• 한국생산제조학회지
• /
• 제7권1호
• /
• pp.22-33
• /
• 1998

A continuum analysis of the evolution of plasticity and Bauschinger effect in a short fiber reinforced metal matrix composite, based on the FEM solution for a single fiber model has been performed to investigate the strengthening behavior. The evolution of matrix field quantities during one cycle of fully reversed loading have been examined in detail. The results indicate that the role of constrained matrix flow in generating different levels of matrix triaxiality during forward and reversed loading provides an important contribution to the developement of the Bauschinger effect in the metal matrix composite. Therefore, even when the plastic flow of the matrix material follows on isotropic hardening behavior, the Bauschinger effect is predicted for the composite material.

• Structural Engineering and Mechanics
• /
• 제30권6호
• /
• pp.665-678
• /
• 2008

The beams components subjected to the loading such as axial, bending and cyclic thermal loads were studied in this research. The used constitutive equations are those of elasto-plasticity coupled to ductile and/or creep damage. The nonlinear kinematic hardening behavior was considered in elastoplasticity modeling. The unified damage law proposed for ductile failure and fatigue by the author of Sermage et al. (2000) and Kachanov's creep damage model applied to cyclic creep and low cycle fatigue of beams. Based on the results of the analysis, the shakedown limit loads were determined through the calculation of the residual strains developed in the beam analysis. The iterative technique determines the shakedown limit load in an iterative manner by performing a series of full coupled elastic-plastic and continuum damage cyclic loading modeling. The maximum load carrying capacity of the beam can withstand, were determined and imposed on the Bree's interaction diagram. Comparison between the shakedown diagrams generated by or without creep and/or ductile damage for the loading patterns was presented.

• 한국연소학회:학술대회논문집
• /
• 한국연소학회 2005년도 제31회 KOSCO SYMPOSIUM 논문집
• /
• pp.78-84
• /
• 2005

The development of eco-friendly low pressure carburizing system with high pressure gas quenching (LPC_GQ, 500kg/charge) led to new stage in the fundamental case-hardening treatments. This is due to its ability to provide tighter tolerances on the carburizing process with notable reductions in distortion of the carburized and hardened workpiece. This system is characteristics by high uniformity and reproducibility of heat treatment results, absence of an intergranular oxidation layer, carburizing of complex shapes, reduced cycle time, low operating costs, simplified production, eliminate post washing, and reduced grinding costs.

• 열처리공학회지
• /
• 제19권5호
• /
• pp.262-269
• /
• 2006

The development of eco-friendly low pressure carburizing system with high pressure gas quenching(LPC-GQ, 500kg/charge) led to new stage in the fundamental case-hardening treatments. This is due to its ability to provide tighter tolerances on the carburizing process with notable reductions in distortion of the carburized and hardened workpiece. This system is characteristics by high uniformity and reproducibility of heat treatment results, absence of an intergranular oxidation layer, carburizing of complex shapes, reduced cycle time, low operating costs, simplified production, eliminate post washing, and reduced grinding costs.

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 2005년도 춘계학술발표회
• /
• pp.465-466
• /
• 2005

(1) SA508 Gr.1a LAS exhibited a moderate cyclic hardening in $310^{\circ}C$ low DO water. A saturation stage or a slightly secondary hardening was occurred with decreasing strain amplitude. (2) Fatigue life of SA508 Gr.1a LAS decreases a little with decreasing strain rate in $310^{\circ}C$ low DO water.

• 열처리공학회지
• /
• 제31권1호
• /
• pp.18-23
• /
• 2018

In this study, low cyclic fatigue test was carried out at room temperature condition for rolled STS304 steel. The results of this study show that rolled STS304 steel has excellent static tensile strength and fatigue characteristics. The relationship between plastic strain range and fatigue life was examined using the triangular wave in order to predict the low cycle fatigue life of rolled STS304 steel by Coffin-Manson equation. Cyclic behavior of rolled STS304 steel was characterized by cyclic hardening with increasing number of cycle through the Hysteresis loop analysis and cyclic response of maximum stress versus number of cycles. It is found that the plastic deformation energy consumed per cycle is reduced by calculating the area of the hysteresis loop.

• 한국재료학회지
• /
• 제25권5호
• /
• pp.221-225
• /
• 2015

In-situ neutron diffraction has been employed to examine the effect of strain path on lattice strain evolution during monotonic and cyclic tension in an extruded Mg-8.5wt.%Al alloy. In the cyclic tension test, the maximum applied stress increased with cycle number. Lattice strain data were acquired for three grain orientations, characterized by the plane normal to the stress axis. The lattice strain in the hard {10.0} orientation, which is unfavorably oriented for both basal slip and {10.2} extension twinning, evolved linearly throughout both tests during loading and unloading. The {00.2} orientation exhibited significant relaxation associated with {10.2} extension twinning. Coupled with a linear lattice strain unloading behavior, this relaxation led to increasingly compressive residual strains in the {00.2} orientation with increasing cycle number. The {10.1} orientation is favorably oriented for basal slip, and thus showed a soft grain behavior. Microyielding occurred in the monotonic tension test and in all cycles of the cyclic test at an applied stress of ~50 MPa, indicating that strain hardening in this orientation was not completely stable from one cycle to the next. The lattice strain unloading behavior was linear in the {10.1} orientation, leading to a compressive residual strain after every cycle, which, however, did not increase systematically from one cycle to the next as in the {00.2} orientation.

• Journal of Welding and Joining
• /
• 제2권1호
• /
• pp.49-57
• /
• 1984

The influence of weld defect, residual stress and microstructure on the Low Cycle Fatigue(L. C. F.) behaviour of AISI 304L austenitic stainless steel weldment has been studied. The specimens were welded by shielded metal are welding process, post weld heat treated(PWHT) at 900.deg.C for 1.5hrs, and tested under total strain controlled condition at room temperature. The results of the experiment showed that weld defect affected the L.C.F. behaviour of weldment deleteriously compared to the residual stress or microstructure, and it reduced the L.C.F. life about 70-80%. The PWHT exhibited beneficial effect on the L.C.F. behaviour and increased the L.C.F. life about 120%. This enhancement by PWHT was attributed to the removal of residual stress and recovery of weld metal ductility. The cyclic stress flow of as welded specimens showed intermediate cyclic softening, whereas those of heat treated specimens showed continuous cyclic hardening, and this difference was explained in terms of the residual stress removal and dislocation behaviour. Scanning electron microscopy studies of fatigue fracture surface showed that weld defects of large size and near weld surface were detrimental to the L.C.F. behaviour of weldment.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집A
• /
• pp.591-596
• /
• 2001

The purpose of this study is to examine the change of half value breadth and residual stress during fatigue process in S45C Steel by X-ray diffraction. For S45C Steel, the relationship between the change in fatigue damage of the specimen and the half value breadth, and residual stress of X-ray diffraction profiles during the fatigue processes has been investigated. The half value breadth(HVB) decreases in he early period of fatigue cycle. The change of HVB is relation to cyclic work hardening. In $10{\sim}20%$ of ratio of fatigue life, the change in the half value breadth is not marked. During fatigue process, the residual stress is changed with fatigue cycle increasing.

• 열처리공학회지
• /
• 제24권2호
• /
• pp.92-98
• /
• 2011

The influence of the cooling condition after solution treatment on the high temperature fatigue resistance of 23Cr-26Ni heat resistant steel was investigated. Two different cooling conditions were applied to the steel after solution treatment at $1200^{\circ}C$ for 3 hours. One specimen was water quenched immediately after the solution treatment. The other one was furnace cooled at a rate of $0.5^{\circ}C/min$ down to $750^{\circ}C$ after the solution treatment. Then, both specimens were aged at $750^{\circ}C$ for 5 hours. Under two different heat treatment conditions, the low cycle fatigue (LCF) test was performed at $600^{\circ}C$ and room temperature (RT). Only cyclic hardening continued from the beginning until fracture at all strain amplitudes during LCF at $600^{\circ}C$. This phenomenon was attributed to the increase in the dislocation density due to cyclic deformation, which resulted in the interaction between the newly created dislocations and precipitates. Cyclic hardening followed by saturation and cyclic softening was observed at RT. Cyclic softening was attributed to the dislocation annihilation rate exceeding the dislocation generation rate. Other probable factor for cyclic softening was some cavities formed around grain boundaries after 20 cycles. WQ and FC have a similar LCF behavior at RT and $600^{\circ}C$ as shown in the cyclic stress response curves.