• 구강회복응용과학지
• /
• 제18권4호
• /
• pp.289-299
• /
• 2002

The bond strength is one of the most important factor in establishing long-term success of esthetic restorative dentistry. So, various restorative materials have been introduced to improve the esthetic and physical properties. Ormocer (organically modified ceramic) was developed as a result of such efforts. This study was performed to compare the shear bond strength of ormocer based adhesive with that of existing dentin adhesive. In this study $Admira^{(R)}$ and $Admira^{(R)}$ bond of the ormocer system are grouped together for ADM, Single $Bond^{(R)}$ which is an one-bottle adhesive and Z-250TM which is hybrid composite resin of BIS-GMA system for SIN, and $Definite^{(R)}$ of ormocer and Etch & $Prime^{(R)}$ 3.0 which is a self etching priming/ bonding agent for ETC. The results of this study were as follows. : (1) In the comparison of shear bond strength according to different adhesive system, shear bond strength was increased in the order of ETC group, SIN group, ADM group. There was no significant difference between ADM group and SIN group. However, there was a significant level of difference between ADM and ETC groups as well as SIN and ETC groups( p<0.05). (2) Examination by a scanning electron microscope showed a well established hybrid layer and resin tag in both ADM group and SIN group, while ETC group showed a minimal formation of the hybrid layer when compared with ADM and SIN groups. From the above results, it may be reasonable to start the clinical application of ormocer system, and it is recommended that ormocer system should be used along with an ormocer based adhesive because ormocer system showed the lower shear bond strength when it used with other existing self etching priming/bonding agent. The self etching priming/bonding agent showed relatively low shear bond strength, and it is considered that the further study should be needed.

• Restorative Dentistry and Endodontics
• /
• 제23권1호
• /
• pp.413-423
• /
• 1998

Dental ceramics exhibit excellent esthetic property, compressive strength, chemical durability, biocompatibility and translucency. This study evaluated the shear bond strength of composite resin to the new heat-pressed ceramic material (IPS-Empress System) depending on the surface treatments and bonding agents. The surface treatments were etching with 4.0% hydrofluoric acid, application of silane, and the combination of the two methods. Composite resin was bonded to ceramic with four kinds of dentin bonding agents(All-Bond 2, Heliobond, Scotch bond Multi-purpose and Tenure bonding agents). The ceramic specimen bonded with composite resin was mounted in the testing jig, and the universal testing machine(Zwick 020, Germany) was used to measure the shear bond strength with the cross head speed of 0.5 mm/min. The results obtained were as follows 1. The mean shear bond strength of the specimens of which the ceramic surface was treated with the combination of hydrofluoric acid and silane before bonding composite resin was significantly higher than those of the other surface treatment groups(p<0.05). 2. In the case of All-Bond 2 and Scotchbond Multi-purpose bonding agent group, the surface treatment methods did not influenced significantly on the shear bond(p>0.05). 3. Of the four bonding agents tested, the shear bond strength of Heliobond was significantly lower than those of other bonding agents regardless of the surface treatment methods(p<0.05). 4. The highest shear bond strength($12.55{\pm}1.92$ MPa) was obtained with Scotchbond Multipurpose preceded by the ceramic surface treatment with the combination of 4% hydrofluoric acid and silane.

• 대한치과보철학회지
• /
• 제48권1호
• /
• pp.8-15
• /
• 2010

연구 목적: 본 연구에서는 자가부식 접착제를 이용한 즉시 상아질 봉쇄 (immediate dentin sealing; IDS)와 지연 상아질 봉쇄 (delayed dentin sealing; DDS)에서 상아질 접착제의 결합강도를 비교하고 즉시 상아질 봉쇄에서 접착제 표면의 오염물을 제거하기 위해 사용되는 air abrasion이 상아질에 대한 미세 인장 결합강도에 어떠한 영향을 주는지에 대해 평가하였다. 연구 재료 및 방법: 1개월 이내에 발거된 사람의 건전한 대구치 30개를 6개의 군으로 분리하였고 상아질 접착제로는 자가부식 접착제 Clearfil SE bond (Kuraray, Okayama, Japan)를 사용하였다. 군분류는 치관부를 삭제하여 상아질을 노출시킨 후 즉시 접착제를 도포하고 복합레진 Filtek Z250 (3M ESPE, St Paul, MN, USA)을 충전한 군을 대조군 (Control), 노출된 상아질에 즉시 상아질 접착제를 도포하고 2주 후 재차 접착제를 도포해 복합레진과 같이 광중합하는 즉시 상아질 봉쇄군 (IDS), 상아질 노출 후 상아질 접착을 즉시 시행하지 않고 2주 후 상아질 접착과 복합레진의 충전을 시행하는 지연 상아질 봉쇄군 (DDS)으로 분류하였다. 그후Control군에 air abrasion을 시행한 군을 C-A, IDS군에 air abrasion을 시행한 군을 IDS-A군, DDS군에 air abrasion을 시행한 군을DDS-A군으로 세분화하였다. Control군과 C-A을 제외한 모든 군은 2주간 Fermit을 이용한 임시수복기간을 두었으며 대조군과 실험군 모두 미세인장 결합강도 실험 전 24시간동안 증류수에 보관 후 미세인장 결합강도를 측정하였다. 측정된 미세인장 결합강도는 one-way ANOVA를 이용하여 비교 분석하였으며 유의차가 있는 경우 Scheffe test를 이용한 사후검증을 시행하였다. 결과: 1. 자가부식 상아질 접착제인 Clearfil SE bond를 치아 삭제 직후 상아질 접착을 시행하고 2주간 임시수복 기간을 거친 후 접착제를 재도포하고 복합레진을 수복한 군과 치아삭제 후 2주간의 임시수복기간을 거친 후 상아질 접착을 시행하고 복합레진을 수복한 군 사이에 상아질-레진 간 미세인장 결합강도는 유의한 차이가 없었다 (P>.05). 2. 자가부식 상아질 접착제인 Clearfil SE bond를 상아질 접착 시행 전 $50{\mu}m$ 크기의 aluminum oxide particle로 air abrasion 처리하는 것은 상아질-레진 간 미세인장 결합강도에 유의한 영향을 주지 않았다 (P>.05).

• Restorative Dentistry and Endodontics
• /
• 제29권2호
• /
• pp.153-161
• /
• 2004

This study investigated that the effect of rewetting agent on dentinal microtensile bond strength(${\mu}TBS$). Human molars were sectioned to expose the superficial dentin surfaces. Samples were divided into two groups according to type of adhesives-Single Bond (S) and One-Step (0)], and again subdivided into five groups by different dentin surface treatment-dry for 15s (D), blot dry (BD) or dry for 15s, and rewet with different rewetting agents [distilled water (DW), Gluma Desensitizer (GD) and Aqua-Prep (AP)] for 30s. After application of adhesive, composite resin was built up on the bonding surface. Each tooth was sectioned to obtain stick with $1\textrm{mm}^2$ cross sectional area and the ${\mu}TBS$ was determined by EZ test. In the S group, the mean ${\mu}TBS$ of GD, AP, and BD group was significantly higher than that of DW and D group (p < 0.05), In the O group, the mean, ${\mu}TBS$ of AP, GD, BD and DW group was significantly higher than that of D group (p < 0.05). The data suggested that Gluma Desensitizer and Aqua-Prep could be successfully used as rewetting agents, and Distilled water could be acceptable in aceton based adhesive system only.

• Restorative Dentistry and Endodontics
• /
• 제34권3호
• /
• pp.223-231
• /
• 2009

본 연구는 인레이 와동에서 인상을 채득하기 전 지각과민처리제 (Isodan)과 2단계 전부식 접착시스템 (One-Step)과 단일단계 자가부식 접착시스템 (All-Bond SE)으로 처리한 후, 복합레진 인레이를 자가 접착형 레진시멘트인 BisCem으로 합착시키는 경우 레진 인레이의 상아질에 대한 미세인장결합강도와 주사현미경적인 분석을 통하여 비교하였다. 본 연구의 결과, 지각과민처리제인 Isodan만을 사용하는 경우 레진 인레이의 결합강도를 감소시킬 수 있으므로 단독 사용보다는 단일 단계 자가부식 시스템 (All-Bond SE)과 같이 사용하는 것이 추천된다.

• 대한치과교정학회지
• /
• 제41권2호
• /
• pp.121-126
• /
• 2011

Objective: The purpose of this study was to evaluate shear bond strength (SBS) and failure site location of brackets bonded to enamel with or without desensitizer application. Methods: Sixty-six freshly extracted human premolar teeth were randomly divided into 3 groups of 22. Group 1 served as the control. Desensitizer was applied to the remaining teeth at two time intervals (Group 2, bonded immediately after Pro-$Relief^{TM}$ (Colgate-Palmolive Co., New York, NY, USA) application and Group 3, bonded 30 days after Pro-$Relief^{TM}$ application with the teeth stored in artificial saliva during the 30 days). Orthodontic brackets were bonded with a light cure composite resin and cured with a halogen light. After bonding, the SBS of the brackets was tested using a universal testing device. Adhesive remnant index (ARI) scores were determined after the brackets failed. Data were analyzed with analysis of variance, Tukey's HSD, and G tests. Results: The SBS was significantly lower in Group 2 than in Groups 1 (p = 0.024) and 3 (p = 0.017). Groups 1 and Group 3 did not differ (p = 0.991). ARI scores did not differ significantly among groups. Conclusions: The Pro-$Relief^{TM}$ desensitizer agent applied immediately before bonding significantly reduces bond strength, but the SBS values still exceed the minimum 5.9 - 7.8 MPa required for adequate clinical performance. Immersing the teeth in artificial saliva for 30 days after applying the Pro-$Relief^{TM}$ desensitizer agent and before bonding increased the SBS to control levels.

• Restorative Dentistry and Endodontics
• /
• 제23권1호
• /
• pp.443-460
• /
• 1998

The purpose of this study was to estimate the changes of tensile bond strength according to the difference in lining materials and lining area. Seventy non-carious extracted human molars were used in the present study, and they were randomly assigned into 2 experimental groups according to the difference in lining materials. Each experimental group was subdivided into 3 groups according to the difference in lining area. Circular cavities were prepared on the dentin surface to a diameter of 1.5mm, 2.0mm, 2.5mm and the prepared cavities were filled with Fuji II LC( Glass Ionomer Cement : GIC) or Dycal. Dentin specimens without circular cavity were used as control group. The primer and bonding agent of All-Bond 2 and composite resin (Z-100, 3M Dental Products, U. S. A.) were applied to the exposed dentin surface with or without lining. Tensile bond strengths for the experimental specimens were then measured. To examine the interface between dentin and liner & between liner and composite resin, two specimens from each group were fabricated and observed under the SEM. The results were as follows. 1. Tensile bond strength for the specimens lined with GIC was higher than that for specimens lined with Dycal. However, there was no significant difference between two groups(p>0.05). 2. Tensile bond strength for the specimens lined with GIC in a diameter of 1.5mm(GIC-1.5mm lining group) was statistically higher than that for the GIC-2.0mm lining group and GIC-2.5mm lining group(p<0.05). 3. Tensile bond strength for the specimens lined with Dycal in a diameter of 2.5mm (Dycal-2.5mm lining group)was statistically lower than that for Dycal-1.5mm lining group and Dycal-2.0mm lining group(p<0.05). 4. It was possible to observe the good adhesion of the resin composite to the GIC and the presence of a fissure between GIC and dentin all along the interface. Interfacial gaps of 7.2-$72.2{\mu}m$ between GIC and dentin were observed. The interfacial gap between GIC and dentin at the cavity base was greater. However, the gap was gradually decreased toward the occlusal portion. 5. It was possible to observe the poor adhesion of the resin composite to the Dycal. The detachment of Dycal was occurred all along the composite resin-Dycal interface, and the gaps of 2.0-$30.1{\mu}m$ were formed. In all the specimens, polymerization shrinkage of resin composite caused the detachment of Dycal from the body of Dycal. At a Dycal-dentin interface. it was possible to observe the good adhesion. but poor adhesion with interfacial gap of 2.9-$26.8{\mu}m$ was observed partially.

• 대한소아치과학회지
• /
• 제37권4호
• /
• pp.445-452
• /
• 2010

최근 CPP-ACP의 초기 우식증의 재광화 및 예방 효과에 대한 연구가 많이 진행되고 있다. 그러나, CPP-ACP 적용으로 인한 법랑질 산부식 저항성 증가가 치면열구전색제 접착에 미치는 영향에 대해서는 연구가 부족한 실정이다. 본 연구에서는 CPP-ACP의 치면 도포 여부와 치면열구전색제의 접착 방법의 차이가 법랑질과 치면열구전색제의 결합력에 미치는 영향에 대하여 미세전단결합강도 측정법으로 알아보고자 하였다. 건전한 제3대구치를 사용하여 150개의 시편을 제작하였으며, 다음과 같이 6군으로 나누었다. I군: 인공타액에 2주 보관 후 35% 인산 산부식 II군: 인공타액에 2주 보관 후 35% 인산 산부식 + 접착제 III군: 인공타액에 2주 보관 후 자가 부식 접착제 IV군: CPP-ACP 2주 적용 후 35% 인산 산부식 V군: CPP-ACP 2주 적용 후 35% 인산 산부식 + 접착제 VI군: CPP-ACP 2주 적용 후 자가 부식 접착제 6군의 시편에 치면열구전색제 접착 후 미세전단결합강도를 측정하여 다음과 같은 결과를 얻었다. CPP-ACP 적용은 전통적인 산부식 방법으로 치면열구전색제를 접착하는 경우에는 결합강도와 산부식 양상에 영향을 미치지 않으나, 자가 부식 접착제를 사용한 경우에는 치면열구전색제의 결합강도를 약화시켰다.

• Restorative Dentistry and Endodontics
• /
• 제22권2호
• /
• pp.720-730
• /
• 1997

This study was performed to observe the histopathological response to the bonding resin directly applied on the remaining pulp tissues. 40 teeth from 3 adult dogs were pulpotomized with a sterile round bur and sharp excarvater. In the control group, $Ca(OH)_2$ powder was applied on the pulp tissue and the cavities were sealed with IRM cement. In the experimental group 1, Superbond C&B was applied on the remaining pulp and the cavities conditioned with 10-3 solution were filled with the mixture of the MMA liquid, PMMA powder and Catalyst. Multi-purpose adhesive was used on the remaining pulp tissue in the experimental group 2 and Z-100 was filled in the cavities. In the experimental group 3, Clearfil photobond applied and directly photo-cured on the pulp tissue, then the cavities were treated with CA agent (10% citric acid and 20% $CaCl_2$ aqueous solution) for 20 seconds, washed and applied with Clearfil photobond then filled with Protect liner. The experimental animals were sacrified at the 1st, 2nd, and 4th week. The specimens were routinely processed and stained with H-E for light microscopic observation. The results were as followed : 1. In the experimental group 1, the number and characteristics of the dentin bridge formation case was similar to those in the control group and less cases were observed in the experimental group 2 and 3 than experimental group 3. The inflammatory response in experimental group 1 was less than that in the control group at 1st week but there had been little difference at between 2nd and 4th week. 2. The number of the dentin bridge in experimental group 2 was less than that in control group and experimental group 1. The inflammatory response of the experimental group 1 was similar to that of experimental group 1 but less than that of the control group. A number of bleeding and vascular congestion were observed. The least inflammatory response was seen in the experimental group 2 among all groups. 3. In the experimental group 3, one case of the dentin bridge formation was observed and that was the same as that in the experimental group 2 but smaller than that of the control and experimental group 1. The inflammatory response of the experimental group 3 was least at the 1st week and most at the 4th week in the all group.

• Restorative Dentistry and Endodontics
• /
• 제29권5호
• /
• pp.454-461
• /
• 2004

The purpose of this study is to compare and to evaluate the effects of the degree of saturation on the progression of artificial root caries lesion. A total of 8 human premolars without any defects and cracks selected and the cementum were removed and the teeth were cleaned with ultrasonic device and pumice without fluoride. Each tooth was sectioned into 6 pieces and they were ground with #800 sandpaper until they had a thickness of 200pm. Specimens were applied with nail vanish except for the 2-3 mm window area after application of bonding agent. Under the constant pH, the specimens were divided into 6 groups (degree of saturation: 0.1415, 0.1503, 0.1597, 0.1676, 0.1771. 0.1977). Each group was immersed in acid buffer solution for 1. 2, 3, 5 days under controlled temperature ($25^{\circ}C$) and imbibed in water and examined using the polarizing microscope. The results were as follows 1. Although the degree of saturation of demineralization solution decreased, the depth of penetration in the dentin was constant. 2. Erosion was observed on the surface of all the teeth in the group I, II. In the group III, IV, V, surfaces were not changed. The teeth in the group VI showed the more mineralized surface but not the shape of the dentinal tubules distinctively. 3. In all groups, the lesion progressed rapidly at the first day of the experiment, but increased gradually as time elapsed.