High dielectric (Ba,Sr)TiO$_3$ thin films were etched in an inductively coupled plasma (ICP) as a function of C1$_2$/Ar gas mixing ratio. Under Cl$_2$(20)/Ar(80), the maximum etch rate of the BST films was 400$\AA$/min and selectivities of BST to Pt and PR were obtained 0.4 and 0.2, respectively. We investigated the etched surface of BST by x-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and x-ray diffraction (XRD). From the result of XPS analysis, we found that residues of Ba-Cl and Ti-Cl bonds remained on the surface of the etched BST for high boiling point. The surface roughness decreased as Cl$_2$ increases in Cl$_2$/Ar plasma because of non-volatile etching products. This changed the nature of the crystallinity of BST. From the result of XRD analysis, the crystalliility of etched BST film maintained as similar to as-deposited BST under Ar only and Cl$_2$(20)/Ar(80). However, (100) orientation intensity of etched BST film abruptly decreased at Cl$_2$ only plasma. It was caused that Cl compounds were redeposited on the etched BST surface and damaged to crystallinity of BST film during the etch process.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.79-79
• /
• 2008

We report the growth of $Ba_{0.5}Sr_{0.5}TiO_3$(BST) thin films and their substrate-dependent electrical characteristics. BST thin films were deposited on alumina(non-single crystal), $Al_2O_3$(100) substrates by Nd:YAG Pulsed Laser Deposition(PLD) with a 355nm wavelength at substrate temperature of $700^{\circ}C$ and post-deposition annealing at $750^{\circ}C$ in flowing $O_2$ atmosphere for 1hours. BST materials had been chosen due to high dielectric permittivity and tunability for high frequency applications, To analyze the oxygen partial pressure effects, deposited films at 1, 10, 50, 100, 150, 200, 300 mTorr. The effects of oxygen pressure on structural properties of the deposited films have been investigated by X-ray diffraction(XRD) and atomic force microscope(AFM), respectively. Then we manufactured a inter-digital capacitor(IDC) patterns twenty fingers and $10{\mu}m$ gap, $700{\mu}m$ length and electrical properties were characterized. The results provide a basis for understanding the growth mechanisms and basic structural and electrical properties of BST thin films as required for tunable microwave devices applications such as varactors and tunable filters.