• Restorative Dentistry and Endodontics
• /
• v.16 no.2
• /
• pp.126-142
• /
• 1991

The purpose of this study was to evaluate the effect of various dentin surface treatments on shear bond strength, microhardness and fracture mode before and after thermocycling. Recently extracted 75 human molars were used. The teeth were sagittal sectioned faciolingually to obtain 150 specimens. They were randomly divided into six groups. Mesial and distal dentinal surfaces of specimens were exposed by grinding and treated respectively with GC-DENTIN CONDITIONER. 10-3 solution of 4-Meta, Cleansar and Primer of GLUMA, Scotchprep of Scotchbond 2, DENTIN CONDITIONER and PRIMER A, B of ALL BOND according to the manufacturers directions. Specimens of one group were not treated. Adhesive agent of Scotchbond 2, were applied and cured on the treated dentin surfaces. After P-50 were cured on them, specimens were stored in 31c water for 24 hours before shear bond strength measurement Shear bond strength was measured in 10 specimens of each group. 10 specimens of each group were thermocycled in $20^{\circ}C$, $60^{\circ}C$,$20^{\circ}C$, $4^{\circ}C$, $20^{\circ}C$ water in order, for 30 seconds respectively, 100 times a day for 7 days. After thermocycling shear bond strength was measured. Microhardness was checked on treated dentin surface and fractured dentin surface in 10 specimens respectievly. Francture modes were observed with SEM The following results were obtained. 1. Before thermocycling. shear bond strengths in the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND were significantly higher than those in other specimens(P<0.01). 2. After thermocycling. shear bond strengths in the specimens treated with Cleanser and Primer of GLUMA, Scotchprep of Scotchbond 2 and DENTIN CONDITIONER and PRIMER A, B of AIL BOND were significantly higher than those in specimens not: treated, treated with GC-DENTIN CONDITIONER and 10-3 solution of 4-Meta(P<0.01). Shear bond strengths in the specimens treated with GC-DENTIN CONDITIONER and PRIMER A, B of ALL BOND were significantly higher than those in other specimens except those treated with Scotchprep of Srotchbond 2(P<0.01). 3. Shear bond strengths after thermocycling were reduced in the specimens not treated, treated with GC-DENTIN CONDITIONER and 10-3 solution of 4-Meta and were increased in the specimens treated with Cleanser and Primer of GLUMA, Scotchprep of Scotchbond 2, without significance, compared with those before thermocycling. In the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND, shear bond strengths after thermocycling were significantly increased, compared with those before thermocycling(P<0.01). 4. Microhardnesses in the fractured surfaces after shear bond strength measurement were significantly increased in the specimens treated with 10-3 solution of 4-Meta and significantly decreased in the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND, compared with those in the treated dentin surfaces(P<0.01). 5. In the specimens treated with Cleanser and Primer of GLUMA, Scotchprep of Scotchbond 2 and DENTIN CONDITIONER and PRIMER A, B of ALL BOND, cohesive fracture modes were observed more than adhesive fracture modes.

• Restorative Dentistry and Endodontics
• /
• v.22 no.1
• /
• pp.470-478
• /
• 1997

The purpose of this study was to investigate the effects of moistening mechods of dentin on the morphologic states of hybrid layers and on the interfacial bond strength between dentin and composite. Specimens were divided into 6 groups based on the surface moistening methods and materials used. After the dentin surface was conditioned with 10 % phoporic acid and irrigated: 1. The dentin surface was dried. Then bonding agent and composite were applied. 2. The dentin surface was blot-dryed. Then primer, bonding atent and composite were applied. 3. The dentin surface was dryed first. Within 20 seconds, the surface was rewetted, then primer, bonding agent and composite were applied. 4. The dentin surface was dryed. Then primer, bonding agnent and composite were applied. 5. The dentin surface was dryed first. Atter 24hrs, the surface was rewetted, and then primer, bonding agent and composite were applied. 6. The surface was conditioned with NaOCl for 5min. Then primer, bonding agent and composite were applied. To reveal the hybrid layer, scanning electron microscopy was used after the samples were ion beam etched. The shear bond strength of each group was tom pared by ANOVA. In groups 2, 3 and 4, the hybrid layer was clearly visible, but the width was more limited in group 4. In group 1 and 5, the hybrid layer was not found, and a gap was formed between dentin and composite. In group 6, the hybrid layer was not found, but the interface between the dentin and composite was intimate. The shear bond strength of each group was as follows: Group 1 : 4MPa, Group 2 : 14MPa, Group 3 : 12MPa, Group 4 : 14MPa, Group 5 : 5MPa, Group 6 : 9MPa.

• Proceedings of the KACD Conference
• /
• 2003.11a
• /
• pp.625-625
• /
• 2003

I. Objectives Self-etching primer adhesive system is affected to dentin surface conditioning and priming. Especially application time of self-etching primer is very important factor of clinical procedure which has direct influence on smear layer, etching reaction and primer penetration to dentin. This study evaluated the influence of application time of self-etching primers on microtensile bond strength (${\mu}{\;}TBS$) to dentin using three self-etching primer adhesive systems.(omitted)

• The Journal of Advanced Prosthodontics
• /
• v.10 no.3
• /
• pp.177-183
• /
• 2018

PURPOSE. The purpose of the current study was to evaluate the effect of incorporating nanoparticles of silver (NAg) and amorphous calcium phosphate (NACP) into a self-etching primer of a resin cement on the microtensile bond strength of dentin, regarding the proven antibacterial feature of NAg and remineralizing effect of NACP. MATERIALS AND METHODS. Flat, mid-coronal dentin from 20 intact extracted human third molars were prepared for cementation using Panavia F2.0 cement. The teeth were randomly divided into the four test groups (n=5) according to the experimental cement primer composition: cement primer without change (control group), primer with 1% (wt) of NACP, primer with 1% (wt) of physical mixture of NACP+Nag, and primer with 1% (wt) of chemical mixture of NACP+Nag. The resin cement was used according to the manufacturer's instructions. After storage in distilled water at $37^{\circ}C$ for 24 h, the bonded samples were sectioned longitudinally to produce $1.0{\times}1.0mm$ beams for micro-tensile bond strength testing in a universal testing machine. Failure modes at the dentin-resin interface were observed using a stereomicroscope. The data were analyzed by one-way ANOVA and Tukey's post-hoc tests and the level of significance was set at 0.05. RESULTS. The lowest mean microtensile bond strength was obtained for the NACP group. Tukey's test showed that the bond strength of the control group was significantly higher than those of the other experimental groups, except for group 4 (chemical mixture of NACP and NAg; P=.67). CONCLUSION. Novel chemical incorporation of NAg-NACP into the self-etching primer of resin cement does not compromise the dentin bond strength.

• Restorative Dentistry and Endodontics
• /
• v.16 no.1
• /
• pp.200-208
• /
• 1991

The purpose of this study was to observe shear bond strength of composite resin to dentin following surface treatment. Freshly extracted forty-eight sound human molars were used in this study. They were stored at $4^{\circ}C$ physiologic saline solution before experiment. The teeth was then mounted with self curing acrylic resin in brass mold. The buccal surfaces of the teeth were grinding approximately 1.5mm by means of water-irrigated grinding wheel to expose the flattened fresh dentin surfaces. The specimens were divided into 6 groups according to preparation and treatment procedures on dentin surfaces; Group 1: Untreated after preparation with No.301 diamond point Group 2: Treated with primer for 60 seconds after preparation with No.301 diamond point Group 3: Untreated after preparation with No.700 fissure carbide bur Group 4: Treated with primer for 60 seconds after preparation with No.700 fissure carbide bur Group 5: Untreated after grinding with 600 grit silicon carbide paper Group 6: Treated with primer for 60 seconds after grinding with 600 grit silicon carbide paper Light cure dental adhesive was applicated to each specimen. Silux plus(3M) was inserted then into polyethylene tube of 3mm diameter and 3mm height, and polymerized to dentin surface. All of the specimens were stored in distilled water at $35.6^{\circ}C$ for 24 hours prior to testing. The shear bond strength was measured using an Instron Universal Testing Machine. The results obtained from this study were as follows: 1. The shear bond strength to dentin was the highest in group II. 2. The shear bond strength to dentin was the lowest in group III. 3. There was no significant difference in shear bond strength to dentin according to preparation instrument. 4. The primer treatment group showed significantly greater shear bond strength than untreated group.

• Restorative Dentistry and Endodontics
• /
• v.27 no.3
• /
• pp.257-269
• /
• 2002

Objective : The purpose of this study was to evaluate the resin infiltration into dentin of one-bottle adhesive systems and self-etching primer bonded to Class V cavities using confocal laser scanning microscope(CLSM). Material and Methods : Forty Class V cavities were prepared from freshly extracted caries-free Human teeth. These teeth were divided into two groups based on the presence of cervical abrasion: Group I, cervical abrasion : Group II, wedge-shaped cavity preparation. Resin-dentin interfaces were produced with two one-bottle dentin bonding systems-ONE COAT BOND(OCB; Coltene$^R$) and Syntac$^R$SPrint$^{TM}$(SS; VIVADENT)-, one self-etching priming system-CLEARFIL$^{TM}$ SE BOND (SB : KURARAY)- and one multi-step dentin bonding system-Scotchbond$^{TM}$Multi-Purpose (SBMP, 3M Dental Products)-as control according to manufacturers' instructions. Cavities were restored with Spectrum$^{R}$(Dentsply). Specimens were immersed in saline for 24 hours and sectioned longitudinally with a low-speed diamond disc. The resin-dentin interfaces were microscopically observed using CLSM. The quality of resin-infiltrated dentin layers were evaluated by five dentists using 0~4 scale. Results : Confocal laser scanning microscopal investigations using primer labeled with rhodamine B showed that the penetration of the primer occurred along the cavity margins. Statistical analysis using one-way ANOVA followed by Duncan's Multiple Range test revealed that the primer penetration of the group 2(wedge-shaped cavity preparation) was more effective than group 1(cervical abrasion) and that of the gingival interfaces was more effective than the occlusal interfaces. In the one-bottle dentin bonding systems, the resin penetration score of OCB was compatible to SBMP, but those of SS and self-etching priming system, SB were lower than SBMP.

• Journal of Biomedical Engineering Research
• /
• v.16 no.4
• /
• pp.533-542
• /
• 1995

The present study investigated the effectiveness of pretreatment on dentin bonding. The adhesive resin was 5% 4-methacryloyloxyethyl trimellitate anhydride (4-META) in methyl methacrylate (MMA) combined with poly-MMA powder. Polymerization of this resin was initiated by tri-n-butyl borage (TBB). Ground bovine dentin samples were etched with either an aqueous solution of 10% citric (10-0 solution) (Group I) or aqueous solution of 10% citric acid and 3% ferric chloride(10-3 solution) (Group ll ). After etching, the primer (an aqueous solution of 35% hydroxyethyl methacrylate (HEM- A) and 5% glutaraldehyde was applied on the differently etched surfaces (Group III , Group IV). The 10-0 treatment showed the lowest tensile bond strength, followed by the 10-3 treatment, primer application after the 10-0 treatment and primer application after the 10-3 treatment. The relationship among the surface morphology after pretreatment, fractured surface morphology and tensile bond strength was examined. It revealed that the surface morphology change by different pretreatment influenced the bond strength and the resulting fractured surface morphology. The correlation of tensile bond strength with the fracture morphology was explained.

• The Journal of Advanced Prosthodontics
• /
• v.9 no.2
• /
• pp.85-92
• /
• 2017

PURPOSE. The aim of this study was to evaluate the effect of tooth surface pre-treatment steps on shear bond strength, which is essential for understanding the adhesive cementation process. MATERIALS AND METHODS. Shear bond strengths of different cements with various tooth surface treatments (none, etching, priming, or etching and priming) on enamel and dentin of human teeth were measured using the Swiss shear test design. Three adhesives (Permaflo DC, Panavia F 2.0, and Panavia V5) and one self-adhesive cement (Panavia SA plus) were included in this study. The interface of the cement and the tooth surface with the different pre-treatments was analyzed using SEM. pH values of the cements and primers were measured. RESULTS. The highest bond strength values for all cements were achieved with etching and primer on enamel ($25.6{\pm}5.3-32.3{\pm}10.4MPa$). On dentin, etching and priming produced the highest bond strength values for all cements ($8.6{\pm}2.9-11.7{\pm}3.5MPa$) except for Panavia V5, which achieved significantly higher bond strengths when pre-treated with primer only ($15.3{\pm}4.1MPa$). Shear bond strength values were correlated with the micro-retentive surface topography of enamel and the tag length on dentin except for Panavia V5, which revealed the highest bond strength with primer application only without etching, resulting in short but sturdy tags. CONCLUSION. The highest bond strength can be achieved for Panavia F 2.0, Permaflo DC, and Panavia SA plus when the tooth substrate is previously etched and the respective primer is applied. The new cement Panavia V5 displayed low technique-sensitivity and attained significantly higher adhesion of all tested cements to dentin when only primer was applied.

• Restorative Dentistry and Endodontics
• /
• v.28 no.6
• /
• pp.498-503
• /
• 2003

The purpose of this study was to evaluate the rewetting effect of water-based primer on the air-dried dentin. In this in vitro study, freshly extracted non-caries human molars and three-step adhesive system(SBMP) were used. Freshly extracted non-caries human molars and three-step adhesive system(SBMP) were used. Flat occlusal dentin surface were prepared using low-speed diamond saw, Prepared teeth were randomly divided into three groups. Group 1.(W): etched(35% phosphoric acid for 15s) and blot-dried, Group 2.(5D): 5s air-dried, Group 3.(30D): 30s ail-dried, To obtain color contrast in CLSM observation, primer was mixed with rhodamine B and bonding resin was mixed with fluorescein. Microscopic sample of each group were obtained after longitudinal section. Morphological investigation of resin-dentin interface and thickness of hybrid layer measurement using CLSM were done. Microtensile bond strength for each specimen was measured. Specimen were observed under microscope to examine the failure patterns of interface between resin and dentin. The results of this study were as follows: 1. The results(mean) of Thickness of hybrid layer were W:19.67, 5D:20.9, 30D:10$\mu\textrm{m}$. Only 30D had statistically significant differences to Wand 5D(P<0.05). 2. The results(mean) of Microtensile bond strength were W:16.02, 5D:14.69, 30D:11.14MPa. Only 30D had statistically significant differences to Wand 5D(P<0.05). 3. There were positive correlation between Thickness of hybrid layer and microtensile bond strength(P<0.05).

• Restorative Dentistry and Endodontics
• /
• v.28 no.5
• /
• pp.392-401
• /
• 2003

The purpose of this study was to evaluate the penetration pattern of dentin adhesives according to the orientation of dentinal tubules with confocal laser scanning microscopy. Specimens having perpendicular. parallel and oblique surface to dentinal tubules were fabricated. The primer of dentin adhesives (ALL $BOND^{\circledR}{\;}2,{\;}CLEARFIL^{TM}$ SE BOND and PQ1) was mixed with fluorescent material. rhodamine B isothio-cyanate (Aldrich Cherm. CO., Milw., USA), It was applied to the specimens according to the instructions of manufactures. The specimens were covered with composite resin (Estelite, shade A2) and then cut to a thickness of 500$\mu\textrm{m}$ with low speed saw (Isomet^{TM}, Buehler. USA). The adhesive pattern of dentin adhesives were observed by fluorescence image using confocal laser scanning microscopy. The results were as follows. 1. For the groups with tubules perpendicular to bonded surface. funnel shape of resin tag was observed in all specimen. However. resin tags were more prominent in phosphoric acid etching system (ALL $BOND^{\circledR}$ 2 and PQ1) than self etching system ($CLEARFIL^{TM}$ SE BOND). 2. For the groups with tubules parallel to bonded surface. rhodamine-labeled primer penetrated into peritubular dentin parallel to the orientation of dentinal tubules. But rhodamine-labeled primer of PQ1 diffused more radially into surrounding intertubular dentin than other dentin adhesive systems. 3. For the groups with tubules oblique to bonded surface. resin tags appeared irregular and discontinuous. But they penetrated deeper into dentinal tubules than other groups.