• Corrosion Science and Technology
• /
• v.9 no.1
• /
• pp.34-38
• /
• 2010

Electrochemical study on cut edge corrosion of prepainted Zn coated (GI) and 55%Al-Zn coated (GL) steels has been performed in wet-dry cyclic conditions. Maximum width of delaminated polymer coating from the cut edge for GI and GL specimens was evaluated under wet-dry cyclic conditions. The cyclic tests were carried out for 1000 h by changing of relative humidity, where the salt of NaCl was deposited on the specimen every 48 h. The cut edge corrosion test under NaCl deposit indicated that the delamination of the GL specimen progresses at a higher rate than the GI. The electrochemical corrosion monitoring was also performed under condition of alternate exposure to immersion in NaCl solution and drying at 60%RH and $25^{\circ}C$. On the basis of the results of the delamination tests and electrochemical measurements, the mechanism of cut edge corrosion for GI and GL were discussed.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.4
• /
• pp.136-143
• /
• 2016

There are various method for evaluating the durability life of concrete structures due to salt damage. The best way is to perform a corrosion test for a rebar embedded in concrete specimen was exposure to marine environment. However, this method has the disadvantage that it takes a long period of time. Also, accelerated corrosion test which was complemented complements the time-consuming weakness is limited to apply because it could not reveal a correlation between long-term exposure test. Accordingly, the purpose of this study is to derive a correlation coefficient between cycle drying-wetting accelerated corrosion test and long-term exposure test. Corrosion initiation time was measured in four types of concrete samples, i.e., two samples mixed with fly ash(FA) and blast furnace slag(BS), and the other two samples having two water/cement ratio(W/C = 0.6, 0.35) without admixture(OPC 60 and OPC 35). The accelerated corrosion test was carried out by two case, i.e., one is a cyclic drying-wetting method(case 1), and the other is a artificial seawater ponding test method(case 2). Whether corrosion occurs, it was measures using half-cell potential method. The results indicated that case 1 is to accelerated the corrosion of rebar about 24~36% as compared with case 2, then the corrosion of rebar embedded in concrete occurred according to the order of OPC60, FA, BS, OPC35. Correlation coefficient between accelerated corrosion test and long-term exposure test, case 1 is 4.23 to 5.42, and case 2 is 6.54 to 7.82.

• Computers and Concrete
• /
• v.15 no.2
• /
• pp.183-198
• /
• 2015

Chloride ingress implies a complex interaction between physical and chemical process, in which heat, moisture and chloride ions transport through concrete cover. Meanwhile, reinforced concrete structure itself undergoes evolution due to variation in temperature, relative humidity and creep effects, which can potentially change the deformation and trigger some micro-cracks in concrete. In addition, all of these process show time-dependent performance with complex interaction between structures and environments. In the present work, a time-dependent behavior of chloride transport in reinforced concrete beam subjected to flexural load is proposed based on the well-known section fiber model. The strain state varies because of stress redistribution caused by the interaction between environment and structure, mainly dominated by thermal stresses and shrinkage stress and creep. Finally, in order to clear the influence of strain state on the chloride diffusivity, experiment test were carried out and a power function used to describe this influence is proposed.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.32 no.6A
• /
• pp.427-435
• /
• 2012

In order to evaluate the effects of exposure conditions on the resistance to sulfate attack of normal and blended cement mortars, several mechanical characteristics of the mortars such as expansion, strength and bulk density were regularly monitored for 52 cycles under sodium sulfate attack. The mortar specimens were exposed to 3 different types of exposure conditions; 1) continuous full immersion(Exposure A), continuous half-immersion(Exposure B) and cyclic wetting-drying(Exposure C). Experimental results indicated that the maximum deterioration was noted in OPC mortar specimens subjected to Exposure B, showing the wide cracks in the portions where attacking solution is adjacent to air. Additionally, the beneficial effect of ground granulated blast-furnace slag and silica fume was clearly observed showing a superior resistance against sodium sulfate attack, because of its lower permeability and densified structure. Thus, it is suggested that when concrete made with normal cement is exposed to sulfate environment, proper considerations on the exposure conditions should be taken.