• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.2
• /
• pp.49-54
• /
• 2003

We have investigated the effects of hydrogen annealing on the physical and electrical properties of $SrBi_{2}Ta_{2}O_9(SBT)$ thin films in the Pt/SBT/Si (MFS) structure and Pt/SBT/Pt (MFM) one, respectively. The microstructure and electrical characteristics of the SBT films were deteriorated after hydrogen annealing due to the damage of the SBT films during the annealing process. To investigate the reason of the degradation of the SBT films in this work, in particular, the effect of the Pt top electrodes, SBT thin films deposited on Si, Pt, respectively, were annealed with the same process conditions. From the XRD, XPS, P-V, and C-V data, it was seen that the SBT itself was degraded after $H_2$ annealing even without the Pt top electrodes. In addition, the degradation of the SBT films after $H_2$ annealing was accelerated by the catalytic reaction of the Pt top electrodes which is so-called hydrogen degradation. To prevent this phenomenon, we proposed the alternative top electrode material, i.e. Ir, and the electrical properties of the SBT thin films were examined in the $Ir/IrO_2/SBT/IrO_2$ structures before and after the H$_2$ annealing and recovery heat-treatment processes. From the results of the P-V measurement, it could be concluded that Ir is one of the promising candidate as the electrode material for degradation resistance in the MFM structure using SBT thin films.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.8
• /
• pp.667-674
• /
• 2000

The stability of ZnO-Pr$_{6}$/O$_{11}$-CoO-Er$_{2}$/O$_3$based varistors was investigated with Er$_{2}$/O$_3$additive content of the range 0.0 to 2.0 mol%. All varistors sintered at 130$0^{\circ}C$ exhibited the thermal runaway within short times even under weak d.c. stress. As a result these varistors were completely degraded. On the contrary the stability of varistors sintered at 135$0^{\circ}C$ was far better than that of 130$0^{\circ}C$. In particular the varistors added with 0.5mol% Er$_{2}$/O$_3$ which the nonlinear exponent is 34.83 and the leakage current is 7.38 $mutextrm{A}$ showed a excellent stability which the variation rate of the varistors voltage the nonlinear coefficient and the leakage current is below 1%, 2%, and 3.5% respectively even under more severe d.c. stress such as (0.80 V$_{1mA}$9$0^{\circ}C$/12h)+(0.85 V$_{1mA}$115$^{\circ}C$/12h)+(0.90 V$_{1mA}$12$0^{\circ}C$12h) Consequently it is estimated that the ZnO-0.5 mol% Pr$_{6}$/O sub 11/-1.0 mol% CoO-0.5 mol% Er$_{2}$/O sub 3/ based varistors will be used to develop the advanced Pr$_{6}$/O$_{11}$-1.0 mol% CoO-0.5 mol% Er$_{2}$/O$_{3}$ based varistors will be used to develop the advanced Pr$_{6}$/O$_{11}$-based ZnO varistors having the high performance and stability in future. future.ure. future.

• Journal of the Korean Wood Science and Technology
• /
• v.33 no.1 s.129
• /
• pp.77-86
• /
• 2005

In order to investigate the ability of log wood for oak mushroom production as a source of an alternative energy, both chemical and physical characteristics of log wood were investigated according to the cultivation periods. Also, both chemical and physical characteristics of material that treated by steam explosion were investigated to confirm the pretreatment effect by remaining enzyme as a control. The contents of ash, water-, alkali- and organic soluble extracts have been increased after the inoculation. It appeard that holocellulose contents substantially decreased and the contents of lignin as another main component of wood remained constant after the inoculation. However this result implied that indeed, a sufficient amount of lignin has been degraded paritially by enzymes of oak mushroom Lentinus edodes if we consider that the amount of holocelulose was substantially reduced. It also indicated that the degree of degradation gradually progressed but crystallinity decreased after the inoculation. The contents of water-, alkali- and organic soluble extracts have been increased by steam explosion. Holocellulose contents increased within narrow limits and lignin contents remained constant. However the contents of holocellulose and lignin have been decreased by steam explosion, considering that the amount of other extractives was relatively increased. The degree of crystallinity and lignin contents reduction by steam explosion was almost similar to the result obtained by increasing cultivation periods. According to the results, log woods for mushroom production have a potential as material for developing alternative energy.

• International Journal of Highway Engineering
• /
• v.13 no.3
• /
• pp.75-82
• /
• 2011

There is the uncertain period of the construction in case of the products meeting the quality standard of KS M 6080, the quality is degraded because of the abrasive loss of the paint caused by vehicle tires as the traffic amount increases and of the loss and detachment of the glass beads providing the retroreflective function. The abrupt degradation of visibility causes the high frequency of traffic accidents at night and increases the traffic accident rate. Additional supplementary construction induces the direct material and construction costs. As the more cost induction effect than the direct cost, the traffic jam caused by the additional construction increases the indirect social costs such as time cost and vehicle cost. Hence, the study is concerned with performing the abrasion resistance test based on the EN 1436 standard to check and improve the quality of various road marking materials resulting in improving the durability of road marking materials. However, even though the difference in the durability lifetime of resins(binders) is bibliographically or theoretically clear, there was no difference in the durability lifetime (retroreflectivity aspect) of the road marking paint using these binders. The reason is that the bonding of beads was very insufficient or that the cross density caused by crack or freshness was low. Moreover, the measured wet retroreflectivity was distributed as the Rw3 or higher class in average on the basis of EN 1436 but was very insufficient on the basis of the minimum wet threshold retroreflectivity with 100mcd/($m^2{\cdot}lx$) managed overseas.

• Applied Chemistry for Engineering
• /
• v.10 no.7
• /
• pp.1052-1060
• /
• 1999

Tire and raw material of tire, i.e., SBR were degraded using pyrolysis process. The yield of pyrolytic oil was increased and that of gas was decreased with increase of operating temperature in pyrolysis. And the yield of pyrolytic oil was increased and that of gas and char was decreased with increase of heating rate. The maximum oil yields of SBR and tire were 86% and 55% each at $700^{\circ}C$ with a heating rate of $20^{\circ}C/min$. The number average molecular weight ranges of SBR and tire were 740~2486, 740~1719, and the calorific value of SBR and tire was 39~40 kJ/g. The oil components were consisted of mostly 50 aromatic compounds. The particle size was decreased and the surface area was increased with increase of operating temperature, and the BET surface area was $47{\sim}63m^2/g$. The optimum condition of pyrolysis was the temperature of $700^{\circ}C$ with heating rate of $20^{\circ}C$, and the reactor was continuously purged with inert gas to sweep the evolved gases from the reaction zone.

• 한국생물공학회:학술대회논문집
• /
• 2000.04a
• /
• pp.89-91
• /
• 2000

Polynuclear aromatic hydrocarbon (PAH) compounds are highly carcinogenic chemicals and common groundwater contaminants that are observed to persist in soils. The adherence and slow release of PAHs in soil is an obstacle to remediation and complicates the assessment of cleanup standards and risks. Biological degradation of PAHs in soil has been an area of active research because biological treatment may be less costly than conventional pumping technologies or excavation and thermal treatment. Biological degradation also offers the advantage to transform PAHs into non-toxic products such as biomass and carbon dioxide. Ample evidence exists for aerobic biodegradation of PAHs and many bacteria capable of degrading PAHs have been isolated and characterized. However, the microbial degradation of PAHs in sediments is impaired due to the anaerobic conditions that result from the typically high oxygen demand of the organic material present in the soil, the low solubility of oxygen in water, and the slow mass transfer of oxygen from overlying water to the soil environment. For these reasons, anaerobic microbial degradation technologies could help alleviate sediment PAH contamination and offer significant advantages for cost-efficient in-situ treatment. But very little is known about the potential for anaerobic degradation of PAHs in field soils. The objectives of this research were to assess: (1) the potential for biodegradation of PAH in field aged soils under denitrification conditions, (2) to assess the potential for biodegradation of naphthalene in soil microcosms under denitrifying conditions, and (3) to assess for the existence of microorganisms in field sediments capable of degrading naphthalene via denitrification. Two kinds of soils were used in this research: Harbor Point sediment (HPS-2) and Milwaukee Harbor sediment (MHS). Results presented in this seminar indicate possible degradation of PAHs in soil under denitrifying conditions. During the two months of anaerobic degradation, total PAH removal was modest probably due to both the low availability of the PAHs and competition with other more easily degradable sources of carbon in the sediments. For both Harbor Point sediment (HPS-2) and Milwaukee Harbor sediment (MHS), PAH reduction was confined to 3- and 4-ring PAHs. Comparing PAH reductions during two months of aerobic and anaerobic biotreatment of MHS, it was found that extent of PAHreduction for anaerobic treatment was compatible with that for aerobic treatment. Interestingly, removal of PAHs from sediment particle classes (by size and density) followed similar trends for aerobic and anaerobic treatment of MHS. The majority of the PAHs removed during biotreatment came from the clay/silt fraction. In an earlier study it was shown that PAHs associated with the clay/silt fraction in MHS were more available than PAHs associated with coal-derived fraction. Therefore, although total PAH reductions were small, the removal of PAHs from the more easily available sediment fraction (clay/silt) may result in a significant environmental benefit owing to a reduction in total PAH bioavailability. By using naphthalene as a model PAH compound, biodegradation of naphthalene under denitrifying condition was assessed in microcosms containing MHS. Naphthalene spiked into MHS was degraded below detection limit within 20 days with the accompanying reduction of nitrate. With repeated addition of naphthalene and nitrate, naphthalene degradation under nitrate reducing conditions was stable over one month. Nitrite, one of the intermediates of denitrification was detected during the incubation. Also the denitrification activity of the enrichment culture from MHS slurries was verified by monitoring the production of nitrogen gas in solid fluorescence denitrification medium. Microorganisms capable of degrading naphthalene via denitrification were isolated from this enrichment culture.

• Journal of the Korea Concrete Institute
• /
• v.23 no.2
• /
• pp.135-144
• /
• 2011

Recently, researches about fiber reinforced polymer (FRP) which has excellent durability, corrosion resistance, and tensile strength as a substitution material to steel tendon have been actively pursued. This study is performed to examine FRP tendon used prestressed beam's safety under service load. The specimen was a prestressed concrete beam with internal bonded FRP tendon. In order to compare the member fatigue capacity, a control specimen of a prestressed concrete beam with ordinary steel tendon was tested. A fatigue load was applied at a load range of 60%, 70%, and 80% of the 40% ultimate load, which was obtained though a static test. The fatigue load was applied as a 1~3 Hz sine wave with 4 point loading setup. Fatigue load with maximum 1 million cycles was applied. The specimen applied with a load ranging between 40~60% did not show a fatigue failure until 1 million cycles. However, it was found that horizontal cracks in the direction of tendons were found and bond force between the tendon and concrete was degraded as the load cycles increased. This fatigue study showed that the prestressed concrete beam using FRP tendon was safe under a fatigue load within a service load range. Fatigue strength of the specimen with FRP and steel tendon after 1 million cycles was 69.2% and 59.8% of the prestressed concrete beam's static strength, respectively.

• Journal of the Korean Geotechnical Society
• /
• v.21 no.4
• /
• pp.51-63
• /
• 2005

Concrete pavement may suffer from material deterioration or structural problems, which lead to surface cracks and deflection of a concrete pavement. Degraded concrete pavement, when it is still under operation, should be recovered by an urgent maintenance to avoid the discontinued service leading to the significant traffic problems and economic loss. Seismic techniques are good tools to assess the structural integrity of concrete runway. It is because seismic techniques can evaluate engineering properties nondestructively and quickly and the evaluation can be extended to subgrade. In this study, a series of numerical simulations of stress-wave propagation were performed to verify feasibility of seismic techniques as an assessment tool. Based on the results of the numerical simulation, a framework of using seismic techniques was presented fur the nondestructive integrated assessment fur structural integrity of concrete runway. And the presented framework was applied to $\bigcirc\bigcirc$ concrete runway with surface cracks, which required urgent maintenance, to identify the causes of the surface cracks. The results obtained from the structural integrity assessment were compared with the measurements of the cores collected from the same runway for verification of the presented framework.

• The Journal of The Korea Institute of Intelligent Transport Systems
• /
• v.17 no.5
• /
• pp.143-150
• /
• 2018

With the rapid development of RF based high speed wireless communication technology, devices that can be applied to IoT networks based on RF bandwidth are rapidly spreading, nevertheless, the development speed of the RF communication is not possible to keep up with the spread of the RF band for wireless communication. In this situation, OWC technology that uses visible light source as a transmitter is attracting attention as a technology that can overcome the band exhaustion problem of RF based wireless communication technology. Although, due to the distortion of the LED illumination shape by camera exposure time and LED blinking period, the LED illumination detection rate is degraded and the RoI setting is inaccurate. In this paper, we propose an adaptive median filter applied LED illumination detection algorithm for low rate CamCom, it is possible to detect a clear RoI and LED illumination. This research will be able to play a role as a complementary material of RF based wireless communication technology efficiently.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.4
• /
• pp.13-16
• /
• 2013

A lot of various researches have been going on to use heat spreader for LED module. Nano porous aluminum anodic oxide (AAO) applied LED, which is produced from anodization, is easy and economically advantageous. Convensional LED module is consist of aluminum/adhesive/copper circuit. The polymer adhesive in this module is used as heat spreader. However the thermal emission of LED component is degraded because of low heat conductivity of polymer and also reliability of LED component is reduced. Therefore, AAO in this work was applied to heat spreader of LED module which has higher heat conductivity compare to polymer. Bonding strength between AAO and copper circuit was improved with Ti/Cu seed layer by copper sputtering process (DBC) before the bonding. And this copper circuit has been fabricated by electro plating method. Peel strength of AAO and copper circuit in this work showed range between 1.18~1.45 kgf/cm with anodizing process which is very suitable for high power LED application.