• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2003.04a
• /
• pp.113-116
• /
• 2003

The investigation of delamination growth behavior in hybrid composite material such as FRMLs should be considered delamination growth rate, dA_D/da$ using the delamination shape factor, $f_S$ instead of traditional fracture mechanics parameters. The main objective of this study is to evaluate the relationship between delamination element (i. e. delamination width, b, delamination contour, c, delamination shape factor, $f_S$ and delamination growth rate, dA_D/da$) and delamination growth in FRMLs under cyclic bending moment. The delamination shape formed along the fatigue crack between aluminum layer and glass fiber/epoxy layer are measured by scanning method. The details of study are as follow : ⅰ) Relationship between crack length, a and delamination width, b. ⅱ) Variation of delamination growth rate, dA_D/da$ was attendant on delamination shape factors, $f_{S1}$, $f_{S2}$, $f_{S3}$. The test result indicated the delamination growth behavior depends in delamination element such as delamination width, b, delamination shape factors, $f_{S1}$, $f_{S2}$, $f_{S3}$.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2003.04a
• /
• pp.398-404
• /
• 2003

Most previous researches for the hybrid composite materials such as FRMLs(Al/AFRP, Al/GFRP) have evaluated the fatigue delamination behavior using the traditional fracture mechanism. However, most previous researches have not generally been firmed yet. Because delamination growth behavior in hybrid composite should be consider delamination growth rate, $dA_D$/da using the delamination shape factors, fs instead of traditional fracture mechanic parameters. The major purpose of this study was to evaluate the relationship between delamination shape factor, fs and delamination growth rate, $dA_D$ . And a propose parameter on the delamination aspect ratio, b/a. The details of the study are as follow : 1) Relationship between crack length, a and delamination width,b. 2) Relationship between delamination aspect ration, b/a and delamination area rate,($(A_D)_{N}(A_D)_{ALL}$. 3) Variation of delamination growth rate, $dA_D/da$ was attendant on delamination shape factors, $fs_1$, $fs_2$, $fs_3$. The test results indicated the delamination growth rate depends on delamination shape factors.

• Journal of Mechanical Science and Technology
• /
• v.18 no.11
• /
• pp.1932-1940
• /
• 2004

Although the previous researches evaluated the fatigue behavior of Al/GFRP laminates using the traditional fracture mechanism, their researches were not sufficient to do it : the damage zone of Al/GFRP laminates was occurred at the delamination zone instead of the crack-metallic damages. Thus, previous researches were not applicable to the fatigue behavior of Al/GFRP laminates. The major purpose of this study was to evaluate delamination behavior using the relationship between crack length (a) and delamination width (b) in Al/GFRP laminate. The details of investigation were as follows: 1) Relationship between the crack length (a) and the delamination width (b), 2) Relationship between the delamination aspect ratio (b/a) and the delamination area rate ((A$\_$D/)/subN// (A$\_$D/)$\_$All/), 3) The effect of delamination aspect ratio (b/a) on the delamination shape factor (f$\_$s/) and the delamination growth rate (dA$\_$D// da). As results, it was known that the delamination aspect ratio (b/a) was decreased and the delamination area rate ((A$\_$D/)$\_$N// (A$\_$D/)$\_$All/) was increased as the normalized crack size (a/W) was increased. And, the delamination shape factors (f$\_$s/) of the ellipse-II(f$\_$s3/) was greater than of the ellipse-I(f$\_$s2/) but that of the triangle (f$\_$s1/) was less than of the ellipse-I(f$\_$s2/).

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.2
• /
• pp.317-326
• /
• 2003

The influence of cyclic bending moment on the delamination and the fatigue crack propagation behavior in Al/GFRP laminate such as the wing section was investigated. The main objective of this study was to evaluate the relationship between crack profile and delamination behavior. And a propose parameter on the delamination growth rate(d $A_{D}$/da) of Al/GFRP laminates with a saw-cut using relationship between delamination area( $A_{D}$) and cycles(N), crack length(a), stress intensity factor range($\Delta$K). Also, the fiber bridging effect factor( $F_{BE}$ ) was propose that the fiber bridging modification factor($\beta$$_{fb}$ ) to evaluate using the delamination growth rate(d $A_{D}$/da). The shape and size of the delamination zone formed along the fatigue crack between aluminum alloy sheet. Class fiber-adhesive layer were measured by an ultrasonic C-scan image. The shape of delamination zone turns out to be semi-elliptic with the contour decreased non-linearly toward the crack tip. It represents that relationship between crack length and delamination growth rate(d $A_{D}$/da) were interdependent by reciprocal action, therefore it's applicable present a model for the delamination growth rate(dA/sib D//da) in Al/GFRP laminates.minates.s.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.1
• /
• pp.55-62
• /
• 2004

Although the previous researches evaluated the fatigue behavior of glass fiber/epoxy laminates using the traditional fracture mechanism, their researches were not sufficient to do it: the damage zone of glass fiber/epoxy laminates was occurred at the delamination zone instead of the crack-metallic damages. Thus, previous researches were not applicable to the fatigue behavior of glass fiber/epoxy laminates. The major purpose of this study was to evaluate delamination behavior using the relationship between crack length and delamination width in hybrid composite material such as Al/GFRP laminate. The details of investigation were as follows : 1) Relationship between crack length and delamination width, 2) Relationship between delamination aspect ratio and delamination area rate, 3) Variation of delamination growth rate is attendant on delamination shape factors. The test results indicated that the delamination growth rate depends on delamination width delamination aspect ratio and delamination shape factors.