• 대한치과보철학회지
• /
• 제37권5호
• /
• pp.658-671
• /
• 1999

The major influencing factors on the strength of all-ceramic crowns are types of dental ceramics, fabrication techniques, methods of abutment preparation and cementation modes of all-ceramic restorations. Zinc phosphate cement and glass-ionomer cement were used as an early lot-ing media for all-ceramic crowns. Recently many studies have reported that resin cements have more advantages in increasing the fracture strength of restorations comparing with zincphosphate cement and glass-ionomer cement. The purpose of this study is to investigate the effect of etching, silane treatment, sandblasting and dentin bonding agents on fracture strengths of dental ceramics. 40 flat dentin specimens and 40 ceramic discs of 1.5mm thickness and 8mm diameter were fabricated, and divided into 4 groups according to surface treatments. Surface treatments before cementation were as follows Group I : (ceramic) : HF etching - silane treatment - application of bonding resin (dentin) : application of dentin bonding agent Group II : (ceramic) : sandblasting - application of bonding resin (dentin) : application of dentin bonding agent Group III : (ceramic) : application of bonding resin (dentin) : application of dentin bonding agent Group IV : (ceramic) : HF etching - silane treatment - application of bonding resin (dentin) : no dentin bonding procedure Dentin specimens and ceramic discs were cemented with dual cure resin cement, and went through thermocycling. Compressive stress es were loaded on the centers of ceramic discs with Instron test-ing machine, and fracture strengths resistance for catastrophic fracture were measured The results were as follows. 1. The group I showed the highest fracture resistance. The next was group II And group III, IV followed. 2. There was a significant difference in the mean value of fracture strengths between group I and group III (p<0.05), but no significant differences between group I and group II, and group II and group III (p>0.05). 3. There was a significant difference in the mean value of fracture strengths between group I and group IV (p<0.05).

• Journal of Korean Dental Science
• /
• 제8권2호
• /
• pp.49-56
• /
• 2015

Purpose: The effect of accelerated aging on color stability of various dual-cured self-adhesive resin cements were evaluated in this study. Materials and Methods: Color stability was examined using three different brands of dual-cured self-adhesive resin cements: G-CEM LinkAce (GC America), MaxCem Elite (Kerr), and PermaCem 2.0 (DMG) with the equivalent color shade. Each resin cement was filled with Teflon mold which has 6 mm diameter and 2 mm thickness. Each specimen was light cured for 20 seconds using light emitting diode (LED) light curing unit. In order to evaluate the effect of accelerated aging on color stability, color parameters (Commission Internationale de l'Eclairage, CIE $L^*$, $a^*$, $b^*$) and color differences (${\Delta}E^*$) were measured at three times: immediately, after 24 hours, and after thermocycling. The $L^*$, $a^*$, $b^*$ values were analyzed using Friedman test and ${\Delta}E^*$ values on the effect of 24 hours and accelerated aging were analyzed using t-test. These values were compared with the limit value of color difference (${\Delta}E^*=3.7$) for dental restoration. One-way ANOVA and Scheff's test (P<0.05) were performed to analyze each ${\Delta}E^*$ values between cements at each test period. Result: There was statistically significant difference in comparison of color specification ($L^*$, $a^*$, $b^*$) values after accelerated aging except $L^*$ value of G-CEM LinkAce (P<0.05). After 24 hours, color difference (${\Delta}E^*$) values were ranged from 2.47 to 3.48 and $L^*$ values decreased and $b^*$ values increased in all types of cement and MaxCem Elite had high color stability (P<0.05). After thermocycling, color change's tendency of cement was varied and color difference (${\Delta}E^*$) values were ranged from 0.82 to 2.87 and G-CEM LinkAce had high color stability (P<0.05). Conclusion: Color stability of dual-cured self-adhesive resin cements after accelerated aging was evaluated and statistically significant color changes occurred within clinically acceptable range.

• 대한심미치과학회지
• /
• 제22권1호
• /
• pp.22-29
• /
• 2013

일반적으로 심미 보철을 진행하기 위해서는 초진 시부터 카메라를 사용해서 최종 보철물을 고려하며 여러 가지 분석을 한다. 이 부분에서 많은 치의들이 디지털카메라를 사용하고 있는 현실을 볼 때, 우리는 이미 digital impression을 시작하고 있는 것이 아닐까 생각한다. 최근 세계적인 photographer들도 필름카메라에서 디지털카메라로 넘어오는 추세가 많아지고 있는 것처럼 심미 치과학에서도 CAD/CAM은 향후 우리가 추구하고자 하는 심미 영역에서의 또 한가지 방향성을 제시해 줄 수 있지 않을까 하는 생각이 든다. 흔히 디지털이라고 하면 편의성, 경제성 등을 먼저 떠올리는 경향이 있다. 그러나 치과 임상적 관점에서 기존의 analog방식을 존중하며 CAD/CAM system이 가지는 그 특수성과 우수성을 고민하고 이를 개선, 발전시키는 것 또한 중요하다고 생각된다. 다만 아쉬운 것은 CAD/CAM 장치와 소재가 급격히 발전하는 이유로 인하여 reference, follow-up이 어려운 경우가 많다. 이에 digital은 변화하는 속도가 굉장히 빠르기 때문에, 여러 가지 소재와 장치들을 접해보고 경험해보면서 그에 맞게끔 발맞춰 적용해 볼 수밖에는 없지만 임상에 적용하여 보다 좋은 결과 얻기 위해서는 전통적인 방식이 기본바탕이 된 상태에서 이루어져야 한다는 점을 강조하고 싶다. 본 연구에서는 심미적 관점에서 전통적인 방식과 CAD/CAM과의 조화 통해서 어떤 접근을 할 수 있는지에 대해서 살펴보고자 한다. 그리고 CAD/CAM 보철이 'Digital art' 영역에 한 축의 역할을 할 수 있기를 기다리고 열망한다.

• 구강회복응용과학지
• /
• 제19권2호
• /
• pp.57-67
• /
• 2003

Suppose that dental occlusion is related to body posture. We want to find out that improving occlusal balance may affect vibration and distribution of C.O.P. in which way, by measuring change of posture and center of gravity (center of pressure, C.O.P.) which plays important role in measuring balance sensation. Total 11 students at Kyung Hee dental college students, 4 females and 9 males (age: 23-30) participated in this test, who have normal occlusion (Angle's classification I), no TMJ problems. All of the participants have no tooth loss except 3rd molar, no prosthesis over single tooth restoration, no orthopedic problems which affect balance sensation, and no otorhinolaryngological problems. First, we registrated bite by centric relation, and then fabricated stabilization splint that is increased 3.5mm vertical dimension around premolar region. By F-scan (Tekscan Inc., Boston, Mass), we measured discrepancy of average contact pressure of left and right foot. And we also measured discrepancy of vibration of C.O.P(center of pressure). before setting stabilization splint and after wearing stabilization splint at intervals of 1 week, 2 weeks, 3 weeks after. In normal human beings, improved occlusal balance by stabilization splint leads to decrease of vibration of C.O.P. (P<0.05). One week after wearing stabilization splint, vibration of C.O.P. decreased reliably (P<0.05), two weeks after wearing stabilization splint, vibration of C.O.P. decreased similarly comparing to before wearing and one week after wearing. (P<0.05) After two weeks and three weeks, however, it was hard to find reliability. (P>0.05) Difference between average contact pressure of right and left foot also decreased. (P<0.05) We could find decrease after one week of wearing stabilization splint (P<0.05) and two weeks after, the decrease was more reliable than one week after. (P<0.05) After two weeks and three weeks, however, it was hard to find reliability. Improvement of occlusal balance leads to decrease of vibration of C.O.P. and decrease of difference between right and left average contact pressure.

• 대한치과보철학회지
• /
• 제56권2호
• /
• pp.114-119
• /
• 2018

목적: 원광대학교 치과대학병원 임플란트 센터에서 임플란트를 식립한 후 1주일 내에 임시보철물을 수복한 다음, 즉시 하중을 가한 환자들을 대상으로 골 흡수량을 측정하고자 하였다. 이러한 후향적 분석을 통하여 임플란트에 대한 즉시 하중의 임상적 근거를 보강하고 주의해야 할 사항 등을 파악하고자 하였다. 대상 및 방법: 2005년 1월 1일부터 2016년 6월 31일 사이에 원광대학교 치과대학병원 임플란트 센터에서 임플란트를 식립한 후 1주일 내에 임시보철물을 수복한 환자들을 대상으로 하여 진료기록부와 방사선 사진을 조사하였다. 총 임플란트의 수는 70개였으며, 임플란트의 제조회사, 길이, 직경, 체결 방식에 따른 변연골의 흡수량을 측정하였다. 변연골의 흡수량을 측정하기 위해 임플란트 식립 직후와 6개월 이후의 치근단 방사선 사진을 비교 분석하였다. 통계 프로그램인 SPSS 22.0을 이용하여 Mann-whitney U test와 Kruskal-wallis test를 시행하였다. 결과: 즉시 하중 임플란트 군에서 임플란트와 지대주의 연결 구조에 따른 변연골 흡수량을 비교한 결과 내부 육각 연결 구조 임플란트에서의 변연골 흡수량은 평균 $1.24{\pm}0.72mm$, 외부 육각 연결 구조 임플란트에서 $1.73{\pm}1.27mm$로 나타났으며 통계적으로 유의한 차이를 보였다. 임플란트 제조회사, 길이, 직경에 따른 변연골 흡수량의 차이는 통계적으로 유의한 차이를 보이지 않았다. 결론: 즉시 하중 임플란트에서 내부 육각 연결 구조 임플란트에서의 변연골 흡수량은 외부 육각 연결 구조 임플란트에서의 변연골 흡수량보다 적게 나타났으며, 임플란트의 다른 조건들에서는 변연골 흡수량에 차이를 보이지 않았다.

• 대한소아치과학회지
• /
• 제29권4호
• /
• pp.592-599
• /
• 2002

광중합형 복합레진 및 다양한 레진 접착제는 최근 소아의 유치 수복에 사용이 증가하고 있다. 본 연구는 유치의 복합레진 수복 시 중합방법과 접착제에 따른 미세누출의 차이를 실험적으로 관찰하고자 하였다. 탈락기에 있는 건전한 유전치 150개의 순면에 직경 1.6mm, 깊이 1.6mm의 와동을 형성하였다. 와동의 충전재로써 1종의 복합레진, 1종의 콤포머, 4종의 레진 접착제를 사용하였다. 중합 광원은 3종을 사용하였다. 충전이 완료된 각 시편은 Sof-Lex 폴리싱 디스크로 표면을 연마한 후 $5^{\circ}C$와 $55^{\circ}C$에 각 30초씩 계류시켜 1,000회 열순환하고 2% methylene blue 수용액에 넣어 색소를 침투시킨 후 저속 diamond cutter($Isomet^{TM}$, Buehler, USA)를 이용하여 순면을 근원심으로 절단하였다. 각 재료별 미세누출의 정도를 관찰하여 다음과 같은 결과를 얻었다. 1. 충전재 및 광중합 방법에 따른 미세누출을 측정한 결과, 콤포머를 사용한 5군에서 충전방법과 관계없이 가장 작았고, Clearfil SE bond를 Optilux 501로 중합한 군에서 가장 컸으나 통계적으로 유의한 차이는 아니었다(P>0.05). 2. 충전재에 따른 미세누출을 측정한 결과, 콤포머를 충전한 5군에서 $1{\sim}4$군의 복합레진 충전군에 비해 더 작은 미세누출을 보였다(P<0.05). 3. 광중합 방법에 따른 미세누출을 측정한 결과, Optilux 501을 사용한 군에서 가장 작았고, Flipo를 사용한 군에서 가장 컸으나 통계적으로 유의한 차이는 아니었다(P>0.05).

• 대한소아치과학회지
• /
• 제32권2호
• /
• pp.293-299
• /
• 2005

소아환자의 수복치료에서 시술시간과 시술과정을 줄이는 것은 중요한 점이다. 복합레진은 물성의 증가로 영구치, 유치 전치부 심미수복재로써 뿐만 아니라 구치부 수복에도 많이 쓰이고 있다. 최근에 개발된 7세대 상아질 결합제는 기존의 복합레진을 치면에 부착하기 위해 필요했던 산부식, 프라이밍, 접착제 도포의 복잡한 과정을 한번의 처리로 단순화하였다. 본 연구에서는 유치 상아질에서 7세대 상아질 결합제의 결합력을 기존에 사용되고 있는 여러 결합제의 결합력과 비교하였다. 1, 2, 3, 4군은 각각 4, 5, 6, 7세대 상아질 결합제를 사용하였다. 유치 상아질을 노출시키고 군에 따라 상아질 면을 처리한 후에 직경 2.5mm, 높이 2.0mm의 주형을 이용하여 복합레진을 접착시키고 열순환을 시행한 다음 전단결합강도를 측정하여 다음과 같은 결론을 얻었다. 1. 5세대 상아질 결합제인 Clearfil SE Bond가 가장 높은 전단결합강도인 $27.87{\pm}5.33\;MPa$를 보였다. 이것은 4, 6, 7세대와 비교했을 때 통계학적으로 유의하였다. 2. 4세대 상아질 결합제의 전단결합강토는 $20.11{\pm}5.73\;MPa$로 6, 7세대보다는 약간 높게 나타났지만 통계적으로 유의한 차이는 보이지 않았다. 3. 6, 7세대 상아질 결합제의 전단결합강도는 유사하게 나타났다.

• 대한소아치과학회지
• /
• 제40권1호
• /
• pp.60-65
• /
• 2013

삼중치는 치아의 형태이상 중 희소한 경우로서 세 개의 치아가 결합된 양상을 보이는 것을 가리키는 용어이다. 그 동안 유치의 결합에 대한 문헌은 많이 보고된 바 있으나 대부분 두 개 치아의 결합에 대한 것이고 세 개 치아에 대한 보고는 드물었다. 삼중치는 치아 우식, 심미적인 문제, 부정 교합, 치주 문제 등을 동반할 수 있어 여러 전문 분야의 협진을 필요로 한다. 이 증례는 1세 11개월 여아의 상악 유전치부에 발생한 드문 증례인 삼중치에 대한 보고이다. 환아는 상악 우측 전치부 순측 치은 종창을 주소로 내원하였으며 3주전 해당 부위에 치아 외상을 입은 병력을 가지고 있었다. 환아의 구강 내 검사 시 상악 우측 유전치부위에 유중절치, 유측절치, 과잉치가 합쳐진 삼중치가 발견되었고 주변으로 누공과 농양이 관찰되었으며 방사선 사진에서 상악 우측 측절치가 결손된 것으로 판단되었다. 해당 치아에 대해 근관치료를 시행하였으며 복합레진을 이용하여 치관부위를 수복하였다.

• Composites Research
• /
• 제33권3호
• /
• pp.125-132
• /
• 2020

치과용 복합레진 Filtek P90 (3M ESPE, USA)과 Clearfil AP-X (Kuraray, Japan)를 대상으로 디지털 이미지 상관법을 이용하여 광중합 시 발생하는 수축거동을 관찰하고 등가탄성계수를 적용한 유한요소해석을 통해 시편표면의 응력분포를 산출하여 수축률분포와 비교하였다. 광조사 중과 광조사 후의 촬영 조건을 달리하여 CCD 카메라를 이용한 시편의 변형사진을 획득하고 디지털 이미지 상관분석을 하였다. DIC 분석 결과 상기의 복합레진 모두에서, 비균일한 수축변형률 분포가 관찰되었으며 링시편 내부의 레진 중심부가 자유로운 유동성으로 레진/링의 계면부보다 큰 수축 변형률이 발생하였다. 레진의 중심으로부터 거리가 멀어질수록 반경방향 평균수축률은 감소하였으며, 광조사동안에 발생한 반경방향 평균수축률은 경화시험종료(10 min) 후 발생한 반경방향 평균수축률 값을 기준으로 P90은 33%, AP-X는 57% 수준이었다. P90과 AP-X가 광조사 중의 수축거동이 크게 달랐음을 확인하였다. 레진/링의 계면부에 가까운 레진에서는 광조사 후에 인장변형률이 급격히 커져서 계면부가 인장응력을 받아 취약하게 됨을 확인하였다.

• 대한치과기공학회지
• /
• 제32권2호
• /
• pp.65-74
• /
• 2010

Purpose : To understand the impact on the strength or restoration force by the change of heating temperature when soldering 18-8 stainless steel round wire which is the chrome-nickel class for dental orthodontic device production. Methods : The following conclusions were made upon the results from tensile strength test, 3 point bending test, and $90^{\circ}$ bending fatigue test with 24 samples that had been applied with condition 1 (before heat treatment - natural) and condition 2 (after heat treatment - mooring 30 seconds after heating up to $500^{\circ}C$, $700^{\circ}C$, and $900^{\circ}C$) to ${\phi}0.4mm$, ${\phi}0.7{\beta}mm$, 18-8 stainless steel round wire (spring hard) by Jinsung Company. Results : When it was heat-treated at $900^{\circ}C$, both ${\phi}0.4mm$ and ${\phi}0.7mm$ showed very low tensile strengths compared to the heat treated cases at $500^{\circ}C$ and $700^{\circ}C$ Yield strengths of both ${\phi}0.4mm$ and ${\phi}0.7mm$ showed very low compared to the heat treated cases at natural, $500^{\circ}C$, and $700^{\circ}C$, as well. Upon the results of 3 point bending test, the heat treated case at $900^{\circ}C$ showed very low in both ${\phi}0.4mm$ and ${\phi}0.7mm$, compared to the heat treated cases at natural, $500^{\circ}C$, and $700^{\circ}C$. Tensile strength of both ${\phi}0.4mm$ and ${\phi}0.7mm$ as well, showed very low compared to the heat treated cases at natural, $500^{\circ}C$, and $700^{\circ}C$. Upon the results of $90^{\circ}$ bending fatigue test, the heat treated case at $900^{\circ}C$ showed the highest wave node resistance in both ${\phi}0.4mm$ and ${\phi}0.7mm$. Conclusion : This study concluded that heating temperature change during wire soldering impacts on the characteristics of orthodntic wire.