fatal and circular as the electron wind force decreases. The results indicate that the open circuit failure caused by slit-like void shape is far less probable to be observed for copper metallization under a normal electromigration stress condition.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.221-226
• /
• 2001

Chloride diffusion effect of cement paste, freezing and thawing test, carbonation of concrete specimen were carried out using inorganic coating material. According to the chloride ions diffusion test, it is elucidated that permeability and diffusion coefficient of Cl￣ ions and apparent coefficient of coated cement paste is smaller than plain cement paste. A durability of coated concrete specimen was enhanced by the experiment result of concrete carbonation and freezing thawing test.

• Journal of the Korea Institute of Building Construction
• /
• v.19 no.5
• /
• pp.421-429
• /
• 2019

The changes in the resistance to chloride ingress of concrete using a ground granulated blast furnace slag (GGBFS) according to curing conditions were examined. The curing conditions were divided in air-dry curing and under-water curing. Three concrete mixures with the GGBFS replacement ratio of 0%(control), 30%, and 60% were prepared. For tests, evaluations of concrete compressive strength, and chloride ion diffusion coefficient were performed. As the GGBFS replacement ratio increased, the concrete compressive strength of the in air-dry cured specimens decreased compared to under-water cured specimens. When the chloride ion diffusion coefficient was measured, the chloride ion diffusion coefficient decreased as the GGBFS replacement ratio increased. However, the diffusion coefficient of the in air-dry cured specimen was increased up to 111% compared with the under-water cured specimen.