• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2004년도 추계학술발표대회 개요집
• /
• pp.43-45
• /
• 2004

Brazing between cemented carbides and steel for tool investigated by copper alloy brazing filler. Copper alloy filler was high liquidus temperature($990^{\circ}C$), therefor the shank(steel) occurred softening. Because brazing sample was necessary to heat treatment after brazing process. This experiment, influence of austenite time and purge temperature on heat treatment were investigated. As a result, these treatments obtained to high deflective strength In case of austenite time was short and purge temperature was low. Especially, nitride precipitated brazing layers was strongly influenced by the deflective strength.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.661-662
• /
• 2006

Development of recycling method at cemented carbide scraps was researched. Some properties of recycled cemented carbides were investigated. Recycled WC fine powder suffered the surface oxidation. Therefore it was necessary to be done by reduction treatment at 1073K-3.6ks under hydrogen atmosphere. When sintering condition at 1673K-3.6ks was treated under vacuum condition, it gained the deflective strength of about 90%, and gained hardness and sintering density about same value compared with commercial alloys. As a result, it was able to recycle only by 7 processes.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.551-554
• /
• 2002

As a general rule, the brazing process between cemented carbides and steel used by Silver (Ag) type brazing filler. The composition of Ag type filler were used Ag-Cu-Zn-Cd type filler mainly. But, the demand of Cadmium (Cd)-free in Ag type filler was raised recently. The reason why Cd-free in Ag brazing filler were occupied to vaporize as a CdO$_2$ when brazing process, because of Cd element was almost low boiling point of all Ag type filler elements. And, CdO$_2$ was a very harmful element for the human body. This experiment was developed Cd-freeing on Ag type filler that was used Indium (In) instead of Cd element. In this experiment, there were changed from 0 to 5% In addition in Ag brazing filler and investigated to most effective percentage of Indium. As a result, the change of In addition instead of Cd, there was a very useful element and obtained same property only 3% In added specimens compared to Cd 19% added specimens. These specimens were obtained same or more deflective strength. In this case, there were obtained 70 MPa over strength and wide brazing temperature range 650-800 C. A factor of deflective strength were influenced by composition and the shape of $\beta$ phase and between $\beta$ phase and cemented carbides interface. Indium element presented as $\alpha$ phase and non-effective factor directly, but it's occupied to solid solution hardening as a phase. $\beta$ phase were composed 84-94% Cu-Ni-Zn elements mainly. Especially, the presence of Ni element in interface was a very important factor. Influence of condensed Ni element in interface layer was increased the ductility and strength of brazing layer. Therefore, these 3% In added Ag type filler were caused to obtain a high brazing strength.

• 한국분말재료학회지
• /
• 제23권5호
• /
• pp.397-401
• /
• 2016

A lean alloy is defined as a low alloy steel with a minimum amount of the alloying element that maintains the characteristics of the sintered alloy. It is well known that the addition of elements such as Cr, P, Si, or Mn improves the mechanical characteristics of the alloy, but decreases the sinterability. The mother alloy is used to avoid an oxidation reaction with the alloying elements of Cr, P, Si or Mn. The purpose of this study is to determine the change in the mechanical properties of Fe-P-Mo and Fe-P-Mn alloys as a result of the addition of Si. In this article, the Fe-P-Mo and Fe-P-Mn alloys to which Si is added are compacted at $7.0g/cm^3$ and then sintered in $H_2-N_2$ at $1120^{\circ}C$. The P around the macropores and large grains reduces due to the formation of $SiO_2$ as the Si content increases. This is caused by the increase in strength owing to reducing intergranular fracture by suppressing the reaction with oxygen.

• 한국산학기술학회논문지
• /
• 제22권6호
• /
• pp.60-66
• /
• 2021

광물자원의 개발 적합성을 가늠하기 위하여 굴착 장비로 지반 굴착을 통하여 코어를 채취한다. 코어를 채취하기 위해서는 시추장비의 가장 앞부분에 굴착을 위한 비트를 설치하여 직접지반을 굴착한다. 굴착을 진행 중에 드릴 비트는 지반과 직적접인 마찰로 인하여 국부에 응력을 받게 된다. 또한 마찰로 인하여 드릴 비트의 파손이 발생할 수 있기 때문에 지반의 조건에 따라 적합한 비트의 사용이 요구된다. 따라서 본 논문에서는 시추장비에 일반적으로 사용되는 세립비트를 기준으로 현재 개발 되어있는 비트의 모델을 이용하여 각각 이종재료와 동종재료의 보강재를 삽입한 새로운 비트 모델의 형상 및 재질을 비교·분석하였다. 그리고 세립비트의 형상을 각각의 형태로 모델링하여 절삭에 필요한 경도 및 항절력을 이론적 수식을 이용하여 계산하여 적합성을 확인하였다. 또한 기존의 모델과 새로운 형태의 설계모델을 Amsys Program을 이용하여 FEM해석을 실시하여 응력과 변형률을 계산한 결과, 응력이 1.92E+7Pa, 변형율 9.6E-5m/m인 응력과 변형율이 최소화된 새로운 모델을 설계하였고 그에 따른 세립비트 형상 및 구조의 최적화 설계를 진행하였다.