• The Journal of Korean Academy of Prosthodontics
• /
• v.37 no.6
• /
• pp.717-729
• /
• 1999

Although many studies on the cytotoxicity of the dental cast base metal alloys and their components have been carried out, the results are rather conflicting because of the different type of cells used and the various experimental procedures taken. Recently a number of scientists have claimed that it would be preferable to focus on the use of cells from relevant specific location of the human bodies. Consequently, the primary cultured oral keratinocyte derived from oral mucous along with nickel chloride and several of widely used dental cast base metal alloys(two Ni-Cr alloys and one Co-Cr alloy)in domestic were selected for this study, from which 1) The amounts of released metal ions were determined using atomic absorption spectrometry, 2) The cytotoxicity of nickel chloride and dental cast base metal alloys was evaluated via MTT assay, and finally, 3) The amounts of released metal ions and the cytotoxicity of nickel chloride were correlated with the cytotoxicity of dental cast base metal alloys And, the results were summarized as follows; 1. Nickel ion from Ni-Cr alloys and Cobalt ion from Co-Cr alloys resulted in maximum releasing rate during first 2h hours, followed by a decrease in releasing rate with time. Chromium ion were found to be minimal in all alloys. 2. In cytotoxic test. with $40{\mu}M,\;80{\mu}M$ of nickel chloride, there were observed an increase in the relative cell number compared to control samples after 24 hours. With $160{\mu}M$, there was found to be no difference in the relative cell number with control, except that 48 hour showed a increase in relative cell number. With $320{\mu}M$, the relative cell number remained constant and decreased after 48 hours, and with $640{\mu}M$, a continuing decrease in relative cell number was observed throughout test period. 3 The sensitivity of primary cultured oral epithelium to nickel was lower compared to the cells used in other studies. 4. CB-80 Soft and Regalloy showed no cytotoxicity to primary cultured oral epithelium and New crown resulted in a slight cytotoxicity. In conclusion, it was shown that the primary cultured oral keratinocytes could be applied successfully as testing cells in cytotoxicity test. Futhermore, the dental cast base metal alloys used in this study were found to be biocompatible.

• The Journal of the Korean dental association
• /
• v.23 no.7 s.194
• /
• pp.577-583
• /
• 1985

The purpose of this investigation was to evaluate scanning electron micrographs of repeatedly cast base metal alloy. For this study two Ni-Cr-Be alloys were used; Rexillium III and Verabond. They were repeatedly cast without addition o new alloy melting with an electric resistant furnace (Castron 8, Yoshida dental equipment Mfg.Co.). They were etched with 10% H₂SO₄ Sol. at 300mA/㎠ for 3 minutes with the use of metal etching unit Oxyetch (OXY dental product Inc.), and ultrasonic cleaning in 18% HC1 Sol. was done. Etched surfaces were examined under a SEM at x 200 and x 750. The surfaces are shown in legends.

• Journal of Technologic Dentistry
• /
• v.11 no.1
• /
• pp.89-93
• /
• 1989

The purpose of this study was to evaluate the effect of sprue length and casting pressure on the relative castability of the base metal alloys, commonly used to make porcelain metal restoration. Samples of total 30 were constucted and devided into 6 groups according to three variables (low, medium, high). The total number of complety cast squares were counted, verified and recorded. The results of this 1. main effect of casting pressure was statistically significant.(P<0.05). 2. main effect of sprue length was not statistically significant.

• Journal of Technologic Dentistry
• /
• v.25 no.1
• /
• pp.9-20
• /
• 2003

Using a nickel-chrome casting alloy called 'Rexillium V' which is also available as base metal alloy for dental ceramic crown, 4 types of mixtures(A, B, C, D) with old and new metal were prepared for cyclic casting. The results of cyclic casting can be outlined as follows: 1. For Vickers hardness after casting, specimen A and D tended to have lower hardness in the course of cyclic casting, while specimen B and C tended to higher hardness. 2. The results of X-ray diffraction analysis showed that major crystal phase contained nickelchrome compounds and carbide. 3. The observation results of SEM photographs after cyclic casting show that there was a significant tendency to have similar structures among experimental groups. 4. The results of EDX analysis after cyclic casting showed that there were little differences in chemical composition between parent metal and base metal alloy. Although industrial nickel-chrome cast alloy did not show any significant change in material properties even through cyclic casting over several times, it is recommended that more there be more in-depth studies on how to detect any potential corrosion, discoloration and toxication of dental ceramic crown implanted in patient's oral cavity.

• Journal of Technologic Dentistry
• /
• v.34 no.4
• /
• pp.353-359
• /
• 2012

Purpose: The aim of this study measured and compared the marginal and internal fit of metal cores with two base metal alloy (Ni-Cr alloy(non-beryllium), Co-Cr alloy). Methods: Maxillary right first molar abutment fabricated by titanium was prepared for this study. Impressions(10ea) were made from titanium model, and study models were poured with improved dental stone. Wax cores of twenty were prepared for burn-out and casting. Ten wax cores cast Ni-Cr alloy(non-Be), and finally ten cast Co-Cr alloy. Marginal and internal fit of cores was evaluated using silicone replica technique and digital microscope(x160). The data were statistically analyzed with the independent samples t-test (${\alpha}$ <.05). Results: Mean(standard deviation, SD) marginal and internal fit total size of Ni-Cr alloy(non-Be) group was $73.3(14.4){\mu}m$ and of Co-Cr alloy group $65.6(17.4){\mu}m$. The marginal and internal fit total size of Ni-Cr alloy group(non-Be) was statistically significantly greater than that of Co-Cr alloy group (P=.004). Conclusion: Co-Cr alloy cores in this study had a better marginal fit than Ni-Cr alloy(non-Be) cores.

• Journal of Technologic Dentistry
• /
• v.31 no.1
• /
• pp.17-21
• /
• 2009

This experimental study was to determine the fitness on each cervical margin of recast using crown base metal alloy. The alloy used in this experimental study was a Ni-Cr alloy(Wirolloy, Bego, Germany) for the fabrication of full cast crown prosthesis. Twenty-five copings were divided into the five groups. And the group A, B, C, D and E were cording successively according to the frequency of recast to five times. Each specimen was recasted without adding new metal. The experimental results were as follows: 1. The group A and B showed good fitness had subtle differences in each cervical margin adaptation, in other words, the mesio and disto cervical margin showed worse adaptation than the bucco and linguo cervical margin. 2. The group C got good fitness in bucco and linguo cervical margins, but the mesio and disto cervical margin showed inaccurate fitness. And I could not get good casting bodies without adding new metal. 3. The group D and E showed bad fitness for each cervical margin. Therefore the group D and E lost its function as a dental restoration.

• Journal of Korea Foundry Society
• /
• v.27 no.3
• /
• pp.120-125
• /
• 2007

The microstructure, mechanical properties and melting range of Ni-Cr-Mo based alloys were investigated to develop Be-free Ni-Cr-Mo base dental alloys for Porcelain-Fused-to-Metal Firing(PFM). All as-cast alloys showed dendritic structure. Rockwell hardness of 20Cr7Mo was increased with addition of Si and Ti. On the contrary, it was decreased with addition of Co. The duplex alloying elemental addition such as 3Co + xTi, 2Si + xCo and 2Si + xTi to 20Cr7Mo resulted in much increase of hardness. Rockwell hardness and compressive strength for 20Cr3CoSiTi or 17Cr6CoSiTi alloy that add Si-Ti had similar values compared to the commercial alloys. Melting range for 20Cr3CoSiTi and 17Cr6CoSiTi alloy that add Si-Ti showed similar or lower than commercial alloys. In conclusion, 20Cr3CoSiTi and 17Cr6CoSiTi alloys can be applied for commercial use.

• Journal of Technologic Dentistry
• /
• v.21 no.1
• /
• pp.87-96
• /
• 1999

In order to examine the influence of sprue(used to make crown supplements) on casting, 3 kinds of sprue materials(wax, wood, plastic) and 3 types of sprue(round, square, triangle) were made and buried and cast, then the comparison and analysis of casting characters among sprue materials and among sprue type show the following results : 1. The comparison of casting characters in accordance with sprue materials shows wax sprue of 83.3%, wood sprue 81.3%, and plastic sprue of 80.7%, Wax sprue was the bast materials for casting, However there was no statistically significant difference of casting characters among was, plastic and wood. 2. The comparison of casting in accordance with sprue types shows square sprue of 94.0%, round sprue of 86.9% and triangle sprue of 84.2%. square sprue had a best casting character. 3. When a ring cast using wood sprue was classified from burying materials. its cutting of casting body and sprue indicated much more than any other sprue material. It seems to be caused by the influence of wood residuals and carbon occurrence.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.6
• /
• pp.732-746
• /
• 2003

Statement of problem. Soft lining materials, also referred to as tissue conditioning materials, tissue heating materials, relining materials, soft liners or tissue conditioners, were first introduced to dentistry by a plastic manufacturer in 1959. Since the introduction of the materials to the dental field, their material properties have been continually improved through the effort of many researchers. Soft lining materials have become widely accepted, particularly by prosthodontists, because of their numerous clinical advantages and ease of manipulation. Unfortunately, few reports have been issued upon the topic of increasing the bond strength between the base metal alloy used in cast denture bases and PMMA soft liner modified with 4-META, nor upon the pattern of debonding and material change in wet environment like a intra oral situation. Purpose. The purposes of this study were comparing the bond strength between base metal alloy used for the cast denture bases and PMMA soft liner modified with 4-META, and describing the pattern of debonding and material property change in wet environment like the intraoral situation. Material and Methods. This study consisted of four experiments: 1. The in vitro measurement of shear bond strength of the adhesive soft liner. 2. The in vitro measurement of shear bond strength of the adhesive soft liner after 2 weeks of aging. 3. A comparison of debonding patterns. 4. An evaluation the Relation time of modified soft liner. The soft liner used in this study was commercially available as Coe-soft (GC America.IL.,USA), which is provided in forms of powder and liquid. This is a PMMA soft liner commonly used in dental clinics. The metal primer used in this study was 4-META containing primer packed in Meta fast denture base resin (Sun Medical Co., Osaka, Japan). The specimens were formed in a single lap joint desist which is useful for evaluating the apparent shear bond strength of adhesively bonded metal plate by tensile loading. Using the $20{\times}20mm$ transparent grid, percent area of adhesive soft liner remaining on the shear area was calculated to classify the debonding patterns. To evaluate the change of the initial flow of the modified adhesive soft liner, the gelation time was measured with an oscillating rheometer (Haake RS150W/ TC50, Haake Co., Germany). It was a stress control and parallel plate type with the diameter of 35mm. Conclusion. Within the conditions and limitations of this study, the following conclusions were drawn as follows. 1. There was significant increase of bond strength in the 5% 4-META, 10% 4-META containing groups and in the primer coated groups versus the control group(P<0.05). 2. After 2 weeks of aging, no significant increase in bond strength was found except for the group containing 10% 4-META (P<0.05). 3. The gelation times of the modified soft liner were 9.3 minutes for the 5% 4-META containing liner and 11.5 minutes for the 10% 4-META liner. 4. The debonding patterns of the 4-META containing group after 2 weeks of aging were similar to those of immediaely after preparation, but the debonding pattern of the primer group showed more adhesive failure after 2 weeks of aging.

• Journal of Technologic Dentistry
• /
• v.8 no.1
• /
• pp.51-55
• /
• 1986

The castability of base metal alloys for dental casting in influenced by burn-out temperature and recent percentage. Burn-out temperatures for casting are set at 200$^{\circ}F$ interval from 1000$^{\circ}F$ to 1800$^{\circ}F$. According to recast metal percent in new cast alloy metal alloys are tested. The results are as followings: 1. In the new alloy(100%), the castability is the most. 2. The burn-out temperature in 1600$\sim$1800$^{\circ}F$, castability of 100% new alloy was more four times than of 50% new alloy plus 50% recast alloy. The using of 50% new alloy and 50% recast alloy, therefore, was unlike in castability. 3. The burn-out temperature in 1600$^{\circ}F$, castability of 100% new alloy was more than four times in soaking 20 minutes, but there was no any difference at 18700$^{\circ}F$. 4. It is investigated that the optimal burn-out temperature is 1600$^{\circ}F$ for the C & B alloy.