• Korean Journal of Crystallography
• /
• v.5 no.2
• /
• pp.51-66
• /
• 1994

Y3Al5O2 and Nd: Y3Al5012 single crystals were grown by Czochralskl technique. The effectt of pulling rate rotation rate, and doping level of Nd3+ ion on the crystal quality were studied Various types of defects were analysed by photo-elastic effect and chemical etching method Finally, spectroscopic and laser poputies of grown crystal were measured. Optirmum pulling rate for good quality was dependant on the doping level of Nd3+ ion. It was found that the suitable pulling rates for pure Y3Al5O12 for 3.0∼3.5 a/o Nd3+ ion doped Y3Al5012 and for more than 40 a/o Nd3+ ion doped Y3Al5012 were 2∼4mm/hr, 0.6∼0.5mm/hr, and less than 0.4mm/hr respectively. Solid-liquid interface was convex at the rotation rate of 27∼60rpm, and concave at the rotation rate of 80∼100rpm. Growth axis was confired to <111> direction and lattice parameter was measured to 12.017A. Core (211) facets,striations, inclusions of metal particles, dislocations and optical inhonngeneities were detected. Four level laser transition of Nd3+ion in YIAls012 single crystal were identified by the spectroscopic measurements. Laser rod with tam diameter and 63mm length was fabricated from grown Nd3+ Y3Al5012 sin91e crystals. 1.8lJ of lasing threshould and 0.49% of soope efficiency were measured by the Pulsed laser action.

• Journal of Sensor Science and Technology
• /
• v.9 no.5
• /
• pp.341-349
• /
• 2000

CsI(Br) single crystals doped with 1, 3, 5 or 10 mole% $Br^-$ ions, as an activator, were grown by Czochralski method. The lattice structure of grown CsI(Br) single crystal was bcc and its lattice constant was $4.568\;{\AA}$. The absorption edge of the CsI(Br) single crystals was observed at 243 nm. The spectral range of the luminescence excited by 243 nm of wavelength was $300{\sim}600\;nm$, and its peak emission appeared at 440 nm. The luminescence intensity was maximum when CsI(Br) was doped with 3 mole % $Br^-$ ions. The energy resolutions of the CsI(Br) scintillator doped with 3 mole % $Br^-$ ions were 15.0% for $^{137}Cs$(662 keV), 13.1% for $^{54}Mn$(835 keV), and 18.0% and 6.3% for $^{22}Na$(511 keV and 1275 keV), respectively. The decay curves had fast and slow components, and the fast component was about 41 ns independent on the concentration of the $Br^-$ ions. The time resolution of CsI(Br) scintillators decreased with increasing of the concentration of $Br^-$ ions.