• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.143-146
• /
• 1999

This study is intended to investigate the properties of expansion of concrete under various curing environment with expansive additives. In construction field, expansive additives, which are anaiable to prevent from the diverse cracks caused by drying shrinkage are not expected to accomplish the expantion we expected because of both the absence of the know ledge change, loss of weight and dynamic of elasticty under various unit contents of expansive additives and curing condtion.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.11a
• /
• pp.553-556
• /
• 2003

This study is analyzed about the factor of adhesive strength characteristics, curing time, asphalt application, test temperature which are liquid waterproofing membrane of rubber-asphalt and chloroprene-rubber type for concrete bridge deck. According to the results, curing time is shorter, adhesive strength is less in chloroprene-rubber type. And also chloroprene-rubber and rubber-asphalt type are showed high adhesive strength in low temperature.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.04a
• /
• pp.861-865
• /
• 2000

During the placement of concrete in cold weather, there are serious problems due to frozen concrete in the early stage. These adverse effects prevent the hardening of concrete. There are special mixing, handling, placement and crying to minimize problems. Heat crying and sheet curing have been used in crying steps in order to reduce problems. However, these curing methods are not efficient because it is hard to obtain the good quality and strength of concrete, and moreover, it needs additional works for curing. In this study, we evaluate the application of cold weather concrete by the dose antifreezing admixture in concrete mix design. Because it is easy to handle inconstruction site and improve the quality of concrete. As the result of this paper is to present a successful case for the practical use of cold weather concrete.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2019.11a
• /
• pp.27-28
• /
• 2019

In this study, the characteristics of compressive strength of ultra high strength concrete supplied with moisture from outside by vacuum water absorbing curing method were investigated. Specimens were prepared by replacing the binder(Silifa fume and GGBS) by 25 wt% with respect to the weight of cement at W/B 0.16. Each specimen was subjected to water Vacuum absorbing curing time 0 min, 30 min, 60 min, 90 min and 120 minutes immediately after the demolding. Curing was performed at $20^{\circ}C$ Air-dry curing, $90^{\circ}C$ steam curing, $90^{\circ}C$ steam curing and $180^{\circ}C$ autoclave curing. Experimental results showed that water absorbing degree increased with increasing water absorbing curing time, and BS25 sample had higher water absorbing degree than SF25 sample at same time. Compressive strength tended to increase up to about 40% in water absorbing degree, but compressive strength decreased again in water absorbing more than 40%.

• Explosives and Blasting
• /
• v.16 no.4
• /
• pp.18-28
• /
• 1998

Effects of blasting vibrations on curing concrete have not been well studied. As a result, unreasonable and strong blasting vibration constraints have been placed on blasting when it occur in the vicinity of curing concrete. To study the effects of blasting on curing concrete blocks of $33.3{\times}27.7{\times}16.2cm$ were molded and placed on the quarry. Several sets of concrete blocks were subjected separately to peak vibrations of 0.25, 0.5, 1.0, 5.0 and 10cm/sec. The impulses of blasting vibrations were applied with thirty-minute intervals. Along with unvibrated concrete blocks, the vibrated concrete samples cored with 60.3mm in diameter were measured for elastic moduli, sonic velocity and uniaxial compressive strength. Test results can be summarized as follows; 1. The blasting vibrations between 6 and 8 hours after pour generally lowered on the uniaxial compressive strength of the concrete. 2. A low blasting vibration of 0.25cm/sec did not affect the uniaxial compressive strength. As the magnitude of the blasting vibration increases, compressive strength of concrete is decreased. 3. Physical properties of the P-wave velocity, Young’s modulus, and Poisson's ratio showed a weakly decreasing trend in the concrete blocks vibrated between 6 and 8 hours after pour.

• Tunnel and Underground Space
• /
• v.5 no.2
• /
• pp.134-143
• /
• 1995

Effects of blasting vibrations on curing concrete have not been well studied. As a result, unreasonable and strong blasting vibration constraints have been placed on blasting when it occurs in the vicinity of curing concrete. To study the effects of blasting on curing concrete blocks of 33.3X27.7X16.2 cm were molded and placed on the quarry. Several sets of concrete blocks were subjected separately to peak vibrations of 0.25, 0.5. 1.0, 5.0, and 10cm/sec. The impulses of blasting vibrations were applied with thirty-minute intervals. Along with unvibrated concrete blocks, the vibrated concrete samples cored with 60.3 mm in diameter were measured for elastic moduli, sonic velocity and uniaxial compressive strength. Test results can be summarized as follows; 1. The blasting vibrations between 6 and 8 hours after pour generally lowered on the uniaxial compressive strength of the concrete. 2. A low blasting vibration of 0.25 cm/sec did not affect the uniaxial compressive strength. As the magnitude of the blasting vibration increases, compressive strength of concrete is decreased. 3. Physical properties of the P-wave velocity, Young's modulus, and Poisson's ratio showed a weakly decreasing trend in the concrete blocks vibrated between 6 and 8 hours after pour.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.11a
• /
• pp.289-292
• /
• 2003

CFRD face slab concrete has a much capability to occur crack due to drying shrinkage and vibrator compaction etc. Because crack of concrete induces structural problem and decrease durability of concrete, it is need to reduce crack of concrete. In the experimental study it was analyzed that the effect of curing of concrete and compaction on CFRD face slab concrete. As a results, it was found that control of construction condition into curing of concrete and compaction improved on construction efficiency of face slab concrete.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.1
• /
• pp.33-40
• /
• 2018

Currently, in South Korea, because of reducing the construction period or treating wasted water, there are some cases of missing wet curing for concrete structure even though for high strength concrete. This air curing conditions is considered to cause increased possibility of compressive strength decrease, and increasing drying or autogenous shrinkages. As a solution of shrinkage of concrete, The authors' research team conducted the research on improving durability of concrete with decreasing autogenous shrinkage by adding the oil or fat to induce the saponification. Therefore, in this research, the influence of curing method on compressive strength, shrinkage on evaporation rate of high strength mortar including high volume supplementary cementitious materials (SCMs) was evaluated depending on various curing methods such as air curing, drying after painting emulsified refined cooking oil (ERCO), and drying after 7 and 28 days' wet curing. The experimental result showed the air curing method caused approximately 50% of decreased compressive strength and 1.9 times of increased shrinkage rather than the 28-day-wet curing method, thus it was known that the wet curing significantly influences on performance of high strength mortar using high volume SCMs. However, the ERCO painting curing caused decreased performance of concrete rather than drying after 7 days curing while it caused improved performance of concrete than entire period air curing.

• Korean Journal of Agricultural Science
• /
• v.18 no.2
• /
• pp.140-147
• /
• 1991

This paper was performed to obtain the data applied to use of synthetic lightweight aggregate concrete affected by alkali silica reaction. The results obtained were summarized as follows : 1. The expansion of each type concrete was increased with increase of curing age, respectively. Also, at the curing age 90 days, the rate of expansion of type A, B, C and D concrete was increased 0.173%, 0.575%, 0.230% and 0.680%, respectively. Specially, the rate of expansion of type D concrete was shown 3.93 times higher than the type A concrete. The cracks width were increased with increase of expansion and at the 0.680% expansion, the maximum width was shown 0.5 mm. 2. The dynamic modulus of elasticity of each type concrete was increased with increase of curing age, respectively. At the curing age 30 days, the highest dynamic modulus of elasticity was showed at each type concrete, respectively. But, it was gradually decreased with increase of curing age at those concrete, respectively. Also, at the curing age A, B, C and D concrete was increased 24.3%, 33.7%, 28.1% and 37.0%, respectively. The rate of loss in type D concrete was shown 1.52 times higher than the type A concrete. 3. The ultrasonic pulse velocity of each type concrete was increased with increase of curing age, respectively. At the curing age 30 days, the highest ultrasonic pulse velocity was showed at each type concrete, respectively. But, it was gradually decreased with increase of curing age at those concrete, respectively. Also, at the curing age 90 days, the percentage loss of ultrasonic pulse velocity of type A, B, C and D concrete was increased 6.4%, 8.7%, 8.5% and 14.2%, respectively. The rate of loss in type D concrete was shown 2.21 times higher than the type A concrete. 4. The relation between dynamic modulus of elasticity and ultrasonic pulse velocity was highly significant. The dynamic modulus of elasticity was increased with increase and decreased with decrease of ultrasonic pulse velocity. Also, the decreasing rate of the dynamic modulus of elasticity was shown 2-7 times higher than the ultrasonic pulse velocity at each age, respectively. 5. The dynamic modulus of elasticity and ultrasonic pulse velocity were decreased with increase of expansion, and the decreasing rates were increased with increase of curing age. The increasing rate of expansion was shown higher than the decreasing rate of dynamic modulus and ultrasonic pulse velocity.

• Advances in concrete construction
• /
• v.5 no.3
• /
• pp.271-288
• /
• 2017

This paper aims to investigate the effects of replacing cement with ground granulated blast furnace slag (GGBFS) in self compacting concrete in the fresh and hardened state. The performance of SCC in moderate climate is well investigated but few studies are available on the effect of hot environment. In this paper, the effect of initial water-curing period and curing conditions on the performance of SCC is reported. Cement was substituted by GGBFS by weight at two different levels of substitution (15% and 25%). Concrete specimens were stored either in a standard environment (T=$20^{\circ}C$, RH=100%) or in the open air in North Africa during the summer period (T=35 to $40^{\circ}C$; R.H=50 to 60%) after an initial humid curing period of 0, 3, 7 or 28 days. Compressive strength at 28 and 90 days, capillary absorption, sorptivity, water permeability, porosity and chloride ion penetration were investigated. The results show that the viscosity and yield stress are decreased with increasing dosage of GGBFS. The importance of humid curing in hot climates in particular when GGBFS is used is also proved. The substitution of cement by GGBFS improves SCC durability at long term. The best performances were observed in concrete specimens with 25% GGBFS and for 28 days water curing.