• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.04a
• /
• pp.333-338
• /
• 2000

At present, reinforced concrete pipe has been widely used as drain pipe. However, many reinforced concrete pipe is exposed at deteriorated environment by the growth of a sulfur-oxidizing bacterium isolated from corroded concrete. The purpose of this study is to evaluate the effects of lining by polymer-modified mortar on the development in durability of reinforced concrete pipe. Polymer-modified mortars ate prepared with various polymer typer as cement modifier and polymer-cement ratio and rested for compressive and flexural strengths, adhesion in tension, acid resistance test, freezing and thawing test, and lining test of product in the field. From the rest results, it is apparent that polymer-modified mortars have good mechanical properties and durability as lining material. In practice, all polymers can be used as lining materials for reinforced concrete pip, and type of polymer, and polymer-cement ratio and curing conditions are controlled for good lining product.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.11a
• /
• pp.589-592
• /
• 2006

The durability of concrete involves resistance to freeze-thaw action, corrosion, permeation, carbonation, chemical attack and so on. Generally, properties of concrete have been well understood under the separate action of these deterioration mechanisms. However, in practice, the degradation of concrete usually is the result of combined action of physical and chemical attack and can be accelerated by the combined action of several deterioration mechanisms. In the present study, to evaluate the combined deterioration by freeze-thaw action and seawater attack, ground granulated blast-furnace slag or silica fume concrete with water or seawater as mixing water was exposed to 300 cycles of freeze-thaw action. Tests were conducted to determined the relative dynamic modulus of elasticity and compressive strength. Furthermore, The MIP analysis were performed on the deteriorated part of concrete due to freeze-thaw action and seawater attack.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.497-502
• /
• 2001

We examined the silicate-based material to develop the surface-treatment agent, which would be used to restore performance of the deteriorated concrete and to inhibit corrosion of the reinforcing bar. As a part of the study, we carried out experiments of the penetration and strengthening properties of concrete treated by the considering agent. The variables of experiment, were the type of silicates, the ratio of distilled water-silicate, the usage of surface-strengthening material, and the usage of biochemical material. The penetrating ability of concrete is assessed by viscosity and surface tension. Also assessments of strengthening effects of concrete are performed on compressive strength, absorption, and water permeability tests.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.499-502
• /
• 2005

Recently sewage facilities mainly consisted of concrete structures are being deteriorated seriously by biodeterioration originated from sulfur-oxidizing bacteria. In this study, to prevent biochemical corrosion of the sewer concrete, antibiotics which prevent growth of sulfur-oxidizing bacteria were developed and antimicrobial performance of it was investigated. After that, to consider applicability of antibiotics to concrete, physical properties such as bond strength, resistance to abraision, water absorption and air permeability of concrete covered with inorganic and complex antibiotics were investigated.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.69-72
• /
• 2006

Recently sewage facilities mainly consisted of concrete structures are being deteriorated seriously by biodeterioration originated from sulfur-oxidizing bacteria. To prevent biochemical corrosion of the sewage concrete, antibiotics which prevent growth of sulfur-oxidizing bacteria were developed. Existing methods to evaluate properties of biochemical corrosion of concrete examine the antimicrobial performance and resistance to sulfuric acid separately, but don't complexly. So, in this study, new method to test properties of biochemical corrosion of concrete complexly is suggested.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.253-254
• /
• 2009

This study was conducted to estimate deterioration reason of jointed concrete pavement. Image analysis tests were performed according to ASTM C 457 using concrete core specimens. Durability factors were estimated according to spacing factor, which is related with air content and air-void information. Test results show that spacing factors of most specimens were estimated above 250$\mu$m so that investigated concrete pavement has the problem of freeze and thawing resistance.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.217-218
• /
• 2010

This study presented the analytical evaluation model effective in the concrete structure repaired with a patching material. The model considered the effect of the repair material on carbon dioxide penetration into the repaired concrete as evaluating the remaining service life of the CO2-deteriorated concrete structure after repair. The diffusion profiles of carbon dioxide as well as the carbonated concrete were effectively able to be modelled with analytical method based on Fick's 1st diffusion law.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1996.10a
• /
• pp.196-200
• /
• 1996

In the case of construction under the marine environment the durability of concrete structures is everely deteriorated by the penetration of salts which results in the corrosion of reinforcing steel. To verify the effect of corrosion protection of reinforcing steel by isolating the penetration of chlorideion this study investigated the bond strength between painting material and concrete, the degree of the penetration-diffusion of chloride ion and the accelerated corrosion test using different potential. Results show that the painted concrete has little the penetration-diffusion of cholride and the reinforcing steel in painted concrete is little corroding.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.04a
• /
• pp.229-234
• /
• 1997

Recently many concrete structures have been deteriorated due to the corrosion of reinforcing steel caused by chloride attack. The chloride attack causes very rapid and serious deterioration. Therefore, It is necessary for highly reliable method to stop the corrosion. Especially, on damaged concrete, it is difficult to stop the progress of steel corrosion that has already occured in concrete. The indirect method of corrosion protection such as eliminating corrosion factors by coating would be hard to be expected for complete stop of corrosion. In this paper, we applied the cathodic protection to chloride attacked marine concrete structures and verified the effect in addition to application of cathodic protection.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05a
• /
• pp.519-522
• /
• 2005

Ka-Hwa highway bridge, located in a corrosive marine environment, had been examined the current condition of reinforcement corrosion in concrete throughout half-cell potentials, electrical resistivity, chloride contamination of concrete, and visual observation. According to the test, the chloride corrosion reinforced concrete structure is not only the protecting film around the reinforcement is deteriorated but also corrosion activity develops, for example, delamination areas of concrete. The purpose of this paper is to report the effects of Ka-Hwa highway bridge damaged by chlodide attack and to present the results of repair of Ka-Hwa highway concrete bridge in domestic marine environment.